CN104907772A - 一种小型suv油箱盖盖面的制备方法 - Google Patents

一种小型suv油箱盖盖面的制备方法 Download PDF

Info

Publication number
CN104907772A
CN104907772A CN201510299248.7A CN201510299248A CN104907772A CN 104907772 A CN104907772 A CN 104907772A CN 201510299248 A CN201510299248 A CN 201510299248A CN 104907772 A CN104907772 A CN 104907772A
Authority
CN
China
Prior art keywords
capping
polishing
sand
baking
mould
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510299248.7A
Other languages
English (en)
Inventor
俞海
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HANSHAN HENGXIANG MACHINERY MANUFACTURING Co Ltd
Original Assignee
HANSHAN HENGXIANG MACHINERY MANUFACTURING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HANSHAN HENGXIANG MACHINERY MANUFACTURING Co Ltd filed Critical HANSHAN HENGXIANG MACHINERY MANUFACTURING Co Ltd
Priority to CN201510299248.7A priority Critical patent/CN104907772A/zh
Publication of CN104907772A publication Critical patent/CN104907772A/zh
Pending legal-status Critical Current

Abstract

一种小型SUV油箱盖盖面的制备方法，涉及汽车配件铸造技术领域，其特征在于：包括设计形状、选择砂、制作盖面、烘烤盖面、打磨盖面、冲洗盖面、精细打磨、检验产品。本发明方法合理、操作方便、实施方便。

Description

一种小型SUV油箱盖盖面的制备方法
技术领域：
本发明涉及汽车配件铸造技术领域，具体涉及一种小型SUV油箱盖盖面的制备方法。
背景技术：
SUV的全称是SportUtility Vehicle，中文意思是运动型多用途汽车。现在主要是指那些设计前卫、造型新颖的四轮驱动越野车。SUV一般前悬架是轿车型的独立悬架，后悬架是非独立悬架，离地间隙较大，在一定程度上既有轿车的舒适性又有越野车的越野性能。由于带有MPV式的座椅多组合功能，使车辆既可载人又可载货，适用范围广。
油箱盖是指汽车上的用于储备汽油的箱子。形状是方形的，用不锈钢做成，密封性很好。只有一个小小的园形入口，这个口只有瓶子的盖子一样大，便于储存。一般是放在汽车的尾部。
每款车型、每种车的油箱盖都是不相同的，并且每种车型对于车子的各个部分的要求都不一样，情况下油箱盖都是大批量生产的，油箱盖在使用长久后容易折断，造成了许多的不必要的麻烦。
发明内容：
本发明所要解决的技术问题在于克服现有的技术缺陷提供一种方法合理、操作方便、实施方便的一种小型SUV油箱盖盖面的制备方法。
本发明所要解决的技术问题采用以下的技术方案来实现：
一种小型SUV油箱盖盖面的制备方法，其特征在于：包括以下步骤，
步骤一、设计形状：按照需求设计铸造模具；
步骤二、选择砂：选择耐高温砂，在耐高温砂中加入C9石油树脂，然后在震荡设备中将两种材料震荡混合；
步骤三、制作盖面：在模具内涂抹一层石英砂，然后再向模具内浇铸铝水和铂水的混合物，其中铂的量是铝的量的1/3；
步骤四、烘烤盖面：将带有混合物的模具放入烘烤箱中烘烤，烘烤的温度为199-259℃，烘烤时间为33-49分钟；
步骤五、打磨盖面：将步骤四中的外盖取出，然后放入装有步骤二的砂的震荡设备中进行震荡打磨，将盖面表面打磨，打磨的时间为10-15分钟；
步骤六、冲洗盖面：将打磨后的盖面取出，然后用蒸馏水冲洗盖面5-8分钟；
步骤七、精细打磨：将冲洗后的盖面静置2分钟后放入抛光机中进行精细化的抛光打磨后得到成品；
步骤八、检验产品：将成品的盖面进行检验，合格的产品包装入库。
本发明的有益效果为：通过两种不同的金属的混合以及其他的几种材料的添加，使得产品的韧性很高，并且加工的方法不难，操作起来并不需要浪费太多的时间。本发明方法合理、操作方便、实施方便。
具体实施方式：
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面进一步阐述本发明。
一种小型SUV油箱盖盖面的制备方法，其特征在于：包括以下步骤，
步骤一、设计形状：按照需求设计铸造模具；
步骤二、选择砂：选择耐高温砂，在耐高温砂中加入C9石油树脂，然后在震荡设备中将两种材料震荡混合；
步骤三、制作盖面：在模具内涂抹一层石英砂，然后再向模具内浇铸铝水和铂水的混合物，其中铂的量是铝的量的1/3；
步骤四、烘烤盖面：将带有混合物的模具放入烘烤箱中烘烤，烘烤的温度为199-259℃，烘烤时间为33-49分钟；
步骤五、打磨盖面：将步骤四中的外盖取出，然后放入装有步骤二的砂的震荡设备中进行震荡打磨，将盖面表面打磨，打磨的时间为10-15分钟；
步骤六、冲洗盖面：将打磨后的盖面取出，然后用蒸馏水冲洗盖面5-8分钟；
步骤七、精细打磨：将冲洗后的盖面静置2分钟后放入抛光机中进行精细化的抛光打磨后得到成品；
步骤八、检验产品：将成品的盖面进行检验，合格的产品包装入库。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。

Claims (1)

1.一种小型SUV油箱盖盖面的制备方法，其特征在于：包括以下步骤，
步骤一、设计形状：按照需求设计铸造模具；
步骤二、选择砂：选择耐高温砂，在耐高温砂中加入C9石油树脂，然后在震荡设备中将两种材料震荡混合；
步骤三、制作盖面：在模具内涂抹一层石英砂，然后再向模具内浇铸铝水和铂水的混合物，其中铂的量是铝的量的1/3；
步骤四、烘烤盖面：将带有混合物的模具放入烘烤箱中烘烤，烘烤的温度为199-259℃，烘烤时间为33-49分钟；
步骤五、打磨盖面：将步骤四中的外盖取出，然后放入装有步骤二的砂的震荡设备中进行震荡打磨，将盖面表面打磨，打磨的时间为10-15分钟；
步骤六、冲洗盖面：将打磨后的盖面取出，然后用蒸馏水冲洗盖面5-8分钟；
步骤七、精细打磨：将冲洗后的盖面静置2分钟后放入抛光机中进行精细化的抛光打磨后得到成品；
步骤八、检验产品：将成品的盖面进行检验，合格的产品包装入库。
CN201510299248.7A 2015-06-01 2015-06-01 一种小型suv油箱盖盖面的制备方法 Pending CN104907772A (zh)