CN104927428A - 丙烯酸有机硅水基涂料及其制备方法 - Google Patents

丙烯酸有机硅水基涂料及其制备方法 Download PDF

Info

Publication number
CN104927428A
CN104927428A CN201510306854.7A CN201510306854A CN104927428A CN 104927428 A CN104927428 A CN 104927428A CN 201510306854 A CN201510306854 A CN 201510306854A CN 104927428 A CN104927428 A CN 104927428A
Authority
CN
China
Prior art keywords
parts
water
based paint
sodium
triethanolamine oleate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510306854.7A
Other languages
English (en)
Inventor
翟红波
杨振枢
韦洪屹
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Polymer New Materials Technology Co Ltd
Original Assignee
Suzhou Polymer New Materials Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Polymer New Materials Technology Co Ltd filed Critical Suzhou Polymer New Materials Technology Co Ltd
Priority to CN201510306854.7A priority Critical patent/CN104927428A/zh
Publication of CN104927428A publication Critical patent/CN104927428A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种丙烯酸有机硅水基涂料及其制备方法，涂料包括以下重量份计的原料：硅酮化合物10~40份、甲基丙烯酸酯50~80份、巴西棕榈蜡100~150份、聚乙二醇20~80份、羧甲基纤维素90~120份、三乙醇胺油酸钠55~85份、氧化亚铜60~110份、丁烷四羧酸酐65~95份、过氧化碳酸钠35~70份、水10~50份。其制备方法：将各组分混合均匀，加入羧甲基纤维素、三乙醇胺油酸钠、氧化亚铜、丁烷四羧酸酐、过氧化碳酸钠，混合均匀加热至50~70℃，冷却。本发明经34~36h即可固化，固化时间短，这是因为三乙醇胺油酸钠缩短了涂料的固化时间。

Description

丙烯酸有机硅水基涂料及其制备方法
技术领域
    本发明涉及丙烯酸有机硅水基涂料及其制备方法。
背景技术
涂料，在中国传统名称为油漆。所谓涂料是涂覆在被保护或被装饰的物体表面，并能与被涂物形成牢固附着的连续薄膜，通常是以树脂、或油、或乳液为主，添加或不添加颜料、填料，添加相应助剂，用有机溶剂或水配制而成的粘稠液体。涂料属于有机化工高分子材料，所形成的涂膜属于高分子化合物类型。按照现代通行的化工产品的分类，涂料属于精细化工产品。现代的涂料正在逐步成为一类多功能性的工程材料，是化学工业中的一个重要行业。丙烯酸涂料的固化效果虽好，但是固化时间较长。
发明内容
本发明针对现有技术的不足，提供一种丙烯酸有机硅水基涂料及其制备方法，固化时间短。
本发明采用以下技术方案：
丙烯酸有机硅水基涂料，包括以下重量份计的原料：硅酮化合物10~40份、甲基丙烯酸酯50~80份、巴西棕榈蜡100~150份、聚乙二醇20~80份、羧甲基纤维素90~120份、三乙醇胺油酸钠55~85份、氧化亚铜60~110份、丁烷四羧酸酐65~95份、过氧化碳酸钠35~70份、水10~50份。
作为优选，丙烯酸有机硅水基涂料，包括以下重量份计的原料：硅酮化合物25份、甲基丙烯酸酯65份、巴西棕榈蜡125份、聚乙二醇50份、羧甲基纤维素105份、三乙醇胺油酸钠70份、氧化亚铜85份、丁烷四羧酸酐80份、过氧化碳酸钠55份、水30份。
作为优选，硅酮化合物为环甲基硅酮或苯甲基硅酮。
作为优选，甲基丙烯酸酯为甲基丙烯酸丁酯或甲基丙烯酸甲酯。
上述丙烯酸有机硅水基涂料的制备方法，包括以下步骤：将硅酮化合物、甲基丙烯酸酯、巴西棕榈蜡、聚乙二醇混合均匀，加入羧甲基纤维素、三乙醇胺油酸钠、氧化亚铜、丁烷四羧酸酐、过氧化碳酸钠、水，混合均匀，加热至50~70℃，冷却即可。
有益效果
    本发明经34~36h即可固化，固化时间短，这是因为三乙醇胺油酸钠缩短了涂料的固化时间。
具体实施方式
    下面结合具体实施例对本发明作进一步详细介绍。
实施例1
丙烯酸有机硅水基涂料，包括以下重量份计的原料：硅酮化合物25份、甲基丙烯酸酯65份、巴西棕榈蜡125份、聚乙二醇50份、羧甲基纤维素105份、三乙醇胺油酸钠70份、氧化亚铜85份、丁烷四羧酸酐80份、过氧化碳酸钠55份、水10份。
硅酮化合物为环甲基硅酮。
甲基丙烯酸酯为甲基丙烯酸丁酯。
上述丙烯酸有机硅水基涂料的制备方法，包括以下步骤：将硅酮化合物、甲基丙烯酸酯、巴西棕榈蜡、聚乙二醇混合均匀，加入羧甲基纤维素、三乙醇胺油酸钠、氧化亚铜、丁烷四羧酸酐、过氧化碳酸钠、水，混合均匀，加热至50℃，冷却即可。
实施例2
丙烯酸有机硅水基涂料，包括以下重量份计的原料：硅酮化合物10份、甲基丙烯酸酯50份、巴西棕榈蜡100份、聚乙二醇20份、羧甲基纤维素90份、三乙醇胺油酸钠55份、氧化亚铜60份、丁烷四羧酸酐65份、过氧化碳酸钠35份、水50份。
硅酮化合物为苯甲基硅酮。
甲基丙烯酸酯为甲基丙烯酸甲酯。
上述丙烯酸有机硅水基涂料的制备方法，包括以下步骤：将硅酮化合物、甲基丙烯酸酯、巴西棕榈蜡、聚乙二醇混合均匀，加入羧甲基纤维素、三乙醇胺油酸钠、氧化亚铜、丁烷四羧酸酐、过氧化碳酸钠、水，混合均匀，加热至70℃，冷却即可。
实施例3
丙烯酸有机硅水基涂料，包括以下重量份计的原料：硅酮化合物40份、甲基丙烯酸酯80份、巴西棕榈蜡150份、聚乙二醇80份、羧甲基纤维素120份、三乙醇胺油酸钠85份、氧化亚铜110份、丁烷四羧酸酐95份、过氧化碳酸钠70份、水30份。
硅酮化合物为苯甲基硅酮。
甲基丙烯酸酯为甲基丙烯酸丁酯。
上述丙烯酸有机硅水基涂料的制备方法，包括以下步骤：将硅酮化合物、甲基丙烯酸酯、巴西棕榈蜡、聚乙二醇混合均匀，加入羧甲基纤维素、三乙醇胺油酸钠、氧化亚铜、丁烷四羧酸酐、过氧化碳酸钠、水，混合均匀，加热至60℃，冷却即可。
对比例1
    与实施例1相同，不同在于：不加三乙醇胺油酸钠。
性能测试
将实施例1~3和对比例1的产品进行性能测试，将产品涂在石板上后，在20℃条件下，观察固化时间，结果见表1。
表1
  实施例1 实施例2 实施例3 对比例1
固化时间h 34 35 36 98
结论：本发明经34~36h即可固化，固化时间短，这是因为三乙醇胺油酸钠缩短了涂料的固化时间。

Claims (5)

1.丙烯酸有机硅水基涂料，其特征在于，包括以下重量份计的原料：硅酮化合物10~40份、甲基丙烯酸酯50~80份、巴西棕榈蜡100~150份、聚乙二醇20~80份、羧甲基纤维素90~120份、三乙醇胺油酸钠55~85份、氧化亚铜60~110份、丁烷四羧酸酐65~95份、过氧化碳酸钠35~70份、水10~50份。
2.根据权利要求1所述的丙烯酸有机硅水基涂料，其特征在于，包括以下重量份计的原料：硅酮化合物25份、甲基丙烯酸酯65份、巴西棕榈蜡125份、聚乙二醇50份、羧甲基纤维素105份、三乙醇胺油酸钠70份、氧化亚铜85份、丁烷四羧酸酐80份、过氧化碳酸钠55份、水30份。
3.根据权利要求1所述的丙烯酸有机硅水基涂料，其特征在于，硅酮化合物为环甲基硅酮或苯甲基硅酮。
4.根据权利要求1所述的丙烯酸有机硅水基涂料，其特征在于，甲基丙烯酸酯为甲基丙烯酸丁酯或甲基丙烯酸甲酯。
5.基于权利要求1所述的丙烯酸有机硅水基涂料的制备方法，其特征在于，包括以下步骤：将硅酮化合物、甲基丙烯酸酯、巴西棕榈蜡、聚乙二醇混合均匀，加入羧甲基纤维素、三乙醇胺油酸钠、氧化亚铜、丁烷四羧酸酐、过氧化碳酸钠、水，混合均匀，加热至50~70℃，冷却即可。
CN201510306854.7A 2015-06-08 2015-06-08 丙烯酸有机硅水基涂料及其制备方法 Pending CN104927428A (zh)