CN104844169A - 一种阻燃陶瓷眼 - Google Patents

一种阻燃陶瓷眼 Download PDF

Info

Publication number
CN104844169A
CN104844169A CN201510200469.4A CN201510200469A CN104844169A CN 104844169 A CN104844169 A CN 104844169A CN 201510200469 A CN201510200469 A CN 201510200469A CN 104844169 A CN104844169 A CN 104844169A
Authority
CN
China
Prior art keywords
powder
aluminum oxide
add
acetone
deionized water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510200469.4A
Other languages
English (en)
Inventor
刘勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI HANSHAN SHUNTAIN TEXTILE Co Ltd
Original Assignee
ANHUI HANSHAN SHUNTAIN TEXTILE Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI HANSHAN SHUNTAIN TEXTILE Co Ltd filed Critical ANHUI HANSHAN SHUNTAIN TEXTILE Co Ltd
Priority to CN201510200469.4A priority Critical patent/CN104844169A/zh
Publication of CN104844169A publication Critical patent/CN104844169A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种阻燃陶瓷眼，其是由下述重量份的原料制得：氧化铝80-90、火砖粉4-6、硼酸锌1-2、水滑石粉3-6、膨润土15-20、硅微粉2-4、碳化硅1-2、植物油1-2、软锰矿粉1-3、纳米BN 1-2、聚乙烯纤维1-2、硅丙乳液0.1-0.3、六偏磷酸钠1-2、环己酮1-2、硬脂酸钡1-2、丙酮0.2-0.3、聚乙二醇1-2、硝酸铝0.3-0.5、去离子水6-12。

Description

一种阻燃陶瓷眼
技术领域
本发明涉及纺织用陶瓷领域，确切地说是一种阻燃陶瓷眼。
背景技术
     陶瓷眼适用于各种绕线机及纺织机械中的过线过丝部件,由精密陶瓷加工，由于硬度较高，表面光滑，漆包线在其表面滑动时顺畅不受损伤。
发明内容
本发明的目的在于提供一种阻燃陶瓷眼。
上述目的通过以下方案实现：
  一种阻燃陶瓷眼，其特征在于：其是由下述重量份的原料制得：
氧化铝80-90、火砖粉4-6、硼酸锌1-2、水滑石粉3-6、膨润土15-20、硅微粉2-4、碳化硅1-2、植物油1-2、软锰矿粉1-3、纳米BN 1-2、聚乙烯纤维1-2、硅丙乳液0.1-0.3、六偏磷酸钠1-2、环己酮1-2、硬脂酸钡1-2、丙酮0.2-0.3、聚乙二醇1-2、硝酸铝0.3-0.5、去离子水6-12。
所述的一种阻燃陶瓷眼，其特征在于：制备方法为：
（1）聚乙二醇、硝酸铝、去离子水于30-40℃下搅拌均匀后，再加入六偏磷酸钠，于45-50℃下搅拌均匀后，调节PH为3.5-4，再加入碳化硅，于60-70℃下40-50转/分搅拌40-60min，得复配料备用；
（2）将氧化铝加入所得复配料中，于60-70℃下搅拌均匀，再静置30-50min，过滤，于75-80℃烘干后，450-550℃煅烧3-5min，得包覆氧化铝备用；
（3）火砖粉、硼酸锌、水滑石粉、膨润土混匀后，加入环己酮、硬脂酸钡、丙酮，球磨5-8小时，取出，干燥，后与包覆氧化铝以及其余原料混匀，加适量水制得浆料;
(4)所得浆料在100-120 ℃干燥3-4 h，粉碎后过80-100目筛，成型，再在580-600 ℃保温3-5小时排胶；最后烧结，随炉冷却，即得。
本发明的有益效果为：
本发明配方合理，制得的纺织用陶瓷眼高致密度、表面光滑平整、性能优异,通过添加硼酸锌以及水滑石粉，使得本发明具有很好的阻燃特性，适用于纺织业，安全可靠；同时本发明通过特殊的复配包膜液，使得碳化硅均匀的包覆在氧化铝表层，增加陶瓷眼的耐磨性和耐腐蚀性，从而增加使用寿命。
具体实施方式
  一种阻燃陶瓷眼，其是由下述重量（kg）的原料制得：
氧化铝80、火砖粉6、硼酸锌2、水滑石粉3、膨润土20、硅微粉4、碳化硅1、植物油2、软锰矿粉1、纳米BN 1、聚乙烯纤维2、硅丙乳液0.1、六偏磷酸钠1、环己酮2、硬脂酸钡2、丙酮0.2、聚乙二醇1、硝酸铝0.5、去离子水12。
所述的一种阻燃陶瓷眼，制备方法为：
（1）聚乙二醇、硝酸铝、去离子水于40℃下搅拌均匀后，再加入六偏磷酸钠，于50℃下搅拌均匀后，调节PH为4，再加入碳化硅，于70℃下50转/分搅拌60min，得复配料备用；
（2）将氧化铝加入所得复配料中，于65℃下搅拌均匀，再静置50min，过滤，于75℃烘干后，450℃煅烧5min，得包覆氧化铝备用；
（3）火砖粉、硼酸锌、水滑石粉、膨润土混匀后，加入环己酮、硬脂酸钡、丙酮，球磨6小时，取出，干燥，后与包覆氧化铝以及其余原料混匀，加适量水制得浆料;
(4)所得浆料在110 ℃干燥4 h，粉碎后过80目筛，成型，再在580℃保温4小时排胶；最后烧结，随炉冷却，即得。
所得陶瓷眼的参数如下：
莫氏硬度 9、导热系数（w/m.K） 26、常温耐压强度(MPa)≥690、常温抗折强度(MPa)≥730、耐火度 （℃）≥2100、最高使用温度(℃)≥1600。

Claims (2)

1.一种阻燃陶瓷眼，其特征在于：其是由下述重量份的原料制得：
氧化铝80-90、火砖粉4-6、硼酸锌1-2、水滑石粉3-6、膨润土15-20、硅微粉2-4、碳化硅1-2、植物油1-2、软锰矿粉1-3、纳米BN 1-2、聚乙烯纤维1-2、硅丙乳液0.1-0.3、六偏磷酸钠1-2、环己酮1-2、硬脂酸钡1-2、丙酮0.2-0.3、聚乙二醇1-2、硝酸铝0.3-0.5、去离子水6-12。
2.根据权利要求1所述的一种阻燃陶瓷眼，其特征在于：制备方法为：
（1）聚乙二醇、硝酸铝、去离子水于30-40℃下搅拌均匀后，再加入六偏磷酸钠，于45-50℃下搅拌均匀后，调节PH为3.5-4，再加入碳化硅，于60-70℃下40-50转/分搅拌40-60min，得复配料备用；
（2）将氧化铝加入所得复配料中，于60-70℃下搅拌均匀，再静置30-50min，过滤，于75-80℃烘干后，450-550℃煅烧3-5min，得包覆氧化铝备用；
（3）火砖粉、硼酸锌、水滑石粉、膨润土混匀后，加入环己酮、硬脂酸钡、丙酮，球磨5-8小时，取出，干燥，后与包覆氧化铝以及其余原料混匀，加适量水制得浆料;
(4)所得浆料在100-120 ℃干燥3-4 h，粉碎后过80-100目筛，成型，再在580-600 ℃保温3-5小时排胶；最后烧结，随炉冷却，即得。
CN201510200469.4A 2015-04-27 2015-04-27 一种阻燃陶瓷眼 Pending CN104844169A (zh)