CN107814529A - A kind of preparation technology of the environmentally friendly jointing agent of ceramic tile - Google Patents
A kind of preparation technology of the environmentally friendly jointing agent of ceramic tile Download PDFInfo
- Publication number
- CN107814529A CN107814529A CN201710887081.5A CN201710887081A CN107814529A CN 107814529 A CN107814529 A CN 107814529A CN 201710887081 A CN201710887081 A CN 201710887081A CN 107814529 A CN107814529 A CN 107814529A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- ceramic tile
- environmentally friendly
- jointing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of preparation technology the invention discloses ceramic tile with environmentally friendly jointing agent, the ceramic tile are made up of with environmentally friendly jointing agent the component of following parts by weight：40 55 parts of latex powder, 3 12 parts of flower extracting liquid, 7 18 parts of diatom ooze, 13 parts of inorganic pigment, 20 30 parts of white cement, 10 20 parts of mineral powder, absorption banket 10 18 parts, 16 parts of nano titanium dioxide powder, 37 parts of processing aid, 15 parts of adhesion promoter, 16 parts of barium carbonate, 15 parts of antimildew disinfectant, except 25 parts of 13 parts of Formaldehyde as Additives and inorfil.The ceramic tile of the present invention realized to there is the suction-operated for going back material with this environment-friendly materials of diatom ooze be added with environmentally friendly jointing agent, meanwhile, add antimildew disinfectant, effectively prevent mouldy phenomenon, keep ceramic tile stitch in it is not mouldy, clean.
Description
Technical field
A kind of building materials technology field of the present invention, and in particular to the preparation technology of the environmentally friendly jointing agent of ceramic tile.
Background technology
Tile pointing agent is also known as face brick jointing agent, and the material is to be equipped with multiple additives warp by cement, quartz sand, filling material
Mechanical mixture uniformly forms, and tile pointing agent is mainly used in the gap filler between ceramic tile and face brick.
At present, jointing agent majority carries out jointing after finishing is completed, and prevents from being caught in dust etc. in seam, still, conventional
Material is not environmentally friendly enough used by jointing agent, harmful, therefore, is badly in need of a kind of environmentally friendly jointing agent.
The content of the invention
In view of the defects and deficiencies of the prior art, the present invention intends to provide a kind of ceramic tile system of environmentally friendly jointing agent
Standby technique, to solve the problems, such as proposed in background technology.
1st, to achieve the above object, the technical solution adopted by the present invention is：A kind of preparation work of the environmentally friendly jointing agent of ceramic tile
Skill, its creativeness are：The ceramic tile is made up of with environmentally friendly jointing agent the component of following parts by weight：Latex powder 40-55 parts, flower
Extract solution 3-12 parts, diatom ooze 7-18 parts, inorganic pigment 1-3 parts, white cement 20-30 parts, mineral powder 10-20 parts, absorption are filled out
Native 10-18 parts, nano titanium dioxide powder 1-6 parts, processing aid 3-7 parts, adhesion promoter 1-5 parts, barium carbonate 1-6 parts, mould proof kill
Microbial inoculum 1-5 parts, except Formaldehyde as Additives 1-3 parts and inorfil 2-5 parts；The preparation technology comprises the following steps：
1）Weigh latex powder according to formula, flower extracting liquid, diatom ooze, inorganic pigment, white cement, mineral powder, absorption are banketed,
Nano titanium dioxide powder, processing aid, adhesion promoter, barium carbonate, antimildew disinfectant, except Formaldehyde as Additives and inorfil；
2）By the latex powder weighed, flower extracting liquid, diatom ooze, inorganic pigment, white cement, mineral powder, absorption banket, nanometer
Titania powder, processing aid, adhesion promoter, barium carbonate, antimildew disinfectant, it is respectively put into baking except Formaldehyde as Additives and inorfil
Dry machine is dried at least more than 24 hours in advance, then naturally cools to room temperature；
3）It will be cooled to the latex powder of room temperature, flower extracting liquid, diatom ooze, inorganic pigment, white cement, mineral powder, absorption are filled out
Soil, nano titanium dioxide powder, processing aid, adhesion promoter, barium carbonate, antimildew disinfectant, mix except Formaldehyde as Additives and inorfil
It is combined and adds in mixer, first with the stirring 120 seconds of 10-30 revs/min of rotating speed, then with 60-80 revs/min of stirring 60 of rotating speed
Second, stagnate 60 seconds, then with the stirring 60 seconds of 60-80 revs/min of rotating speed, then with the stirring 120 seconds of 10-30 revs/min of rotating speed；
4）Take out the mixing after stirring and close material, be heated to 40~50 DEG C；
5）The ceramic tile prepared is taken out to be positioned in the container for drying sealing with environmentally friendly jointing agent.
Further, the environmentally friendly jointing agent of a kind of ceramic tile, is made up of the component of following parts by weight：Latex powder 45-50 parts, flower
Piece extract solution 5-10 parts, diatom ooze 10-15 parts, inorganic pigment 1-2 parts, white cement 22-28 parts, mineral powder 12-18 parts, absorption
Banket 12-16 parts, nano titanium dioxide powder 2-5 parts, processing aid 4-6 parts, adhesion promoter 2-4 parts, barium carbonate 2-5 parts, mould proof
Bactericide 2-4 parts, except Formaldehyde as Additives 1-2 parts and inorfil 3-4 parts.
Further, the environmentally friendly jointing agent of a kind of ceramic tile, is made up of the component of following parts by weight：48 parts of latex powder, flower
7 parts of extract solution, 12 parts of diatom ooze, 2 parts of inorganic pigment, 25 parts of white cement, 15 parts of mineral powder, absorption are banketed 14 part, nanometers two
3 parts of titanium dioxide powder, 5 parts of processing aid, 3 parts of adhesion promoter, 4 parts of barium carbonate, 3 parts of antimildew disinfectant, except 2 parts of Formaldehyde as Additives and nothing
4 parts of machine fiber.
The present invention has the beneficial effect that：The ceramic tile of the present invention with being added with this environment-friendly materials of diatom ooze in environmentally friendly jointing agent,
Realize to there is the suction-operated for going back material, meanwhile, antimildew disinfectant is added, effectively prevent mouldy phenomenon, keeps ceramic tile seam
It is inside not mouldy, cleaning.
Embodiment
Present embodiment use technical scheme be：
Embodiment 1
A kind of preparation technology of the environmentally friendly jointing agent of ceramic tile, component group of the ceramic tile with environmentally friendly jointing agent by following parts by weight
Into：40 parts of latex powder, 3 parts of flower extracting liquid, 7 parts of diatom ooze, inorganic pigment 1-3 parts, 20 parts of white cement, 10 parts of mineral powder,
Absorption banket 10 parts, 1 part of nano titanium dioxide powder, 3 parts of processing aid, 1 part of adhesion promoter, 1 part of barium carbonate, antimildew disinfectant 1
Part, except 2 parts of 1 part of Formaldehyde as Additives and inorfil；The preparation technology comprises the following steps：
1）Weigh latex powder according to formula, flower extracting liquid, diatom ooze, inorganic pigment, white cement, mineral powder, absorption are banketed,
Nano titanium dioxide powder, processing aid, adhesion promoter, barium carbonate, antimildew disinfectant, except Formaldehyde as Additives and inorfil；
2）By the latex powder weighed, flower extracting liquid, diatom ooze, inorganic pigment, white cement, mineral powder, absorption banket, nanometer
Titania powder, processing aid, adhesion promoter, barium carbonate, antimildew disinfectant, it is respectively put into baking except Formaldehyde as Additives and inorfil
Dry machine is dried at least more than 24 hours in advance, then naturally cools to room temperature；
3）It will be cooled to the latex powder of room temperature, flower extracting liquid, diatom ooze, inorganic pigment, white cement, mineral powder, absorption are filled out
Soil, nano titanium dioxide powder, processing aid, adhesion promoter, barium carbonate, antimildew disinfectant, mix except Formaldehyde as Additives and inorfil
It is combined and adds in mixer, first with the stirring 120 seconds of 10-30 revs/min of rotating speed, then with 60-80 revs/min of stirring 60 of rotating speed
Second, stagnate 60 seconds, then with the stirring 60 seconds of 60-80 revs/min of rotating speed, then with the stirring 120 seconds of 10-30 revs/min of rotating speed；
4）Take out the mixing after stirring and close material, be heated to 40~50 DEG C；
5）The ceramic tile prepared is taken out to be positioned in the container for drying sealing with environmentally friendly jointing agent.
Embodiment 2
A kind of preparation technology of the environmentally friendly jointing agent of ceramic tile, component group of the ceramic tile with environmentally friendly jointing agent by following parts by weight
Into：55 parts of latex powder, 12 parts of flower extracting liquid, 18 parts of diatom ooze, 3 parts of inorganic pigment, 30 parts of white cement, 20 parts of mineral powder,
Absorption banket 18 parts, 6 parts of nano titanium dioxide powder, 7 parts of processing aid, 5 parts of adhesion promoter, 6 parts of barium carbonate, antimildew disinfectant 5
Part, except 5 parts of 3 parts of Formaldehyde as Additives and inorfil；The preparation technology comprises the following steps：
1）Weigh latex powder according to formula, flower extracting liquid, diatom ooze, inorganic pigment, white cement, mineral powder, absorption are banketed,
Nano titanium dioxide powder, processing aid, adhesion promoter, barium carbonate, antimildew disinfectant, except Formaldehyde as Additives and inorfil；
2）By the latex powder weighed, flower extracting liquid, diatom ooze, inorganic pigment, white cement, mineral powder, absorption banket, nanometer
Titania powder, processing aid, adhesion promoter, barium carbonate, antimildew disinfectant, it is respectively put into baking except Formaldehyde as Additives and inorfil
Dry machine is dried at least more than 24 hours in advance, then naturally cools to room temperature；
3）It will be cooled to the latex powder of room temperature, flower extracting liquid, diatom ooze, inorganic pigment, white cement, mineral powder, absorption are filled out
Soil, nano titanium dioxide powder, processing aid, adhesion promoter, barium carbonate, antimildew disinfectant, mix except Formaldehyde as Additives and inorfil
It is combined and adds in mixer, first with the stirring 120 seconds of 10-30 revs/min of rotating speed, then with 60-80 revs/min of stirring 60 of rotating speed
Second, stagnate 60 seconds, then with the stirring 60 seconds of 60-80 revs/min of rotating speed, then with the stirring 120 seconds of 10-30 revs/min of rotating speed；
4）Take out the mixing after stirring and close material, be heated to 40~50 DEG C；
5）The ceramic tile prepared is taken out to be positioned in the container for drying sealing with environmentally friendly jointing agent.
Embodiment 3
A kind of preparation technology of the environmentally friendly jointing agent of ceramic tile, component group of the ceramic tile with environmentally friendly jointing agent by following parts by weight
Into：48 parts of latex powder, 7 parts of flower extracting liquid, 12 parts of diatom ooze, 2 parts of inorganic pigment, 25 parts of white cement, 15 parts of mineral powder, suction
It is attached banket 14 parts, 3 parts of nano titanium dioxide powder, 5 parts of processing aid, 3 parts of adhesion promoter, 4 parts of barium carbonate, 3 parts of antimildew disinfectant,
Except 4 parts of 2 parts of Formaldehyde as Additives and inorfil；The preparation technology comprises the following steps：
1）Weigh latex powder according to formula, flower extracting liquid, diatom ooze, inorganic pigment, white cement, mineral powder, absorption are banketed,
Nano titanium dioxide powder, processing aid, adhesion promoter, barium carbonate, antimildew disinfectant, except Formaldehyde as Additives and inorfil；
2）By the latex powder weighed, flower extracting liquid, diatom ooze, inorganic pigment, white cement, mineral powder, absorption banket, nanometer
Titania powder, processing aid, adhesion promoter, barium carbonate, antimildew disinfectant, it is respectively put into baking except Formaldehyde as Additives and inorfil
Dry machine is dried at least more than 24 hours in advance, then naturally cools to room temperature；
3）It will be cooled to the latex powder of room temperature, flower extracting liquid, diatom ooze, inorganic pigment, white cement, mineral powder, absorption are filled out
Soil, nano titanium dioxide powder, processing aid, adhesion promoter, barium carbonate, antimildew disinfectant, mix except Formaldehyde as Additives and inorfil
It is combined and adds in mixer, first with the stirring 120 seconds of 10-30 revs/min of rotating speed, then with 60-80 revs/min of stirring 60 of rotating speed
Second, stagnate 60 seconds, then with the stirring 60 seconds of 60-80 revs/min of rotating speed, then with the stirring 120 seconds of 10-30 revs/min of rotating speed；
4）Take out the mixing after stirring and close material, be heated to 40~50 DEG C；
5）The ceramic tile prepared is taken out to be positioned in the container for drying sealing with environmentally friendly jointing agent.
The ceramic tile of embodiment 1~3 is realized to going back material with this environment-friendly materials of diatom ooze are added with environmentally friendly jointing agent
Suction-operated, meanwhile, add antimildew disinfectant, effectively prevent mouldy phenomenon, keep not mouldy in ceramic tile seam, clean.
It is described above, it is merely illustrative of the technical solution of the present invention and unrestricted, those of ordinary skill in the art are to this hair
The other modifications or equivalent substitution that bright technical scheme is made, without departing from the spirit and scope of technical solution of the present invention,
It all should cover among scope of the presently claimed invention.
Claims (3)
- A kind of 1. ceramic tile preparation technology of environmentally friendly jointing agent, it is characterised in that：The ceramic tile is with environmentally friendly jointing agent by following heavy Measure the component composition of part：Latex powder 40-55 parts, flower extracting liquid 3-12 parts, diatom ooze 7-18 parts, inorganic pigment 1-3 parts, plain boiled water Mud 20-30 parts, mineral powder 10-20 parts, adsorb banket 10-18 parts, nano titanium dioxide powder 1-6 parts, processing aid 3-7 Part, adhesion promoter 1-5 parts, barium carbonate 1-6 parts, antimildew disinfectant 1-5 parts, except Formaldehyde as Additives 1-3 parts and inorfil 2-5 parts；Institute Preparation technology is stated to comprise the following steps：1）Weigh latex powder according to formula, flower extracting liquid, diatom ooze, inorganic pigment, white cement, mineral powder, absorption are banketed, Nano titanium dioxide powder, processing aid, adhesion promoter, barium carbonate, antimildew disinfectant, except Formaldehyde as Additives and inorfil；2）By the latex powder weighed, flower extracting liquid, diatom ooze, inorganic pigment, white cement, mineral powder, absorption banket, nanometer Titania powder, processing aid, adhesion promoter, barium carbonate, antimildew disinfectant, it is respectively put into baking except Formaldehyde as Additives and inorfil Dry machine is dried at least more than 24 hours in advance, then naturally cools to room temperature；3）It will be cooled to the latex powder of room temperature, flower extracting liquid, diatom ooze, inorganic pigment, white cement, mineral powder, absorption are filled out Soil, nano titanium dioxide powder, processing aid, adhesion promoter, barium carbonate, antimildew disinfectant, mix except Formaldehyde as Additives and inorfil It is combined and adds in mixer, first with the stirring 120 seconds of 10-30 revs/min of rotating speed, then with 60-80 revs/min of stirring 60 of rotating speed Second, stagnate 60 seconds, then with the stirring 60 seconds of 60-80 revs/min of rotating speed, then with the stirring 120 seconds of 10-30 revs/min of rotating speed；4）Take out the mixing after stirring and close material, be heated to 40~50 DEG C；5）The ceramic tile prepared is taken out to be positioned in the container for drying sealing with environmentally friendly jointing agent.
- A kind of 2. preparation technology of the environmentally friendly jointing agent of ceramic tile according to claim 1, it is characterised in that：By following weight The component composition of part：Latex powder 45-50 parts, flower extracting liquid 5-10 parts, diatom ooze 10-15 parts, inorganic pigment 1-2 parts, plain boiled water Mud 22-28 parts, mineral powder 12-18 parts, adsorb banket 12-16 parts, nano titanium dioxide powder 2-5 parts, processing aid 4-6 Part, adhesion promoter 2-4 parts, barium carbonate 2-5 part antimildew disinfectant 2-4 parts, except Formaldehyde as Additives 1-2 parts and inorfil 3-4 parts.
- A kind of 3. preparation technology of the environmentally friendly jointing agent of ceramic tile according to claim 1, it is characterised in that：By following weight The component composition of part：48 parts of latex powder, 7 parts of flower extracting liquid, 12 parts of diatom ooze, 2 parts of inorganic pigment, 25 parts of white cement, mineral 15 parts of powder, absorption banket 14 parts, it is 3 parts of nano titanium dioxide powder, 5 parts of processing aid, 3 parts of adhesion promoter, 4 parts of barium carbonate, anti- Mould 3 parts of bactericide, except 4 parts of 2 parts of Formaldehyde as Additives and inorfil.