CN104891932A - 耐水性石膏 - Google Patents
耐水性石膏 Download PDFInfo
- Publication number
- CN104891932A CN104891932A CN201510273533.1A CN201510273533A CN104891932A CN 104891932 A CN104891932 A CN 104891932A CN 201510273533 A CN201510273533 A CN 201510273533A CN 104891932 A CN104891932 A CN 104891932A
- Authority
- CN
- China
- Prior art keywords
- parts
- gypsum
- water
- emulsions
- polyvinyl alcohol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种耐水性石膏,涉及建筑材料技术领域,由以下重量份的原材料制成:石膏60~80份,硼砂15~25份,水泥12~25份,明矾膨胀剂8~13份,硬脂酸乳液5~10份,聚乙烯醇乳液4~8份,石蜡乳液17~28份,防水剂2~10份。与现有技术相比,本发明能够提高石膏的耐水性。
Description
技术领域
本发明涉及建筑材料技术领域,尤其是一种耐水性石膏。
背景技术
石膏属于气硬性胶凝材料,适合做轻质墙体材料,具有生产能耗低,工艺性能好等优点,但石膏也存在弱点:耐水性差,产生耐水性差的原因是:1. 石膏具有很大的溶解度;2.石膏存在大量的微裂缝和孔隙,这些微裂缝和孔隙易吸水。建筑体一般要求材料的耐水性较强,石膏的耐水性差限制了石膏在建筑领域的应用。
发明内容
本发明所要解决的技术问题是提供一种耐水性石膏,它可以解决石膏耐水性差的问题。
为了解决上述问题,本发明所采用的技术方案是:这种耐水性石膏,由以下重量份的原材料制成:石膏60~80份,硼砂15~25份,水泥12~25份,明矾膨胀剂8~13份,硬脂酸乳液5~10份,聚乙烯醇乳液4~8份,石蜡乳液17~28份,防水剂2~10份。
上述技术方案中,更具体的技术方案还可以是:由以下重量份的原材料制成:石膏70份,硼砂20份,水泥18份,明矾膨胀剂11份,硬脂酸乳液7份,聚乙烯醇乳液6份,石蜡乳液20份,防水剂6份。
由于采用了上述技术方案,本发明与现有技术相比具有如下有益效果:
1、在石膏中掺入硬脂酸乳液和石蜡乳液能够改变石膏的性能,将石膏的亲水性质改变成憎水性质。
2、聚乙烯醇乳液在石膏中形成具有阻水作用的不规则网膜,降低石膏的吸水率。
3、提高石膏耐水性后,扩大了在建筑领域的应用范围。
具体实施方式
以下结合具体实施例对本发明作进一步详述:
实施例1:
这种耐水性石膏,由以下重量份的原材料制成:石膏60份,硼砂15份,水泥12份,明矾膨胀剂8份,硬脂酸乳液5份,聚乙烯醇乳液4份,石蜡乳液17份,防水剂2份。
制法:将石膏加入水泥、明矾膨胀剂、硬脂酸乳液、聚乙烯醇乳液、石蜡乳液和减水剂搅拌均匀得到石膏混合物,加热烘干石膏混合物,加热的温度为200℃,加热的时间为20分钟,制得耐水性石膏。
以下是检验石膏耐水性的实验:
将该耐水性石膏按照检测标准GB/T 9776-2008,检测到本发明的石膏的抗拉强度为15Mpa,抗折强度为5Mpa;将本发明的石膏放入水中浸泡200小时,再照检测标准GB/T 9776-2008,检测到本发明的石膏的抗拉强度为14.9Mpa,抗折强度为5Mpa。
上述实验表明本发明的石膏在水中长时间浸泡后,石膏的抗拉强度和抗折强度没有明显变化,本发明的石膏耐水性较强。
实施例2:
这种耐水性石膏,由以下重量份的原材料制成:石膏80份,硼砂25份,水泥25份,明矾膨胀剂13份,硬脂酸乳液10份,聚乙烯醇乳液8份,石蜡乳液28份,防水剂10份。
制法:将石膏加入水泥、明矾膨胀剂、硬脂酸乳液、聚乙烯醇乳液、石蜡乳液和减水剂搅拌均匀得到石膏混合物,加热烘干石膏混合物,加热的温度为500℃,加热的时间为5分钟,制得耐水性石膏。
以下是检验石膏耐水性的实验:
将该耐水性石膏按照检测标准GB/T 9776-2008,检测到本发明的石膏的抗拉强度为15Mpa,抗折强度为5Mpa;将本发明的石膏放入水中浸泡200小时,再照检测标准GB/T 9776-2008,检测到本发明的石膏的抗拉强度为14.9Mpa,抗折强度为5Mpa。
上述实验表明本发明的石膏在水中长时间浸泡后,石膏的抗拉强度和抗折强度没有明显变化,本发明的石膏耐水性较强。
实施例3:
这种耐水性石膏,由以下重量份的原材料制成:石膏70份,硼砂20份,水泥18份,明矾膨胀剂11份,硬脂酸乳液7份,聚乙烯醇乳液6份,石蜡乳液20份,防水剂6份。
制法:将石膏加入水泥、明矾膨胀剂、硬脂酸乳液、聚乙烯醇乳液、石蜡乳液和减水剂搅拌均匀得到石膏混合物,加热烘干石膏混合物,加热温度为350℃,加热时间为12分钟,制得耐水性石膏。
以下是检验石膏耐水性的实验:
将该耐水性石膏按照检测标准GB/T 9776-2008,检测到本发明的石膏的抗拉强度为15Mpa,抗折强度为5Mpa;将本发明的石膏放入水中浸泡200小时,再照检测标准GB/T 9776-2008,检测到本发明的石膏的抗拉强度为14.9Mpa,抗折强度为5Mpa。
上述实验表明本发明的石膏在水中长时间浸泡后,石膏的抗拉强度和抗折强度没有明显变化,本发明的石膏耐水性较强。
Claims (2)
1.一种耐水性石膏,其特征在于由以下重量份的原材料制成:石膏60~80份,硼砂15~25份,水泥12~25份,明矾膨胀剂8~13份,硬脂酸乳液5~10份,聚乙烯醇乳液4~8份,石蜡乳液17~28份,防水剂2~10份。
2.根据权利要求1所述的耐水性石膏,其特征在于由以下重量份的原材料制成:石膏70份,硼砂20份,水泥18份,明矾膨胀剂11份,硬脂酸乳液7份,聚乙烯醇乳液6份,石蜡乳液20份,防水剂6份。