CN104845348A - 一种利用蜂窝陶瓷微粉负载复合阻燃剂的高效改性pc复合料及其制备方法 - Google Patents

一种利用蜂窝陶瓷微粉负载复合阻燃剂的高效改性pc复合料及其制备方法 Download PDF

Info

Publication number
CN104845348A
CN104845348A CN201510208076.8A CN201510208076A CN104845348A CN 104845348 A CN104845348 A CN 104845348A CN 201510208076 A CN201510208076 A CN 201510208076A CN 104845348 A CN104845348 A CN 104845348A
Authority
CN
China
Prior art keywords
flame retardant
micro mist
honey comb
ceramic honey
modified
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510208076.8A
Other languages
English (en)
Inventor
项孝泓
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhu Zhongli Parts Co Ltd
Original Assignee
Wuhu Zhongli Parts Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhu Zhongli Parts Co Ltd filed Critical Wuhu Zhongli Parts Co Ltd
Priority to CN201510208076.8A priority Critical patent/CN104845348A/zh
Publication of CN104845348A publication Critical patent/CN104845348A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种改性PC阻燃料，具体涉及一种利用蜂窝陶瓷微粉负载复合阻燃剂的高效改性PC复合料及其制备方法，该复合材料在制备过程中以聚磷酸铵、甲基膦酸二甲酯作为环保复合阻燃增效剂，并将其在高压条件下渗透负载于具有多孔吸附性的蜂窝陶瓷微粉中，这样处理使得阻燃剂在PC料中分散更为均匀，阻燃效率更高，且蜂窝陶瓷微粉的加入进一步提升了PC料的力学性能，增进抗腐防蚀能力，本发明制备的改性PC复合料生产工艺简单，产品质优价廉，使用安全环保，极具市场竞争力。

Description

一种利用蜂窝陶瓷微粉负载复合阻燃剂的高效改性PC复合料及其制备方法
技术领域
本发明涉及一种改性PC阻燃料，具体涉及一种利用蜂窝陶瓷微粉负载复合阻燃剂的高效改性PC复合料及其制备方法。
背景技术
聚碳酸酯（PC）是一种无色透明的无定性热塑性材料，具有无色透明、耐热、抗冲击、阻燃等性能，具有良好的机械性能，应用十分广泛，其中阻燃PC是其较为重要的一个应用方向。
在传统的生产过程中，为了提高PC的阻燃性能，主要是在生产过程中直接添加阻燃剂，这就导致了材料的阻燃效果低下不均，阻燃剂利用率低，因此需要从工艺和配方上着手，提高阻燃剂在PC料中的利用率，从而获得性能更优的阻燃料。
发明内容
本发明的目的在于，提供一种利用蜂窝陶瓷微粉负载复合阻燃剂的高效改性PC复合料及其制备方法，以期获得高效的阻燃效果，为了实现上述目的，本发明采用的技术方案如下：
一种利用蜂窝陶瓷微粉负载复合阻燃剂的高效改性PC复合料及其制备方法，其特征在于，该复合料由以下重量份的原料制成：蜂窝陶瓷微粉8-10、聚磷酸铵2-3、甲基膦酸二甲酯3-4、PC 50-60、三甲硅基甲基膦酸二甲酯3-5、甲基硅油1-2、甲基丙烯酸缩水甘油酯3-4、硅烷偶联剂0.1-0.2、二硬脂基季戊四醇二亚磷酸酯0.05-0.1、超细橡胶粉10-12。
所述的一种利用蜂窝陶瓷微粉负载复合阻燃剂的高效改性PC复合料及其制备方法，其特征在于，所述的制备方法包含以下步骤：
（1）先将蜂窝陶瓷微粉与聚磷酸铵、甲基膦酸二甲酯、硅烷偶联剂混合，完全搅拌均匀后将混合物料加压至40-60Mpa，保持40-50min后缓慢卸压，待混合物料恢复至常压后再次充分搅拌混合，得蜂窝陶瓷微粉负载聚磷酸铵-甲基膦酸二甲酯复合阻燃剂材料备用；
（2）将步骤（1）所得的材料与余下成分一起投入高速混料机中混合均匀，送入双螺杆造粒机中挤出造粒，即得改性PC阻燃料。
有益效果：本发明以聚磷酸铵、甲基膦酸二甲酯作为环保复合阻燃增效剂，并将其在高压条件下渗透负载于具有多孔吸附性的蜂窝陶瓷微粉中，这样处理使得阻燃剂在PC料中分散更为均匀，阻燃效率更高，且蜂窝陶瓷微粉的加入进一步提升了PC料的力学性能，增进抗腐防蚀能力，本发明制备的改性PC复合料生产工艺简单，产品质优价廉，使用安全环保，极具市场竞争力。
具体实施方式
实施例
本实施例的复合材料由以下重量份的原料制成：蜂窝陶瓷微粉10、聚磷酸铵3、甲基膦酸二甲酯3.5、PC 58、三甲硅基甲基膦酸二甲酯4、甲基硅油1.8、甲基丙烯酸缩水甘油酯4、硅烷偶联剂0.2、二硬脂基季戊四醇二亚磷酸酯0.06、超细橡胶粉11。
所述的一种利用蜂窝陶瓷微粉负载复合阻燃剂的高效改性PC复合料及其制备方法，其制备方法如下：
（1）先将蜂窝陶瓷微粉与聚磷酸铵、甲基膦酸二甲酯、硅烷偶联剂混合，完全搅拌均匀后将混合物料加压至50Mpa，保持45min后缓慢卸压，待混合物料恢复至常压后再次充分搅拌混合，得蜂窝陶瓷微粉负载聚磷酸铵-甲基膦酸二甲酯复合阻燃剂材料备用；
（2）将步骤（1）所得的材料与余下成分一起投入高速混料机中混合均匀，送入双螺杆造粒机中挤出造粒，即得改性PC阻燃料。
本实施例制得的复合材料性能测试结果如下：
检测项目 检测值
拉伸强度 53.2MPa
断裂伸长率 52%
冲击强度 17.2MPa
弯曲强度 68.5MPa
阻燃等级（UL-94） V-0

Claims (2)

1.一种利用蜂窝陶瓷微粉负载复合阻燃剂的高效改性PC复合料，其特征在于，该改性PC复合料由以下重量份的原料制成：蜂窝陶瓷微粉8-10、聚磷酸铵2-3、甲基膦酸二甲酯3-4、PC 50-60、三甲硅基甲基膦酸二甲酯3-5、甲基硅油1-2、甲基丙烯酸缩水甘油酯3-4、硅烷偶联剂0.1-0.2、二硬脂基季戊四醇二亚磷酸酯0.05-0.1、超细橡胶粉10-12。
2.如权利要求1所述的一种利用蜂窝陶瓷微粉负载复合阻燃剂的高效改性PC复合料及其制备方法，其特征在于，所述的制备方法包含以下步骤：
（1）先将蜂窝陶瓷微粉与聚磷酸铵、甲基膦酸二甲酯、硅烷偶联剂混合，完全搅拌均匀后将混合物料加压至40-60Mpa，保持40-50min后缓慢卸压，待混合物料恢复至常压后再次充分搅拌混合，得蜂窝陶瓷微粉负载聚磷酸铵-甲基膦酸二甲酯复合阻燃剂材料备用；
（2）将步骤（1）所得的材料与余下成分一起投入高速混料机中混合均匀，送入双螺杆造粒机中挤出造粒，即得改性PC阻燃料。
CN201510208076.8A 2015-04-28 2015-04-28 一种利用蜂窝陶瓷微粉负载复合阻燃剂的高效改性pc复合料及其制备方法 Pending CN104845348A (zh)