CN104927526A - Water-borne acrylic amino baking varnish special for intelligent ashtray metal shell - Google Patents
Water-borne acrylic amino baking varnish special for intelligent ashtray metal shell Download PDFInfo
- Publication number
- CN104927526A CN104927526A CN201510396919.1A CN201510396919A CN104927526A CN 104927526 A CN104927526 A CN 104927526A CN 201510396919 A CN201510396919 A CN 201510396919A CN 104927526 A CN104927526 A CN 104927526A
- Authority
- CN
- China
- Prior art keywords
- water
- parts
- borne acrylic
- metal shell
- baking vanish
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to water-borne acrylic amino baking varnish special for an intelligent ashtray metal shell. The water-borne acrylic amino baking varnish comprises, by weight, 15-17 parts of water, 0.5-0.7 part of dispersing agents, 18-20 parts of organic pigments, 40-50 parts of water-borne acrylic resin, 4.0-5.5 parts of amino resin, 7-9 parts of propanediol butyl ether, 4-6 parts of isopropanol, 4.1-4.3 parts of catalyst, 0.2-0.4 part of defoamer, 0.4-0.6 part of flatting agents, 1.1-1.3 parts of adhesive force improver and 0.8-1.2 parts of PH modifier. The performance of the water-borne acrylic amino baking varnish is changed by adjusting the ratio between the water-borne acrylic resin and the amino resin, the prepared water-borne acrylic amino baking varnish special for the intelligent ashtray metal shell has a reasonable hardness value, good impact resistance, good flexibility, good water resistance and good alcohol resistance and large adhesive force, and therefore the service life of the water-borne acrylic amino baking varnish is prolonged.
Description
Technical field
The present invention relates to a kind of baking vanish, specifically the special-purpose aqueous acrylic-amino baking vanish of a kind of Intelligent ashtray metal shell.
Background technology
Baking vanish, be that one emerging in Furniture manufacture is sprayed paint making method (technique), its method is: in the substrate being polished to certain degree of roughness (normally high density plate material), sprays some layers of paint, and shapes through high bake.This technique is higher to paint requirements at present, and color developing is good.The furniture items such as baking finish process is widely used in moving door, cabinet desk, also start day by day to penetrate in other material surface complete processing.Baking vanish is divided into two large classes, and a class low temperature baking vanish solidification value is 90 °-100 °, and an other class is just called high temperature baking vanish, and its solidification value is 230 °-240 °.
Water soluble acrylic acid amino-stoving varnish owing to having high gloss, hardness, Bao Sebao light, the advantage such as heat-resisting become important industrial coating, be widely used in the goods industries such as automobile, household electrical appliances, pail pack, bike, sewing machine, stapler, bookshelf, play metal finishing and provide protection, a lot of Intelligent ashtray can be seen in existing market, what the metal shell above it sprayed is exactly water soluble acrylic acid amino-stoving varnish, but along with the continuous growth of duration of service, understand some above metal shell on Intelligent ashtray and impact print, and meet waterborne spray paint and easily come off, therefore existing water soluble acrylic acid amino-stoving varnish is in hardness, shock-resistance, snappiness, sticking power, Shortcomings in water tolerance and alcohol resistance, cause the existing water soluble acrylic acid amino-stoving varnish life-span shorter, and the proportioning of water-borne acrylic resin and aminoresin is the hardness affecting paint film, shock-resistance, snappiness, the basic reason of the multiple performance such as water tolerance and alcohol resistance.
Summary of the invention
For above-mentioned technical problem, the invention provides a kind of have good water-borne acrylic resin and aminoresin proportioning, preparation method is easy, the special-purpose aqueous acrylic-amino baking vanish of Intelligent ashtray metal shell that preparation technology is easy, there is rational hardness value, good shock-resistance, snappiness, water tolerance and alcohol resistance, higher sticking power, thus the work-ing life of improving Intelligent ashtray metal shell.
Technical problem to be solved by this invention realizes by the following technical solutions:
The special-purpose aqueous acrylic-amino baking vanish of a kind of Intelligent ashtray metal shell, this baking vanish is made up of the component of following weight part: water 15-17 part, dispersion agent 0.5-0.7 part, pigment dyestuff 18-20 part, water-borne acrylic resin 40-50 part, aminoresin 4.0-5.5 part, propandiol butyl ether 7-9 part, Virahol 4-6 part, catalyzer 4.1-4.3 part, defoamer 0.2-0.4 part, flow agent 0.4-0.6 part, adhesion promoter 1.1-1.3 part and PH conditioning agent 0.8-1.2 part.
As a preferred embodiment of the present invention, described catalyzer is aqueous isopropanol.
A preparation method for the special-purpose aqueous acrylic-amino baking vanish of Intelligent ashtray metal shell, bag following steps:
(1), by the water of 40%, dispersion agent, 30% water-borne acrylic resin put into agitation vat successively, stirrer stir 5-15 minute;
(2), add pigment dyestuff, 35% defoamer, by sand mill, fineness is milled to less than 25 μm, obtained aqueous color paste;
(3), by the water-borne acrylic resin of 70%, aminoresin, propandiol butyl ether, Virahol, catalyzer, flow agent, adhesion promoter, 60% water and defoamer join in clean paint mixing cylinder successively, with high speed dispersor dispersion 5-10 minute, then add PH conditioning agent adjustment pH value;
(4), in paint mixing cylinder, add aqueous color paste obtained in step (2), high speed dispersor dispersion 15-25 minute, then obtains required baking vanish with after 180 order filter-cloth filterings.
The invention has the beneficial effects as follows: the present invention is by the performance by regulating the proportioning of water-borne acrylic resin and aminoresin to change water soluble acrylic acid amino-stoving varnish, the Intelligent ashtray metal shell special-purpose aqueous acrylic-amino baking vanish prepared has rational hardness value, good shock-resistance, snappiness, water tolerance and alcohol resistance, higher sticking power, thus the work-ing life of improving Intelligent ashtray metal shell.
Embodiment
The technique means realized to make the present invention and creation characteristic are easy to understand, and set forth further below to the present invention.
Embodiment one:
The special-purpose aqueous acrylic-amino baking vanish of a kind of Intelligent ashtray metal shell, this baking vanish is made up of the component of following weight part: 15 parts, water, dispersion agent 0.5 part, pigment dyestuff 18 parts, water-borne acrylic resin 40 parts, 5.5 parts, aminoresin, propandiol butyl ether 7 parts, Virahol 4 parts, catalyzer 4.1 parts, defoamer 0.2 part, flow agent 0.4 part, adhesion promoter 1.1 parts and PH conditioning agent 0.8 part.
Described catalyzer is aqueous isopropanol.
A preparation method for the special-purpose aqueous acrylic-amino baking vanish of Intelligent ashtray metal shell, bag following steps:
(1), by the water of 40%, dispersion agent, 30% water-borne acrylic resin put into agitation vat successively, stirrer stirs 5 minutes;
(2), add pigment dyestuff, 35% defoamer, by sand mill, fineness is milled to less than 25 μm, obtained aqueous color paste;
(3), by the water-borne acrylic resin of 70%, aminoresin, propandiol butyl ether, Virahol, catalyzer, flow agent, adhesion promoter, 60% water and defoamer join in clean paint mixing cylinder successively, disperse 5 minutes with high speed dispersor, then add PH conditioning agent adjustment pH value;
(4), in paint mixing cylinder, add aqueous color paste obtained in step (2), high speed dispersor disperses 15 minutes, then obtains required baking vanish with after 180 order filter-cloth filterings.
Embodiment two:
The special-purpose aqueous acrylic-amino baking vanish of a kind of Intelligent ashtray metal shell, this baking vanish is made up of the component of following weight part: 15.5 parts, water, dispersion agent 0.55 part, pigment dyestuff 18.5 parts, water-borne acrylic resin 44 parts, 5.0 parts, aminoresin, propandiol butyl ether 7.5 parts, Virahol 4.5 parts, catalyzer 4.15 parts, defoamer 0.25 part, flow agent 0.45 part, adhesion promoter 1.15 parts and PH conditioning agent 0.9 part.
Described catalyzer is aqueous isopropanol.
A preparation method for the special-purpose aqueous acrylic-amino baking vanish of Intelligent ashtray metal shell, bag following steps:
(1), by the water of 40%, dispersion agent, 30% water-borne acrylic resin put into agitation vat successively, stirrer stirs 7 minutes;
(2), add pigment dyestuff, 35% defoamer, by sand mill, fineness is milled to less than 25 μm, obtained aqueous color paste;
(3), by the water-borne acrylic resin of 70%, aminoresin, propandiol butyl ether, Virahol, catalyzer, flow agent, adhesion promoter, 60% water and defoamer join in clean paint mixing cylinder successively, disperse 7 minutes with high speed dispersor, then add PH conditioning agent adjustment pH value;
(4), in paint mixing cylinder, add aqueous color paste obtained in step (2), high speed dispersor disperses 17 minutes, then obtains required baking vanish with after 180 order filter-cloth filterings.
Embodiment three:
The special-purpose aqueous acrylic-amino baking vanish of a kind of Intelligent ashtray metal shell, this baking vanish is made up of the component of following weight part: 16 parts, water, dispersion agent 0.6 part, pigment dyestuff 19 parts, water-borne acrylic resin 46 parts, 4.7 parts, aminoresin, propandiol butyl ether 8 parts, Virahol 8 parts, catalyzer 4.2 parts, defoamer 0.3 part, flow agent 0.5 part, adhesion promoter 1.2 parts and PH conditioning agent 1.0 parts.
Described catalyzer is aqueous isopropanol.
A preparation method for the special-purpose aqueous acrylic-amino baking vanish of Intelligent ashtray metal shell, bag following steps:
(1), by the water of 40%, dispersion agent, 30% water-borne acrylic resin put into agitation vat successively, stirrer stirs 9 minutes;
(2), add pigment dyestuff, 35% defoamer, by sand mill, fineness is milled to less than 25 μm, obtained aqueous color paste;
(3), by the water-borne acrylic resin of 70%, aminoresin, propandiol butyl ether, Virahol, catalyzer, flow agent, adhesion promoter, 60% water and defoamer join in clean paint mixing cylinder successively, disperse 8 minutes with high speed dispersor, then add PH conditioning agent adjustment pH value;
(4), in paint mixing cylinder, add aqueous color paste obtained in step (2), high speed dispersor disperses 20 minutes, then obtains required baking vanish with after 180 order filter-cloth filterings.
Embodiment four:
The special-purpose aqueous acrylic-amino baking vanish of a kind of Intelligent ashtray metal shell, this baking vanish is made up of the component of following weight part: water 15-17 part, dispersion agent 0.65 part, pigment dyestuff 19.5 parts, water-borne acrylic resin 48 parts, 4.3 parts, aminoresin, propandiol butyl ether 8.5 parts, Virahol 5.5 parts, catalyzer 4.25 parts, defoamer 0.35 part, flow agent 0.55 part, adhesion promoter 1.25 parts and PH conditioning agent 1.1 parts.
Described catalyzer is aqueous isopropanol.
A preparation method for the special-purpose aqueous acrylic-amino baking vanish of Intelligent ashtray metal shell, bag following steps:
(1), by the water of 40%, dispersion agent, 30% water-borne acrylic resin put into agitation vat successively, stirrer stirs 12 minutes;
(2), add pigment dyestuff, 35% defoamer, by sand mill, fineness is milled to less than 25 μm, obtained aqueous color paste;
(3), by the water-borne acrylic resin of 70%, aminoresin, propandiol butyl ether, Virahol, catalyzer, flow agent, adhesion promoter, 60% water and defoamer join in clean paint mixing cylinder successively, disperse 9 minutes with high speed dispersor, then add PH conditioning agent adjustment pH value;
(4), in paint mixing cylinder, add aqueous color paste obtained in step (2), high speed dispersor disperses 23 minutes, then obtains required baking vanish with after 180 order filter-cloth filterings.
Embodiment five:
The special-purpose aqueous acrylic-amino baking vanish of a kind of Intelligent ashtray metal shell, this baking vanish is made up of the component of following weight part: 17 parts, water, dispersion agent 0.7 part, pigment dyestuff 20 parts, water-borne acrylic resin 50 parts, 4.0 parts, aminoresin, propandiol butyl ether 9 parts, Virahol 6 parts, catalyzer 4.3 parts, defoamer 0.4 part, flow agent 0.6 part, adhesion promoter 1.3 parts and PH conditioning agent 1.2 parts.
Described catalyzer is aqueous isopropanol.
A preparation method for the special-purpose aqueous acrylic-amino baking vanish of Intelligent ashtray metal shell, bag following steps:
(1), by the water of 40%, dispersion agent, 30% water-borne acrylic resin put into agitation vat successively, stirrer stirs 15 minutes;
(2), add pigment dyestuff, 35% defoamer, by sand mill, fineness is milled to less than 25 μm, obtained aqueous color paste;
(3), by the water-borne acrylic resin of 70%, aminoresin, propandiol butyl ether, Virahol, catalyzer, flow agent, adhesion promoter, 60% water and defoamer join in clean paint mixing cylinder successively, disperse 10 minutes with high speed dispersor, then add PH conditioning agent adjustment pH value;
(4), in paint mixing cylinder, add aqueous color paste obtained in step (2), high speed dispersor disperses 25 minutes, then obtains required baking vanish with after 180 order filter-cloth filterings.
The contrast of Intelligent ashtray metal shell special-purpose aqueous acrylic-amino baking vanish in each performance that above-described embodiment one, embodiment two, embodiment three, embodiment four and embodiment five prepare according to the material of each weight part is as shown in table 1.
Table 1
As known from Table 1, embodiment two, embodiment three, the special-purpose aqueous acrylic-amino baking vanish of the Intelligent ashtray metal shell that water-borne acrylic resin in embodiment four and aminoresin proportioning prepare, in hardness, shock-resistance, snappiness, sticking power, the performance such as water tolerance and alcohol resistance is obviously better than embodiment one, the special-purpose aqueous acrylic-amino baking vanish of the Intelligent ashtray metal shell that the water-borne acrylic resin of embodiment five and aminoresin proportioning prepare, water-borne acrylic resin wherein in embodiment two and aminoresin proportioning are 8.8/1, water-borne acrylic resin in embodiment four and aminoresin proportioning are 11.2/1, therefore, the special-purpose aqueous acrylic-amino baking vanish of the Intelligent ashtray metal shell that water-borne acrylic resin and aminoresin proportioning prepare between 8.8/1-11.2/1 is better in over-all properties, thus improve the work-ing life of Intelligent ashtray metal shell, reach object.
The technician of the industry should understand; the present invention is not restricted to the described embodiments; the just principle of the present invention described in above-described embodiment and specification sheets; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.
Claims (3)
1. the special-purpose aqueous acrylic-amino baking vanish of Intelligent ashtray metal shell, is characterized in that: this baking vanish is made up of the component of following weight part: water 15-17 part, dispersion agent 0.5-0.7 part, pigment dyestuff 18-20 part, water-borne acrylic resin 40-50 part, aminoresin 4.0-5.5 part, propandiol butyl ether 7-9 part, Virahol 4-6 part, catalyzer 4.1-4.3 part, defoamer 0.2-0.4 part, flow agent 0.4-0.6 part, adhesion promoter 1.1-1.3 part and PH conditioning agent 0.8-1.2 part.
2. the special-purpose aqueous acrylic-amino baking vanish of a kind of Intelligent ashtray metal shell according to claim 1, is characterized in that: described catalyzer is aqueous isopropanol.
3. the preparation method of the special-purpose aqueous acrylic-amino baking vanish of a kind of Intelligent ashtray metal shell according to claim 1 and 2, is characterized in that: bag following steps:
(1), by the water of 40%, dispersion agent, 30% water-borne acrylic resin put into agitation vat successively, stirrer stir 5-15 minute;
(2), add pigment dyestuff, 35% defoamer, by sand mill, fineness is milled to less than 25 μm, obtained aqueous color paste;
(3), by the water-borne acrylic resin of 70%, aminoresin, propandiol butyl ether, Virahol, catalyzer, flow agent, adhesion promoter, 60% water and defoamer join in clean paint mixing cylinder successively, with high speed dispersor dispersion 5-10 minute, then add PH conditioning agent adjustment pH value;
(4), in paint mixing cylinder, add aqueous color paste obtained in step (2), high speed dispersor dispersion 15-25 minute, then obtains required baking vanish with after 180 order filter-cloth filterings.