CN103351809A - 一种防锈蚀led灯散热涂料及其制备方法 - Google Patents

一种防锈蚀led灯散热涂料及其制备方法 Download PDF

Info

Publication number
CN103351809A
CN103351809A CN2013102434142A CN201310243414A CN103351809A CN 103351809 A CN103351809 A CN 103351809A CN 2013102434142 A CN2013102434142 A CN 2013102434142A CN 201310243414 A CN201310243414 A CN 201310243414A CN 103351809 A CN103351809 A CN 103351809A
Authority
CN
China
Prior art keywords
parts
minute
coating
stirring reaction
propylene glycol
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013102434142A
Other languages
English (en)
Other versions
CN103351809B (zh
Inventor
茆文斌
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JINLING ELECTRONIC CO Ltd
Original Assignee
JINLING ELECTRONIC CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JINLING ELECTRONIC CO Ltd filed Critical JINLING ELECTRONIC CO Ltd
Priority to CN201310243414.2A priority Critical patent/CN103351809B/zh
Publication of CN103351809A publication Critical patent/CN103351809A/zh
Application granted granted Critical
Publication of CN103351809B publication Critical patent/CN103351809B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种防锈蚀LED灯散热涂料及其制备方法，其特征在于由下列重量份的原料制成：有机硅树脂45-48、聚酰胺多胺环氧氯丙烷树脂24-26、氮化铝32-34、二甲苯50-56、醋酸丁酯25-28、乌洛托品2-3、苯基三乙氧基硅烷3-5、苯胺甲基三乙氧基硅烷2-3、炭黑N339 10-20、N660炭黑5-15、异氰脲酸三缩水甘油酯1-2、癸二酸丙二醇聚酯5-8、邻苯二甲酸聚酯3-5、异戊二烯2-3、丙烯酸-2-羟基丙酯4-6、丙二醇3-4、叔丁基过氧化氢1-2、间氨基甲胺1-2、乙二胺1-2、成膜剂3-4。本发明原料中增加乌洛托品成分，增加了涂料的防锈蚀性能，使得本发明涂料可以用于各种污染的环境，增加其耐高温、耐盐雾的能力。

Description

一种防锈蚀LED灯散热涂料及其制备方法
技术领域
本发明属于涂料技术领域，涉及一种散热涂料，更具体地说，是一种防锈蚀LED灯散热涂料及其制备方法。
背景技术
随着LED 灯使用范围的迅速扩大，延长LED 灯使用寿命也已成为急需解决的问题。目前一般的LED灯并没有采用特别的散热措施，采用灯壳自然散热，这种方式使得LED灯使用一段时间后，出现灯壳老化，由于灯壳长时间高温，使得LED使用寿命下降；不能满足LED灯发展现状与要求。
发明内容
本发明的目的是提供一种防锈蚀LED灯散热涂料及其制备方法，本发明涂料具有粘结力大，耐老化、散热系数大的优点。
本发明所采用的技术方案是：
一种防锈蚀LED灯散热涂料，其特征在于由下列重量份的原料制成：
有机硅树脂45-48、聚酰胺多胺环氧氯丙烷树脂24-26、氮化铝32-34、二甲苯50-56、醋酸丁酯25-28、乌洛托品2-3、苯基三乙氧基硅烷3-5、苯胺甲基三乙氧基硅烷2-3、炭黑N339 10-20、N660炭黑5-15、异氰脲酸三缩水甘油酯1-2、癸二酸丙二醇聚酯5-8、邻苯二甲酸聚酯3-5、异戊二烯2-3、丙烯酸-2- 羟基丙酯4-6、丙二醇3-4、叔丁基过氧化氢1-2、间氨基甲胺1-2、乙二胺1-2、成膜剂3-4。
所述的成膜剂由以下重量份的原料制得：
原料组成硼化钒2-4、交联剂 TAC2-3、双十四碳醇酯4-5、过氧化环己酮1-2、苯乙烯3-4、丙烯腈1-2、二甲苯8-10、丙二醇12-13；
制备方法是：将交联剂TAC、双十四碳醇酯混合，加入到二甲苯中，搅拌10-20分钟，加入过氧化环己酮，搅拌反应30-40分钟后，加入苯乙烯，搅拌反应45-60分钟，再加入丙烯腈与硼化钒、丙二醇，搅拌反应2-3小时，即得。
所述的防锈蚀LED灯散热涂料的制备方法，其特征在于包括以下步骤：
将异氰脲酸三缩水甘油酯、癸二酸丙二醇聚酯、邻苯二甲酸聚酯、丙烯酸-2- 羟基丙酯加入到二甲苯与醋酸丁酯混合溶剂中，加热至100-105℃，搅拌20-30分钟，然后，加入苯基三乙氧基硅烷、异氰脲酸三缩水甘油酯，搅拌反应30-40分钟，再加入叔丁基过氧化氢、丙二醇、异戊二烯，反应50-60分钟，再加入其它剩余成分，搅拌反应2-3小时，研磨除渣即得。
本发明施工时，散热涂料喷涂施工，在180-200 ℃下高温烘干30-50分钟，即可成膜，得到散热涂层。
本发明原料中增加乌洛托品成分，增加了涂料的防锈蚀性能，使得本发明涂料可以用于各种污染的环境，增加其耐高温、耐盐雾的能力。
发明具有耐老化，粘结力大，散热效果好，可以在200℃下长期使用，而力学性能不变的优点。
具体实施方式
一种防锈蚀LED灯散热涂料，由下列重量份（公斤）的原料制成：
有机硅树脂45、聚酰胺多胺环氧氯丙烷树脂26、氮化铝34、二甲苯50、醋酸丁酯25、乌洛托品3、苯基三乙氧基硅烷5、苯胺甲基三乙氧基硅烷2、炭黑N339 20、N660炭黑15、异氰脲酸三缩水甘油酯2、癸二酸丙二醇聚酯8、邻苯二甲酸聚酯3、异戊二烯3、丙烯酸-2- 羟基丙酯4、丙二醇4、叔丁基过氧化氢2、间氨基甲胺1、乙二胺2、成膜剂4。
所述的成膜剂由以下重量份（公斤）的原料制得：
原料组成硼化钒4、交联剂 TAC2、双十四碳醇酯5、过氧化环己酮1、苯乙烯4、丙烯腈2、二甲苯10、丙二醇13；制备方法是：将交联剂TAC、双十四碳醇酯混合，加入到二甲苯中，搅拌10-20分钟，加入过氧化环己酮，搅拌反应30-40分钟后，加入苯乙烯，搅拌反应45-60分钟，再加入丙烯腈与硼化钒、丙二醇，搅拌反应2-3小时，即得。
防锈蚀LED灯散热涂料的制备方法，包括以下步骤：
将异氰脲酸三缩水甘油酯、癸二酸丙二醇聚酯、邻苯二甲酸聚酯、丙烯酸-2- 羟基丙酯加入到二甲苯与醋酸丁酯混合溶剂中，加热至100-105℃，搅拌20-30分钟，然后，加入苯基三乙氧基硅烷、异氰脲酸三缩水甘油酯，搅拌反应30-40分钟，再加入叔丁基过氧化氢、丙二醇、异戊二烯，反应50-60分钟，再加入其它剩余成分，搅拌反应2-3小时，研磨除渣即得。
将本发明涂料涂于LED灯壳体上，在80℃和300W 紫外光辐照条件下人工加速老化试验，耐老化时间5300 小时，耐温高温250℃，粘结剪切力23MPa.，导热系数280W/（m·K）。

Claims (2)

1.一种防锈蚀LED灯散热涂料，其特征在于由下列重量份的原料制成：
有机硅树脂45-48、聚酰胺多胺环氧氯丙烷树脂24-26、氮化铝32-34、二甲苯50-56、醋酸丁酯25-28、乌洛托品2-3、苯基三乙氧基硅烷3-5、苯胺甲基三乙氧基硅烷2-3、炭黑N339 10-20、N660炭黑5-15、异氰脲酸三缩水甘油酯1-2、癸二酸丙二醇聚酯5-8、邻苯二甲酸聚酯3-5、异戊二烯2-3、丙烯酸-2- 羟基丙酯4-6、丙二醇3-4、叔丁基过氧化氢1-2、间氨基甲胺1-2、乙二胺1-2、成膜剂3-4；
所述的成膜剂由以下重量份的原料制得：
原料组成硼化钒2-4、交联剂 TAC2-3、双十四碳醇酯4-5、过氧化环己酮1-2、苯乙烯3-4、丙烯腈1-2、二甲苯8-10、丙二醇12-13；
制备方法是：将交联剂TAC、双十四碳醇酯混合，加入到二甲苯中，搅拌10-20分钟，加入过氧化环己酮，搅拌反应30-40分钟后，加入苯乙烯，搅拌反应45-60分钟，再加入丙烯腈与硼化钒、丙二醇，搅拌反应2-3小时，即得。
2.根据权利要求1所述的防锈蚀LED灯散热涂料的制备方法，其特征在于包括以下步骤：
将异氰脲酸三缩水甘油酯、癸二酸丙二醇聚酯、邻苯二甲酸聚酯、丙烯酸-2- 羟基丙酯加入到二甲苯与醋酸丁酯混合溶剂中，加热至100-105℃，搅拌20-30分钟，然后，加入苯基三乙氧基硅烷、异氰脲酸三缩水甘油酯，搅拌反应30-40分钟，再加入叔丁基过氧化氢、丙二醇、异戊二烯，反应50-60分钟，再加入其它剩余成分，搅拌反应2-3小时，研磨除渣即得。
CN201310243414.2A 2013-06-19 2013-06-19 一种防锈蚀led灯散热涂料及其制备方法 Active CN103351809B (zh)