CN105347773A - 一种适合冬季使用的氯氧镁水泥及其制备方法 - Google Patents

一种适合冬季使用的氯氧镁水泥及其制备方法 Download PDF

Info

Publication number
CN105347773A
CN105347773A CN201510864737.2A CN201510864737A CN105347773A CN 105347773 A CN105347773 A CN 105347773A CN 201510864737 A CN201510864737 A CN 201510864737A CN 105347773 A CN105347773 A CN 105347773A
Authority
CN
China
Prior art keywords
winter
cement
preparation
magnesium oxide
magnesium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201510864737.2A
Other languages
English (en)
Other versions
CN105347773B (zh
Inventor
肖学英
文静
安生霞
李颖
常成功
郑卫新
董金美
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Qinghai Institute of Salt Lakes Research of CAS
Original Assignee
Qinghai Institute of Salt Lakes Research of CAS
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Qinghai Institute of Salt Lakes Research of CAS filed Critical Qinghai Institute of Salt Lakes Research of CAS
Priority to CN201510864737.2A priority Critical patent/CN105347773B/zh
Publication of CN105347773A publication Critical patent/CN105347773A/zh
Application granted granted Critical
Publication of CN105347773B publication Critical patent/CN105347773B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及水泥制备技术领域，尤其是一种适合冬季使用的氯氧镁水泥的制备方法，包括如下步骤：将氧化镁、氯化镁和水按照物质的量比为3～9:1:11～20混合形成浆体；向所述浆体中加入外加剂，形成泥浆，对所述泥浆养护3天以上获得所述适合冬季使用的氯氧镁水泥；所述外加剂质量为所述氧化镁质量的0.5～2倍；其中，所述外加剂选自：硅酸、乙醇、碳酸钙、硬脂酸钠、葡萄糖、十二酸、硫酸亚铁中的一种或多种。本发明可以提高水泥水化过程的放热温度，在环境温度较低的情况下促进浆体的凝结硬化，缩短制品的脱模周期，促进原料的水化反应，提高水泥制品的强度。

Description

一种适合冬季使用的氯氧镁水泥及其制备方法
技术领域
本发明涉及水泥制备技术领域，尤其是氯氧镁水泥的改进技术。
背景技术
氯氧镁水泥是由法国科学家sorel于1867年发明的一种快硬、早强、高强材料。由于它优异的力学性能，致使它的用途十分广泛。
镁水泥的水化反应虽然是一个放热反应，在水化过程中也会产生大量的热量，但是在环境温度相对较低(如我国西部地区冬季，环境温度最低能达到零下30℃左右)的情况下，镁水泥制品凝结硬化速度慢，脱模周期长，严重影响制品的生产效率。
发明内容
为克服现有技术的不足，本发明的目的在于提供一种适合冬季使用的氯氧镁水泥的制备方法，包括如下步骤：
将氧化镁、氯化镁和水按照物质的量比为3～9:1:11～20混合形成浆体；
向所述浆体中加入外加剂，形成泥浆，对所述泥浆养护3天以上获得所述适合冬季使用的氯氧镁水泥；所述外加剂质量为所述氧化镁质量的0.5～2倍；其中，所述外加剂选自：硅酸、乙醇、碳酸钙、硬脂酸钠、葡萄糖、十二酸(月桂酸)、硫酸亚铁中的一种或多种。
进一步地，所述氧化镁、氯化镁、和水按照物质的量比为3～7:1:11～15。
本发明还提供这种适合冬季使用的氯氧镁水泥，包括物质的量比为3～9:1:11～20的氧化镁、氯化镁和水；以及外加剂，所述外加剂质量为所述氧化镁质量的0.5～2倍；其中，所述外加剂选自：硅酸、乙醇、碳酸钙、硬脂酸钠、葡萄糖、十二酸(月桂酸)、硫酸亚铁中的一种或多种。
有益效果：
本发明通过在现有的氯氧镁水泥中添加外加剂，提高水泥水化过程的放热温度，促进镁水泥水化过程的进行，避免硬化温度太低对镁水泥材料水化产物种类和含量的影响，从而进一步影响材料的结构和体积稳定性。
具体实施方式
下面结合具体实施方式对本发明作详细介绍。
本发明提供的一种适合冬季使用的氯氧镁水泥的制备方法，包括如下步骤：
步骤一：将氧化镁、氯化镁、和水按照物质的量比为3～9:1:11～20混合形成浆体。其中所述氧化镁、氯化镁、和水的物质的量之比可简称为“水泥摩尔比”。所述氧化镁、氯化镁、和水按照物质的量之比也可以优选更佳的为3～7:1:11～15。
其中，氧化镁是一种活性氧化镁，其可以有多种来源，例如轻烧粉、苛性粉、盐湖副产品等，各种来源获得后将先行测试活性氧化镁的含量。
步骤二：向所述浆体中加入外加剂，形成泥浆。所述外加剂质量为所述氧化镁质量的0.5～2倍；其中，所述外加剂选自：硅酸、乙醇、碳酸钙、硬脂酸钠、葡萄糖、十二酸(月桂酸)、硫酸亚铁中的一种或多种。
步骤三：在20℃恒温水浴下养护3天，期间持续检测所述泥浆的温度。其中，本发明在恒温水浴中养护是为了与对比例保持相同的养护环境，以便进行性能对比，在其他实施例中，所述泥浆也可以在室温或环境温度下养护完成。
对比例
将氧化镁、氯化镁、和水按照物质的量比为3～9:1:11～20混合形成浆体。然后在20℃恒温水浴下养护3天，期间持续检测所述浆体的温度。
下面，将结合各个实施例及对比例展示本发明的氯氧镁水泥特性，如表1所示。
表1实施例1～10以及对比例1～3的水化反应参数以及水泥性能
(续上表)
从表1可知，添加了外加剂后的各个实施例，其水化过程的温度均比对应的对比例有所提高。由此说明，本发明通过在现有的氯氧镁水泥中添加外加剂，可以提高水泥水化过程的放热温度，在环境温度较低的情况下促进浆体的凝结硬化，缩短制品的脱模周期，促进原料的水化反应，提高水泥制品的强度。
以上所述为本发明的具体实施方式，其目的是为了清楚说明本发明而作的举例，并非是对本发明的实施方式的限定。对于所属领域的普通技术人员来说，在上述说明的基础上还可以做出其它不同形式的变化或变动。这里无需也无法对所有的实施方式予以穷举。凡在本发明的精神和原则之内所作的任何修改、等同替换和改进等，均应包含在本发明权利要求的保护范围之内。

Claims (3)

1.一种适合冬季使用的氯氧镁水泥的制备方法，其特征在于，包括如下步骤：
将氧化镁、氯化镁和水按照物质的量比为3～9:1:11～20混合形成浆体；
向所述浆体中加入外加剂，形成泥浆，对所述泥浆养护3天以上获得所述适合冬季使用的氯氧镁水泥；所述外加剂质量为所述氧化镁质量的0.5～2倍；其中，所述外加剂选自：硅酸、乙醇、碳酸钙、硬脂酸钠、葡萄糖、十二酸、硫酸亚铁中的一种或多种。
2.根据权利要求1所述适合冬季使用的氯氧镁水泥的制备方法，其特征在于，所述氧化镁、氯化镁、和水按照物质的量比为3～7:1:11～15。
3.一种适合冬季使用的氯氧镁水泥，其特征在于，包括物质的量比为3～9:1:11～20的氧化镁、氯化镁和水；以及外加剂，所述外加剂质量为所述氧化镁质量的0.5～2倍；其中，所述外加剂选自硅酸、乙醇、碳酸钙、硬脂酸钠、葡萄糖、十二酸、硫酸亚铁中的一种或多种。
CN201510864737.2A 2015-11-30 2015-11-30 一种适合冬季使用的氯氧镁水泥及其制备方法 Active CN105347773B (zh)