CN104876535A - High-luster red porcelain product - Google Patents
High-luster red porcelain product Download PDFInfo
- Publication number
- CN104876535A CN104876535A CN201510261891.0A CN201510261891A CN104876535A CN 104876535 A CN104876535 A CN 104876535A CN 201510261891 A CN201510261891 A CN 201510261891A CN 104876535 A CN104876535 A CN 104876535A
- Authority
- CN
- China
- Prior art keywords
- parts
- porcelain product
- luster
- red porcelain
- clay
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a high-luster red porcelain product. The high-luster red porcelain product is prepared from the following raw materials in parts by weight: 3-8 parts of kaolin, 1-5 parts of a dispersing agent, 6-13 parts of nano aluminum dioxide, 2-8 parts of silicon oxide, 6-8 parts of colored argil, 6-14 parts of bauxite clay, 3-6 parts of zinc oxide, 25-33 parts of purple clay, 3-5 parts of nano sodium dioxide, 4-9 parts of ferrous oxide, 5-8 parts of nano zinc dioxide, 2.5-6 parts of zircon flour, 1-4 parts of calcite, 4-11 parts of aluminum nitride, 3.5-8 parts of sodium sulfate and 2.1-5 parts of light calcined magnesia. The high-luster red porcelain product has the beneficial effects that the red porcelain product is high in luster and uniformity, high in viscidity and long in service life, and can be used for producing various tea wares.
Description
Technical field
The present invention relates to a kind of Boccaro ceramic ware of high brightness.
Background technology
Purple-clay product, also known as " boccaro ware ", " purple sand ceramics ", is a kind of ceramic product made with special potter's clay, and it can be made into ceramic conventional in various daily life, and as current popular electric soup cooker, namely electric cooker electrothermal dark-red pottery inner bag is.Due to the uniqueness of purple sand material, add to dark-red enameled pottery and more preferably use U.S..Yixing tender tea leaves kettle with coarse sand system it, sand of officiallying enroll, without rustic ear, is made tea with dark-red enameled pottery, lid neither take perfume (or spice) by force again without ripe soup gas, do not lose original flavor, color all accumulates.But existing purple-clay product cohesiveness is inadequate, well can not play cohesive action, and then cause purple-clay product to ftracture, cause reduce work-ing life.
Summary of the invention
For the deficiencies in the prior art, the problem to be solved in the present invention is, provides a kind of Boccaro ceramic ware, has good brightness and uniformity coefficient, can be used for the making of multiple tea set, and viscosity is good simultaneously, long service life.
For solving prior art problem, technical scheme provided by the invention is, a kind of Boccaro ceramic ware of high brightness, and it is made up of the raw material of following parts by weight:
Kaolin 3-8 part, dispersion agent 1-5 part, nanometer titanium dioxide aluminium 6-13 part, silicon oxide 2-8 part, coloured potter's clay 6-8 part, bauxite clay 6-14 part, zinc oxide 3-6 part, Red Stone Ware 25-33 part, nanometer titanium dioxide sodium 3-5 part, iron protoxide 4-9 part, Nano zinc dioxide impact-resistant 5-8 part, zircon flour 2.5-6 part, calcite 1-4 part, aluminium nitride 4-11 part, sodium sulfate 3.5-8 part, light calcined magnesia 2.1-5 part.
The invention has the beneficial effects as follows: Boccaro ceramic ware of the present invention, have good brightness and uniformity coefficient, can be used for the making of multiple tea set, viscosity is good simultaneously, long service life.
Embodiment
embodiment 1
A Boccaro ceramic ware for high brightness, it is made up of the raw material of following parts by weight:
Kaolin 3 parts, dispersion agent 1 part, 6 parts, nanometer titanium dioxide aluminium, silicon oxide 2 parts, 6 parts, coloured potter's clay, bauxite clay 6 parts, 3 parts, zinc oxide, Red Stone Ware 25 parts, 3 parts, nanometer titanium dioxide sodium, iron protoxide 4 parts, Nano zinc dioxide impact-resistant 5 parts, zircon flour 2.5 parts, 1 part, calcite, aluminium nitride 4 parts, 3.5 parts, sodium sulfate, light calcined magnesia 2.1 parts.
embodiment 2
A Boccaro ceramic ware for high brightness, it is made up of the raw material of following parts by weight:
Kaolin 8 parts, dispersion agent 5 parts, 13 parts, nanometer titanium dioxide aluminium, silicon oxide 8 parts, 8 parts, coloured potter's clay, bauxite clay 14 parts, 6 parts, zinc oxide, Red Stone Ware 33 parts, 5 parts, nanometer titanium dioxide sodium, iron protoxide 9 parts, Nano zinc dioxide impact-resistant 8 parts, zircon flour 6 parts, 4 parts, calcite, aluminium nitride 11 parts, 8 parts, sodium sulfate, light calcined magnesia 5 parts.
Claims (1)
1. a Boccaro ceramic ware for high brightness, is characterized in that: it is made up of the raw material of following parts by weight:
Kaolin 3-8 part, dispersion agent 1-5 part, nanometer titanium dioxide aluminium 6-13 part, silicon oxide 2-8 part, coloured potter's clay 6-8 part, bauxite clay 6-14 part, zinc oxide 3-6 part, Red Stone Ware 25-33 part, nanometer titanium dioxide sodium 3-5 part, iron protoxide 4-9 part, Nano zinc dioxide impact-resistant 5-8 part, zircon flour 2.5-6 part, calcite 1-4 part, aluminium nitride 4-11 part, sodium sulfate 3.5-8 part, light calcined magnesia 2.1-5 part.