CN104911776A - 一种新型不吸湿耐磨抗菌聚丙烯纤维再生棉混纺纱及其制备方法 - Google Patents
一种新型不吸湿耐磨抗菌聚丙烯纤维再生棉混纺纱及其制备方法 Download PDFInfo
- Publication number
- CN104911776A CN104911776A CN201510285509.XA CN201510285509A CN104911776A CN 104911776 A CN104911776 A CN 104911776A CN 201510285509 A CN201510285509 A CN 201510285509A CN 104911776 A CN104911776 A CN 104911776A
- Authority
- CN
- China
- Prior art keywords
- parts
- cotton
- polypropylene
- wear
- yarn
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种新型不吸湿耐磨抗菌聚丙烯纤维再生棉混纺纱,其特征在于,由下列重量份的原料制备制成:废旧棉织品40-43、棉纱边角料15-17、巴西棕榈蜡1-2、脂肪醇聚氧乙烯醚硫酸钠1-2、硅丙乳液5-7、预胶化淀粉3-4、聚丙烯39-44、纳米氧化锌3-5、液体石蜡12-14、纳米二氧化钛9-10、羧甲基纤维素1.5-2、甘油硬脂酸酯1-2、水适量;本发明将废旧棉织品等制成的再生棉纤维经过表面防水、防晒处理后与防晒改性后的聚丙烯纤维混纺成纱,制成的混纺纱结实、耐磨、高强、比重轻,不易吸湿,可以用来制造泳衣等水下用服装或者渔网用丝等,提升了再生棉纤维的质量,拓宽了再生棉的使用范围。
Description
技术领域
本发明涉及纺织技术领域,特别是一种新型不吸湿耐磨抗菌聚丙烯纤维再生棉混纺纱及其制备方法。
背景技术
随着全球人口剧增,世界各国都将控制耕地的利用,棉花、麻、养蚕的桑树的种植都将受到限制,传统棉纺织原料受到多重制约。相关资料显示,2010年国内再生棉纱使用的边角料等原料量共计能达到300万吨左右。按50%的是棉型再生纱来估算,按每亩棉花产量200公斤计算,相当于约700余万亩棉田的产量。再生纱既实现了资源的循环利用,节约了有限的资源,又解决了边角料处理难题,为环境治理作出了贡献。但是由于原料经过开松后,纤维长度缩短、强力下降、耐光性差、容易霉变,这就限制了再生棉纱的利用。
聚丙烯纤维是以丙烯聚合得到的等规聚丙烯为原料纺制而成的合成纤维,在我国的商品名为丙纶。聚丙烯纤维质轻、强度高、弹性好、耐磨、耐腐蚀、具有电绝缘性和保暖性,回潮率低,同时价格低廉,耐化学性质好,在装饰织物领域具有广泛的运用,但是由于聚丙烯纤维的耐热、耐老化性差,限制了其在服装领域的应用。
发明内容
本发明的目的是提供一种新型不吸湿耐磨抗菌聚丙烯纤维再生棉混纺纱及其制备方法。通过在再生棉纤维表面浸渍一层具有防水、提高强度以及耐光性的处理剂,使得再生棉纤维改善了传统容易吸湿的特点,可以与聚丙烯纤维混纺成纱,用来制造泳衣、渔网、包装袋布等。
为了实现本发明的目的,本发明通过以下方案实施:
一种新型不吸湿耐磨抗菌聚丙烯纤维再生棉混纺纱,由下列重量份的原料制备制成:废旧棉织品40-43、棉纱边角料15-17、巴西棕榈蜡1-2、脂肪醇聚氧乙烯醚硫酸钠1-2、硅丙乳液5-7、预胶化淀粉3-4、聚丙烯39-44、纳米氧化锌3-5、液体石蜡12-14、纳米二氧化钛9-10、羧甲基纤维素1.5-2、甘油硬脂酸酯1-2、水适量;
本发明所述一种新型不吸湿耐磨抗菌聚丙烯纤维再生棉混纺纱,由以下具体步骤制成:
(1)将预胶化淀粉放入搅拌釜中,加入总量25倍量的水,加热至50℃,以120转/分的速度搅拌直至完全溶解,将巴西棕榈蜡与脂肪醇聚氧乙烯醚硫酸钠研磨30分钟后加入到搅拌釜中,再加入一半量的纳米二氧化钛、硅丙乳液,以150转/分的速度搅拌40分钟形成处理浆料;
(2)将废旧棉织品、棉纱边角料混合以后使用机器打碎至纤维长度为2-3毫米,将打碎的混合纤维浸入处理浆料中40-50分钟,然后在80-90℃温度下烘干,再将烘干后的纤维经过梳棉、精梳工艺制成再生混合纤维棉条;
(3)将聚丙烯加热至完全熔融,然后与液体石蜡、纳米氧化锌混合,搅拌均匀后通过熔融纺丝工艺制得混合聚丙烯短纤维,然后将其浸渍在加热至45℃的乙醇中45分钟后取出,在90-100℃下烘干;
(4)将羧甲基纤维素加入30倍量的水中,加热至40-50℃,搅拌至形成透明溶液后加入其余剩余成分,充分分散制成二次浸渍浆料,然后将步骤(3)处理后的混合聚丙烯短纤维继续浸渍在二次浸渍浆料中,最后烘干得到改性混合聚丙烯短纤维;
(5)将步骤(2)得到的再生混合纤维棉条与步骤(4)得到的改性混合聚丙烯短纤维进行并条、粗砂、细纱工艺即得本发明。
本发明的有益效果是:本发明首先通过将废旧棉织品、棉纱边角料打碎,然后放入特制的处理剂中浸渍,内含巴西棕榈蜡、纳米二氧化钛、硅丙乳液能够提高纤维的强度、弹性、防水性、防晒性,可以改善棉纤维易吸湿的特点。第二步是将聚丙烯与液体石蜡、纳米氧化锌等熔融纺丝后用热乙醇第一次浸渍溶去液体石蜡,可以形成多孔表面的聚丙烯纤维,再用纳米二氧化钛分散液再一次浸渍,将纳米二氧化钛均匀地分散在聚丙烯纤维表面,进一步提高抗紫外线性能。
本发明将废旧棉织品等制成的再生棉纤维经过表面防水、防晒处理后与防晒改性后的聚丙烯纤维混纺成纱,制成的混纺纱结实、耐磨、高强、比重轻,不易吸湿,可以用来制造泳衣等水下用服装或者渔网用丝等,提升了再生棉纤维的质量,拓宽了再生棉的使用范围。
具体实施方案
下面通过具体实例对本发明进行详细说明。
一种新型不吸湿耐磨抗菌聚丙烯纤维再生棉混纺纱,由下列重量份(公斤)的原料制备制成:废旧棉织品40、棉纱边角料15、巴西棕榈蜡1、脂肪醇聚氧乙烯醚硫酸钠1、硅丙乳液5、预胶化淀粉3、聚丙烯39、纳米氧化锌3、液体石蜡12、纳米二氧化钛9、羧甲基纤维素1.5、甘油硬脂酸酯1、水适量;
本发明所述一种新型不吸湿耐磨抗菌聚丙烯纤维再生棉混纺纱,由以下具体步骤制成:
(1)将预胶化淀粉放入搅拌釜中,加入总量25倍量的水,加热至50℃,以120转/分的速度搅拌直至完全溶解,将巴西棕榈蜡与脂肪醇聚氧乙烯醚硫酸钠研磨30分钟后加入到搅拌釜中,再加入一半量的纳米二氧化钛、硅丙乳液,以150转/分的速度搅拌40分钟形成处理浆料;
(2)将废旧棉织品、棉纱边角料混合以后使用机器打碎至纤维长度为2-3毫米,将打碎的混合纤维浸入处理浆料中50分钟,然后在80-90℃温度下烘干,再将烘干后的纤维经过梳棉、精梳工艺制成再生混合纤维棉条;
(3)将聚丙烯加热至完全熔融,然后与液体石蜡、纳米氧化锌混合,搅拌均匀后通过熔融纺丝工艺制得混合聚丙烯短纤维,然后将其浸渍在加热至45℃的乙醇中45分钟后取出,在90-100℃下烘干;
(4)将羧甲基纤维素加入30倍量的水中,加热至40-50℃,搅拌至形成透明溶液后加入其余剩余成分,充分分散制成二次浸渍浆料,然后将步骤(3)处理后的混合聚丙烯短纤维继续浸渍在二次浸渍浆料中,最后烘干得到改性混合聚丙烯短纤维;
(5)将步骤(2)得到的再生混合纤维棉条与步骤(4)得到的改性混合聚丙烯短纤维进行并条、粗砂、细纱工艺即得本发明。
经检测,本发明产品的与纯棉纱对比,线密度减少8.95%,断裂强度增加7.5%。
Claims (2)
1.一种新型不吸湿耐磨抗菌聚丙烯纤维再生棉混纺纱,其特征在于,由下列重量份的原料制备制成:废旧棉织品40-43、棉纱边角料15-17、巴西棕榈蜡1-2、脂肪醇聚氧乙烯醚硫酸钠1-2、硅丙乳液5-7、预胶化淀粉3-4、聚丙烯39-44、纳米氧化锌3-5、液体石蜡12-14、纳米二氧化钛9-10、羧甲基纤维素1.5-2、甘油硬脂酸酯1-2、水适量。
2.根据权利要求1所述一种新型不吸湿耐磨抗菌聚丙烯纤维再生棉混纺纱,其特征在于,由以下具体步骤制成:
(1)将预胶化淀粉放入搅拌釜中,加入总量25倍量的水,加热至50℃,以120转/分的速度搅拌直至完全溶解,将巴西棕榈蜡与脂肪醇聚氧乙烯醚硫酸钠研磨30分钟后加入到搅拌釜中,再加入一半量的纳米二氧化钛、硅丙乳液,以150转/分的速度搅拌40分钟形成处理浆料;
(2)将废旧棉织品、棉纱边角料混合以后使用机器打碎至纤维长度为2-3毫米,将打碎的混合纤维浸入处理浆料中40-50分钟,然后在80-90℃温度下烘干,再将烘干后的纤维经过梳棉、精梳工艺制成再生混合纤维棉条;
(3)将聚丙烯加热至完全熔融,然后与液体石蜡、纳米氧化锌混合,搅拌均匀后通过熔融纺丝工艺制得混合聚丙烯短纤维,然后将其浸渍在加热至45℃的乙醇中45分钟后取出在90-100℃下烘干;
(4)将羧甲基纤维素加入30倍量的水中,加热至40-50℃,搅拌至形成透明溶液后加入其余剩余成分,充分分散制成二次浸渍浆料,然后将步骤(3)处理后的混合聚丙烯短纤维继续浸渍在二次浸渍浆料中,最后烘干得到改性混合聚丙烯短纤维;
(5)将步骤(2)得到的再生混合纤维棉条与步骤(4)得到的改性混合聚丙烯短纤维进行并条、粗砂、细纱工艺即得本发明。