CN104909673A - 一种萜烯树脂包覆改性玻化微珠保温砂浆及其制作方法 - Google Patents

一种萜烯树脂包覆改性玻化微珠保温砂浆及其制作方法 Download PDF

Info

Publication number
CN104909673A
CN104909673A CN201510332070.1A CN201510332070A CN104909673A CN 104909673 A CN104909673 A CN 104909673A CN 201510332070 A CN201510332070 A CN 201510332070A CN 104909673 A CN104909673 A CN 104909673A
Authority
CN
China
Prior art keywords
glazed hollow
thermal
minute
hollow beads
terpine resin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510332070.1A
Other languages
English (en)
Inventor
徐�明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hefei Ji Ke New Material Co Ltd
Original Assignee
Hefei Ji Ke New Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hefei Ji Ke New Material Co Ltd filed Critical Hefei Ji Ke New Material Co Ltd
Priority to CN201510332070.1A priority Critical patent/CN104909673A/zh
Publication of CN104909673A publication Critical patent/CN104909673A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种萜烯树脂包覆改性玻化微珠保温砂浆，在玻化微珠表面包覆一层熔融状态的萜烯树脂，形成了兼具增强和疏水特性的高分子树脂层，从而封闭玻化微珠因各种原因产生的表面缺陷，阻止了玻化微珠对水的吸附和吸收，从而降低了吸水率，同时还覆盖一层改性后的鸡毛梗，再覆盖其他有效助剂，显著降低了玻化微珠掺入时的因受压和碰撞引起的破碎率，改善了玻化微珠的优异性能，制得的保温砂浆适用于各种墙体的内、外保温抹灰工程，具有较好的隔热性能、极佳的温度稳定性和化学稳定性，同时还能够提高砂浆的抗裂性能、抗冲击韧性、抗渗性能，克服了砂浆在使用过程中产生的墙面空鼓、开裂、剥落等问题。

Description

一种萜烯树脂包覆改性玻化微珠保温砂浆及其制作方法
技术领域
本发明涉及保温砂浆技术领域，具体涉及一种萜烯树脂包覆改性玻化微珠保温砂浆及其制作方法。
背景技术
目前，保温砂浆主要分为有机类与无机类，有机保温砂浆虽然保温性能优异但其防火性能存在缺陷且污染较大。近年来，我国相继发生因引燃有机保温材料引起的严重火灾，导致社会各界对有机保温材料应用安全性质疑，从而限制了有机保温材料的应用，无机保温砂浆的优点则显现出来。
应用较多的无机保温砂浆主要是玻化微珠保温砂浆，它属于轻集料无机保温砂浆，相比有机类保温砂浆，它除了具有与水泥等胶凝材料相容性好、材料间黏结力高的特点外，还具有相对较高的抗压强度、良好的耐候性、防火性和透气性等优点，且施工方便，是一种综合性能好、绿色环保的新型建筑保温材料。然而由于玻化微珠颗粒强度极低，在砂浆拌合过程中，玻化微珠破损率较高，导致玻化微珠保温砂浆存在干密度大、导热系数明显增大、吸水率明显增加、保温性能下降等缺陷，如何降低玻化微珠在受压、装卸和搅拌过程中的破损率，充分发挥其优异性能，以提高保温砂浆的各项性能指标是目前现有技术亟待解决的难题。
发明内容
本发明的目的就是提供一种萜烯树脂包覆改性玻化微珠保温砂浆及其制作方法，以克服现有技术的不足。
本发明的目的是这样实现的：
一种萜烯树脂包覆改性玻化微珠保温砂浆，其特征在于，由下列重量份的原料制成：普通硅酸盐水泥110-160、砂子10-15、钢渣微粉13-17、玻化微珠55-65、鸡毛梗3-5、异丁基三乙氧基硅烷1.6-2.7、松香乳液2.1-3.4、磷钨酸钾0.4-0.7、萜烯树脂20-26、黄糊精0.9-1.3。
所述的一种萜烯树脂包覆改性玻化微珠保温砂浆的制备方法，其特征在于包括以下步骤：
（1）将鸡毛梗烘干、脱脂超细研磨成粉，加入黄糊精、异丁基三乙氧基硅烷超声分散研磨1-2小时，烘干；
（2）将玻化微珠于105℃下干燥2小时冷却至室温，投入翻转式混合反应釜内，升温至100-115℃，将熔融状态的萜烯树脂喷洒在玻化微珠表面，加入步骤（1）物料翻转混合10-20分钟后，再喷洒松香乳液，翻转混合10-20分钟，烘干制得改性玻化微珠；
（3）将钢渣微粉高温煅烧处理后加入普通硅酸盐水泥于翻转式混合反应釜内翻转20-30分钟混匀，再加入改性玻化微珠及其它剩余成分翻转混合20-30分钟，将搅拌好的物料用自动包装机包好出料。
本发明有以下有益效果：本发明制备工艺简单操作简便，在玻化微珠表面包覆一层熔融状态的萜烯树脂，形成了兼具增强和疏水特性的高分子树脂层，从而封闭玻化微珠因各种原因产生的表面缺陷，阻止了玻化微珠对水的吸附和吸收，从而降低了吸水率，同时还覆盖一层改性后的鸡毛梗，再覆盖其他有效助剂，显著降低了玻化微珠掺入时的因受压和碰撞引起的破碎率，改善了玻化微珠的优异性能，制得的保温砂浆适用于各种墙体的内、外保温抹灰工程，具有较好的隔热性能、极佳的温度稳定性和化学稳定性，同时还能够提高砂浆的抗裂性能、抗冲击韧性、抗渗性能，克服了砂浆在使用过程中产生的墙面空鼓、开裂、剥落等问题。
具体实施方式
所述的一种萜烯树脂包覆改性玻化微珠保温砂浆，其特征在于，由下列重量份的原料制成：普通硅酸盐水泥134、砂子12、钢渣微粉14、玻化微珠57、鸡毛梗4、异丁基三乙氧基硅烷2.6、松香乳液2.5、磷钨酸钾0.5、萜烯树脂23、黄糊精0.9。
制作方法包括以下步骤：
（1）将鸡毛梗烘干、脱脂超细研磨成粉，加入黄糊精、异丁基三乙氧基硅烷超声分散研磨1-2小时，烘干；
（2）将玻化微珠于105℃下干燥2小时冷却至室温，投入翻转式混合反应釜内，升温至100-115℃，将熔融状态的萜烯树脂喷洒在玻化微珠表面，加入步骤（1）物料翻转混合10-20分钟后，再喷洒松香乳液，翻转混合10-20分钟，烘干制得改性玻化微珠；
（3）将钢渣微粉高温煅烧处理后加入普通硅酸盐水泥于翻转式混合反应釜内翻转20-30分钟混匀，再加入改性玻化微珠及其它剩余成分翻转混合20-30分钟，将搅拌好的物料用自动包装机包好出料。
使用本发明生产的玻化微珠保温砂浆的技术参数指标如下：
（1）干密度：279kg/m3；
（2）抗压强度：0.93MPa；
（3）导热系数：0.066W/（m·K）。

Claims (2)

1.一种萜烯树脂包覆改性玻化微珠保温砂浆，其特征在于，由下列重量份的原料制成：普通硅酸盐水泥110-160、砂子10-15、钢渣微粉13-17、玻化微珠55-65、鸡毛梗3-5、异丁基三乙氧基硅烷1.6-2.7、松香乳液2.1-3.4、磷钨酸钾0.4-0.7、萜烯树脂20-26、黄糊精0.9-1.3。
2.根据权利要求1所述的一种萜烯树脂包覆改性玻化微珠保温砂浆的制作方法，其特征在于包括以下步骤：
（1）将鸡毛梗烘干、脱脂超细研磨成粉，加入黄糊精、异丁基三乙氧基硅烷超声分散研磨1-2小时，烘干；
（2）将玻化微珠于105℃下干燥2小时冷却至室温，投入翻转式混合反应釜内，升温至100-115℃，将熔融状态的萜烯树脂喷洒在玻化微珠表面，加入步骤（1）物料翻转混合10-20分钟后，再喷洒松香乳液，翻转混合10-20分钟，烘干制得改性玻化微珠；
（3）将钢渣微粉高温煅烧处理后加入普通硅酸盐水泥于翻转式混合反应釜内翻转20-30分钟混匀，再加入改性玻化微珠及其它剩余成分翻转混合20-30分钟，将搅拌好的物料用自动包装机包好出料。
CN201510332070.1A 2015-06-16 2015-06-16 一种萜烯树脂包覆改性玻化微珠保温砂浆及其制作方法 Pending CN104909673A (zh)