CN104876501A - Crack sealer for building exterior wall tile, and preparation method and construction process thereof - Google Patents

Crack sealer for building exterior wall tile, and preparation method and construction process thereof Download PDF

Info

Publication number
CN104876501A
CN104876501A CN201510190008.3A CN201510190008A CN104876501A CN 104876501 A CN104876501 A CN 104876501A CN 201510190008 A CN201510190008 A CN 201510190008A CN 104876501 A CN104876501 A CN 104876501A
Authority
CN
China
Prior art keywords
agent
parts
rubber powder
seconds
cement
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510190008.3A
Other languages
Chinese (zh)
Inventor
郭跃峰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jining Yuefeng Building Material Science & Technology Co Ltd
Original Assignee
Jining Yuefeng Building Material Science & Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jining Yuefeng Building Material Science & Technology Co Ltd filed Critical Jining Yuefeng Building Material Science & Technology Co Ltd
Priority to CN201510190008.3A priority Critical patent/CN104876501A/en
Publication of CN104876501A publication Critical patent/CN104876501A/en
Pending legal-status Critical Current

Abstract

The invention provides a crack sealer for a building exterior wall tile, and a preparation method and a construction process thereof; the crack sealer contains an inorganic admixture composed of cement, coal ash, 70-100-mesh coarse quartz sand, 100-200-mesh fine quartz sand, rubber powder, a water repellent, hydroxypropyl methyl cellulose, an inhibitory alkali efflorescence agent, a rubber powder optimizing element and a mortar optimization agent; and the crack sealer further comprises an additive. The preparation method comprises the following steps: mixing various components, drying for 24 h, naturally cooling to room temperature, stirring, heating, and stirring again; and the construction process comprises the following steps: cleaning a position to be sealed, fully filling at the position to be sealed, compacting the paste like crack sealer, and finally, cleanly processing the redundant crack sealer on the surface of the tile. The crack sealer prepared by the preparation method disclosed by the invention is capable of effectively preventing free calcium in cement mortar from being separated out and has the anti-cracking property, the waterproof property and the good endurance; according to the construction process disclosed by the invention, the esthetic effect of a decorative tile material can be more obvious; and furthermore, the crack sealer is low in cost, simple to construct, environmentally friendly and energy-saving.

Description

A kind of external wall tile pointing agent and preparation method thereof and construction technology
Technical field
The present invention relates to building material technical field, specifically a kind of external wall tile pointing agent and preparation method thereof and construction technology.
Background technology
Along with the lasting steady-state growth of China's economic total volume, energy supply and demand contradiction highlights day by day, has now become the bottleneck of restriction China sustained economic development.Since reform and opening-up, construction industry develop the mainstay industry becoming China's Economic development rapidly.Along with the increase of civil construction completed floor space, the increasing of building energy consumption will certainly be brought.Nearly 2,000,000,000 square metres of China's annual town and country newly constructed house floor area of building, wherein more than 80% is highly energy-consuming building, and nearly 40,000,000,000 square metres of existed building, more than 95% is high energy consumption building.Unit of China floor area of building energy consumption is more than 2-3 times of developed country.According to Ministry of Construction's prediction, the development of coming 10 years Building Trade in China still can higher than the tempo of national economy, and wherein dwelling construction also will be in growth form developing period.Estimate Eleventh Five-Year Plan end, whole society's house completed floor space will reach 9,000,000,000 square metres, and wherein New Dwelling will reach more than 6,000,000,000 square metres.Building energy conservation task is great.The power loss of China's house house is roughly body of wall and accounts for 50%, and roofing accounts for 10%, and door and window accounts for 25%, and vault and ground account for 15%.Chinese architecture will realize fractional energy savings 50% in 2015, and need external external wall to carry out modernization overlay, the development of wall heat insulation material is very crucial, the Bright Prospect of energy-saving and heat-insulating material industry.
It is be major ingredient with white cement that jointing agent also makes spackling, ditch stitch agent, adds a small amount of mineral dye, polymkeric substance and micro-anti-microbial inoculum, the dry powdery material of composition, it does not have water resistance, being divided into has sandbox and without sandbox, the former is mainly used on wide brickwork joint, and the latter is mainly used on narrow brickwork joint.Traditional jointing agent along with time and climate change gradually aging decolouring ftracture, waterproof, endurance quality are poor, and the adhesive mortar that after coming off, rainwater directly can wash away body of wall and ceramic tile makes the adhesive mortar life-span greatly shorten, and also loses aesthetic simultaneously.
In order to change the deficiency of existing jointing agent, present invention is a kind of effectively can stop the precipitation of sand-cement slurry Free Calcium, decorative block material is reached, and long-term aesthetic is more remarkable and cost is low, construction simple, the jointing agent of environmental protection and energy saving, the guardian technique of this kind of jointing agent should be considered from the following aspect: 1) will be applicable to most of ceramic tile and stone material seam, can strengthen the decorative effect of plane materiel; 2) there is effect of water proof anti-seepage and mildew-resistant, there is anticracking, water resistant and good weather resistance, construct simply and environmental protection and energy saving.
Summary of the invention
Technical assignment of the present invention is for the deficiencies in the prior art, there is provided a kind of and there is anticracking, water resistant and good weather resistance, effectively can stop the precipitation of sand-cement slurry Free Calcium simultaneously, make the aesthetic of decorative block material more remarkable and cost is low, construction is simple simultaneously, the external wall tile pointing agent of environmental protection and energy saving.
The technical solution adopted for the present invention to solve the technical problems is:
The agent of a kind of external wall tile pointing, comprise inorganic adulterant and admixture, described inorganic adulterant comprises the raw material of following parts by weight:
Cement: 2800-3800 part, flyash: 350-650 part, rubble sand: 3200-4000 part,
Fine quartz sand: 2200-2600 part, rubber powder: 50-130 part, hydrophober: 14-16 part,
Vltra tears: 14-16 part, suppresses accumulation of salt in the surface soil agent: 19-21 part,
Rubber powder optimizes element: 29-31 part, and agent optimized by mortar: 9-16 part;
Wherein, the specification of rubble sand is 70-100 order, and the specification of fine quartz sand is 100-200 order.
Further, described inorganic adulterant comprises the raw material of following parts by weight:
Cement: 3000-3600 part, flyash: 400-600 part, rubble sand: 3300-3855 part,
Fine quartz sand: 2400-2485 part, rubber powder: 55-120 part, hydrophober: 14-16 part,
Vltra tears: 14-16 part, suppresses accumulation of salt in the surface soil agent: 19-21 part,
Rubber powder optimizes element: 29-31 part, and agent optimized by mortar: 9-16 part;
Wherein, the specification of rubble sand is 70-100 order, and the specification of fine quartz sand is 100-200 order.
Prioritizing selection, described inorganic adulterant comprises the raw material of following parts by weight:
Cement: 3000 parts, flyash: 600 parts, rubble sand: 3855 parts,
Fine quartz sand: 2400 parts, rubber powder: 55 parts, hydrophober: 15 parts,
Vltra tears: 15 parts, suppresses accumulation of salt in the surface soil agent: 20 parts,
Rubber powder optimizes element: 30 parts, and agent optimized by mortar: 10 parts;
Wherein, the specification of rubble sand is 70-100 order, and the specification of fine quartz sand is 100-200 order.
Prioritizing selection, described inorganic adulterant comprises the raw material of following parts by weight:
Cement: 3600 parts, flyash: 400 parts, rubble sand: 3300 parts,
Fine quartz sand: 2485 parts, rubber powder: 120 parts, hydrophober: 15 parts,
Vltra tears: 15 parts, suppresses accumulation of salt in the surface soil agent: 20 parts,
Rubber powder optimizes element: 30 parts, and agent optimized by mortar: 15 parts;
Wherein, the specification of rubble sand is 70-100 order, and the specification of fine quartz sand is 100-200 order.
Prioritizing selection, described cement is 425 silicate cement.
Prioritizing selection, the viscosity unit of described Vltra tears is 4-10 ten thousand mpas.
Prioritizing selection, described rubber powder optimization element, mortar are optimized agent and are professional building materials.
The Second Problem that the present invention solves is the preparation method of above-mentioned a kind of external wall tile pointing agent, and the method is carried out according to following steps:
1) take according to formula the cement, flyash, rubble sand, fine quartz sand, rubber powder, hydrophober, Vltra tears, the agent of the suppression accumulation of salt in the surface soil, the rubber powder that forms inorganic adulterant and optimize element and mortar optimization agent, and take the admixture of 0.35%-0.45% again according to the weight of inorganic adulterant;
2) dryer is put in the cement taken, flyash, rubble sand, fine quartz sand, rubber powder, hydrophober, Vltra tears, the agent of the suppression accumulation of salt in the surface soil, rubber powder optimization element and mortar optimization agent respectively and dry more than at least 24 hours in advance, then naturally cool to room temperature;
3) optimize agent and mix by being cooled to the cement of room temperature, flyash, rubble sand, fine quartz sand, rubber powder, hydrophober, Vltra tears, the agent of the suppression accumulation of salt in the surface soil, rubber powder optimization element and mortar and add in stirrer, first stir 120 seconds with rotating speed 10-30 rev/min, then stir 60 seconds with rotating speed 60-80 rev/min, stagnate 60 seconds, then stir 60 seconds with rotating speed 60-80 rev/min, then stir 120 seconds with rotating speed 10-30 rev/min;
4) take out the inorganic adulterant be uniformly mixed, be heated to 40 ~ 50 DEG C;
5) again stirrer is opened, the inorganic adulterant of 40 ~ 50 DEG C slowly adding admixture and mix while stir 120 seconds with rotating speed 10-30 rev/min, ensure to add in 120 seconds, then stir 60 seconds with rotating speed 60-80 rev/min, stagnate 60 seconds, then stir 60 seconds with rotating speed 60-80 rev/min, then stir 120 seconds with rotating speed 10-30 rev/min;
6) take out the jointing agent prepared to be positioned in the container of dry sealing.
The 3rd problem that the present invention solves is the construction technology of above-mentioned a kind of external wall tile pointing agent, carries out according to the following steps during this construction technology:
1) first clear up ceramic tile gap, ensure to need the position of joint filling without oil and floating ash, and can too dry at joint filling position time suitably sprinkle water carry out moistening;
2) clean container is then selected, water is poured in clean container, then the ratio mixing four kilograms of jointing agents according to every premium on currency slowly adds have been prepared and the jointing agent taken, and the even paste be stirred to without fecula group, leave standstill and again stir after 3-5 minute and fill up the position, ceramic tile gap cleared up;
3) with instrument, the paste jointing agent filled up is carried out compacting, after 15-30 minute paste jointing agent primary solidification, with micro-wet sponge by jointing agent process unnecessary for ceramic tile surface totally.
Compared with prior art, the beneficial effect produced is for a kind of external wall tile pointing of the present invention agent and preparation method thereof and construction technology:
The external wall tile pointing agent using preparation method of the present invention to prepare effectively can stop the precipitation of sand-cement slurry Free Calcium, also has anticracking, water resistant and good endurance quality simultaneously; The aesthetic of decorative block material can be made more remarkable according to construction technology of the present invention and cost is low, construction is simple, environmental protection and energy saving.
Embodiment
Embodiment 1:
Take cement by weight: 3000 parts, flyash: 600 parts, rubble sand: 3855 parts,
Fine quartz sand: 2400 parts, rubber powder: 55 parts, hydrophober: 15 parts,
Vltra tears: 15 parts, suppresses accumulation of salt in the surface soil agent: 20 parts,
Rubber powder optimizes element: 30 parts, and agent optimized by mortar: 10 parts;
Powdery high efficiency water reducing agent 38 parts selected by admixture;
Wherein, the specification of rubble sand is 70-100 order, and the specification of fine quartz sand is 100-200 order.
Prioritizing selection, described cement is 425 silicate cement; The viscosity unit of described Vltra tears is 4-10 ten thousand mpas; Described rubber powder optimization element, mortar are optimized agent and are professional building materials.
This preparation method carries out according to the following steps:
1) according to formula take form inorganic adulterant cement 3000 parts, 600 parts, flyash, rubble sand 3855 parts, fine quartz sand 2400 parts, rubber powder 55 parts, hydrophober 15 parts, Vltra tears 15 parts, suppress accumulation of salt in the surface soil agent 20 parts, rubber powder optimizes plain 30 parts, agent 10 parts optimized by mortar, powdery high efficiency water reducing agent 38 parts;
2) dryer is put in the cement taken, flyash, rubble sand, fine quartz sand, rubber powder, hydrophober, Vltra tears, the agent of the suppression accumulation of salt in the surface soil, rubber powder optimization element and mortar optimization agent respectively and dry more than at least 24 hours in advance, then naturally cool to room temperature;
3) each component being cooled to room temperature is added in stirrer together, first stir 120 seconds with rotating speed 20 revs/min, then stir 60 seconds with rotating speed 70 revs/min, stagnate 60 seconds, then stir 60 seconds with rotating speed 70 revs/min, then stir 120 seconds with rotating speed 20 revs/min;
4) take out the inorganic adulterant be uniformly mixed, be heated to 45 DEG C;
5) again stirrer is opened, the inorganic adulterant of 45 DEG C slowly adding admixture and mix while stir 120 seconds with rotating speed 20 revs/min, ensure to add in 120 seconds, then stir 60 seconds with rotating speed 70 revs/min, stagnate 60 seconds, then stir 60 seconds with rotating speed 70 revs/min, then stir 120 seconds with rotating speed 20 revs/min;
6) take out the jointing agent prepared to be positioned in the container of dry sealing.
After having prepared, property indices of the present invention as shown in Table 1 below:
Table 1:
Embodiment 2:
Take cement by weight: 3600 parts, flyash: 400 parts, rubble sand: 3300 parts,
Fine quartz sand: 2485 parts, rubber powder: 120 parts, hydrophober: 15 parts,
Vltra tears: 15 parts, suppresses accumulation of salt in the surface soil agent: 20 parts,
Rubber powder optimizes element: 30 parts, and agent optimized by mortar: 15 parts;
Powdery high efficiency water reducing agent 40 parts selected by admixture;
Wherein, the specification of rubble sand is 70-100 order, and the specification of fine quartz sand is 100-200 order.
Prioritizing selection, described cement is 425 silicate cement; The viscosity unit of described Vltra tears is 4-10 ten thousand mpas; Described rubber powder optimization element, mortar are optimized agent and are professional building materials.
This preparation method is identical with the step of preparation method in above-described embodiment 1.
After having prepared, property indices of the present invention as shown in Table 2 below:
Table 2:
Embodiment 3:
Take cement by weight: 3800 parts, flyash: 350 parts, rubble sand: 3200 parts,
Fine quartz sand: 2600 parts, rubber powder: 130 parts, hydrophober: 16 parts,
Vltra tears: 16 parts, suppresses accumulation of salt in the surface soil agent: 21 parts,
Rubber powder optimizes element: 31 parts, and agent optimized by mortar: 16 parts;
Powdery high efficiency water reducing agent 45 parts selected by admixture;
Wherein, the specification of rubble sand is 70-100 order, and the specification of fine quartz sand is 100-200 order.
Prioritizing selection, described cement is 425 silicate cement; The viscosity unit of described Vltra tears is 4-10 ten thousand mpas; Described rubber powder optimization element, mortar are optimized agent and are professional building materials.
This preparation method is identical with the step of preparation method in above-described embodiment 1.
Embodiment 4:
Take cement by weight: 2800 parts, flyash: 650 parts, rubble sand: 4000 parts,
Fine quartz sand: 2200 parts, rubber powder: 50 parts, hydrophober: 14 parts,
Vltra tears: 14 parts, suppresses accumulation of salt in the surface soil agent: 19 parts,
Rubber powder optimizes element: 29 parts, and agent optimized by mortar: 9 parts;
Powdery high efficiency water reducing agent 35 parts selected by admixture;
Wherein, the specification of rubble sand is 70-100 order, and the specification of fine quartz sand is 100-200 order.
Prioritizing selection, described cement is 425 silicate cement; The viscosity unit of described Vltra tears is 4-10 ten thousand mpas; Described rubber powder optimization element, mortar are optimized agent and are professional building materials.
This preparation method is identical with the step of preparation method in above-described embodiment 1.
The construction technology of the described external wall tile pointing agent prepared by above-mentioned four embodiments is carried out according to the following steps:
1) first clear up ceramic tile gap, ensure to need the position of joint filling without oil and floating ash, and can too dry at joint filling position time suitably sprinkle water carry out moistening;
2) clean container is then selected, water is poured in clean container, then the ratio mixing four kilograms of jointing agents according to every premium on currency slowly adds have been prepared and the jointing agent taken, and the even paste be stirred to without fecula group, leave standstill and again stir after 3-5 minute and fill up the position, ceramic tile gap cleared up;
3) with instrument, the paste jointing agent filled up is carried out compacting, after 15-30 minute paste jointing agent primary solidification, with micro-wet sponge by jointing agent process unnecessary for ceramic tile surface totally.
It should be noted that the paste jointing agent prepared need complete in 4-5 hour, other mixing materials cannot be added; According to actual service condition, 1kg jointing agent can meet the joint filling demand of 4-20 square metre of ceramic tile, and actual amount is different from the how many difference of constructional method, joint filling width and filler.Be sure not to fill up when moist, rainy, after joint filling, in 24 hours, jade-like stone is avoided drenching with rain; Prepare in the process of jointing agent, lead-free can be selected according to practical situation.
Above-described four embodiments are only preferred embodiments of the present invention; wherein; described embodiment 1 and embodiment 2 are most preferred embodiment; the preparation method of above-described external wall tile pointing agent and construction technology are also better preparation method of the present invention and construction technology; not the present invention is imposed any restrictions; every technical spirit according to the present invention above embodiment and construction technology process are done any simple modification, change and equivalent structure change, all still belong in the protection domain of technical solution of the present invention.

Claims (9)

1. the agent of external wall tile pointing, is characterized in that, comprises inorganic adulterant and admixture, and described inorganic adulterant comprises the raw material of following parts by weight:
Cement: 2800-3800 part, flyash: 350-650 part, rubble sand: 3200-4000 part,
Fine quartz sand: 2200-2600 part, rubber powder: 50-130 part, hydrophober: 14-16 part,
Vltra tears: 14-16 part, suppresses accumulation of salt in the surface soil agent: 19-21 part,
Rubber powder optimizes element: 29-31 part, and agent optimized by mortar: 9-16 part;
Wherein, the specification of rubble sand is 70-100 order, and the specification of fine quartz sand is 100-200 order.
2. a kind of external wall tile pointing according to claim 1 agent, is characterized in that, described inorganic adulterant comprises the raw material of following parts by weight:
Cement: 3000-3600 part, flyash: 400-600 part, rubble sand: 3300-3855 part,
Fine quartz sand: 2400-2485 part, rubber powder: 55-120 part, hydrophober: 14-16 part,
Vltra tears: 14-16 part, suppresses accumulation of salt in the surface soil agent: 19-21 part,
Rubber powder optimizes element: 29-31 part, and agent optimized by mortar: 9-16 part;
Wherein, the specification of rubble sand is 70-100 order, and the specification of fine quartz sand is 100-200 order.
3. a kind of external wall tile pointing according to claim 2 agent, is characterized in that, described inorganic adulterant comprises the raw material of following parts by weight:
Cement: 3000 parts, flyash: 600 parts, rubble sand: 3855 parts,
Fine quartz sand: 2400 parts, rubber powder: 55 parts, hydrophober: 15 parts,
Vltra tears: 15 parts, suppresses accumulation of salt in the surface soil agent: 20 parts,
Rubber powder optimizes element: 30 parts, and agent optimized by mortar: 10 parts;
Wherein, the specification of rubble sand is 70-100 order, and the specification of fine quartz sand is 100-200 order.
4. a kind of external wall tile pointing according to claim 2 agent, is characterized in that, described inorganic adulterant comprises the raw material of following parts by weight:
Cement: 3600 parts, flyash: 400 parts, rubble sand: 3300 parts,
Fine quartz sand: 2485 parts, rubber powder: 120 parts, hydrophober: 15 parts,
Vltra tears: 15 parts, suppresses accumulation of salt in the surface soil agent: 20 parts,
Rubber powder optimizes element: 30 parts, and agent optimized by mortar: 15 parts;
Wherein, the specification of rubble sand is 70-100 order, and the specification of fine quartz sand is 100-200 order.
5. a kind of external wall tile pointing agent according to claim 1,2,3 or 4, is characterized in that, described cement is 425 silicate cement.
6. a kind of external wall tile pointing agent according to claim 1,2,3 or 4, is characterized in that, the viscosity unit of described Vltra tears is 4-10 ten thousand mpas.
7. a kind of external wall tile pointing agent according to claim 1,2,3 or 4, is characterized in that, described rubber powder optimization element, mortar are optimized agent and be professional building materials.
8. a preparation method for external wall tile pointing agent according to any one of the claims 1-4, is characterized in that, the method is carried out according to following steps:
1) take according to formula the cement, flyash, rubble sand, fine quartz sand, rubber powder, hydrophober, Vltra tears, the agent of the suppression accumulation of salt in the surface soil, the rubber powder that forms inorganic adulterant and optimize element and mortar optimization agent, and take the admixture of 0.35%-0.45% again according to the weight of inorganic adulterant;
2) dryer is put in the cement taken, flyash, rubble sand, fine quartz sand, rubber powder, hydrophober, Vltra tears, the agent of the suppression accumulation of salt in the surface soil, rubber powder optimization element and mortar optimization agent respectively and dry more than at least 24 hours in advance, then naturally cool to room temperature;
3) optimize agent and mix by being cooled to the cement of room temperature, flyash, rubble sand, fine quartz sand, rubber powder, hydrophober, Vltra tears, the agent of the suppression accumulation of salt in the surface soil, rubber powder optimization element and mortar and add in stirrer, first stir 120 seconds with rotating speed 10-30 rev/min, then stir 60 seconds with rotating speed 60-80 rev/min, stagnate 60 seconds, then stir 60 seconds with rotating speed 60-80 rev/min, then stir 120 seconds with rotating speed 10-30 rev/min;
4) take out the inorganic adulterant after stirring, be heated to 40 ~ 50 DEG C;
5) again stirrer is opened, the inorganic adulterant of 40 ~ 50 DEG C slowly adding admixture and mix while stir 120 seconds with rotating speed 10-30 rev/min, ensure to add in 120 seconds, then stir 60 seconds with rotating speed 60-80 rev/min, stagnate 60 seconds, then stir 60 seconds with rotating speed 60-80 rev/min, then stir 120 seconds with rotating speed 10-30 rev/min;
6) take out the jointing agent prepared to be positioned in the container of dry sealing.
9. a construction technology for external wall tile pointing agent as described in the claims 8, is characterized in that, this construction technology is carried out according to the following steps:
1) first clear up ceramic tile gap, ensure to need the position of joint filling without oil and floating ash, and can too dry at joint filling position time suitably sprinkle water carry out moistening;
2) clean container is then selected, water is poured in clean container, then the ratio mixing four kilograms of jointing agents according to every premium on currency slowly adds have been prepared and the jointing agent taken, and the even paste be stirred to without fecula group, leave standstill and again stir after 3-5 minute and fill up the position, ceramic tile gap cleared up;
3) with instrument, the paste jointing agent filled up is carried out compacting, after 15-30 minute paste jointing agent primary solidification, with micro-wet sponge by jointing agent process unnecessary for ceramic tile surface totally.
CN201510190008.3A 2015-04-21 2015-04-21 Crack sealer for building exterior wall tile, and preparation method and construction process thereof Pending CN104876501A (en)