CN104877435A - green tea seed powder-containing flame-retardant low-odor printing ink - Google Patents
green tea seed powder-containing flame-retardant low-odor printing ink Download PDFInfo
- Publication number
- CN104877435A CN104877435A CN201510205323.9A CN201510205323A CN104877435A CN 104877435 A CN104877435 A CN 104877435A CN 201510205323 A CN201510205323 A CN 201510205323A CN 104877435 A CN104877435 A CN 104877435A
- Authority
- CN
- China
- Prior art keywords
- ink
- parts
- green tea
- tea seed
- seed powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the field of printing ink, and particularly relates to green tea seed powder-containing flame-retardant low-odor printing ink. The ink is prepared from the following raw materials in parts by weight: 1-2 parts of sodium allysulfonate, 3-5 parts of active magnesium hydroxide, 1-2 parts of green tea seed powder, 1-3 parts of polyoxyethylene laurate, 6-9 parts of long oil alkyd resin, 25-30 parts of phenolic resin, 10-12 parts of tripropylene glycol diacrylate, 15-20 parts of mineral oil, 8-14 parts of a pigment, 8-15 parts of glycerine, and 1-2 parts of an additive. In the ink disclosed by the invention, the phenolic resin is taken as a vehicle, the long oil alkyd resin is supplemented, and the green tea seed powder containing various biological active ingredients are added, so that the usability of finished ink products is improved; and in combination with the components such as the additive and the active magnesium hydroxide and the like, the ink has an excellent printing performance when in use, the printing efficiency is improved, the ink flows rapidly, products are clear in pattern, and the ink is antimicrobial, corrosion-resistant, heat-resistant and flame-retardant, therefore, the ink is safe and durable.
Description
Technical field
The present invention relates to printing-ink field, be specifically related to a kind of fire-retardant low smell printing-ink containing green tea seed powder.
Background technology
Ink is a class coloured material very conventional in daily life, it is by the mode of the printing carrier as word and pattern, it is the gluey fluid of a kind of stickiness, be widely used in the various printings such as books and periodicals, packing and decorating, building decoration, along with social demand increases, ink kind and output is respective extension and growth also, improves the use properties of ink, and the production model reaching efficient energy-saving is the inevitable direction of following ink development all the time.
The factor affecting the use properties of ink is mainly the performance of the moietys such as pigment, low-melting ink vehicle, stopping composition and auxiliary agent, and such as pigment affects weather resistance and the tinting strength of ink; Low-melting ink vehicle directly affects set speed, the rate of drying and printing quality etc. of ink.Therefore, improve the use properties of ink, the performance from improving these compositions is needed to set about, improve the consistency between each raw material simultaneously, reach collaborative effect promoted, thus improve existing ink ubiquitous heap ink, fall the problems such as printing quality such as version, scumming, dirty version, set-off, to enhance productivity, avoid the waste of resource.
Summary of the invention
The object of the invention is to, provide a kind of fire-retardant low smell printing-ink containing green tea seed powder, to achieve these goals, the technical solution used in the present invention is as follows:
A kind of fire-retardant low smell printing-ink containing green tea seed powder, it is characterized in that, this ink is made up of the raw material of following weight part: sodium allyl sulfonate 1-2, active hydrogen magnesium oxide 3-5, green tea seed powder 1-2, lauric acid polyoxyethylene ester 1-3, long oil alkyd 6-9, resol 25-30, tri (propylene glycol) diacrylate 10-12, mineral oil 15-20, pigment 8-14, glycerine 8-15, auxiliary agent 1-2;
The raw material of following weight part is comprised: polymine 1-2 in described auxiliary agent, Triethylene glycol 0.5-0.8, trimethyl benzyl ammonia chloride 0.1-0.2, silicon sol 5-8, microfine diatomaceous 1-3, deionized water is appropriate, preparation method is: be first dissolved in by polymine in appropriate deionized water, be mixed with the solution of 20-30%, add Triethylene glycol again, trimethyl benzyl ammonia chloride, be stirred to after it dissolves completely and drop into microfine diatomaceous, after ground and mixed 30-40min, gained pulp concentration is dry, the powder obtained mixes with silicon sol again, complete dispersed with stirring evenly after and get final product.
Described a kind of fire-retardant low smell printing-ink containing green tea seed powder, its preparation method is: first sodium allyl sulfonate, green tea seed powder are mixed with glycerine, mix with other remaining component after stirring, continue to be stirred to after material dissolves dispersion completely, by mixed material heating to 40-60 DEG C, after insulation 10-15min, be cooled to room temperature, and drop into fully grinding in sand mill, make the particle diameter of gained slurry be≤20 μm, to obtain final product.
Ink prepared by the present invention using resol as low-melting ink vehicle, and is aided with long oil alkyd, and have good mobility and transferability, smell is low, has excellent adhesive ability; Green tea seed powder is that green tea seed is directly pulverized and formed, and containing multiple bioactive ingredients, has the effects such as certain dispersion, infiltration, lubrication, sterilization, the use properties of ink finished product can be improved, be combined with the wettability improving ink again, prevent the auxiliary agent of the effects such as coating foaming and the magnesian flame retardant properties of active hydrogen, make this ink have excellent printing performance in use, printing efficiency is improved, flowing is rapid, goods clear patterns, Antimicrobial preservative, heat-proof combustion-resistant is not only safe but also durable.
Embodiment
Embodiment
Printing-ink prepared by the present embodiment is made up of the raw material of following weight part: sodium allyl sulfonate 2, active hydrogen magnesium oxide 3, green tea seed powder 1, lauric acid polyoxyethylene ester 3, long oil alkyd 8, resol 28, tri (propylene glycol) diacrylate 12, mineral oil 18, pigment 10, glycerine 12, auxiliary agent 1; Wherein auxiliary agent is made up of the raw material of following weight part: polymine 1, Triethylene glycol 0.5, trimethyl benzyl ammonia chloride 0.1, silicon sol 6, microfine diatomaceous 2, deionized water is appropriate, preparation method is: be first dissolved in by polymine in appropriate deionized water, be mixed with the solution of 30%, add Triethylene glycol, trimethyl benzyl ammonia chloride again, be stirred to after it dissolves completely and drop into microfine diatomaceous, after ground and mixed 40min, gained pulp concentration is dry, the powder obtained mixes with silicon sol again, complete dispersed with stirring evenly after and get final product.
The preparation method of this printing-ink is: first sodium allyl sulfonate, green tea seed powder are mixed with glycerine, mix with other remaining component after stirring, continue to be stirred to after material dissolves dispersion completely, by mixed material heating to 40-60 DEG C, room temperature is cooled to after insulation 15min, and drop into fully grinding in sand mill, make the particle diameter of gained slurry be≤20 μm, to obtain final product.
By the ink printing obtained by the present embodiment on PE film, after its complete drying, this ink in the performance test results of substrate surface is:
| Test item | Detected result |
| Tinting strength | 102 |
| Viscosity (s/25 DEG C) | 54 |
| Sticking power/% | ≥100 |
| First dryness (mm) | 12 |
| Glossiness (60 DEG C, specular gloss instrument) | ＞75 |
| Ethanol-tolerant, soda acid, water tolerance | Nondiscoloration, not come off |
Above-mentioned test is all followed relevant criterion and is carried out.
Claims (2)
1. the fire-retardant low smell printing-ink containing green tea seed powder, it is characterized in that, this printing-ink is made up of the raw material of following weight part: sodium allyl sulfonate 1-2, active hydrogen magnesium oxide 3-5, green tea seed powder 1-2, lauric acid polyoxyethylene ester 1-3, long oil alkyd 6-9, resol 25-30, tri (propylene glycol) diacrylate 10-12, mineral oil 15-20, pigment 8-14, glycerine 8-15, auxiliary agent 1-2;
Described auxiliary agent is made up of the raw material of following weight part: polymine 1-2, Triethylene glycol 0.5-0.8, trimethyl benzyl ammonia chloride 0.1-0.2, silicon sol 5-8, microfine diatomaceous 1-3, deionized water is appropriate, preparation method is: be first dissolved in by polymine in appropriate deionized water, be mixed with the solution of 20-30%, add Triethylene glycol again, trimethyl benzyl ammonia chloride, be stirred to after it dissolves completely and drop into microfine diatomaceous, after ground and mixed 30-40min, gained pulp concentration is dry, the powder obtained mixes with silicon sol again, complete dispersed with stirring evenly after and get final product.
2. a kind of fire-retardant low smell printing-ink containing green tea seed powder as claimed in claim 1, its preparation method is: first sodium allyl sulfonate, green tea seed powder are mixed with glycerine, mix with other remaining component after stirring, continue to be stirred to after material dissolves dispersion completely, by mixed material heating to 40-60 DEG C, after insulation 10-15min, be cooled to room temperature, and drop into fully grinding in sand mill, make the particle diameter of gained slurry be≤20 μm, to obtain final product.