CN104927124A - Antibacterial antistatic and wear-resistant rubber floor - Google Patents

Antibacterial antistatic and wear-resistant rubber floor Download PDF

Info

Publication number
CN104927124A
CN104927124A CN201510285881.0A CN201510285881A CN104927124A CN 104927124 A CN104927124 A CN 104927124A CN 201510285881 A CN201510285881 A CN 201510285881A CN 104927124 A CN104927124 A CN 104927124A
Authority
CN
China
Prior art keywords
parts
rubber floor
rubber
floor
wear
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510285881.0A
Other languages
Chinese (zh)
Inventor
项宗武
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI TONGFENG RUBBER & PLASTIC INDUSTRY Co Ltd
Original Assignee
ANHUI TONGFENG RUBBER & PLASTIC INDUSTRY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI TONGFENG RUBBER & PLASTIC INDUSTRY Co Ltd filed Critical ANHUI TONGFENG RUBBER & PLASTIC INDUSTRY Co Ltd
Priority to CN201510285881.0A priority Critical patent/CN104927124A/en
Publication of CN104927124A publication Critical patent/CN104927124A/en
Pending legal-status Critical Current

Abstract

The invention discloses an antibacterial antistatic and wear-resistant rubber floor which is prepared from the following raw materials in parts by weight: 20 to 30 parts of chloroprene rubber, 33 to 43 parts of butadiene-acrylonitrile rubber, 25 to 30 parts of ethylene propylene diene monomer, 2 to 4 parts of magnesium oxide, 0.5 to 1.5 parts of stearic acid, 15 to 28 parts of semi-reinforcing furnace black, 4 to 8 parts of zinc oxide, 0.3 to 0.8 parts of a thiuram type accelerator, 4 to 8 parts of 2,2,4-trimethyl-1,2-dihydroquinoline polymer, 1.5 to 1.8 parts of isothiazolinone, 0.5 to 0.8 parts of calcium hypochlorite and 3 to 5 parts of conductive fibers. The floor is coated with a coating, so that the rubber floor has the antibacterial effect on surface bacteria, the service life of the rubber floor is prolonged, and the later cleaning and replacement costs of the rubber floor are reduced; the conductive fibers are added, so that the rubber floor has permanent antistatic property; epoxy resin in the coating of the rubber floor, a compound polybenzoxazine material and glycerin alkyd resin serve as film-forming substances, so that the wear resistance, impact resistance, corrosion resistance and adhesion of the rubber floor are greatly improved.

Description

A kind of antibiotic antistatic abrasive rubber floor
Technical field
The present invention relates to field, floor, specifically a kind of antibiotic antistatic abrasive rubber floor.
Background technology
Along with improving constantly of people's quality of the life, the finishing in the places such as sales field, hospital and family requires also to improve thereupon.In the lay-up on ground, except can using ceramic tile, wood floors, can also lay with other various types of functional floors.At home and abroad, occasionally have hear sales field, dining room or other places of business because client falls injured and event that is that compensate, if these places of business adopt the floor that antiskid property is good, relatively must reduce the generation that this type of compensates event.In functional floor, the surperficial antiskid property of rubber floor covering is good, can effectively avoid people to slide into, and is particularly useful for being laid in hospital or sales field.But at present rubber floor covering or only have germ resistance, or only have static electricity resistance, or only have non-corrosibility, but there is no the floor of comprehensive germ resistance, static resistance and non-corrosibility.
Summary of the invention
The object of the present invention is to provide a kind of antibiotic antistatic abrasive rubber floor, to solve the problem proposed in above-mentioned background technology.
For achieving the above object, the invention provides following technical scheme:
A kind of antibiotic antistatic abrasive rubber floor, be made up of the raw material of following weight parts:
Chloroprene rubber 20-30 part, paracril 33-43 part, terpolymer EP rubber 25-30 part, magnesium oxide 2-4 part, stearic acid 0.5-1.5 part, semi-reinforcing furnace black 15-28 part, zinc oxide 4-8 part, thiuram type accelerator 0.3-0.8 part, 2,2,4-trimethylammonium-1,2-dihyaroquinoline polymer 4-8 part, isothiazolinone 1.5-1.8 part, Losantin 0.5-0.8 part, electro-conductive fiber 3-5;
Described rubber floor covering scribbles wear-resistant paint, and its raw material of described wear-resistant paint comprises by weight: composite polyphenylene Bing oxazine material 52-55 part, epoxy resin 37-40 part, glyptal 22-25 part, talcum powder 5-8 part, organobentonite 4-5 part, nano titanium oxide 9-12 part, mica powder 9-12 part, titanate coupling agent 1.8-2.2 part, solidifying agent 1.6-1.9 part, defoamer 1-1.3 part, toughner 3.2-3.6 part, mould inhibitor 0.8-1.2 part, pigment 2.2-2.5 part, solvent 65-70 part.
Preferably, described a kind of antibiotic antistatic abrasive rubber floor, is characterized in that, be made up of the raw material of following weight parts:
Chloroprene rubber 25 parts, paracril 37 parts, terpolymer EP rubber 28 parts, 4 parts, magnesium oxide, stearic acid 1 part, semi-reinforcing furnace black 23 parts, 6 parts, zinc oxide, thiuram type accelerator 0.6 part, 2,2,4-trimethylammonium-1,2-dihyaroquinoline polymer 6 parts, isothiazolinone 1.6 parts, Losantin 0.6 part, electro-conductive fiber 4.
Preferably, its raw material of described wear-resistant paint comprises by weight: composite polyphenylene Bing oxazine material 52 parts, epoxy resin 37 parts, glyptal 25 parts, talcum powder 8 parts, organobentonite 4 parts, nano titanium oxide 10 parts, mica powder 10 parts, titanate coupling agent 1.8 parts, 1.6 parts, solidifying agent, defoamer 1 part, toughner 3.3 parts, mould inhibitor 1 part, pigment 2.4 parts, solvent 65 parts; Wherein, solvent is mixed by weight 6:5 by acetone, polyglycerol.
Preferably, described electro-conductive fiber is carbon fiber.
Preferably, described carbon fiber is continuity carbon fiber or staple fibre.
Preferably, described top layer through alkali-treated, described alkaline purification be by slice after top layer be placed in that temperature is 22 DEG C, concentration be 3% aqueous sodium hydroxide solution soak 60 ~ 90 minutes.
Compared with prior art, the invention has the beneficial effects as follows:
Rubber floor covering of the present invention the bacterium of effects on surface can not only have anti-microbial effect, extend the duration of service of rubber floor covering, reduce the cost that rubber floor covering was cleaned and replaced to the later stage, also rubber floor covering of the present invention is made to have permanent antistatic by adding electro-conductive fiber, coating on rubber floor covering, epoxy resin in coating and composite polyphenylene Bing oxazine material, glyptal, as filmogen, significantly improve wear-resisting, impact resistance of the present invention and protection against corrosion, adhesion property.
Embodiment
Below in conjunction with specific embodiment, the present invention is further illustrated.
Embodiment 1
A kind of antibiotic antistatic abrasive rubber floor of the present invention, is made up of the component of following weight part:
Chloroprene rubber 20 parts, paracril 38 parts, terpolymer EP rubber 30 parts, 2 parts, magnesium oxide, stearic acid 0.8 part, semi-reinforcing furnace black 25 parts, 7 parts, zinc oxide, thiuram type accelerator 0.4 part, 2,2,4-trimethylammonium-1,2-dihyaroquinoline polymer 5 parts, isothiazolinone 1.5 parts, Losantin 0.8 part, electro-conductive fiber 3.2.
Embodiment 2
The present embodiment and embodiment 1 not difference are only, described top layer is rubber, and described rubber consists of: with parts by weight,
Chloroprene rubber 30 parts, paracril 33 parts, terpolymer EP rubber 25 parts, 3 parts, magnesium oxide, stearic acid 1.3 parts, semi-reinforcing furnace black 17 parts, 4 parts, zinc oxide, thiuram type accelerator 0.7 part, 2,2,4-trimethylammonium-1,2-dihyaroquinoline polymer 7 parts, isothiazolinone 1.8 parts, Losantin 0.5 part, electro-conductive fiber 4.5.
Embodiment 3
The present embodiment and embodiment 1 not difference are only, described top layer is rubber, and described rubber consists of: with parts by weight,
Chloroprene rubber 25 parts, paracril 37 parts, terpolymer EP rubber 28 parts, 4 parts, magnesium oxide, stearic acid 1 part, semi-reinforcing furnace black 23 parts, 6 parts, zinc oxide, thiuram type accelerator 0.6 part, 2,2,4-trimethylammonium-1,2-dihyaroquinoline polymer 6 parts, isothiazolinone 1.6 parts, Losantin 0.6 part, electro-conductive fiber 4.
Described rubber floor covering scribbles wear-resistant paint, and its raw material of described wear-resistant paint comprises by weight: composite polyphenylene Bing oxazine material 52 parts, epoxy resin 37 parts, glyptal 25 parts, talcum powder 8 parts, organobentonite 4 parts, nano titanium oxide 10 parts, mica powder 10 parts, titanate coupling agent 1.8 parts, 1.6 parts, solidifying agent, defoamer 1 part, toughner 3.3 parts, mould inhibitor 1 part, pigment 2.4 parts, solvent 65 parts; Wherein, solvent is mixed by weight 6:5 by acetone, polyglycerol.
Described top layer through alkali-treated, described alkaline purification be by slice after top layer be placed in that temperature is 22 DEG C, concentration be 3% aqueous sodium hydroxide solution soak 60 ~ 90 minutes.
Described electro-conductive fiber is carbon fiber, and described carbon fiber is continuity carbon fiber or staple fibre.

Claims (6)

1. an antibiotic antistatic abrasive rubber floor, is characterized in that, is made up of the raw material of following weight parts:
Chloroprene rubber 20-30 part, paracril 33-43 part, terpolymer EP rubber 25-30 part, magnesium oxide 2-4 part, stearic acid 0.5-1.5 part, semi-reinforcing furnace black 15-28 part, zinc oxide 4-8 part, thiuram type accelerator 0.3-0.8 part, 2,2,4-trimethylammonium-1,2-dihyaroquinoline polymer 4-8 part, isothiazolinone 1.5-1.8 part, Losantin 0.5-0.8 part, electro-conductive fiber 3-5;
Described rubber floor covering scribbles wear-resistant paint, and its raw material of described wear-resistant paint comprises by weight: composite polyphenylene Bing oxazine material 52-55 part, epoxy resin 37-40 part, glyptal 22-25 part, talcum powder 5-8 part, organobentonite 4-5 part, nano titanium oxide 9-12 part, mica powder 9-12 part, titanate coupling agent 1.8-2.2 part, solidifying agent 1.6-1.9 part, defoamer 1-1.3 part, toughner 3.2-3.6 part, mould inhibitor 0.8-1.2 part, pigment 2.2-2.5 part, solvent 65-70 part.
2. a kind of antibiotic antistatic abrasive rubber floor according to claim 1, is characterized in that, be made up of the raw material of following weight parts:
Chloroprene rubber 25 parts, paracril 37 parts, terpolymer EP rubber 28 parts, 4 parts, magnesium oxide, stearic acid 1 part, semi-reinforcing furnace black 23 parts, 6 parts, zinc oxide, thiuram type accelerator 0.6 part, 2,2,4-trimethylammonium-1,2-dihyaroquinoline polymer 6 parts, isothiazolinone 1.6 parts, Losantin 0.6 part, electro-conductive fiber 4.
3. a kind of antibiotic antistatic abrasive rubber floor according to claim 1, it is characterized in that, its raw material of described wear-resistant paint comprises by weight: composite polyphenylene Bing oxazine material 52 parts, epoxy resin 37 parts, glyptal 25 parts, talcum powder 8 parts, organobentonite 4 parts, nano titanium oxide 10 parts, mica powder 10 parts, titanate coupling agent 1.8 parts, 1.6 parts, solidifying agent, defoamer 1 part, toughner 3.3 parts, mould inhibitor 1 part, pigment 2.4 parts, solvent 65 parts; Wherein, solvent is mixed by weight 6:5 by acetone, polyglycerol.
4. a kind of antibiotic antistatic abrasive rubber floor according to claim 1, it is characterized in that, described electro-conductive fiber is carbon fiber.
5. a kind of antibiotic antistatic abrasive rubber floor according to claim 3, it is characterized in that, described carbon fiber is continuity carbon fiber or staple fibre.
6. a kind of antibiotic antistatic abrasive rubber floor according to claim 1, it is characterized in that, described top layer through alkali-treated, described alkaline purification be by slice after top layer be placed in that temperature is 22 DEG C, concentration be 3% aqueous sodium hydroxide solution soak 60 ~ 90 minutes.
CN201510285881.0A 2015-05-29 2015-05-29 Antibacterial antistatic and wear-resistant rubber floor Pending CN104927124A (en)