CN104804672A - 一种核电站电缆附件用热熔胶 - Google Patents
一种核电站电缆附件用热熔胶 Download PDFInfo
- Publication number
- CN104804672A CN104804672A CN201510191654.1A CN201510191654A CN104804672A CN 104804672 A CN104804672 A CN 104804672A CN 201510191654 A CN201510191654 A CN 201510191654A CN 104804672 A CN104804672 A CN 104804672A
- Authority
- CN
- China
- Prior art keywords
- melt adhesive
- hot melt
- nuclear power
- parts
- cables
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种核电站电缆附件用热熔胶，按重量计，含有：聚烯烃共聚物热熔胶和/或聚酰胺热熔胶100份；马来酸酐接枝改性聚合物0-20份；聚丙烯酸酯橡胶和/或乙烯-丙烯酸酯橡胶0-20份；含苯环的树脂或含苯环的弹性体0.5-50份；阻燃剂0-200份；抗氧剂0.5-10份；抗辐射剂0.1-8份。本发明核电站电缆附件用热熔胶能够耐受高温热老化和高剂量辐照，满足第三代核电需求。
Description
技术领域
本发明涉及一种热熔胶，尤其涉及一种核电站特别是核电站核岛内的电缆附件用热熔胶，满足核电站电缆附件90℃60年老化寿命需要。
背景技术
热熔胶是一种单组分的、无水、无溶剂、常温下为固体、高温熔融后对材料表面进行粘接的胶黏剂。由于具有粘接强度大、固化速度快等优点，热熔胶自从问世以来就被广泛应用于食品包装、书本装订、一次性卫生用品行业、家具行业、电缆附件等诸多领域。
在一些特殊使用场合如核电站用热缩电力电缆附件产品，对于热熔胶有较高要求。核电站用热缩电力电缆附件产品使用的热熔胶不仅要通过基本的性能测试，还需要通过核电站用电缆附件的型式实验。热熔胶需要耐受高温热老化和高剂量辐照，在经过高温热老化和高剂量辐照处理以后还需要能承受高温高压水蒸汽以及碱性溶液对材料的破坏。
第三代核电站电缆附件还要求带热熔胶的电缆附件必须通过90℃60年老化寿命测试。一般的EVA热熔胶由于抗氧剂用量比较少，没有添加抗辐照剂，耐热性和耐辐照性都不好，长时间耐热、大辐射剂量辐照下会变脆，失去热熔胶的密封性能，而耐热性好的聚酰胺和聚酯类热熔胶直接使用不能耐受高剂量辐照、高温高压水蒸汽以及碱性溶液对材料的破坏。提高热熔胶的软化点，使热熔胶部分交联虽能提高热熔胶的耐温性能，但是又带来了热熔胶的流动性明显变差，失去热熔胶在高温下的流淌密封性能。
因此，为了满足第三代核电技术的需要，在技术上迫切需要对现有的热熔胶进行改性，制备出软化点基本不变、流动性能基本不变的热熔胶，该热熔胶需要能够耐受高温热老化和高剂量辐照，满足第三代核电需求，保证核电站电缆附件产品长时间安全地运行。
目前，进口的电缆附件也仅仅能够满足90℃40年老化寿命要求，满足不了核电站对电缆附件通过90℃60年老化寿命测试的要求。
发明内容
本发明的目的在于克服现有的热熔胶不耐长时间高温热老化、不耐高剂量辐照、不能承受高温高压水蒸汽和碱性溶液对材料的破坏的缺陷，提供一种能够耐受高温热老化和高剂量辐照，在经过高温热老化和高剂量辐照处理以后还能承受高温高压水蒸汽以及碱性溶液对材料的破坏，满足第三代核电需求的热熔胶。
为实现上述目的，本发明所提供核电站电缆附件用热熔胶，按重量计，含有：
聚烯烃共聚物热熔胶和/或聚酰胺热熔胶100份；
马来酸酐接枝改性聚合物0-20份；
聚丙烯酸酯橡胶和/或乙烯-丙烯酸酯橡胶0-20份；
含苯环的树脂或含苯环的弹性体0.5-50份；
阻燃剂0-200份；
抗氧剂0.5-10份；
抗辐射剂0.1-8份。
优选地，所述聚烯烃共聚物热熔胶含有一种或多种增粘树脂。
优选地，所述增粘树脂为萜烯树脂、石油树脂、松香树脂或蜡中的一种或若干种。
优选地，所述聚酰胺热熔胶为二聚酸聚酰胺热熔胶，由二元酸直接与多元胺共聚聚合而成。
优选地，所述马来酸酐接枝改性聚合物为马来酸酐接枝改性乙烯-醋酸乙烯共聚物、马来酸酐接枝改性聚乙烯、马来酸酐接枝改性乙烯-丙烯酸乙酯共聚物、马来酸酐接枝改性乙烯-丁烯共聚物、马来酸酐接枝改性乙烯-辛烯共聚物中的一种或若干种。
优选地，所述含苯环的树脂或弹性体为聚苯乙烯树脂、高苯乙烯橡胶、丁苯橡胶、SBS、SIS、SEBS中的一种或若干种。
优选地，所述抗氧剂是受阻酚类抗氧剂和/或硫醚类辅助抗氧剂和/或受阻胺辅助抗氧剂。
优选地，所述抗辐射剂为多苯环抗辐射剂和/或抗辐射抗紫外剂。
本发明核电站电缆附件用热熔胶具有以下有益效果：
1.本发明核电站电缆附件用热熔胶当中加入耐高温热老化和高剂量辐照性能好的聚丙烯酸酯橡胶和/或乙烯-丙烯酸酯橡胶和/或含苯环的树脂或弹性体，提高热熔胶的耐高温热老化性能和耐高剂量辐照性能。
2.本发明核电站电缆附件用热熔胶当中加入大量的抗氧化剂和抗辐射剂，能进一步提高整个材料耐受长时间高温热老化和高剂量辐照的性能，大大降低了氧化以及γ射线对材料的降解作用。
3.本发明核电站电缆附件用热熔胶软化点在80-160℃，与正常电缆附件使用的热熔胶的软化点接近，可以提高电缆附件的密封性和防水性能。
4.本发明制备的热熔胶能够耐受高温热老化和高剂量辐照，满足第三代核电需求。
具体实施方式
为详细说明本发明的技术内容、配方比例、所实现目的及效果，以下结合实施方式详予说明。
本发明核电站电缆附件用热熔胶，按重量计，含有：
聚烯烃共聚物热熔胶和/或聚酰胺热熔胶100份；
马来酸酐接枝改性聚合物0-20份；
聚丙烯酸酯橡胶和/或乙烯-丙烯酸酯橡胶0-20份；
含苯环的树脂或含苯环的弹性体0.5-50份；
阻燃剂0-200份；
抗氧剂0.5-10份；
抗辐射剂0.1-8份。
优选地，所述聚烯烃共聚物热熔胶含有一种或多种增粘树脂。
优选地，所述增粘树脂为萜烯树脂、石油树脂、松香树脂或蜡中的一种或若干种。
优选地，所述聚酰胺热熔胶为二聚酸聚酰胺热熔胶，由二元酸直接与多元胺共聚聚合而成。
优选地，所述马来酸酐接枝改性聚合物为马来酸酐接枝改性乙烯-醋酸乙烯共聚物、马来酸酐接枝改性聚乙烯、马来酸酐接枝改性乙烯-丙烯酸乙酯共聚物、马来酸酐接枝改性乙烯-丁烯共聚物、马来酸酐接枝改性乙烯-辛烯共聚物中的一种或若干种。
优选地，所述含苯环的树脂或弹性体为聚苯乙烯树脂、高苯乙烯橡胶、丁苯橡胶、SBS、SIS、SEBS中的一种或若干种。
优选地，所述抗氧剂是受阻酚类抗氧剂和/或硫醚类辅助抗氧剂和/或受阻胺辅助抗氧剂。
优选地，所述抗辐射剂为多苯环抗辐射剂和/或抗辐射抗紫外剂。
核电站电缆附件用阻燃热熔胶可以通过在上述热熔胶的基础上增加复合阻燃剂的方法实现。
将以上材料混合均匀，经过捏合机或密炼机或反应釜熔融或双螺杆熔融造粒，即可获得本发明热熔胶。
以下记载了本实施方式的几个具体实施例，除另有说明，所有份数均以重量计：
实施例1
将乙烯共聚物热熔胶（乙烯- 醋酸乙烯共聚物热熔胶）100 份、马来酸酐接枝改性聚合物5份、聚丙烯酸酯橡胶20份、聚苯乙烯树脂2份、抗氧剂1010 3份、抗氧剂CPL 1份，抗氧剂RD 2份，抗辐射剂3份混合均匀，在100-130 ℃下使用双螺杆造粒制成热熔胶颗粒，热熔胶的性能见表1。
本发明热熔胶应用在核电站电缆附件中，满足核电站用电缆附件90℃60年老化寿命需要，用该材料与满足核电站设计要求的反应堆用阻燃绝缘料一起生产的电缆附件在受到严酷条件下的γ射线辐照后，使用该材料制作的电缆附件依然能够保持其电气性能；该材料还能承受高温高压水蒸气以及碱性溶液对材料的破坏。
实施例2
将聚酰胺热熔胶100份、高苯乙烯橡胶15份、抗氧剂1076 3 份、抗氧剂300 3份，抗辐射剂UV-328 2份混合均匀，在100-200度温度下使用捏合机或者密炼机混合约1小时后，将混炼好的热熔胶压成片或切成热熔胶胶粒。热熔胶的性能见表1。
本发明热熔胶应用在核电站电缆附件中，满足核电站用电缆附件90℃60年老化寿命需要和高辐射要求。
实施例3
将聚烯烃共聚物热熔胶80份、聚酰胺热熔胶20份、马来酸酐接枝改性共聚物10份、乙烯-丙烯酸酯橡胶5重量份、高苯乙烯橡胶10份、抗氧剂1076 3 份、抗氧剂苯乙烯化二苯胺4份，MD1024 1份，抗辐射剂UV-531 5份混合均匀，在100-160 ℃下使用密炼机或双螺杆造粒制成热熔胶颗粒，热熔胶的性能见表1。
本发明热熔胶应用在核电站的电缆附件中，满足核电站用电缆附件90℃60年老化寿命需要和高辐射要求。
实施例4
将聚烯烃共聚物热熔胶40份、聚酰胺热熔胶60份、马来酸酐接枝改性共聚物3份、丁苯橡胶5份、抗氧剂CPL 3份、抗氧剂330 1份，抗辐射剂UV329 5份混合均匀，在100-160 ℃下使用密炼机或双螺杆造粒制成热熔胶颗粒，热熔胶的性能见表1。
本发明热熔胶应用在核电站电缆附件中，满足核电站用电缆附件90℃60年老化寿命需要和高辐射要求。
实施例5
将聚烯烃共聚物热熔胶70份、聚酰胺热熔胶30份、马来酸酐接枝改性共聚物10份、SBS 5份、抗氧剂1010 3份、抗氧剂168 2份，抗氧剂DLTP 2份，抗氧剂RD 2份，抗氧剂MD1024 1份，抗辐射剂744 8份、复合阻燃剂60份混合均匀，在100-160 ℃下使用双螺杆造粒制成热熔胶颗粒，热熔胶的性能见表1。
本发明热熔胶应用在核电站的电缆附件中，满足核电站电缆附件90℃60年老化寿命需要和高辐射要求。
表1 热熔胶（25℃）主要性能
| 项目 | 实施例1 | 实施例2 | 实施例3 | 实施例4 | 实施例5 |
| 软化点 | 100℃ | 140℃ | 120℃ | 130℃ | 130℃ |
| 剥离强度（电缆附件） | 200N/25mm | 120 N /25mm | 180 N /25mm | 160 N /25mm | 140 N /25mm |
| 剥离强度（电缆附件） | 180 N /25mm | 130 N /25mm | 160 N /25mm | 140 N /25mm | 130 N /25mm |
| 90℃60年老化寿命要求 | 满足 | 满足 | 满足 | 满足 | 满足 |
| 第三代核电站严酷条件下高辐射要求 | 满足 | 满足 | 满足 | 满足 | 满足 |
对比例1
本对比例1与实施例1的区别在于：将实施例1中的聚丙烯酸酯橡胶20份删除，其余原材料不变，制备方法不变。
测试结果表明，对比例1电缆附件的热熔胶内层不能满足核电站用电缆附件90℃60年老化寿命需要和高辐射要求。
根据表1以及对比例1相关性能测试结果可知，具有含苯环的树脂或含苯环的弹性体的热熔胶能够满足满足核电站用电缆附件90℃60年老化寿命需要和高辐射要求。
本发明并不局限于上述具体实施方式，熟悉本技术领域的人员还可据此做出多种变化，但任何与本发明等同或相类似的变化都应涵盖在本发明权利要求的范围内。
Claims (8)
1.一种核电站电缆附件用热熔胶，其特征在于，按重量计，含有：
聚烯烃共聚物热熔胶和/或聚酰胺热熔胶100份；
马来酸酐接枝改性聚合物0-20份；
聚丙烯酸酯橡胶和/或乙烯-丙烯酸酯橡胶0-20份；
含苯环的树脂或含苯环的弹性体0.5-50份；
阻燃剂0-200份；
抗氧剂0.5-10份；
抗辐射剂0.1-8份。
2.如权利要求1所述的核电站电缆附件用热熔胶，其特征在于：所述聚烯烃共聚物热熔胶含有一种或多种增粘树脂。
3.如权利要求2所述的核电站电缆附件用热熔胶，其特征在于：所述增粘树脂为萜烯树脂、石油树脂、松香树脂或蜡中的一种或若干种。
4.如权利要求1所述的核电站电缆附件用热熔胶，其特征在于：所述聚酰胺热熔胶为二聚酸聚酰胺热熔胶，由二元酸直接与多元胺共聚聚合而成。
5.如权利要求4所述的核电站电缆附件用热熔胶，其特征在于：所述马来酸酐接枝改性聚合物为马来酸酐接枝改性乙烯-醋酸乙烯共聚物、马来酸酐接枝改性聚乙烯、马来酸酐接枝改性乙烯-丙烯酸乙酯共聚物、马来酸酐接枝改性乙烯-丁烯共聚物、马来酸酐接枝改性乙烯-辛烯共聚物中的一种或若干种。
6.如权利要求5所述的核电站电缆附件用热熔胶的制备方法，其特征在于：所述含苯环的树脂或弹性体为聚苯乙烯树脂、高苯乙烯橡胶、丁苯橡胶、SBS、SIS、SEBS中的一种或若干种。
7.如权利要求1所述的核电站电缆附件用热熔胶，其特征在于：所述抗氧剂是受阻酚类抗氧剂和/或硫醚类辅助抗氧剂和/或受阻胺辅助抗氧剂。
8.如权利要求1所述的核电站电缆附件用热熔胶，其特征在于：所述抗辐射剂为多苯环抗辐射剂和/或抗辐射抗紫外剂。