CN104895297A - Anti-bacterial, anti-static and anti-corrosive rubber floor - Google Patents
Anti-bacterial, anti-static and anti-corrosive rubber floor Download PDFInfo
- Publication number
- CN104895297A CN104895297A CN201510285731.XA CN201510285731A CN104895297A CN 104895297 A CN104895297 A CN 104895297A CN 201510285731 A CN201510285731 A CN 201510285731A CN 104895297 A CN104895297 A CN 104895297A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber floor
- rubber
- floor covering
- floor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an anti-bacterial, anti-static and anti-corrosive rubber floor. The anti-bacterial, anti-static and anti-corrosive rubber floor is formed by raw material comprising, by weight, 20 to 30 parts of neoprene, 33 to 43 parts of chemigum, 25 to 30 parts of ethylene-propylene-diene monomer rubber, 2 to 4 parts of magnesium oxide, 0.5 to 1.5 parts of stearic acid, 15 to 28 parts of semi-reinforcing furnace black, 4 to 8 parts of zinc oxide, 0.3 to 0.8 parts of thiuram type accelerators, 4 to 8 parts of antioxidant RD, 1.5 to 1.8 parts of isothiazolinone, 0.5 to 0.8 parts of calcium hypochlorite and 3 to 5 parts of conductive fibers. The floor is coated with coating liquid. The anti-bacterial, anti-static and anti-corrosive rubber floor has following beneficial effects: an anti-bacterial effect is exerted upon bacteria on the surface; service lifetime of the rubber floor is prolonged; cost for cleaning and replacing the rubber floor at the later period is reduced; the rubber floor has permanent anti-static performance by adding the conductive fibers; the coating liquid of the rubber floor adopts acrylic resin, compound polybenzoxazine material and keto-aldehyde resin KR-80 F as film forming matter such that strength, adhesive force and corrosion-resistant performance are enhanced; the hydrophobic property of the rubber floor is improved so that the floor is prevented from foaming and falling by being soaked under water; and an anti-corrosion effect is obtained.
Description
Technical field
The present invention relates to field, floor, specifically a kind of antibiotic antistatic anticorrosion rubber floor covering.
Background technology
Along with improving constantly of people's quality of the life, the finishing in the places such as sales field, hospital and family requires also to improve thereupon.In the lay-up on ground, except can using ceramic tile, wood floors, can also lay with other various types of functional floors.At home and abroad, occasionally have hear sales field, dining room or other places of business because client falls injured and event that is that compensate, if these places of business adopt the floor that antiskid property is good, relatively must reduce the generation that this type of compensates event.In functional floor, the surperficial antiskid property of rubber floor covering is good, can effectively avoid people to slide into, and is particularly useful for being laid in hospital or sales field.But at present rubber floor covering or only have antibiotic property, or only have static electricity resistance, or only have anticorrosive property, but there is no the floor of comprehensive antibiotic property, antistatic behaviour and anticorrosive property.
Summary of the invention
The object of the present invention is to provide a kind of antibiotic antistatic anticorrosion rubber floor covering, to solve the problem proposed in above-mentioned background technology.
For achieving the above object, the invention provides following technical scheme:
A kind of antibiotic antistatic anticorrosion rubber floor covering, be made up of the raw material of following weight parts:
Neoprene 20-30 part, acrylonitrile-butadiene rubber 33-43 part, ethylene propylene diene rubber 25-30 part, magnesia 2-4 part, stearic acid 0.5-1.5 part, semi-reinforcing furnace black 15-28 part, zinc oxide 4-8 part, thuriam acceserator 0.3-0.8 part, 2,2,4-trimethyl-1,2-dihyaroquinoline condensate 4-8 part, OIT 1.5-1.8 part, calcium hypochlorite 0.5-0.8 part, conductive fiber 3-5;
Described rubber floor covering scribbles anticorrosive coating, and its raw material of described anticorrosive coating comprises by weight: acrylic resin 20-50 part, composite polyphenylene Bing oxazine material 30-50 part, aldehyde ketone resin KR-80F 10-20 part, paraffin 0-1 part, zirconium chloride 0-0.5 part, lignin fibre 1-6 part, aluminum-zirconium coupling agent TL-4 1-2 part, curing compound 1-5 part, dispersing agent 0-0.5 part, defoamer 1-2 part, mould inhibitor 0-2 part, pigment 1-5 part, solvent 50-100 part; Wherein, solvent be by n-butanol and dimethylbenzene in mass ratio 6:5 be mixed.
Preferably, a kind of antibiotic antistatic anticorrosion rubber floor covering, be made up of the raw material of following weight parts:
Neoprene 25 parts, acrylonitrile-butadiene rubber 37 parts, ethylene propylene diene rubber 28 parts, 4 parts, magnesia, stearic acid 1 part, semi-reinforcing furnace black 23 parts, 6 parts, zinc oxide, thuriam acceserator 0.6 part, 2,2,4-trimethyl-1,2-dihyaroquinoline condensate 6 parts, OIT 1.6 parts, calcium hypochlorite 0.6 part, conductive fiber 4.
Preferably, its raw material of described anticorrosive coating comprises by weight: acrylic resin 40 parts, composite polyphenylene Bing oxazine material 48 parts, aldehyde ketone resin KR-80F 17 parts, 0.5 part, paraffin, zirconium chloride 0.1 part, lignin fibre 5 parts, aluminum-zirconium coupling agent TL-4 1.2 parts, 2.5 parts, curing compound, dispersing agent 0.1 part, defoamer 1.3 parts, mould inhibitor 1.4 parts, pigment 1.8 parts, solvent 61 parts; Wherein, solvent be by n-butanol and dimethylbenzene in mass ratio 6:5 be mixed.
Preferably, described conductive fiber is carbon fiber.
Preferably, described carbon fiber is continuity carbon fiber or short fiber.
Preferably, described top layer through alkali-treated, described alkali treatment be by slice after top layer be placed in that temperature is 22 DEG C, concentration be 3% sodium hydrate aqueous solution soak 60 ~ 90 minutes.
Compared with prior art, the invention has the beneficial effects as follows:
Rubber floor covering of the present invention the bacterium of effects on surface can not only have antibacterial action, extend the service time of rubber floor covering, reduce the cost that rubber floor covering was cleaned and replaced to the later stage, also rubber floor covering of the present invention is made to have permanent antistatic by adding conductive fiber, coating on rubber floor covering adopts acrylic resin, composite polyphenylene Bing oxazine material, aldehyde ketone resin KR-80F is as film forming matter and add solvent, substantially increase intensity, adhesive power and Corrosion Protection, and enhance hydrophobicity of the present invention, the present invention is avoided to foam under the immersion of water, come off thus lose anticorrosion ability.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention is further illustrated.
Embodiment 1
A kind of antibiotic antistatic anticorrosion of the present invention rubber floor covering, is made up of the component of following weight portion:
Neoprene 20 parts, acrylonitrile-butadiene rubber 38 parts, ethylene propylene diene rubber 30 parts, 2 parts, magnesia, stearic acid 0.8 part, semi-reinforcing furnace black 25 parts, 7 parts, zinc oxide, thuriam acceserator 0.4 part, 2,2,4-trimethyl-1,2-dihyaroquinoline condensate 5 parts, OIT 1.5 parts, calcium hypochlorite 0.8 part, conductive fiber 3.2.
Embodiment 2
The present embodiment and embodiment 1 not difference are only, described top layer is rubber, and described rubber consists of: with parts by weight,
Neoprene 30 parts, acrylonitrile-butadiene rubber 33 parts, ethylene propylene diene rubber 25 parts, 3 parts, magnesia, stearic acid 1.3 parts, semi-reinforcing furnace black 17 parts, 4 parts, zinc oxide, thuriam acceserator 0.7 part, 2,2,4-trimethyl-1,2-dihyaroquinoline condensate 7 parts, OIT 1.8 parts, calcium hypochlorite 0.5 part, conductive fiber 4.5.
Embodiment 3
The present embodiment and embodiment 1 not difference are only, described top layer is rubber, and described rubber consists of: with parts by weight,
Neoprene 25 parts, acrylonitrile-butadiene rubber 37 parts, ethylene propylene diene rubber 28 parts, 4 parts, magnesia, stearic acid 1 part, semi-reinforcing furnace black 23 parts, 6 parts, zinc oxide, thuriam acceserator 0.6 part, 2,2,4-trimethyl-1,2-dihyaroquinoline condensate 6 parts, OIT 1.6 parts, calcium hypochlorite 0.6 part, conductive fiber 4.
Described rubber floor covering scribbles anticorrosive coating, and its raw material of described anticorrosive coating comprises by weight: acrylic resin 40 parts, composite polyphenylene Bing oxazine material 48 parts, aldehyde ketone resin KR-80F 17 parts, 0.5 part, paraffin, zirconium chloride 0.1 part, lignin fibre 5 parts, aluminum-zirconium coupling agent TL-4 1.2 parts, 2.5 parts, curing compound, dispersing agent 0.1 part, defoamer 1.3 parts, mould inhibitor 1.4 parts, pigment 1.8 parts, solvent 61 parts; Wherein, solvent be by n-butanol and dimethylbenzene in mass ratio 6:5 be mixed.
Described top layer through alkali-treated, described alkali treatment be by slice after top layer be placed in that temperature is 22 DEG C, concentration be 3% sodium hydrate aqueous solution soak 60 ~ 90 minutes.
Described conductive fiber is carbon fiber, and described carbon fiber is continuity carbon fiber or short fiber.
Claims (6)
1. an antibiotic antistatic anticorrosion rubber floor covering, is characterized in that, is made up of the raw material of following weight parts:
Neoprene 20-30 part, acrylonitrile-butadiene rubber 33-43 part, ethylene propylene diene rubber 25-30 part, magnesia 2-4 part, stearic acid 0.5-1.5 part, semi-reinforcing furnace black 15-28 part, zinc oxide 4-8 part, thuriam acceserator 0.3-0.8 part, 2,2,4-trimethyl-1,2-dihyaroquinoline condensate 4-8 part, OIT 1.5-1.8 part, calcium hypochlorite 0.5-0.8 part, conductive fiber 3-5;
Described rubber floor covering scribbles anticorrosive coating, and its raw material of described anticorrosive coating comprises by weight: acrylic resin 20-50 part, composite polyphenylene Bing oxazine material 30-50 part, aldehyde ketone resin KR-80F 10-20 part, paraffin 0-1 part, zirconium chloride 0-0.5 part, lignin fibre 1-6 part, aluminum-zirconium coupling agent TL-4 1-2 part, curing compound 1-5 part, dispersing agent 0-0.5 part, defoamer 1-2 part, mould inhibitor 0-2 part, pigment 1-5 part, solvent 50-100 part; Wherein, solvent be by n-butanol and dimethylbenzene in mass ratio 6:5 be mixed.
2. a kind of antibiotic antistatic anticorrosion rubber floor covering according to claim 1, is characterized in that, be made up of the raw material of following weight parts:
Neoprene 25 parts, acrylonitrile-butadiene rubber 37 parts, ethylene propylene diene rubber 28 parts, 4 parts, magnesia, stearic acid 1 part, semi-reinforcing furnace black 23 parts, 6 parts, zinc oxide, thuriam acceserator 0.6 part, 2,2,4-trimethyl-1,2-dihyaroquinoline condensate 6 parts, OIT 1.6 parts, calcium hypochlorite 0.6 part, conductive fiber 4.
3. a kind of antibiotic antistatic anticorrosion rubber floor covering according to claim 1, it is characterized in that, its raw material of described anticorrosive coating comprises by weight: acrylic resin 40 parts, composite polyphenylene Bing oxazine material 48 parts, aldehyde ketone resin KR-80F 17 parts, 0.5 part, paraffin, zirconium chloride 0.1 part, lignin fibre 5 parts, aluminum-zirconium coupling agent TL-4 1.2 parts, 2.5 parts, curing compound, dispersing agent 0.1 part, defoamer 1.3 parts, mould inhibitor 1.4 parts, pigment 1.8 parts, solvent 61 parts; Wherein, solvent be by n-butanol and dimethylbenzene in mass ratio 6:5 be mixed.
4. a kind of antibiotic antistatic anticorrosion rubber floor covering according to claim 1, it is characterized in that, described conductive fiber is carbon fiber.
5. a kind of antibiotic antistatic anticorrosion rubber floor covering according to claim 3, it is characterized in that, described carbon fiber is continuity carbon fiber or short fiber.
6. a kind of antibiotic antistatic anticorrosion rubber floor covering according to claim 1, it is characterized in that, described top layer through alkali-treated, described alkali treatment be by slice after top layer be placed in that temperature is 22 DEG C, concentration be 3% sodium hydrate aqueous solution soak 60 ~ 90 minutes.