CN104894609A - 一种软金属产品的成型加工方法 - Google Patents

一种软金属产品的成型加工方法 Download PDF

Info

Publication number
CN104894609A
CN104894609A CN201510337913.7A CN201510337913A CN104894609A CN 104894609 A CN104894609 A CN 104894609A CN 201510337913 A CN201510337913 A CN 201510337913A CN 104894609 A CN104894609 A CN 104894609A
Authority
CN
China
Prior art keywords
soft metal
metal product
hanger
plastic cylinder
liquid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510337913.7A
Other languages
English (en)
Inventor
张拥军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201510337913.7A priority Critical patent/CN104894609A/zh
Publication of CN104894609A publication Critical patent/CN104894609A/zh
Pending legal-status Critical Current

Abstract

一种软金属产品的成型加工方法，该方法的特点是可以实现在软金属产品的表面再镀上一层“黄金膜”，从而可以改善软金属产品普遍存在的易变形、易损伤、抗压差、自我恢复能力差等缺陷。

Description

一种软金属产品的成型加工方法
技术领域
本发明涉及软金属产品领域，尤其涉及一种软金属产品的成型加工方法。
背景技术
在日常生活中，软金属产品是最为常见的一种金属产品。其中，最为常见的软件金属产品可以包括由黄金、银等软金属加工成型的戒指、手镯、手链以及耳环等软金属产品。在实践中发现，由黄金、银等软金属加工成型的戒指、手镯、手链以及耳环等软金属产品普遍存在易变形、易损伤、抗压差、自我恢复能力差等缺陷。
发明内容
本发明实施例公开了一种软金属产品的成型加工方法，用于改善软金属产品普遍存在的易变形、易损伤、抗压差、自我恢复能力差等缺陷。
其中，一种软金属产品的成型加工方法，包括：
步骤1：将软金属产品挂在导电的挂架上；
步骤2：将挂有软金属产品的挂架浸入装有包含金盐的液体的塑料缸体中，该挂架套嵌在塑料缸体的转轴上；其中，该塑料缸体的内侧壁周围设有钛网，该钛网与该挂架以及软金属产品均不接触，该液体含金量的允许范围是6％-16％，该液体PH值的允许范围是2.6-8.6；
步骤3：给该挂架连通负电以及给该钛网连通正电之后，转动该塑料缸体的转轴，从而驱动该挂架带着软金属产品转动，以执行电铸作业；
步骤4：给该挂架以及该钛网断电之后，取出经电铸作业后的软金属产品进行清洗后检查是否合格，如果不合格，重新执行步骤1～步骤4；如果合格，结束加工作业。
其中，软金属产品包括黄金产品、银产品。
其中，包含金盐的液体的温度允许范围是30°～44°。
其中，所述电铸作业的时间长度范是6-8小时。
与现有技术相比，本发明实施例具有以下有益效果：
本发明实施例中，可以实现在软金属产品的表面再镀上一层“黄金膜”，从而可以改善软金属产品普遍存在的易变形、易损伤、抗压差、自我恢复能力差等缺陷。
附图说明
为了更清楚地说明本发明实施例中的技术方案，下面将对实施例中所需要使用的附图作简单地介绍，显而易见地，下面描述中的附图仅仅是本发明的一些实施例，对于本领域普通技术人员来讲，在不付出创造性劳动的前提下，还可以根据这些附图获得其他的附图。
图1是本发明实施例公开的一种软金属产品的成型加工方法的流程图；
图2是本发明实施例公开的一种黄金产品的成型加工方法的示意图。
具体实施方式
下面将结合本发明实施例中的附图，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
本发明实施例公开了一种软金属产品的成型加工方法，用于改善软金属产品普遍存在的易变形、易损伤、抗压差、自我恢复能力差等缺陷。以下分别进行详细说明。
请参阅图1，图1是本发明实施例公开的一种软金属产品的成型加工方法的流程图。如图1所示，该方法可以包括以下步骤：
步骤1：将软金属产品挂在导电的挂架上；
步骤2：将挂有软金属产品的挂架浸入装有包含金盐的液体的塑料缸体中，该挂架套嵌在塑料缸体的转轴上；其中，该塑料缸体的内侧壁周围设有钛网，该钛网与该挂架以及软金属产品均不接触，该液体含金量的允许范围是6％-16％，该液体PH值的允许范围是2.6-8.6；
步骤3：给该挂架连通负电以及给该钛网连通正电之后，转动该塑料缸体的转轴，从而驱动该挂架带着软金属产品转动，以执行电铸作业；
步骤4：给该挂架以及该钛网断电之后，取出经电铸作业后的软金属产品进行清洗后检查是否合格，如果不合格，重新执行步骤1～步骤4；如果合格，结束加工作业。
其中，软金属产品包括黄金产品、银产品。
其中，包含金盐的液体的温度理想值为30°～44°。
其中，所述电铸作业的时间长度范是6-8小时。
本发明实施例中，金盐是行业的俗称，其化学名称是氰化亚金钾，化学式KAu(CN)2。
在图1所描述的方法中，可以实现在软金属产品的表面再镀上一层“黄金膜”，从而可以改善软金属产品普遍存在的易变形、易损伤、抗压差、自我恢复能力差等缺陷。
为了更好理解本发明实施例公开的软金属产品的成型加工方法，下面以黄金产品为例进行举例描述。请参阅图2，图2是本发明实施例公开的一种黄金产品的成型加工方法的示意图。如图2所示，可以包括以下步骤：
步骤1：将黄金产品挂在导电的挂架上；
步骤2：将挂有黄金产品的挂架浸入装有包含金盐的液体的塑料缸体中，该挂架套嵌在塑料缸体的转轴上；其中，该塑料缸体的内侧壁周围设置有钛网，该钛网与该挂架以及黄金产品均不接触，该液体含金量为11％，该液体PH值为5.6；
步骤3：给该挂架连通负电以及给该钛网连通正电之后，转动该塑料缸体的转轴，从而驱动该挂架带着黄金产品转动，以执行电铸作业；
步骤4：给该挂架以及该钛网断电之后，取出经电铸作业后的黄金产品进行清洗后检查是否合格，如果不合格，重新执行步骤1～步骤4；如果合格，结束加工作业。
本发明实施例中，可以采用手工方式或者借助于外力将挂有黄金产品的挂架浸入装有包含金盐的液体的塑料缸体中，本发明实施例不作限定。
本发明实施例中，可以采用手工方式或者借助于外力来转动该塑料缸体的转轴，从而驱动该挂架带着黄金产品转动，以执行电铸作业，本发明实施例不作限定。
在图2所描述的方法中，可以实现在黄金产品的表面再镀上一层“黄金膜”，从而可以改善黄金产品普遍存在的易变形、易损伤、抗压差、自我恢复能力差等缺陷。
以上对本发明实施例公开的一种软金属产品的成型加工方法进行了详细介绍，本文中应用了具体个例对本发明的原理及实施方式进行了阐述，以上实施例的说明只是用于帮助理解本发明的方法及其核心思想；同时，对于本领域的一般技术人员，依据本发明的思想，在具体实施方式及应用范围上均会有改变之处，综上所述，本说明书内容不应理解为对本发明的限制。

Claims (4)

1.一种软金属产品的成型加工方法，其特征在于，包括：
步骤1：将软金属产品挂在导电的挂架上；
步骤2：将挂有软金属产品的挂架浸入装有包含金盐的液体的塑料缸体中，该挂架套嵌在塑料缸体的转轴上；其中，该塑料缸体的内侧壁周围设有钛网，该钛网与该挂架以及软金属产品均不接触，该液体含金量的允许范围是6％-16％，该液体PH值的允许范围是2.6-8.6；
步骤3：给该挂架连通负电以及给该钛网连通正电之后，转动该塑料缸体的转轴，从而驱动该挂架带着软金属产品转动，以执行电铸作业；
步骤4：给该挂架以及该钛网断电之后，取出经电铸作业后的软金属产品进行清洗后检查是否合格，如果不合格，重新执行步骤1～步骤4；如果合格，结束加工作业。
2.根据权利要求1所述的方法，其特征在于，软金属产品包括黄金产品、银产品。
3.根据权利要求1所述的方法，其特征在于，包含金盐的液体的温度理想值为30°～44°。
4.根据权利要求1～3任一项所述的方法，其特征在于，所述电铸作业的时间长度范是6-8小时。
CN201510337913.7A 2015-06-10 2015-06-10 一种软金属产品的成型加工方法 Pending CN104894609A (zh)