CN104877533A - 一种用于两栖船舰和船坞的涂料组合物 - Google Patents

一种用于两栖船舰和船坞的涂料组合物 Download PDF

Info

Publication number
CN104877533A
CN104877533A CN201510304169.0A CN201510304169A CN104877533A CN 104877533 A CN104877533 A CN 104877533A CN 201510304169 A CN201510304169 A CN 201510304169A CN 104877533 A CN104877533 A CN 104877533A
Authority
CN
China
Prior art keywords
component
paint composition
order
dock
resistance
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201510304169.0A
Other languages
English (en)
Other versions
CN104877533B (zh
Inventor
黄福川
黄祖强
卢朝霞
黄佩芳
黄旖瑶
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangxi University
Original Assignee
Guangxi University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangxi University filed Critical Guangxi University
Priority to CN201510304169.0A priority Critical patent/CN104877533B/zh
Publication of CN104877533A publication Critical patent/CN104877533A/zh
Application granted granted Critical
Publication of CN104877533B publication Critical patent/CN104877533B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种用于两栖船舰和船坞的涂料组合物，由质量比50％的A组分和50％B组分组成；A组分为聚天门冬氨酸酯；B组分由脂肪族异氰酸酯、二氧化钛、三聚磷酸二氢铝、奥氏体不锈钢粉、滑石粉、钛酸酯、碳化硅粉、液态芳香二氨、二乙基甲苯二胺、碳酸乙烯酯组成。本发明组合物的优点：①固化时间可调。聚天门冬氨酸酯与HDI三聚体的反应速度可以采用不同的取代基团的聚天门冬氨酸酯而获得。②具有高拉伸强度、高光泽度、良好的耐磨性、渗透性、耐冲刷性和耐微生物侵蚀性。③优异的附着力，其反应速度慢、时间长，对底材的侵润时间长，附着好。④优异的耐腐蚀性：耐紫外线性能和热稳定性。⑤便于采用常规高压充气喷涂，便于提高施工效率。

Description

一种用于两栖船舰和船坞的涂料组合物
技术领域
本发明属于功能涂料领域，特别涉及一种用于两栖船舰和船坞的涂料组合物。
背景技术
由于两栖船舰和船坞的使用是完全敞开，海水是一种具有很强腐蚀性的电解质，因此船坞处于海洋腐蚀环境中，受到的潜在腐蚀破坏是非常大的。考虑到腐蚀的影响必须选择物理和化学性能优异的防腐涂料。
聚天门冬酸酯聚脲涂料是一种新型脂肪族、慢反应、高性能的材料。它是由HDI三聚体和聚天门冬氨酸酯反应而成，具有特点表现为：①固化时间可调。聚天门冬氨酸酯与HDI三聚体的反应速度可以采用不同的取代基团的聚天门冬氨酸酯而获得。②具有高拉伸强度、高光泽度、良好的耐磨性、渗透性、耐冲刷性和耐微生物侵蚀性。③优异的附着力，其反应速度慢、时间长，对底材的侵润时间长，附着好。④优异的耐腐蚀性：耐紫外线性能和热稳定性。⑤便于采用常规高压充气喷涂，便于提高施工效率。
发明内容
本发明的技术问题是提供一种固化时间可调，具有高拉伸强度、高光泽度、良好的耐磨性、渗透性、耐冲刷性和耐微生物侵蚀性，优异的附着力，优异的耐腐蚀性，便于采用常规高压充气喷涂，便于提高施工效率的用于两栖船舰和船坞的涂料组合物。
本发明采用如下技术方案解决上述技术问题：
一种用于两栖船舰和船坞的涂料组合物，由质量比50％的A组分和50％B组分组成；其中，A组分为聚天门冬氨酸酯；B组分的组成为：
组分 质量百分数含量
脂肪族异氰酸酯HDI三聚体 余量
275目二氧化钛 1.8％～2.2％
三聚磷酸二氢铝 3.0％～4.0％
400目奥氏体不锈钢粉 3.0％～4.0％
325目滑石粉 5.0％～6.0％
钛酸酯 0.4％～0.8％
325目碳化硅粉 2.0％～3.0％
液态芳香二氨H-256MBOEA 13.0％～15.0％
二乙基甲苯二胺DETDA 4.0％～7.0％
碳酸乙烯酯EC 1.5％～3.0％
本发明的涂料组合物的显著优点有：①固化时间可调。聚天门冬氨酸酯与HDI三聚体的反应速度可以采用不同的取代基团的聚天门冬氨酸酯而获得。②具有高拉伸强度、高光泽度、良好的耐磨性、渗透性、耐冲刷性和耐微生物侵蚀性。③优异的附着力，其反应速度慢、时间长，对底材的侵润时间长，附着好。④优异的耐腐蚀性：耐紫外线性能和热稳定性。⑤便于采用常规高压充气喷涂，便于提高施工效率。
具体实施方式
实施例1：
由质量比50％的A组分和50％B组分组成；其中，A组分为聚天门冬氨酸酯；
B组分的组成为：
组分 质量百分数含量
脂肪族异氰酸酯(HDI三聚体) 62.9％
二氧化钛(275目) 2.0％
三聚磷酸二氢铝 3.0％
奥氏体不锈钢粉(400目) 3.5％
滑石粉(325目) 5.0％
钛酸酯 0.6％
碳化硅粉(325目) 2.0％
液态芳香二氨(H-256MBOEA) 14.0％
二乙基甲苯二胺(DETDA) 5.0％
碳酸乙烯酯(EC) 2.0％
实施例2：
由质量比50％的A组分和50％B组分组成；其中，A组分为聚天门冬氨酸酯；
B组分的组成为：
组分 质量百分数含量
脂肪族异氰酸酯(HDI三聚体) 59.7％
二氧化钛(275目) 2.1％
三聚磷酸二氢铝 3.5％
奥氏体不锈钢粉(400目) 3.5％
滑石粉(325目) 5.5％
钛酸酯 0.7％
碳化硅粉(325目) 2.5％
液态芳香二氨(H-256MBOEA) 14.0％
二乙基甲苯二胺(DETDA) 6.0％
碳酸乙烯酯(EC) 2.5％
实施例3：
由质量比50％的A组分和50％B组分组成；
其中，A组分为聚天门冬氨酸酯；
B组分的组成为：
组分 质量百分数含量
脂肪族异氰酸酯(HDI三聚体) 60.4％
二氧化钛(275目) 2.0％
三聚磷酸二氢铝 4.0％
奥氏体不锈钢粉(400目) 3.0％
滑石粉(325目) 6.0％
钛酸酯 0.6％
碳化硅粉(325目) 3.0％
液态芳香二氨(H-256MBOEA) 14.0％
二乙基甲苯二胺(DETDA) 5.0％
碳酸乙烯酯(EC) 2.0％
实施例3涂料的主要技术指标：

Claims (1)

1.一种用于两栖船舰和船坞的涂料组合物，其特征在于,由质量比50％的A组分和50％B组分组成；
其中，A组分为聚天门冬氨酸酯；
B组分由以下质量百分数含量的各组分组成：
脂肪族异氰酸酯HDI三聚体 余量，
275目二氧化钛 1.8％～2.2％，
三聚磷酸二氢铝 3.0％～4.0％，
400目奥氏体不锈钢粉 3.0％～4.0％，
325目滑石粉 5.0％～6.0％，
钛酸酯 0.4％～0.8％，
325目碳化硅粉 2.0％～3.0％，
液态芳香二氨H-256MBOEA 13.0％～15.0％，
二乙基甲苯二胺DETDA 4.0％～7.0％，
碳酸乙烯酯EC 1.5％～3.0％；
B组分的各组分质量百分数含量总和为 100％。
CN201510304169.0A 2015-06-05 2015-06-05 一种用于两栖船舰和船坞的涂料组合物 Active CN104877533B (zh)