CN104963048A - 一种具有防辐射功效的混纺再生棉纱及其制备方法 - Google Patents

一种具有防辐射功效的混纺再生棉纱及其制备方法 Download PDF

Info

Publication number
CN104963048A
CN104963048A CN201510283171.4A CN201510283171A CN104963048A CN 104963048 A CN104963048 A CN 104963048A CN 201510283171 A CN201510283171 A CN 201510283171A CN 104963048 A CN104963048 A CN 104963048A
Authority
CN
China
Prior art keywords
parts
cotton yarn
cotton
polypropylene
fiber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510283171.4A
Other languages
English (en)
Inventor
刘勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI HANSHAN SHUNTAIN TEXTILE Co Ltd
Original Assignee
ANHUI HANSHAN SHUNTAIN TEXTILE Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI HANSHAN SHUNTAIN TEXTILE Co Ltd filed Critical ANHUI HANSHAN SHUNTAIN TEXTILE Co Ltd
Priority to CN201510283171.4A priority Critical patent/CN104963048A/zh
Publication of CN104963048A publication Critical patent/CN104963048A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种具有防辐射功效的混纺再生棉纱，其特征在于，由下列重量份的原料制备制成：废旧棉织品34-40、棉纱边角料15-17、银纤维7-9、纳米二氧化钛9-10、硅藻泥3-4、硅油1-2、单硬脂酸甘油酯1-1.5、环氧树脂乳液6-7、聚丙烯39-44、纳米氧化锌3-5、液体石蜡12-14、羧甲基纤维素1.5-2、水适量；本发明采用废旧棉织品等再生成纤维与银纤维混合，然后与表面改性的聚丙烯短纤维混纺纱进行并条，混纺成本发明产品，中和了各种纤维的特点，弥补了棉纤维与聚丙烯纤维防晒性差的缺点，同时增强了强度，具有良好的抗电磁辐射效果，面料弹性好，不易变形，非常适合制造孕妇防辐射服等产品。

Description

一种具有防辐射功效的混纺再生棉纱及其制备方法
技术领域
本发明涉及纺织技术领域，特别是一种具有防辐射功效的混纺再生棉纱及其制备方法。
背景技术
随着全球人口剧增，世界各国都将控制耕地的利用，棉花、麻、养蚕的桑树的种植都将受到限制，传统棉纺织原料受到多重制约。相关资料显示，2010年国内再生棉纱使用的边角料等原料量共计能达到300万吨左右。按50%的是棉型再生纱来估算，按每亩棉花产量200公斤计算，相当于约700余万亩棉田的产量。再生纱既实现了资源的循环利用，节约了有限的资源，又解决了边角料处理难题，为环境治理作出了贡献。但是由于原料经过开松后，纤维长度缩短、强力下降、耐光性差、容易霉变，这就限制了再生棉纱的利用。
聚丙烯纤维是以丙烯聚合得到的等规聚丙烯为原料纺制而成的合成纤维，在我国的商品名为丙纶。聚丙烯纤维质轻、强度高、弹性好、耐磨、耐腐蚀、具有电绝缘性和保暖性，回潮率低，同时价格低廉，耐化学性质好，在装饰织物领域具有广泛的运用，但是由于聚丙烯纤维的耐热、耐老化性差，限制了其在服装领域的应用。
发明内容
本发明的目的是提供一种具有防辐射功效的混纺再生棉纱及其制备方法。本发明首先通过将废旧棉织品、废棉下脚料纤维打碎，放入特制的处理浆料中浸渍，能够提高纤维的强度、弹性以及防晒性，再与银纤维混合进过梳棉等工序制成再生混合纤维棉条；然后将聚丙烯与液体石蜡、纳米氧化锌等熔融纺丝后用热乙醇第一次浸渍溶去液体石蜡，可以形成多孔表面的聚丙烯纤维，再用纳米二氧化钛分散液再一次浸渍，将纳米二氧化钛均匀地分散在聚丙烯纤维表面，进一步提高抗紫外线性能；最后将两种纤维混纺成纱，强度比纯棉纱相应的变大，提高再生棉纱的质量，同时由于银纤维的添加，具有良好的抗电磁辐射效果，面料弹性好，且持久，在较大拉伸力下不易变形，非常适合制造孕妇防辐射服等产品。
为了实现本发明的目的，本发明通过以下方案实施：
一种具有防辐射功效的混纺再生棉纱，由下列重量份的原料制备制成：废旧棉织品34-40、棉纱边角料15-17、银纤维7-9、纳米二氧化钛9-10、硅藻泥3-4、硅油1-2、单硬脂酸甘油酯1-1.5、环氧树脂乳液6-7、聚丙烯39-44、纳米氧化锌3-5、液体石蜡12-14、羧甲基纤维素1.5-2、水适量；
本发明所述一种具有防辐射功效的混纺再生棉纱，由以下具体步骤制成：
（1）将环氧树脂乳液与单硬脂酸甘油酯放入搅拌釜中，加热至70℃，开始搅拌然后加入总量10倍量的水，依次加入加入一半量的纳米二氧化钛、硅藻泥、硅油，以120-150转/分的速度搅拌30-40分钟形成处理浆料；
（2）将废旧棉织品、棉纱边角料混合以后使用机器打碎至纤维长度为2-3毫米，将打碎的混合纤维浸入处理浆料中40-50分钟，然后在80-90℃温度下烘干，再将烘干后的纤维与银纤维混合，经过梳棉、精梳工艺制成再生混合纤维棉条；
（3）将聚丙烯加热至完全熔融，然后与液体石蜡、纳米氧化锌混合，搅拌均匀后通过熔融纺丝工艺制得混合聚丙烯短纤维，然后将其浸渍在加热至45℃的乙醇中30-40分钟后取出，在90-100℃下烘干；
（4）将羧甲基纤维素加入30倍量的水中，加热至40-50℃，搅拌至形成透明溶液后加入其余剩余成分，充分分散制成二次浸渍浆料，然后将步骤（3）处理后的混合聚丙烯短纤维继续浸渍在二次浸渍浆料中，最后烘干得到改性混合聚丙烯短纤维；
（5）将步骤（2）得到的再生混合纤维棉条与步骤（4）得到的改性混合聚丙烯短纤维进行并条、粗砂、细纱工艺即得本发明。
本发明的有益效果是：本发明采用废旧棉织品等再生成纤维与银纤维混合，然后与表面改性的聚丙烯短纤维混纺纱进行并条，混纺成本发明产品，中和了各种纤维的特点，弥补了棉纤维与聚丙烯纤维防晒性差的缺点，同时增强了强度，具有良好的抗电磁辐射效果，面料弹性好，且持久，不易变形，非常适合制造孕妇防辐射服等产品。而且本发明采用废旧棉织品再生纤维，降低成本且不会降低产品质量，节能环保。
具体实施方案
下面通过具体实例对本发明进行详细说明。
一种具有防辐射功效的混纺再生棉纱，由下列重量份（公斤）的原料制备制成：废旧棉织品34、棉纱边角料15、银纤维7、纳米二氧化钛9、硅藻泥3、硅油1、单硬脂酸甘油酯1、环氧树脂乳液6、聚丙烯39、纳米氧化锌3、液体石蜡12、羧甲基纤维素1.5、水适量；
本发明所述一种具有防辐射功效的混纺再生棉纱，由以下具体步骤制成：
（1）将环氧树脂乳液与单硬脂酸甘油酯放入搅拌釜中，加热至70℃，开始搅拌然后加入总量10倍量的水，依次加入加入一半量的纳米二氧化钛、硅藻泥、硅油，以150转/分的速度搅拌30钟形成处理浆料；
（2）将废旧棉织品、棉纱边角料混合以后使用机器打碎至纤维长度为2-3毫米，将打碎的混合纤维浸入处理浆料中40分钟，然后在80-90℃温度下烘干，再将烘干后的纤维与银纤维混合，经过梳棉、精梳工艺制成再生混合纤维棉条；
（3）将聚丙烯加热至完全熔融，然后与液体石蜡、纳米氧化锌混合，搅拌均匀后通过熔融纺丝工艺制得混合聚丙烯短纤维，然后将其浸渍在加热至45℃的乙醇中30分钟后取出，在90-100℃下烘干，；
（4）将羧甲基纤维素加入30倍量的水中，加热至40-50℃，搅拌至形成透明溶液后加入其余剩余成分，充分分散制成二次浸渍浆料，然后将步骤（3）处理后的混合聚丙烯短纤维继续浸渍在二次浸渍浆料中，最后烘干得到改性混合聚丙烯短纤维；
（5）将步骤（2）得到的再生混合纤维棉条与步骤（4）得到的改性混合聚丙烯短纤维进行并条、粗砂、细纱工艺即得本发明。
经检测，本发明产品的与纯棉纱对比，线密度减少12.2%，断裂强度增加9.15%。

Claims (2)

1.一种具有防辐射功效的混纺再生棉纱，其特征在于，由下列重量份的原料制备制成：废旧棉织品34-40、棉纱边角料15-17、银纤维7-9、纳米二氧化钛9-10、硅藻泥3-4、硅油1-2、单硬脂酸甘油酯1-1.5、环氧树脂乳液6-7、聚丙烯39-44、纳米氧化锌3-5、液体石蜡12-14、羧甲基纤维素1.5-2、水适量。
2.根据权利要求1所述一种具有防辐射功效的混纺再生棉纱，其特征在于，由以下具体步骤制成：
（1）将环氧树脂乳液与单硬脂酸甘油酯放入搅拌釜中，加热至70℃，开始搅拌然后加入总量10倍量的水，依次加入加入一半量的纳米二氧化钛、硅藻泥、硅油，以120-150转/分的速度搅拌30-40分钟形成处理浆料；
（2）将废旧棉织品、棉纱边角料混合以后使用机器打碎至纤维长度为2-3毫米，将打碎的混合纤维浸入处理浆料中40-50分钟，然后在80-90℃温度下烘干，再将烘干后的纤维与银纤维混合，经过梳棉、精梳工艺制成再生混合纤维棉条；
（3）将聚丙烯加热至完全熔融，然后与液体石蜡、纳米氧化锌混合，搅拌均匀后通过熔融纺丝工艺制得混合聚丙烯短纤维，然后将其浸渍在加热至45℃的乙醇中30-40分钟后取出，在90-100℃下烘干；
（4）将羧甲基纤维素加入30倍量的水中，加热至40-50℃，搅拌至形成透明溶液后加入其余剩余成分，充分分散制成二次浸渍浆料，然后将步骤（3）处理后的混合聚丙烯短纤维继续浸渍在二次浸渍浆料中，最后烘干得到改性混合聚丙烯短纤维；
（5）将步骤（2）得到的再生混合纤维棉条与步骤（4）得到的改性混合聚丙烯短纤维进行并条、粗砂、细纱工艺即得本发明。
CN201510283171.4A 2015-05-29 2015-05-29 一种具有防辐射功效的混纺再生棉纱及其制备方法 Pending CN104963048A (zh)