CN104773983A - 防渗抗裂抹面砂浆 - Google Patents
防渗抗裂抹面砂浆 Download PDFInfo
- Publication number
- CN104773983A CN104773983A CN201510155092.5A CN201510155092A CN104773983A CN 104773983 A CN104773983 A CN 104773983A CN 201510155092 A CN201510155092 A CN 201510155092A CN 104773983 A CN104773983 A CN 104773983A
- Authority
- CN
- China
- Prior art keywords
- ton
- mortar
- cement
- main part
- plastering mortar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种防渗抗裂抹面砂浆,包括主体材料和添加剂,其中:所述的主体材料由30~40wt%的水泥、45~55wt%的石英砂和余量的粉煤灰组成;所述的添加剂包括羟丙基甲基纤维素、木质纤维、聚乙稀醇、灰钙和可再分散乳胶粉;以主体材料为基准,所述各添加剂的用量分别为:羟丙基甲基纤维素2~3kg/吨、木质纤维3~4kg/吨、聚乙稀醇0.5~1.5kg/吨、灰钙20~30kg/吨、可再分散乳胶粉6~10kg/吨。采用上述原料配比所得的砂浆抗裂性能好,杜绝空鼓;易施工,且施工后墙面平整度好;防渗性能好,大大减低墙体渗水。
Description
技术领域
本发明涉及一种建筑材料,具体涉及一种防渗抗裂抹面砂浆。
背景技术
随着建筑事业的不断发展,对工程的质量要求也越来越高,防渗抗裂是一个十分重要而且迫切需要加以解决的问题。采用防水砂浆是最重要的措施,而掺入外加剂又是提高砂浆抗渗能力的最基础手段。在砂浆中加入一定量的纤维和防水剂,可以达到日趋提高的防渗抗裂的使用要求,也能显著提高砂浆的耐久性。
公布号为CN102190467A的发明专利,公开了一种抗渗抗裂干混砂浆,其组分和质量百分比组成包括:20~90%的水泥,2~40%的钡矿,该钡矿是毒重石、工业碳酸钡、重晶石或工业硫酸钡的一种或两种以上的混合物,1~30%的湿法绢云母粉,0.05~5%的防水砂浆外加剂,0~5%的氧化铁红,以及0.01~5%的纤维。该发明所述砂浆可广泛用于民用建筑,具有较好的抗渗抗裂性能而且易于施工,但是其中水泥的用量较大。已有的研究表明,当水泥掺量较大时,可以获得较大的粘接强度但也会增加砂浆的收缩,而且会增加砂浆的弹性模量、降低砂浆的柔韧性,导致砂浆在墙面使用时具有热应力变形,影响抗裂砂浆的耐久性。公布号为CN103319128A的发明专利公开了一种建筑外墙抹面抗裂砂浆及其制备方法,该建筑外墙抹面抗裂砂浆包含以下按重量百分数计的原料:水泥30-40%、掺合物4-10%、细骨料30-55%、重质碳酸钙8-15%、聚合物胶粉2-5%、抗裂纤维0.4-1.2%、木质纤维0.2-0.6%、触变润滑剂0.4-1.2%。该发明采用较低用量的水泥、粉煤灰及较高用量的黄砂,搭配适量的聚合物胶粉、抗裂纤维、木质纤维和触变润滑剂使所得砂浆具有较好的拉伸粘结强度,和易性及柔韧性较好,并具有较好的防渗抗裂性,但其性能还有待进一步提高。
发明内容
本发明要解决的技术问题是提供一种具有更好的防渗抗裂性的防渗抗裂抹面砂浆。
本发明所述的防渗抗裂抹面砂浆,包括主体材料和添加剂,其中:
所述的主体材料由30~40wt%的水泥、45~55wt%的石英砂和余量的粉煤灰组成;
所述的添加剂包括羟丙基甲基纤维素、木质纤维、聚乙稀醇、灰钙和可再分散乳胶粉;
以主体材料为基准,所述各添加剂的用量分别为:羟丙基甲基纤维素2~3kg/吨、木质纤维3~4kg/吨、聚乙稀醇0.5~1.5kg/吨、灰钙20~30kg/吨、可再分散乳胶粉6~10kg/吨。
本发明所述技术方案中,石英砂用作骨料,在施工中能提高平整度及饱和度;粉煤灰填充砂浆缝隙,并对水泥起辅助作用;羟丙基甲基纤维素主要起到保水缓凝作用,确保砂浆的失水性;聚乙稀醇可提高砂浆的粘度,并增加其强度;木质纤维使得砂浆简易施工;灰钙进一步提高砂浆的强度,特别是改善砂浆的和易性;可再分散乳胶粉把砂浆结构分散再合成,并可形成液膜,保证砂浆能够充分水化。
上述技术方案中,优选主体材料由35~40wt%的水泥、50~55wt%的石英砂和余量的粉煤灰组成;进一步优选主体材料由40wt%的水泥、50wt%的石英砂和余量的粉煤灰组成。
上述技术方案中,各添加剂的用量分别为:羟丙基甲基纤维素2~2.5kg/吨、木质纤维3~3.5kg/吨、聚乙稀醇0.5~1kg/吨、灰钙20~25kg/吨、可再分散乳胶粉6~8kg/吨;进一步优选各添加剂的用量分别为:羟丙基甲基纤维素2.5kg/吨、木质纤维3.5kg/吨、聚乙稀醇1kg/吨、灰钙25kg/吨、可再分散乳胶粉8kg/吨。
上述技术方案中,述的水泥为现有技术中常规使用的水泥,优选采用PO42.5水泥。
上述技术方案中,所述石英砂的粒度选择与现有技术相同,优选采用20~40目的石英砂。
上述技术方案中,优选采用的木质纤维,直径为5~10μm的抗裂纤维(即聚丙烯纤维)。
上述技术方案中,所述的可再分散乳胶粉具体是可再分散乳胶粉DN-4100(它是一种乙烯/醋酸乙烯共聚的可再分散性乳胶粉)。
本发明所述的防渗抗裂抹面砂浆的制备方法为:
1)按配比称取各原料,备用;
2)按水泥、粉煤灰、石英砂、羟丙基甲基纤维素、木质纤维、聚乙稀醇、灰钙、可再分散乳胶粉的顺序,将各原料加入到砂浆混合机械中,搅拌均匀,即得。
在具体使用时,将本发明制备的砂浆与水按1:3~5的重量比混合均匀,即可进行施工。
与现有技术相比,采用上述原料配比所得的砂浆具有如下特点:
①抗裂性能好,杜绝空鼓;
②易施工,且施工后墙面平整度好;
③防渗性能好,大大减低墙体渗水。
具体实施方式
下面结合具体实施例对本发明作进一步的详述,以更好地理解本发明的内容,但本发明并不限于以下实施例。
实施例1
一、防渗抗裂抹面砂浆的配方:
防渗抗裂抹面砂浆由主体材料和添加剂组成,其中:
所述的主体材料由40wt%的水泥(PO42.5水泥)、50wt%的石英砂20~40目和余量的粉煤灰组成;
以1吨主体材料为基准,所述各添加剂的用量分别为:羟丙基甲基纤维素2.5kg/吨、木质纤维3.5kg/吨、聚乙稀醇1kg/吨、灰钙25kg/吨、可再分散乳胶粉8kg/吨。
二、制备方法:
1)按配比称取各原料,备用;
2)水泥、粉煤灰、石英砂、羟丙基甲基纤维素、木质纤维、聚乙稀醇、灰钙、可再分散乳胶粉的顺序将原料加入到搅拌机中,搅拌5min,即得到所述的防渗抗裂抹面砂浆。
实施例2
一、防渗抗裂抹面砂浆的配方:
防渗抗裂抹面砂浆由主体材料和添加剂组成,其中:
所述的主体材料由30wt%的水泥(PO42.5水泥)、55wt%的石英砂30~40目和余量的粉煤灰组成;
以1吨主体材料为基准,所述各添加剂的用量分别为:羟丙基甲基纤维素3kg/吨、木质纤维3kg/吨、聚乙稀醇1.5kg/吨、灰钙20kg/吨、可再分散乳胶粉6kg/吨。
二、制备方法:
1)按配比称取各原料,备用;
2)水泥、粉煤灰、石英砂、羟丙基甲基纤维素、木质纤维、聚乙稀醇、灰钙、可再分散乳胶粉的顺序,将原料加入到搅拌机中,搅拌5min,即得到所述的防渗抗裂抹面砂浆。
实施例3
一、防渗抗裂抹面砂浆的配方:
防渗抗裂抹面砂浆由主体材料和添加剂组成,其中:
所述的主体材料由40wt%的水泥(PO42.5水泥)、45wt%的石英砂20~40目和余量的粉煤灰组成;
以1吨主体材料为基准,所述各添加剂的用量分别为:纤维素2kg/吨、木质纤维4kg/吨、聚乙稀醇1kg/吨、灰钙30kg/吨、可再分散乳胶粉9kg/吨。
二、制备方法:
1)按配比称取各原料,备用;
2)水泥、粉煤灰、石英砂、羟丙基甲基纤维素、木质纤维、聚乙稀醇、灰钙、可再分散乳胶粉的顺序,将原料加入到搅拌机中,搅拌5min,即得到所述的防渗抗裂抹面砂浆。
实施例4
一、防渗抗裂抹面砂浆的配方:
防渗抗裂抹面砂浆由主体材料和添加剂组成,其中:
所述的主体材料由35wt%的水泥(PO42.5水泥)、45wt%的石英砂20~30目和余量的粉煤灰组成;
以1吨主体材料为基准,所述各添加剂的用量分别为:羟丙基甲基纤维素2.5kg/吨、木质纤维3.8kg/吨、聚乙稀醇0.5kg/吨、灰钙22kg/吨、可再分散乳胶粉10kg/吨。
二、制备方法:
1)按配比称取各原料,备用;
2)水泥、粉煤灰、石英砂、羟丙基甲基纤维素、木质纤维、聚乙稀醇、灰钙、可再分散乳胶粉的顺序,将原料加入到搅拌机中,搅拌5min,即得到所述的防渗抗裂抹面砂浆。
将上述实施例1~4制得的砂浆按照JG158-2004的《胶粉聚苯颗粒外墙保温系统》的实验方法进行检测,测试结果如下表1所示:
表1:
按照JG158-2004的《胶粉聚苯颗粒外墙保温系统》的实验方法进行检测:施工操作时,所述建筑外墙抹面抗裂砂浆的和易性及柔韧性非常好;与水泥砂浆拉伸粘结强度为1.36Mpa(28d);浸水48小时后,与保温板的拉伸粘结强度达到0.49Mpa;抹面经过80次高温-淋水循环和32次加热-冷冻循环后末见渗水裂缝,末见粉化、空鼓、剥落等现象,其抗裂性优异。
Claims (3)
1.防渗抗裂抹面砂浆,包括主体材料和添加剂,其特征在于:
所述的主体材料由30~40wt%的水泥、45~55wt%的石英砂和余量的粉煤灰组成;
所述的添加剂包括羟丙基甲基纤维素、木质纤维、聚乙稀醇、灰钙和可再分散乳胶粉;
以主体材料为基准,所述各添加剂的用量分别为:羟丙基甲基纤维素2~3kg/吨、木质纤维3~4kg/吨、聚乙稀醇0.5~1.5kg/吨、灰钙20~30kg/吨、可再分散乳胶粉6~10kg/吨。
2.根据权利要求1所述的防渗抗裂抹面砂浆,其特征在于:所述的主体材料由40wt%的水泥、50wt%的石英砂和余量的粉煤灰组成。
3.根据权利要求1或2所述的防渗抗裂抹面砂浆,其特征在于:以主体材料为基准,所述各添加剂的用量分别为:羟丙基甲基纤维素2.5kg/吨、木质纤维3.5kg/吨、聚乙稀醇1kg/吨、灰钙25kg/吨、可再分散乳胶粉8kg/吨。