CN104829148A - 一种助磨剂加料方法 - Google Patents

一种助磨剂加料方法 Download PDF

Info

Publication number
CN104829148A
CN104829148A CN201510220336.3A CN201510220336A CN104829148A CN 104829148 A CN104829148 A CN 104829148A CN 201510220336 A CN201510220336 A CN 201510220336A CN 104829148 A CN104829148 A CN 104829148A
Authority
CN
China
Prior art keywords
grinding aid
solvent
mother liquor
grinding
cement
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510220336.3A
Other languages
English (en)
Inventor
张大康
龙卫红
冯方波
明金龙
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Xiangyang Conch New Material Technology Co Ltd
Original Assignee
Hubei Xintongling Wanxiang Science and Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hubei Xintongling Wanxiang Science and Technology Co Ltd filed Critical Hubei Xintongling Wanxiang Science and Technology Co Ltd
Priority to CN201510220336.3A priority Critical patent/CN104829148A/zh
Publication of CN104829148A publication Critical patent/CN104829148A/zh
Pending legal-status Critical Current

Abstract

本发明属于化学建材技术领域，具体涉及一种助磨剂加料方法。本发明所解决的技术问题是提供一种助磨剂加料方法，以改善水泥助磨剂难以调整配方及助磨剂与熟料混合不均匀的技术问题。本发明助磨剂加料方法步骤如下：A、配制助磨剂母液；B、助磨剂母液与溶剂按下述体积比混合得混合液：助磨剂母液1份:溶剂0.1～100份；C、再将混合液加入水泥球磨机中。混合得混合液：助磨剂母液1份:溶剂0.1～1000份；C、再将混合液加入水泥球磨机中。本发明利用助磨剂在溶剂中溶解，在搅拌下得到充分的混匀，低浓度的助磨剂体积更大，更多更好的附着在粉体的新生表面上，保持了颗粒的分散，阻止了颗粒之间的聚结和团聚，从而提高设备的工作台时。

Description

一种助磨剂加料方法
技术领域
本发明属于化学建材技术领域，具体涉及一种助磨剂加料方法。
背景技术
在粉磨系统中，为了提高粉磨效果而使用助磨剂来提高台时。在实际使用过程中，液体助磨剂直接随管道经磨头螺旋筒流入磨机内，由于助磨剂只能分散在一个很小的面积上，不能混合均匀，没有充分发挥助磨剂效果。传统的加入方式是助磨剂计量后直接加入，小部分的助磨剂与大量的熟料存在混合均匀问题。特别当水泥企业水泥磨机工作状况或水泥各种矿物成分改变时，这种助磨剂传统的配制和使用方法很难做到适时调整水泥助磨剂的配方；此外，由于水泥助磨剂是两种以上原料液体按一定比例经物理混合而成，时间长不仅引起原料液体分层，而且易产生化学络合和加成反应，造成水泥助磨剂配方成分的改变。基于以上两个原因，造成目前水泥助磨剂产品在水泥生产过程中使用时，效果不稳定，严重影响了产品质量，降低了企业的效益。
本发明的发明人欲提供一种能克服上述技术缺陷的助磨剂加料方法。
发明内容
本发明所解决的技术问题是提供一种助磨剂加料方法，以改善水泥助磨剂难以调整配方，以及助磨剂与熟料混合不均匀的技术问题。
解决本发明技术问题是通过以下技术方案实现的：
本发明提供的助磨剂加料方法，步骤如下：
A、配制助磨剂母液；
B、助磨剂母液与溶剂按下述体积比混合得混合液：助磨剂母液1份:溶剂0.1～100份；
C、再将混合液加入水泥球磨机中。
其中，所述的助磨剂为三乙醇胺，三异丙醇胺等小分子助磨剂，或为多羟基二乙烯三胺分子量较大的助磨剂，或为聚羧酸等高分子助磨剂。
所述溶剂为水、甲醇、乙醇、四氢呋喃等极性溶剂，出于成本及环境因素考虑，优选水与乙醇。特别的，优选为水。
优选的助磨剂与溶剂范围按体积比计为：助磨剂母液:溶剂＝1:0.1～100。特别的，针对三乙醇胺，三异丙醇胺等小分子助磨剂，优选范围为1:0.1～10；针对多羟基二乙烯三胺等分子量较大的助磨剂，优选范围为1:1～10；针对聚羧酸等高分子助磨剂，优选范围为1:10～100。
本发明利用助磨剂在溶剂中溶解，在搅拌下得到充分的混匀，低浓度的助磨剂体积更大，更多更好的附着在粉体的新生表面上，保持了颗粒的分散，阻止了颗粒之间的聚结和团聚，从而提高设备的工作台时。
本发明的有益效果为：(1)助磨剂加入量和溶剂加入量能准确控制；(2)对助磨剂进行了一定比例的稀释；(3)该加入方式能够更好的促进助磨剂与熟料的混合状态，提高台时。
具体实施方式
以下通过实施例形式的具体实施方式，对本发明的上述内容再作进一步的详细说明，说明但不限制本发明。
实施例1
A、按常规方法配制三乙醇胺助磨剂母液；
B、将助磨剂母液三乙醇胺与水按不同按体积比进行稀释，得稀释液；
C、稀释液加入到实验室小磨系统中，所用水泥为峨胜水泥厂P.O32.5水泥，熟料(95％)、石膏(5％)。
检测粉磨后水泥的性能指标结果见表1。
表1粉磨后水泥的性能指标(助磨剂母液三乙醇胺:水)
实施例2
A、按常规方法配制聚羧酸助磨剂母液；
B、将聚羧酸助磨剂母液与水按不同按体积(1:10～1:100)比进行稀释，得稀释液；
C、稀释液加入到实验室小磨系统中，所用水泥为峨胜水泥厂P.O32.5水泥，熟料(95％)、石膏(5％)。
检测粉磨后水泥的性能指标结果见表2。
表2粉磨后水泥的性能指标(助磨剂母液聚羧酸:水)
由上述实例可见，采用本发明技术后，助磨剂母液与溶剂在搅拌后得到低浓度的助磨剂，分散的助磨剂分子更易于附着到粉体的新生表面上，保持了颗粒的分散，阻止了颗粒之间的聚结和团聚。稀释后加入的助磨剂粉磨得到的水泥的筛余降低，比表面积增加，3天强度和28天强度均比以母液方式加入得到的水泥的强度要高。
综上，本发明技术简单易行，现场工艺流程改造方便，可行性强，应用前景广。

Claims (8)

1.助磨剂加料方法，其特征在于步骤如下：
A、配制助磨剂母液；
B、助磨剂母液与溶剂按下述体积比混合得混合液：助磨剂母液1份:溶剂0.1～100份；
C、再将混合液加入水泥球磨机中。
2.根据权利要求1所述的助磨剂加料方法，其特征在于：所述助磨剂为三乙醇胺，三异丙醇胺、聚羧酸、多羟基二乙烯三胺。
3.根据权利要求1所述的助磨剂加料方法，其特征在于：所述溶剂为水、甲醇、乙醇或四氢呋喃。
4.根据权利要求3所述的助磨剂加料方法，其特征在于：所述溶剂为水或乙醇。
5.根据权利要求4所述的助磨剂加料方法，其特征在于：所述溶剂为水。
6.根据权利要求2-5任一项所述的助磨剂加料方法，其特征在于：所述助磨剂为三乙醇胺或三异丙醇胺，助磨剂母液与溶剂按下述体积比混合得混合液：助磨剂母液1份:溶剂0.1～10份。
7.根据权利要求2-5任一项所述的助磨剂加料方法，其特征在于：所述助磨剂为多羟基二乙烯三胺，助磨剂母液与溶剂按下述体积比混合得混合液：助磨剂母液1份:溶剂0.1～10份。
8.根据权利要求2-5任一项所述的助磨剂加料方法，其特征在于：所述助磨剂为聚羧酸，助磨剂母液与溶剂按下述体积比混合得混合液：助磨剂母液1份:溶剂10～100份。
CN201510220336.3A 2015-05-04 2015-05-04 一种助磨剂加料方法 Pending CN104829148A (zh)