CN105347773B - 一种适合冬季使用的氯氧镁水泥及其制备方法 - Google Patents
一种适合冬季使用的氯氧镁水泥及其制备方法 Download PDFInfo
- Publication number
- CN105347773B CN105347773B CN201510864737.2A CN201510864737A CN105347773B CN 105347773 B CN105347773 B CN 105347773B CN 201510864737 A CN201510864737 A CN 201510864737A CN 105347773 B CN105347773 B CN 105347773B
- Authority
- CN
- China
- Prior art keywords
- magnesia
- additive
- cement
- winter
- oxychloride cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及水泥制备技术领域，尤其是一种适合冬季使用的氯氧镁水泥的制备方法，包括如下步骤：将氧化镁、氯化镁和水按照物质的量比为3～9:1:11～20混合形成浆体；向所述浆体中加入外加剂，形成泥浆，对所述泥浆养护3天以上获得所述适合冬季使用的氯氧镁水泥；所述外加剂质量为所述氧化镁质量的0.5～2倍；其中，所述外加剂选自：硅酸、乙醇、碳酸钙、硬脂酸钠、葡萄糖、十二酸、硫酸亚铁中的一种或多种。本发明可以提高水泥水化过程的放热温度，在环境温度较低的情况下促进浆体的凝结硬化，缩短制品的脱模周期，促进原料的水化反应，提高水泥制品的强度。
Description
技术领域
本发明涉及水泥制备技术领域，尤其是氯氧镁水泥的改进技术。
背景技术
氯氧镁水泥是由法国科学家sorel于1867年发明的一种快硬、早强、高强材料。由于它优异的力学性能，致使它的用途十分广泛。
镁水泥的水化反应虽然是一个放热反应，在水化过程中也会产生大量的热量，但是在环境温度相对较低(如我国西部地区冬季，环境温度最低能达到零下30℃左右)的情况下，镁水泥制品凝结硬化速度慢，脱模周期长，严重影响制品的生产效率。
发明内容
为克服现有技术的不足，本发明的目的在于提供一种适合冬季使用的氯氧镁水泥的制备方法，包括如下步骤：
将氧化镁、氯化镁和水按照物质的量比为3～9:1:11～20混合形成浆体；
向所述浆体中加入外加剂，形成泥浆，对所述泥浆养护3天以上获得所述适合冬季使用的氯氧镁水泥；所述外加剂质量为所述氧化镁质量的0.5～2倍；其中，所述外加剂选自：硅酸、乙醇、碳酸钙、硬脂酸钠、葡萄糖、十二酸(月桂酸)、硫酸亚铁中的一种或多种。
进一步地，所述氧化镁、氯化镁、和水按照物质的量比为3～7:1:11～15。
本发明还提供这种适合冬季使用的氯氧镁水泥，包括物质的量比为3～9:1:11～20的氧化镁、氯化镁和水；以及外加剂，所述外加剂质量为所述氧化镁质量的0.5～2倍；其中，所述外加剂选自：硅酸、乙醇、碳酸钙、硬脂酸钠、葡萄糖、十二酸(月桂酸)、硫酸亚铁中的一种或多种。
有益效果：
本发明通过在现有的氯氧镁水泥中添加外加剂，提高水泥水化过程的放热温度，促进镁水泥水化过程的进行，避免硬化温度太低对镁水泥材料水化产物种类和含量的影响，从而进一步影响材料的结构和体积稳定性。
具体实施方式
下面结合具体实施方式对本发明作详细介绍。
本发明提供的一种适合冬季使用的氯氧镁水泥的制备方法，包括如下步骤：
步骤一：将氧化镁、氯化镁、和水按照物质的量比为3～9:1:11～20混合形成浆体。其中所述氧化镁、氯化镁、和水的物质的量之比可简称为“水泥摩尔比”。所述氧化镁、氯化镁、和水按照物质的量之比也可以优选更佳的为3～7:1:11～15。
其中，氧化镁是一种活性氧化镁，其可以有多种来源，例如轻烧粉、苛性粉、盐湖副产品等，各种来源获得后将先行测试活性氧化镁的含量。
步骤二：向所述浆体中加入外加剂，形成泥浆。所述外加剂质量为所述氧化镁质量的0.5～2倍；其中，所述外加剂选自：硅酸、乙醇、碳酸钙、硬脂酸钠、葡萄糖、十二酸(月桂酸)、硫酸亚铁中的一种或多种。
步骤三：在20℃恒温水浴下养护3天，期间持续检测所述泥浆的温度。其中，本发明在恒温水浴中养护是为了与对比例保持相同的养护环境，以便进行性能对比，在其他实施例中，所述泥浆也可以在室温或环境温度下养护完成。
对比例
将氧化镁、氯化镁、和水按照物质的量比为3～9:1:11～20混合形成浆体。然后在20℃恒温水浴下养护3天，期间持续检测所述浆体的温度。
下面，将结合各个实施例及对比例展示本发明的氯氧镁水泥特性，如表1所示。
表1 实施例1～10以及对比例1～3的水化反应参数以及水泥性能
(续上表)
从表1可知，添加了外加剂后的各个实施例，其水化过程的温度均比对应的对比例有所提高。由此说明，本发明通过在现有的氯氧镁水泥中添加外加剂，可以提高水泥水化过程的放热温度，在环境温度较低的情况下促进浆体的凝结硬化，缩短制品的脱模周期，促进原料的水化反应，提高水泥制品的强度。
以上所述为本发明的具体实施方式，其目的是为了清楚说明本发明而作的举例，并非是对本发明的实施方式的限定。对于所属领域的普通技术人员来说，在上述说明的基础上还可以做出其它不同形式的变化或变动。这里无需也无法对所有的实施方式予以穷举。凡在本发明的精神和原则之内所作的任何修改、等同替换和改进等，均应包含在本发明权利要求的保护范围之内。
Claims (3)
1.一种适合冬季使用的氯氧镁水泥的制备方法，其特征在于，包括如下步骤：
将氧化镁、氯化镁和水按照物质的量比为3～9:1:11～20混合形成浆体；
向所述浆体中加入外加剂，形成泥浆，对所述泥浆养护3天以上获得所述适合冬季使用的氯氧镁水泥；所述外加剂质量为所述氧化镁质量的0.5～2倍；其中，所述外加剂选自：硅酸、碳酸钙、硬脂酸钠、葡萄糖中的一种或多种。
2.根据权利要求1所述适合冬季使用的氯氧镁水泥的制备方法，其特征在于，所述氧化镁、氯化镁、和水按照物质的量比为3～7:1:11～15。
3.一种适合冬季使用的氯氧镁水泥，其特征在于，包括物质的量比为3～9:1:11～20的氧化镁、氯化镁和水；以及外加剂，所述外加剂质量为所述氧化镁质量的0.5～2倍；其中，所述外加剂选自硅酸、碳酸钙、硬脂酸钠、葡萄糖中的一种或多种。