CN105777015B - A kind of tile pointing agent and preparation method thereof - Google Patents
A kind of tile pointing agent and preparation method thereof Download PDFInfo
- Publication number
- CN105777015B CN105777015B CN201610203971.5A CN201610203971A CN105777015B CN 105777015 B CN105777015 B CN 105777015B CN 201610203971 A CN201610203971 A CN 201610203971A CN 105777015 B CN105777015 B CN 105777015B
- Authority
- CN
- China
- Prior art keywords
- parts
- tile pointing
- pointing agent
- tile
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of tile pointing agent and preparation method thereof, the tile pointing agent includes following components by weight：0.18 0.25 parts of 25 parts of 30 40 parts of cement, 69 parts of quartz sand, iron oxide or titanium oxide, 36 parts of redispersable latex powder, 1.3 2.1 parts of hydroxypropyl methyl cellulose, 0.4 0.7 parts of calcium formate, 0.34 0.48 parts of water reducer, 0.8 1.2 parts of mill base, 0.5 0.8 parts of thixotropic lubricant and cellulose ether.The tile pointing agent cohesive force of the present invention is strong, can be in close contact with facing, not produce crack, antiseepage outlet capacity is good, can effective waterproof.
Description
Technical field
The present invention relates to building material field, and in particular to a kind of tile pointing agent and preparation method thereof.
Background technology
Tile pointing agent is also known as face brick jointing agent, is formed by cement, quartz sand, filling material and various additive compounds, is to use
The joint filler in gap between filling ceramic tile or stone material, be engaged with the ornament materials such as ceramic tile, stone material provide facing attractive in appearance and
Ensure the bonding between tapestry brick and antiseepage.With the fast development of Building Trade in China, the requirement to tile pointing agent is increasingly
Height, consumption is also increasing.In the raw material of jointing agent, cement is an indispensable part.But cement because its rigidity is big,
Fragility alkalescence is strong, crack easily occurs, plays drum and comes off, causes infiltration, had a strong impact on the quality of life of user.
The content of the invention
In view of this, it is an object of the invention to provide a kind of tile pointing agent.The tile pointing agent cohesive force is strong, water-impervious
Ability is good.
To achieve the above object, the technical solution adopted by the present invention is as follows：
A kind of tile pointing agent, by weight including following components：30-40 parts of cement, 6-9 parts of quartz sand, iron oxide or
2-5 parts of titanium oxide, 3-6 parts of redispersable latex powder, 1.3-2.1 parts of hydroxypropyl methyl cellulose, 0.4-0.7 parts of calcium formate, subtract
0.18-0.25 parts of 0.34-0.48 parts of aqua, 0.8-1.2 parts of mill base, 0.5-0.8 parts of thixotropic lubricant and cellulose ether.
The redispersable latex powder is the spray-dried rear powder formed of polymer emulsion, also referred to as dry powder glue.It is this
Powder can be reduced into emulsion rapidly after contact with water, and keep and initial latex identical property, i.e., after moisture evaporation, this
Planting film has high-flexibility, high-weatherability and the high-adhesion to various base materials.
The quartz sand is the broken quartz particles processed of quartz warp, and quartz is a kind of nonmetallic mineral,
It is a kind of hard, wear-resisting, stable chemical performance silicate mineral, its main mineral constituent is SiO2.Quartz sand is important
Industrial mineral raw material, non-chemical dangerous material, be widely used in glass, casting, ceramics and fire proofing material, smelting duriron, flux for metallurgy,
The industry such as metallurgy, building, chemical industry, plastics, rubber, abrasive material, filtrate.Industrially often quartz sand is divided into：It is common quartz sand, refined
Quartz sand, glass sand, tekite sand and silicon powder etc..
The calcium formate is also referred to as formic acid calcium, and molecular formula is C2H204Ca, as feed addictive, it is adaptable to all kinds of animals,
The effects such as with acidifying, mould proof, antibacterial, industrially it is also used for concrete, grout additive, the tanning of leather or as preservative
Use.
The mill base is the semi-products being dispersed in by pigment or pigment and inserts in paint vehicle, with pure oil for adhesive
Title oil pastes, the title resin mill base by adhesive of resin paint vehicle, by medium of water add surfactant-dispersed form
Color stuffing slurry be referred to as aqueous color paste.
Further, the cement is Portland cement.
Further, the quartz sand is SILICA FUME.The SILICA FUME is also silicon ash or poly- silicon ash, is ferroalloy in smelting Si
When iron and industrial silicon (metallic silicon), what is produced in ore-smelting electric furnace has beaten volatility very strong SiO2With Si gases after discharge with
Air rapid oxidation condensation precipitation.
Further, the particle diameter of the SILICA FUME is 0.2-0.3 μm.
Further, the viscosity of the hydroxypropyl methyl cellulose is the mPas of 15-18 ten thousand.The hydroxypropyl methyl fiber
Element, also known as hydroxypropyl methylcellulose, HPMC, English abbreviation is HPMC.It is the cotton fiber from high purity
Element is made through special etherificate in the basic conditions as raw material.Hydroxypropyl methyl cellulose as cement mortar water-loss reducer,
Retarder makes mortar have pumping.In slurry of plastering, gypsum material, powder of lacquer putty for use on or other building materials as binder, it is possible to increase
Smear, extends operable time.
Further, the water reducer for how based water reducer or polycarboxylic acid salt's water reducer.
Further, the thixotroping value of the thixotropic lubricant is more than 7.The thixotropic lubricant is by special working process
, it is adaptable to the powdery rheologic additive of mineral base (dry mash) system and paste system.Thixotropic lubricant primarily directed to
The performance of the improvement of application property, open hour and uniformity in cement based system, increase mortar, plaster, bottom ash, motar and
The workability and sag resistance of adhesive, prevent self-leveling cement to be layered.
Further：The cellulose ether is hydroxypropylcelluloether ether or hydroxyethyl ether cellulose.
The second object of the present invention is the preparation method for providing the tile pointing agent, and it is concretely comprised the following steps：According to
Than weighing said components, it is mixed evenly, produces the tile pointing agent.
The present invention also aims to protect application of the tile pointing agent during tile pointing.
The beneficial effects of the invention are as follows：
The tile pointing agent cohesive force of the present invention is strong, can be in close contact with facing, not produce crack, antiseepage outlet capacity is good,
Can effective waterproof.
Embodiment
Embodiment 1
A kind of tile pointing agent, consisting of：425R Portland cements 40kg, particle diameter are 0.2 μm of SILICA FUME
9kg, iron oxide 5kg, redispersable latex powder 3kg, viscosity are 150,000 mPas hydroxypropyl methyl cellulose 2.1kg, formic acid
Calcium 0.4kg, how based water reducer 0.48kg, mill base 0.8kg, PT-CZ01 (thixotropic lubricant) 0.8kg and hydroxypropylcelluloether ether
0.25kg。
The preparation method of the tile pointing agent is：Said components are weighed according to proportioning, are mixed evenly, are produced described
Tile pointing agent.
Embodiment 2
A kind of tile pointing agent, consisting of：325R Portland cements 30kg, particle diameter are 0.3 μm of SILICA FUME
6kg, titanium oxide 2kg, redispersable latex powder 6kg, viscosity are 180,000 mPas hydroxypropyl methyl cellulose 1.3kg, formic acid
Calcium 0.7kg, polycarboxylic acid salt's water reducer 0.34kg, mill base 1.2kg, PT-CZ11 (thixotropic lubricant) 0.5kg and hydroxy ethyl fiber
Plain ether 0.25kg.
The preparation method of the tile pointing agent is：Said components are weighed according to proportioning, are mixed evenly, are produced described
Tile pointing agent.
Embodiment 3
A kind of tile pointing agent, consisting of：425 Portland cement 36kg, particle diameter are 0.24 μm of SILICA FUME
7.5kg, titanium oxide 3.2kg, redispersable latex powder 4.5kg, viscosity are 160,000 mPas polycarboxylic acid salt's water reducer
0.42kg, mill base 1.0kg, Optibent602 (thixotropic lubricant) 0.64kg and hydroxypropylcelluloether ether 0.23kg.
The preparation method of the tile pointing agent is：Said components are weighed according to proportioning, are mixed evenly, are produced described
Tile pointing agent.
Comparative example 1
A kind of tile pointing agent, consisting of：525R Portland cements 32kg, particle diameter are 0.3 μm of SILICA FUME
8kg, titanium oxide 3kg, redispersable latex powder 5kg, viscosity are 170,000 mPas hydroxypropyl methyl cellulose 1.5kg, poly- carboxylic
Barbiturates water reducer 0.45kg, mill base 0.9kg, Optibent987 (thixotropic lubricant) 0.7kg and hydroxyethyl ether cellulose
0.21kg。
The preparation method of the tile pointing agent is：Said components are weighed according to proportioning, are mixed evenly, are produced described
Tile pointing agent.
Comparative example 2
A kind of tile pointing agent, consisting of：325R Portland cements 38kg, particle diameter are 0.2 μm of SILICA FUME
6.5kg, titanium oxide 2.5kg, redispersable latex powder 5kg, viscosity for 150,000 mPas hydroxypropyl methyl cellulose 1.6kg,
Calcium formate 0.6kg, how based water reducer 0.45kg, mill base 0.9kg and hydroxyethyl ether cellulose 0.21kg.
The preparation method of the tile pointing agent is：Said components are weighed according to proportioning, are mixed evenly, are produced described
Tile pointing agent.
Comparative example 3
Jointing agent system is carried out with formula described in Publication No. CN101085907 application for a patent for invention embodiment and method
It is standby.Specially：It is accurate to weigh 42.5# portland cements 400kg, quartz sand 600kg more than 80 mesh, water reducer 3kg, water-loss reducer
0.5kg, adhesive 5kg, hydrophober 1.2kg, lignin fibre 3kg, iron oxide black 30kg.Then mixer is started, first water
Mud put into mixer, then successively water-loss reducer, adhesive, water reducer, hydrophober, fiber, pigment input mixer mixed
2-3 minutes, then quartz sand input mixer be sufficiently mixed 15 minutes, pack, produce the jointing agent.
Comparative example 4
Jointing agent is carried out with formula described in Publication No. CN104876501A application for a patent for invention embodiment 2 and method
Prepare.Specially：The rubble English that 3600 parts of 425 silicate cement, 400 parts of flyash, specification are 70-100 mesh is weighed by weight
3300 parts of sand, 2485 parts of the fine quartz sand that specification is 100-200 mesh, 120 parts of rubber powder, 15 parts of hydrophober, viscosity unit are 4-10
Ten thousand mpas 15 parts of hydroxypropyl methyl cellulose, suppress 20 parts of accumulation of salt in the surface soil agent, 30 parts of rubber powder optimization element, 15 parts of agent of mortar optimization,
40 parts of powdery high efficiency water reducing agent.The rubber powder optimization element, mortar optimization agent are professional building materials.
The preparation method of the jointing agent is：
1) according to formula weigh constitute inorganic admixture 3855 parts of 600 parts of 3000 parts of cement, flyash, rubble sand,
2400 parts of fine quartz sand, 55 parts of rubber powder, 15 parts of hydrophober, 15 parts of hydroxypropyl methyl cellulose, 20 parts of suppression accumulation of salt in the surface soil agent, rubber powder are excellent
Change 30 parts of element, 10 parts of agent of mortar optimization, 38 parts of powdery high efficiency water reducing agent；
2) by the cement weighed, flyash, rubble sand, fine quartz sand, rubber powder, hydrophober, hydroxypropyl methyl cellulose,
Suppress accumulation of salt in the surface soil agent, rubber powder optimization element and mortar optimization agent and be respectively put into dryer drying at least more than 24 hours in advance, then from
So it is cooled to room temperature；
3) each component that will be cooled to room temperature is added in mixer together, first with the stirring 120 seconds of 20 revs/min of rotating speed, then
With rotating speed, 70 revs/min are stirred 60 seconds, are stagnated 60 seconds, then with the stirring 60 seconds of 70 revs/min of rotating speed, then with 20 revs/min of stirrings of rotating speed
120 seconds；
4) the inorganic admixture that stirring is mixed is taken out, is heated to 45 DEG C；
5) mixer is again turned on, powdery high efficiency water reducing agent is slowly added to while with the stirring 120 seconds of 20 revs/min of rotating speed
With 45 DEG C of the inorganic admixture mixed, it is ensured that added in 120 seconds, then with the stirring 60 seconds of 70 revs/min of rotating speed, 60 are stagnated
Second, then with the stirring 60 seconds of 70 revs/min of rotating speed, then with the stirring 120 seconds of 20 revs/min of rotating speed；
6) jointing agent prepared is taken out to be positioned in dry sealed container.
Jointing agent performance test
The hook prepared to embodiment 1-3 (being respectively experimental group 1-3) and comparative example 1-4 (being respectively control group 1-4)
Stitch agent and carry out performance detection, testing result is as shown in the table：
Thus prove, tile pointing agent cohesive force of the invention is strong, can be in close contact with facing, not produce crack, antiseepage
Outlet capacity is good, can effective waterproof.
Finally illustrate, the above embodiments are merely illustrative of the technical solutions of the present invention and it is unrestricted, although with reference to compared with
The present invention is described in detail good embodiment, it will be understood by those within the art that, can be to skill of the invention
Art scheme is modified or equivalent substitution, and without departing from the objective and scope of technical solution of the present invention, it all should cover at this
Among the right of invention.
Claims (8)
1. a kind of tile pointing agent, it is characterised in that by weight including following components：30-40 parts of cement, 6-9 parts of SILICA FUME,
Iron oxide or 2-5 parts of titanium oxide, 3-6 parts of redispersable latex powder, 1.3-2.1 parts of hydroxypropyl methyl cellulose, calcium formate 0.4-
0.7 part, 0.34-0.48 parts of water reducer, 0.8-1.2 parts of mill base, 0.5-0.8 parts of thixotropic lubricant and cellulose ether 0.18-0.25
Part；The thixotroping value of the thixotropic lubricant is more than 7.
2. a kind of tile pointing agent according to claim 1, it is characterised in that the cement is Portland cement.
3. a kind of tile pointing agent according to claim 1, it is characterised in that the particle diameter of the SILICA FUME is 0.2-0.3 μ
m。
4. a kind of tile pointing agent according to claim 1, it is characterised in that the viscosity of the hydroxypropyl methyl cellulose
For the mPas of 15-18 ten thousand.
5. a kind of tile pointing agent according to claim 1, it is characterised in that the water reducer for how based water reducer or poly-
Metal carboxylate water reducer.
6. a kind of tile pointing agent according to claim 1, it is characterised in that：The cellulose ether is hydroxypropyl cellulose
Ether or hydroxyethyl ether cellulose.
7. the preparation method of a kind of tile pointing agent described in claim 1, it is characterised in that concretely comprise the following steps：According to proportioning
Said components are weighed, are mixed evenly, the tile pointing agent is produced.
8. application of the tile pointing agent described in claim any one of 1-6 during tile pointing.