CN104927087A - 一种复配杀菌活性碳酸钙 - Google Patents
一种复配杀菌活性碳酸钙 Download PDFInfo
- Publication number
- CN104927087A CN104927087A CN201510265960.5A CN201510265960A CN104927087A CN 104927087 A CN104927087 A CN 104927087A CN 201510265960 A CN201510265960 A CN 201510265960A CN 104927087 A CN104927087 A CN 104927087A
- Authority
- CN
- China
- Prior art keywords
- calcium carbonate
- parts
- compound
- stearic acid
- activated calcium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种复配杀菌活性碳酸钙,其是由下述重量份的原料制得:水泥5-8、电石渣13-15、二氧化钛4-6、熔结凝灰岩5-8、铝粉0.1-0.2、茶籽饼粉2-4、纯碱0.2-0.4、石膏3-5、荒山泥土0.2-0.4、煤矸石3-5、钢渣粉0.2-0.4、糖钙1-2、蜂蜜0.3-0.5、淀粉0.3-0.5、硬脂酸0.1-0.2、过氧化苯甲酰0.3-0.5、叔丁基过氧化氢0.1-0.2、水适量。
Description
技术领域
本发明涉及碳酸钙领域,确切地说是一种复配杀菌活性碳酸钙。
背景技术
活性碳酸钙是以碳酸钙为基料,采用多功能表面活性剂和复合型高效加工助剂,对无机粉体表面进行改性活化处理而成。经改性处理后的碳酸钙粉体,表面形成一种特殊的包层结构,能显著改善在聚烯烃等高聚物基体中的分散性和亲和性,并且能与高聚物基体间产生界面作用,从而提高制品的抗冲击强度,是一种性能优良的增量型填充助剂。
发明内容
本发明的目的在于提供一种复配杀菌活性碳酸钙。
上述目的通过以下方案实现:
一种复配杀菌活性碳酸钙,其特征在于:其是由下述重量份的原料制得: 碳酸钙100-120、十四烷基二甲基苄基氯化铵0.2-0.4、异氰脲酸三烯丙酯2-3、硬脂酰胺2-4、纳米三氧化二铝0.5-1.5,交联剂TAC1.2-2.4、二氧化钛6-8、异噻唑啉酮0.1-0.2、淀粉0.3-0.5、硬脂酸1-2、甲基丙烯酸酯1-2、过氧化苯甲酰0.3-0.5、水适量。
所述的一种复配杀菌活性碳酸钙,其特征在于:制备方法包括以下步骤:
(1)将碳酸钙与适量水混匀后,再加入十四烷基二甲基苄基氯化铵、异氰脲酸三烯丙酯、硬脂酰胺、搅拌均匀,再研磨1-2小时,得改性悬浮液备用;
(2)将二氧化钛加入到适量去离子水中,40-45℃下搅拌均匀后,再将淀粉、甲基丙烯酸酯、过氧化苯甲酰加入其中,35-40℃下搅拌均匀,得到复配溶液;
(3)将改性悬浮液与复配溶液混匀,球磨混合均匀得到混合浆料,加入除硬脂酸外其余原料,35-38℃下反应50-60min;
(4)步骤(3)所得反应后的浆料50-60℃下干燥30-60h,后在80-100℃下真空干燥,得复配碳酸钙粉体;
(5)将步骤(4)所得复配碳酸钙粉体置于转鼓上,40-50转/分下30-40℃下预热10-20min,再将硬脂酸加热至70-80℃,雾化,均匀喷于复配碳酸钙粉体上,同时搅拌10-15min,即得。
本发明的有益效果为:
本发明含有各种复配改性剂,纳米三氧化二铝、二氧化钛、异噻唑啉酮等起到很好的杀菌作用,同时通过均匀分散搅拌,使得它们均匀得分散于碳酸钙表面,增加杀菌作用,同时有效地防止微细化粒子的自聚,增加其在塑料、橡胶中的相容性和分散性;本发明采用雾化喷淋的方式完全充分地利用了硬脂酸,采用真空干燥的方法,使避免复配粉体二次团聚。 本发明制得的产品应用于PVC塑料上,由于其表面化学键合的改性剂与PVC塑料具有良好相容性,表现出强的内润滑作用,从而削弱了PVC 分子间的作用力,使得体系流变性能改变,可提高挤出速度,使制品外观光滑细腻;同时也说明在同等条件下,改性碳酸钙可以增加填充量,也能达到良好节约成本的作用。
具体实施方式
一种复配杀菌活性碳酸钙,其是由下述重量(kg)的原料制得: 碳酸钙120、十四烷基二甲基苄基氯化铵0.4、异氰脲酸三烯丙酯2、硬脂酰胺2、纳米三氧化二铝0.5,交联剂TAC1.4、二氧化钛6、异噻唑啉酮0.2、淀粉0.5、硬脂酸1、甲基丙烯酸酯1、过氧化苯甲酰0.3、水适量。
所述的一种复配杀菌活性碳酸钙,制备方法包括以下步骤:
(1)将碳酸钙与适量水混匀后,再加入十四烷基二甲基苄基氯化铵、异氰脲酸三烯丙酯、硬脂酰胺、搅拌均匀,再研磨1小时,得改性悬浮液备用;
(2)将二氧化钛加入到适量去离子水中,40℃下搅拌均匀后,再将淀粉、甲基丙烯酸酯、过氧化苯甲酰加入其中,35℃下搅拌均匀,得到复配溶液;
(3)将改性悬浮液与复配溶液混匀,球磨混合均匀得到混合浆料,加入除硬脂酸外其余原料,35℃下反应60min;
(4)步骤(3)所得反应后的浆料50℃下干燥30h,后在80℃下真空干燥,得复配碳酸钙粉体;
(5)将步骤(4)所得复配碳酸钙粉体置于转鼓上,40转/分下40℃下预热10min,再将硬脂酸加热至80℃,雾化,均匀喷于复配碳酸钙粉体上,同时搅拌10min,即得。
将普通碳酸钙和本实施例的活性碳酸钙分别按配方混料,室温放置8h 后在PLE331 型转矩流变仪进行流变实验,结果如表1 所示:
表1 流变实验结果
所述的材料配方为:PVC 100 份,复合稳定剂5 份,KM355P 6 份,普通CaCO3 或本实施例的活性碳酸钙30 份
从表1 可以看出,加入本实施例的活性碳酸钙与普通碳酸钙相比,扭矩降低,塑化时间明显缩短,熔融温度下降,塑化速度变快,说明本实施例的活性碳酸钙与PVC 塑料体系相容性好,有利于加工。
Claims (2)
1.一种复配杀菌活性碳酸钙,其特征在于:其是由下述重量份的原料制得: 碳酸钙100-120、十四烷基二甲基苄基氯化铵0.2-0.4、异氰脲酸三烯丙酯2-3、硬脂酰胺2-4、纳米三氧化二铝0.5-1.5,交联剂TAC1.2-2.4、二氧化钛6-8、异噻唑啉酮0.1-0.2、淀粉0.3-0.5、硬脂酸1-2、甲基丙烯酸酯1-2、过氧化苯甲酰0.3-0.5、水适量。
2.根据权利要求1所述的一种复配杀菌活性碳酸钙,其特征在于:制备方法包括以下步骤:
(1)将碳酸钙与适量水混匀后,再加入十四烷基二甲基苄基氯化铵、异氰脲酸三烯丙酯、硬脂酰胺、搅拌均匀,再研磨1-2小时,得改性悬浮液备用;
(2)将二氧化钛加入到适量去离子水中,40-45℃下搅拌均匀后,再将淀粉、甲基丙烯酸酯、过氧化苯甲酰加入其中,35-40℃下搅拌均匀,得到复配溶液;
(3)将改性悬浮液与复配溶液混匀,球磨混合均匀得到混合浆料,加入除硬脂酸外其余原料,35-38℃下反应50-60min;
(4)步骤(3)所得反应后的浆料50-60℃下干燥30-60h,后在80-100℃下真空干燥,得复配碳酸钙粉体;
(5)将步骤(4)所得复配碳酸钙粉体置于转鼓上,40-50转/分下30-40℃下预热10-20min,再将硬脂酸加热至70-80℃,雾化,均匀喷于复配碳酸钙粉体上,同时搅拌10-15min,即得。