CN104789109A - Environment-friendly and water-borne finish paint for woodenware and preparation method of environment-friendly and water-borne finish paint - Google Patents
Environment-friendly and water-borne finish paint for woodenware and preparation method of environment-friendly and water-borne finish paint Download PDFInfo
- Publication number
- CN104789109A CN104789109A CN201510238350.6A CN201510238350A CN104789109A CN 104789109 A CN104789109 A CN 104789109A CN 201510238350 A CN201510238350 A CN 201510238350A CN 104789109 A CN104789109 A CN 104789109A
- Authority
- CN
- China
- Prior art keywords
- water
- agent
- environment
- parts
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses environment-friendly and water-borne finish paint for woodenware, relating to the technical field of water-borne paint. The environment-friendly and water-borne finish paint is prepared from the following components in parts by weight: 78.5-83.5 parts of acrylic acid modified polyurethane, 3.5-6.5 parts of a film forming additive, 0.3-0.6 part of a wetting agent, 0.1-0.4 part of a water-borne defoaming agent, 0.3-1 part of a water-borne slipping agent, 0.5-0.75 part of a flatting agent, 0.2-1.5 parts of an antibacterial preservative, 5-8 parts of insect and worm preventing powder, 0.2-0.6 part of a PH regulator and 10-15 parts of water, wherein the insect and worm preventing powder is a mixture composed of 2-3.5 parts of cortex meliae powder and 3-4.5 parts of celastrus angulatus powder. The environment-friendly and water-borne finish paint has the beneficial effects that the environment-friendly and water-borne finish paint for woodenware, prepared by using a method according to a special formula, is favorable in insect and worm preventing effect, strong in scratch resistance, high in wear resistance and hardness and capable of greatly prolonging the service life of a product; and meanwhile, other performances can also conform to the national relevant standards.
Description
Technical field
The present invention relates to water-miscible paint technical field, particularly environment-friendly water-based lacquer as woodenware finish of one and preparation method thereof.
Background technology
Along with the development of society and the enhancing of people's environmental consciousness, the environmental regulation that various countries formulate all has strict restriction to volatile organic compounds in coating (VOC), as standard GB/T 1851-2009 " in upholstery material, solvent wood coatings limits of harmful substances ", GB24410-2009 " in indoor decorating and refurnishing materials, water-borne wood coating limits of harmful substances ", the limitation of VOC in indoor paint is proposed and explicitly calls for.
Wood lacquer can give timber, rattan articles color, gloss, and it can also be helped to resist destruction because humidity, chemical corrosion etc. cause, but the mothproof effect of current wood lacquer insect protected is poor, not wear-resisting, and scratch resistance capability is strong, and hardness is not high.
Summary of the invention
In view of this, an object of the present invention is to provide a kind of environment-friendly water-based lacquer as woodenware finish, has insect protected, scratch resistance, the advantage that wear-resisting, hardness is high.
The present invention is solved the problems of the technologies described above by following technique means:
The invention provides a kind of environment-friendly water-based lacquer as woodenware finish, composed of the following components by weight: acrylic acid modified polyurethane 78.5-83.5 part, film coalescence aid 3.5-6.5 part, wetting agent 0.3-0.6 part, water-based defoamer 0.1-0.4 part, water-based slip(ping)agent 0.3-1 part, flow agent 0.5-0.75 part, fungicidal preservative 0.2-1.5 part, Anti-moth-eating powder 5-8 part, PH conditioning agent 0.2-0.6 part, water 10-15 part, described Anti-moth-eating powder is the mixture of 2-3.5 part Cortex Meliae powder and 3-4.5 part Celastrus angulatus pulvis.
A kind of new type resin of vinylformic acid and polyurethane polyureas being combined by polymerizations such as core-shell structure copolymer of aforesaid propylene acid modified polyurethane, it not only has the weathering resistance chemical resistant properties of acrylic resin and inherits the performances such as the high adhesive force wear resistance of urethane resin and high rigidity to the wettability of pigment.
Wetting agent adopts non-ionic wetting agent, mainly containing simple function group, oleoyl alkylene oxide block multipolymer, to color stuffing dissemination, and improves color developing.
Water-based defoamer is the one in non-ionic type defoamer, molecular antifoaming agent, has good consistency and can principal characteristic.
Flow agent adopts and can impel coating in drying and forming-film process, form smooth, smooth, a uniform film.Can effectively reduce
cover with paint, lacquer, colour wash, etc.liquid
surface tension, improve it
levelling propertywith a class material of homogeneity, can improve and cover with paint, lacquer, colour wash, etc. liquid
perviousness, the possibility producing spot and spot when brushing can be reduced, increase spreadability, make film forming even, natural.
Anti-moth-eating powder is the mixture of Cortex Meliae powder and Celastrus angulatus pulvis, and Cortex Meliae powder dries grinds, bitter by the bark of China tree and root skin; Cold in nature; Poisonous; There is effect of desinsection and treatment tinea.The compound that the active insecticidal components of Celastrus angulatus is separated from celastrus angulatus, Celastrus angulatus has the active insecticidal components having anesthesia, food refusal and stomach poison function.Celastrus angulatus pulvis is made up of Celastrus angulatus, and the mixture of Cortex Meliae powder and Celastrus angulatus pulvis is vegetable insecticide, and environmental protection is harmless.
Further, composed of the following components by weight: acrylic acid modified polyurethane 79-82 part, film coalescence aid 4-5.5 part, wetting agent 0.45-0.5 part, water-based defoamer 0.2-0.35 part, water-based slip(ping)agent 0.5-0.7 part, flow agent 0.55-0.65 part, fungicidal preservative 0.4-1.3 part, Anti-moth-eating powder 6-7 part, PH conditioning agent 0.3-0.5 part, water 12-14 part, described Anti-moth-eating powder is the mixture of 2-3 part Cortex Meliae powder and 3.5-4 part Celastrus angulatus pulvis.
Further, composed of the following components by weight: acrylic acid modified polyurethane 81 parts, film coalescence aid 4 parts, wetting agent 0.5 part, water-based defoamer 0.3 part, water-based slip(ping)agent 0.7 part, flow agent 0.6 part, fungicidal preservative 1.1 parts, 7 parts, Anti-moth-eating powder, PH conditioning agent 0.4 part, 13 parts, water, described Anti-moth-eating powder is the mixture of 3 parts of Cortex Meliae powder and 4 parts of Celastrus angulatus pulvis.
Further, described film coalescence aid is Lauryl Alcohol ester, contributes to film forming matter film forming at low temperatures.
Further, described fungicidal preservative adopts not containing the isothiazolinone disinfecting agent of VOC, has thermotolerance, plays sterilization and anticorrosion effect simultaneously.
Further, described flow agent is polyether polyester modified organic silicon oxygen alkane flow agent, be greatly improved by the consistency of polyethers, polyester modification siloxanes and resin, reduce surface tension, the effect of the ability that control surface flows, the slip that increases, nonshrink hole, antiblocking is also all fine.
The preparation method of a kind of environment-friendly water-based lacquer as woodenware finish of the present invention, specifically comprises the following steps:
A. the formula feeding by described is for subsequent use;
B. wetting agent and water are added mixing machine, with the speed blending dispersion 7 minutes of 800 revs/min;
C. in described dispersion liquid, water-based defoamer is added, with the speed blending dispersion 4 minutes of 600 revs/min;
D. keep rotating speed constant, in described dispersion liquid, add acrylic acid modified polyurethane successively, film coalescence aid, water-based slip(ping)agent, modified polyorganosiloxane flow agent, fungicidal preservative and Anti-moth-eating powder;
E. in described dispersion liquid, add pH adjusting agent, regulate the potential of hydrogen scope of described dispersion liquid to be 8 ~ 9, with the speed blending dispersion 15 minutes of 600 revs/min.
Beneficial effect of the present invention: adopt the environment-friendly water-based lacquer as woodenware finish that special formulation of the present invention and method obtain, there is good anti-moth and insect prevention result, scratch resistance capability is strong, wear-resisting, hardness is high, substantially increase the work-ing life of product, meanwhile, other performances also meet relevant national standard.
Embodiment
Embodiment 1
Environment-friendly water-based lacquer as woodenware finish, composed of the following components by weight: acrylic acid modified polyurethane adopts the product of Weng Kaier company limited, and model is H-40, weight is 78.5Kg, film coalescence aid 3.5Kg, wetting agent 0.3Kg, water-based defoamer 0.4Kg, water-based slip(ping)agent 1Kg, polyether polyester modified organic silicon oxygen alkane flow agent 0.5Kg, isothiazolinone disinfecting agent 0.5Kg, Anti-moth-eating powder 5Kg, PH conditioning agent 0.3Kg, water 11Kg, Anti-moth-eating powder is the mixture of 2Kg Cortex Meliae powder and 3Kg Celastrus angulatus pulvis.Cortex Meliae powder dries grinds, bitter by the bark of China tree and root skin; Cold in nature; Poisonous; There is effect of desinsection and treatment tinea.The compound that the active insecticidal components of Celastrus angulatus is separated from celastrus angulatus, has and has anesthesia, food refusal and stomach poison function.Celastrus angulatus pulvis is made up of Celastrus angulatus, and the mixture of Cortex Meliae powder and Celastrus angulatus pulvis is vegetable insecticide, and environmental protection is harmless, adds Cortex Meliae powder and Celastrus angulatus pulvis makes it have good anti-moth and insect prevention result in environment-friendly water-based lacquer as woodenware finish.The acrylic acid modified polyurethane adopted, its feature, except the feature acting on acrylic paint, turn increases wear-resisting and that chemical resistance is strong feature, makes hardness of paint film better, and the examination of pencil rule is 1H, and fullness ratio is better.Film coalescence aid is Lauryl Alcohol ester, also with the one in dipropylene and dipropylene glycol methyl ether or two kinds of mixing arbitrarily, can contribute to film forming matter film forming at low temperatures.
The preparation method of environment-friendly water-based lacquer as woodenware finish, adds mixing machine by wetting agent and water, with the speed blending dispersion 7 minutes of 800 revs/min; Water-based defoamer is added again, with the speed blending dispersion 4 minutes of 600 revs/min in above-mentioned dispersion liquid; Keep rotating speed constant, in described dispersion liquid, add acrylic acid modified polyurethane successively, Lauryl Alcohol ester, water-based slip(ping)agent, polyether polyester modified organic silicon oxygen alkane flow agent, isothiazolinone disinfecting agent, Cortex Meliae powder and Celastrus angulatus pulvis; Finally in above-mentioned dispersion liquid, add pH adjusting agent, the potential of hydrogen scope regulating dispersion liquid is 8 ~ 9, within 15 minutes, namely can be made into product with the speed blending dispersion of 600 revs/min.
Embodiment 2
Environment-friendly water-based lacquer as woodenware finish, composed of the following components by weight, acrylic acid modified polyurethane 83.5Kg, film coalescence aid 6.5Kg, wetting agent 0.45Kg, water-based defoamer 0.3Kg, water-based slip(ping)agent 0.7Kg, polyether polyester modified organic silicon oxygen alkane flow agent 0.6Kg, isothiazolinone disinfecting agent 1.1Kg, pH adjusting agent 0.4Kg, water 13Kg, Anti-moth-eating powder is the mixture of 3Kg Cortex Meliae powder and 4Kg Celastrus angulatus pulvis.
The preparation method of above-mentioned environment-friendly water-based lacquer as woodenware finish is with embodiment 1.
Embodiment 3
Environment-friendly water-based lacquer as woodenware finish, composed of the following components by weight, acrylic acid modified polyurethane 81Kg, film coalescence aid 4Kg, wetting agent 0.5Kg, water-based defoamer 0.1Kg, water-based slip(ping)agent 0.6Kg, polyether polyester modified organic silicon oxygen alkane flow agent 0.75Kg, isothiazolinone disinfecting agent 0.8Kg, pH adjusting agent 0.35Kg, water 12Kg, Anti-moth-eating powder is the mixture of 2.5Kg Cortex Meliae powder and 4.5Kg Celastrus angulatus pulvis.
The preparation method of above-mentioned environment-friendly water-based lacquer as woodenware finish is with embodiment 1.
In above-mentioned three examples, acrylic acid modified polyurethane adopts the product of Weng Kaier company limited, model is H-40, water-based defoamer adopts Dongguan City Gauss to enter the product of Fine Chemical Co., Ltd, product type is GSK-713 defoamer, pH adjusting agent adopts the product of the credible Chemical Co., Ltd. of Yixing City, and product type is the pH adjusting agent of KX-pH.
By carrying out Performance Detection to the environment-friendly water-based lacquer as woodenware finish of above-described embodiment gained, property indices sees the following form:
| Performance index | Embodiment 1 | Embodiment 2 | Embodiment 3 | Common ring water-retentivity lacquer as woodenware finish |
| Insect protected is mothproof | Very good | Very good | Very good | Nothing |
| Scratch resistance | Very good | Good | Good | Better |
| Wear-resisting | Very good | Very good | Very good | Better |
| Hardness | 3H | 3H | 3H | H |
As can be seen from the above table, environment-friendly water-based lacquer as woodenware finish of the present invention has extraordinary anti-moth and insect prevention result relative to common environment-friendly water-based lacquer as woodenware finish, and scratch resistance capability is strong, and abrasion resistant effect is good, hardness is 3H, and other indexs meet the standard of GB1851-2009 and GB24410-2009.
What finally illustrate is, above embodiment is only in order to illustrate technical scheme of the present invention and unrestricted, although with reference to preferred embodiment to invention has been detailed description, those of ordinary skill in the art is to be understood that, can modify to technical scheme of the present invention or equivalent replacement, and not departing from aim and the scope of technical solution of the present invention, it all should be encompassed in the middle of right of the present invention.
Claims (7)
1. an environment-friendly water-based lacquer as woodenware finish, it is characterized in that: composed of the following components by weight: acrylic acid modified polyurethane 78.5-83.5 part, film coalescence aid 3.5-6.5 part, wetting agent 0.3-0.6 part, water-based defoamer 0.1-0.4 part, water-based slip(ping)agent 0.3-1 part, flow agent 0.5-0.75 part, fungicidal preservative 0.2-1.5 part, Anti-moth-eating powder 5-8 part, PH conditioning agent 0.2-0.6 part, water 10-15 part, described Anti-moth-eating powder is the mixture of 2-3.5 part Cortex Meliae powder and 3-4.5 part Celastrus angulatus pulvis.
2. environment-friendly water-based lacquer as woodenware finish as claimed in claim 1, it is characterized in that: composed of the following components by weight: acrylic acid modified polyurethane 79-82 part, film coalescence aid 4-5.5 part, wetting agent 0.45-0.5 part, water-based defoamer 0.2-0.35 part, water-based slip(ping)agent 0.5-0.7 part, flow agent 0.55-0.65 part, scratching resistant 0.6-0.8 part, fungicidal preservative 0.4-1.3 part, Anti-moth-eating powder 6-7 part, PH conditioning agent 0.3-0.5 part, water 12-14 part, described Anti-moth-eating powder is the mixture of 2-3 part Cortex Meliae powder and 3.5-4 part Celastrus angulatus pulvis.
3. environment-friendly water-based lacquer as woodenware finish as claimed in claim 1, it is characterized in that: composed of the following components by weight: acrylic acid modified polyurethane 81 parts, film coalescence aid 4 parts, wetting agent 0.5 part, water-based defoamer 0.3 part, water-based slip(ping)agent 0.7 part, flow agent 0.6 part, fungicidal preservative 1.1 parts, 7 parts, Anti-moth-eating powder, PH conditioning agent 0.4 part, 13 parts, water, described Anti-moth-eating powder is the mixture of 3 parts of Cortex Meliae powder and 4 parts of Celastrus angulatus pulvis.
4. environment-friendly water-based lacquer as woodenware finish as described in one of claim 1-3, is characterized in that: described film coalescence aid is Lauryl Alcohol ester.
5. environment-friendly water-based lacquer as woodenware finish as described in one of claim 1-3, is characterized in that: described fungicidal preservative adopts not containing the isothiazolinone disinfecting agent of VOC.
6. environment-friendly water-based lacquer as woodenware finish as described in one of claim 1-3, is characterized in that: described flow agent is polyether polyester modified organic silicon oxygen alkane flow agent.
7. a preparation method for environment-friendly water-based lacquer as woodenware finish, is characterized in that: comprise the following steps successively:
A. the formula feeding by described is for subsequent use;
B. wetting agent and water are added mixing machine, with the speed blending dispersion 7 minutes of 800 revs/min;
C. in described dispersion liquid, water-based defoamer is added, with the speed blending dispersion 4 minutes of 600 revs/min;
D. keep rotating speed constant, in described dispersion liquid, add acrylic acid modified polyurethane successively, film coalescence aid, water-based slip(ping)agent, polyether polyester modified organic silicon oxygen alkane flow agent, isothiazolinone disinfecting agent and Anti-moth-eating powder;
E. in described dispersion liquid, add pH adjusting agent, regulate the potential of hydrogen scope of described dispersion liquid to be 8 ~ 9, with the speed blending dispersion 15 minutes of 600 revs/min.