CN104762823B - A kind of method that utilization subtraction principle production depth alternately dyes Fabrics - Google Patents
A kind of method that utilization subtraction principle production depth alternately dyes Fabrics Download PDFInfo
- Publication number
- CN104762823B CN104762823B CN201510172725.3A CN201510172725A CN104762823B CN 104762823 B CN104762823 B CN 104762823B CN 201510172725 A CN201510172725 A CN 201510172725A CN 104762823 B CN104762823 B CN 104762823B
- Authority
- CN
- China
- Prior art keywords
- fabric
- foam
- dressing liquid
- liquid
- methods according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention provides a kind of method that utilization subtraction principle production depth alternately dyes Fabrics.The method includes the steps of:A, preparation dressing liquid;B, above-mentioned dressing liquid is foamed, form foam;C, by the way of discontinuous applying, foam is put on the single or double of fabric;D, the fabric to being applied with foam are first dried, and are then baked again or decatize;E, process is baked or the fabric of decatize is dyeed, obtain the fabric of style is alternately dyeed with the depth;Wherein:With the stereometer of dressing liquid, the dressing liquid includes 50 500g/L of cellulose fibre reaction suppressor, 10 80g/L of 0 50g/L of catalyst and foaming agent.The present invention is by discontinuously applying foam to fabric, while can react with the OH on cellulose fibre using cellulose fibre reaction suppressor, reduces reactivity of the dyestuff to cellulose fibre, produces a kind of fabric for replacing Color with the depth.
Description
Technical field
The present invention relates to a kind of method that utilization subtraction principle production depth alternately dyes the fabric of style, belongs to weaving neck
Domain.
Background technology
With the development in epoch, consumer is not limited solely to comfortableness for the requirement of clothing, increasing to consume
Person likes pursuing individual character, attractive in appearance and fashion, and the textile of some great characteristics is also increasingly favored by people.Therefore it is each
The PRINTED FABRIC of kind of various kinds, pattern gray yarn fabric, satin yarn dyeing fabric, gradual change yarn dyed fabric etc. arise at the historic moment, and greatly enrich mesh
Front textile garment market.But the fabric produced by these traditional production methods, its flower pattern or pattern effect still can
There is certain systematicness, style is excessively single, it is impossible to meet the requirement in market.
Therefore, the fabric for researching and developing new-type dyeing style becomes this area problem demanding prompt solution.
The content of the invention
To solve above-mentioned technical problem, it is an object of the invention to provide a kind of depth alternately dyes the fabric of style, should
The flower pattern or pattern effect changing style of fabric.
The present invention also aims to provide a kind of method that utilization subtraction principle produces above-mentioned fabrics.
To reach above-mentioned purpose, the invention provides a kind of utilization subtraction principle production depth alternately dyes Fabrics
Method, comprises the following steps:
Step a:Prepare dressing liquid;
Step b:Above-mentioned dressing liquid is foamed, foam is formed;
Step c:By the way of discontinuous applying, foam is put on the single or double of fabric;
Step d:Fabric to being applied with foam is first dried, and is then baked again or decatize;
Step e:Process is baked or the fabric of decatize is dyeed, obtain the fabric of style is alternately dyeed with the depth;
Wherein:With the stereometer of dressing liquid, the dressing liquid includes cellulose fibre reaction suppressor 50-500g/L, urges
Agent 0-50g/L and foaming agent 10-80g/L.
In the above-mentioned methods, the cellulose fibre inhibitor is to refer to react with-the OH on cellulose fibre, is reduced
Auxiliary agent of the dyestuff to the reactivity of cellulose fibre.
In the above-mentioned methods, it is preferable that the cellulose fibre reaction suppressor is resin, waterproofing agent, anion-modified
One kind in agent;It is preferably capable of the resin of the reactive group-OH closings on cellulose fibre as the resin of inhibitor,
It is highly preferred that the resin cross-linking agent is 2D resins or melmac, the waterproofing agent is without fluoro water proofing agent or fluorine-containing anti-
Water preparation, the waterproofing agent used by this area are used equally to the present invention.
In the above-mentioned methods, anion-modified dose of be to make cotton fiber surface presentation negative charge anion-modified dose.
In the above-mentioned methods, it is preferable that the catalyst includes MgCl2。
In the above-mentioned methods, it is preferable that the dressing liquid also includes foam stabilizer 1-20g/L.
The present invention is not particularly limited to foaming agent and foam stabilizer, and the foaming agent and foam stabilizer used by this area is used equally to
The present invention.
In the above-mentioned methods, it is preferable that described when foaming to dressing liquid, blowing ratio is 1:5-15;More preferably 1:
8-10, wherein, blowing ratio refers to the volume ratio of the liquid before foaming and the liquid after foaming.
In the above-mentioned methods, it is preferable that described when foam is applied on fabric, liquid carrying rate is 6-15%;More preferably
7-10%.
In the above-mentioned methods, when applying foam to fabric, blowing ratio is set as 1:5-15, liquid carrying rate are 6-15%, make bubble
Foam volume is not enough to form continuous coating on the surface of fabric, to cause the uneven applying of dressing liquid.
In the above-mentioned methods, foam is applied on fabric by the way of discontinuous applying, wherein, it is described " by foam
Be applied on fabric " belong to foam finishing technology, its be by replacing water with air dilute dressing liquid reduce liquid carrying rate, change
Carrying carrier, is substituted for fraction water and most of air (i.e. by mode of the original water as carrier:Foam) as load
Body enters fabric to carry dressing liquid.
In actual production process in order to ensure foam apply uniformity, it usually needs larger blowing ratio, will arrange
Liquid is sufficiently distributed.And in the inventive solutions, by the applied amount and blowing ratio of foam, the two techniques are joined
Number is set to a relatively low value, as the foam volume being applied on fabric is little and it is discontinuous to supply, so as to occur in that foam
Discontinuous applying of the dressing liquid to fabric, i.e., on fabric, some regions are applied with dressing liquid, and some regions do not apply dressing liquid,
The region applied on fabric is presented irregular alternate phenomenon with the region not applied, and the fabric for finally giving can have irregular
, random flower pattern or pattern effect, changing style.
In the above-mentioned methods, it is preferable that the temperature of the drying is 70-100 DEG C, the time of drying is 0.5-2min.
In the above-mentioned methods, it is preferable that the temperature for baking is 130-170 DEG C, the time for baking is 1-6min.Its
In, the purpose for baking is to make fully to react between resin and fiber.
In said method, it is preferable that the temperature of the decatize is 101-105 DEG C, the time of decatize is 7-15min;It is more excellent
Selection of land, the temperature of the decatize is 102-103 DEG C, and the time of decatize is 8-11min.
In the above-mentioned methods, it is preferable that the dyestuff for adopting that dyes is for reactive dye, reducing dye or direct dyess;
More preferably reactive dye.When dyeing to fabric, staining method can be piece dyeing or garment dyeing.
In the above-mentioned methods, it is preferable that the method is additionally included in after dyeing terminates, and fabric is carried out including soaping and solid
The post-processing step of color.
In the above-mentioned methods, it is preferable that the material of the fabric is cellulose fibre, or cellulose fibre is fine with other
The combination of dimension;It is highly preferred that the fabric is the blend fabric of textile, pure fiber crops, tencel, cotton and fiber crops, the blending of cotton and tencel knitting
The blend fabric of thing or cotton and terylene.
In the above-mentioned methods, it is preferable that the fabric is knitting fabric or shuttle-woven fabric.
In the above-mentioned methods, when put on foam on fabric, by the way of one side applying or two-sided applying.Wherein,
Two-sided applying refer to when foam maker formed foam after, be all applied to the two sides of fabric immediately by foam applicator.
Dressing liquid used by the present invention includes cellulose fibre reaction suppressor, when the inhibitor is resin, former
Reason is as follows:After cellulose fibre is reacted with resin finishing liquid, the reactive group-OH on cellulose fibre is resin-blocked, leads
Cause its reactivity to dyestuff to decline, therefore be applied with when dyeing where resin that to obtain color shallower, and where not applying resin,
Due to cellulose fibre not with resin reaction, therefore color it is deeper, so as to a kind of alternate Color of depth, and this is presented
Whether the alternate Color of kind of the depth substantially can also be adjusted by the temperature that controls bake and time, baking temperature
Height, time are long, then substantially, vice versa for the alternate Color of the fabric depth.
The present invention using foam finishing equipment can applying foam discontinuous to fabric the characteristics of, and novelty using fine
Cellulose fiber and resin, waterproofing agent, exist with dyestuff after the cellulose fibre reaction suppressor reaction such as anion-modified dose and react
Property difference, produce it is a kind of with the depth replace Color fabric.The technical scheme that the present invention is provided has and following has
Beneficial effect:
1) by being adjusted to liquid carrying rate and blowing ratio in the scope of appropriateness, fabric just can obtain the flower pattern of gradual change
Effect, it is easy to operate.
2) whether the alternate Color of the fabric depth substantially can be adjusted by the temperature that controls bake and time.
Baking temperature is high, and then the alternate Color of the fabric depth is obvious for the time length of baking, and this control method is simple and convenient.
3) applying dressing liquid discontinuous to fabric after baking, the following process of fabric can select the high-volume of piece dyeing to add
Work, it is also possible to select the processing mode of garment dyeing small lot, processing mode is very flexible.
4) directly apply resin compared with directly dyestuff is applied, the cleaning for machining rear equipment is more simple and convenient.
Description of the drawings
Design sketchs of the Fig. 1 for the fabric in embodiment 1 after the dyeing of subtraction principle.
Specific embodiment
In order to be more clearly understood to the technical characteristic of the present invention, purpose and beneficial effect, now to skill of the invention
Art scheme carry out it is described further below, but it is not intended that to the present invention can practical range restriction.
Embodiment 1
A kind of method that utilization subtraction principle production depth alternately dyes Fabrics is present embodiments provided, is adopted
The organizational structure and specification of textile shuttle-woven fabric be:120×80 80/2×80/2Poplin.The method includes the steps of:
1) prepare dressing liquid:The component and content of dressing liquid is shown in Table 1;
The component and content of 1 dressing liquid of table
2) dressing liquid is foamed, design parameter is shown in Table 2;
3) foam is applied to fabric:Foam, design parameter such as table 2 are discontinuously applied to the two-sided of fabric using foaming machine
It is shown;
The parameter of 2 foaming machine of table
Speed | Blowing ratio | Liquid carrying rate | Grammes per square metre | Fabric width | Proportion | Mixing rotating speed |
100m/min | 1:8 | 6% | 127g/m2 | 1.5m | 1.10kg/L | 600r/min |
4) fabric is first dried, is then baked:Drying temperature is 90 DEG C, and drying time is 1min;
The fabric after drying is baked using baker, the baking temperature of baker is 150 DEG C, the time of baking is
4min, speed are 35m/min;
5) to baking after fabric dye:Take Evercion Red H-E3B (TAITEX (ASIA) COMPANY
LIMITED the fabric after) reactive dye are to baking is dyeed;
6) fabric is soaped and fixation after dyeing, is obtained article.The surface of the fabric presents depth friendship
The dyeing style (as shown in Figure 1) replaced.
The article of the present embodiment is carried out into related color fastness test, method of testing and test result are as shown in table 3.
3 test result of table
Content from table 3 can be seen that every test index of fabric and can reach requirement.
From figure 1 it appears that after processing to fabric the step of according to embodiment 1, fabric face is presented the depth and hands over
The dyeing style replaced, design are similar to irregular flakes.In embodiment 1, by the applied amount and blowing ratio of foam
The two technological parameters are respectively set to 1:8 and 6%, cause the foam volume being applied on fabric little and supply discontinuous,
So as to occur in that discontinuous applying of the foam finishing liquid to fabric, i.e., on fabric, some regions are applied with dressing liquid, some regions
Dressing liquid is not applied, the region applied on fabric is presented irregular alternate phenomenon with the region not applied.
Resin cross-linking agent in dressing liquid, is reacted with-the OH of cellulose fibre under the hot conditionss for baking, is caused
Its reactivity to dyestuff declines (because dyestuff is also to carry out contaminating in reaction ability with the-OH of cellulose), therefore is applied with whole
Color is obtained when dyeing where reason liquid shallower;And where not applying dressing liquid, due to cellulose fibre not with resin reaction, because
This obtains, and color is deeper, and so as to a kind of alternate Color of depth is presented, and substantially also whether the alternate Color of this depth
Can be adjusted by controlling the temperature that bake and time, baking temperature is high, the time is long, then the fabric depth alternately dyes effect
Substantially, vice versa for fruit.
Embodiment 2
The present embodiment provides a kind of method that utilization subtraction principle production depth alternately dyes Fabrics, and what is adopted is pure
The organizational structure and specification of cotton shuttle-woven fabric be:150 × 76 80/2 × 80/2Oxford, the method includes the steps of:
1) prepare dressing liquid:The component and content of dressing liquid is shown in Table 4;
2) dressing liquid is foamed, design parameter is shown in Table 5;
The component and content of 4 dressing liquid of table
3) foam is applied to fabric:Foam, design parameter such as table 5 are discontinuously applied to the two-sided of fabric using foaming machine
It is shown;
The parameter of 5 foaming machine of table
Speed | Blowing ratio | Liquid carrying rate | Grammes per square metre | Fabric width | Proportion | Mixing rotating speed |
100m/min | 1:9 | 7% | 142g/m2 | 1.5m | 1.10kg/L | 600r/min |
4) fabric is first dried, is then baked again:Drying temperature is 90 DEG C, and drying time is 1min;
The fabric after drying is baked using baker, the baking temperature of baker is 160 DEG C, the time of baking is
3min, speed are 45m/min;
5) to baking after fabric dye:(Hensel steps weaving dyeization (China) to be had to take Novacron Red FN-R
Limit company) reactive dye to baking after fabric dye;
6) fabric is soaped and fixation treatment after dyeing, is obtained article.The surface of the fabric presents depth
Shallow alternate dyeing style.
The article of the present embodiment is carried out into related color fastness test, method of testing and test result are as shown in table 6.
6 test result of table
Content from table 6 can be seen that every test index of fabric and can reach requirement.
Embodiment 3
The present embodiment provides a kind of method that utilization subtraction principle production depth alternately dyes Fabrics, and what is adopted is pure
The organizational structure and specification of cotton knitted fabric be:30s/1 100%Cotton Pique, the method includes the steps of:
1) prepare dressing liquid:The component and content of dressing liquid is shown in Table 7;
The component and content of 7 dressing liquid of table
2) dressing liquid is foamed, design parameter is shown in Table 8;
3) foam is applied to fabric:Foam, design parameter such as table 8 are discontinuously applied to the two-sided of fabric using foaming machine
It is shown;
4) fabric is first dried, is then baked again:Drying temperature is 100 DEG C, and drying time is 0.5min;
The fabric after drying is baked using baker, the baking temperature of baker is 160 DEG C, the time of baking is
2min, speed are 20m/min;
The parameter of 8 foaming machine of table
Speed | Blowing ratio | Liquid carrying rate | Grammes per square metre | Fabric width | Proportion | Mixing rotating speed |
25m/min | 1:9 | 7% | 170g/m2 | 1.5m | 1.06kg/L | 600r/min |
5) to baking after fabric dye:Take Levafix Brilliant Red E-BA (DYSTAR CHINA
LIMITED the fabric after) reactive dye are to baking is dyeed;
6) fabric is soaped after dyeing and the Final finishing such as fixation, is obtained article.The surface of the fabric is presented
Go out the depth and alternately dye style.
The article of the present embodiment is carried out into related color fastness test, method of testing and test result are as shown in table 9.
9 test result of table
Content from table 9 can be seen that every test index of fabric and can reach requirement.
Embodiment 4
The present embodiment provides a kind of method that utilization subtraction principle production depth alternately dyes Fabrics, and what is adopted is pure
The organizational structure and specification of cotton shuttle-woven fabric be:120 × 80 80/2 × 80/2Poplin, the method includes the steps of:
1) prepare dressing liquid:The composition and content of dressing liquid is shown in Table 10;
The component and content of 10 dressing liquid of table
2) dressing liquid is foamed, design parameter is shown in Table 11;
3) foam is applied to fabric:Foam, design parameter such as table are discontinuously applied to the two-sided of fabric using foaming machine
Shown in 11;
The parameter of 11 foaming machine of table
Speed | Blowing ratio | Liquid carrying rate | Grammes per square metre | Fabric width | Proportion | Mixing rotating speed |
100m/min | 1:8 | 6% | 127g/m2 | 1.5m | 1.10kg/L | 600r/min |
4) fabric is first dried, then carries out decatize again:Drying temperature is 90 DEG C, and drying time is 1min;
Decatize is carried out using steamer to the fabric after drying during decatize, steam temperature is 102 DEG C, and steaming time is
10min;
5) fabric after decatize is dyeed:Take Evercion Red H-E3B (TAITEX (ASIA) COMPANY
LIMITED) reactive dye are dyeed to the fabric after decatize;
6) fabric is soaped after dyeing and the Final finishing such as fixation, is obtained article.The surface of the fabric is presented
Go out the depth and alternately dye style.
The article of the present embodiment is carried out into related color fastness test, method of testing and test result are as shown in table 12.
12 test result of table
Content from table 12 can be seen that every test index of fabric and can reach requirement.
Embodiment 5
The present embodiment provides a kind of method that utilization subtraction principle production depth alternately dyes Fabrics, and what is adopted is pure
The organizational structure and specification of cotton shuttle-woven fabric be:120 × 80 80/2 × 80/2Poplin, the method includes the steps of:
1) prepare dressing liquid:The composition and content of dressing liquid is shown in Table 13;
2) dressing liquid is foamed, design parameter is shown in Table 14;
The component and content of 13 dressing liquid of table
3) foam is applied to fabric:Foam, design parameter such as table are discontinuously applied to the two-sided of fabric using foaming machine
Shown in 14;
The parameter of 14 foaming machine of table
Speed | Bubble ratio | Liquid carrying rate | Grammes per square metre | Fabric width | Proportion | Mixing rotating speed |
100m/min | 1:8 | 7% | 127g/m2 | 1.5m | 1.08kg/L | 600r/min |
4) fabric is first dried, is then baked again:Drying temperature is 100 DEG C, and drying time is 1min;
The fabric after drying is baked using baker, baking temperature is 150 DEG C, the time is baked for 4min;
5) to baking after fabric dye:Take Remazol Brilliant Violet 5R (DYSTAR CHINA
LIMITED the fabric after) reactive dye are to baking is dyeed;
6) fabric is soaped after dyeing and the Final finishing such as fixation, is obtained article.The surface of the fabric is presented
Go out the depth and alternately dye style.
The article of the present embodiment is carried out into related color fastness test, method of testing and test result are as shown in Table 15.
15 test result of table
Content from table 15 can be seen that every test index of fabric and can reach requirement.
Embodiment 6:
A kind of method that utilization subtraction principle production depth alternately dyes Fabrics is present embodiments provided, is adopted
The organizational structure and specification of shuttle-woven fabric be:120 × 80 80/2 × 80/2Poplin of 70%Cotton/30%Tencel.Should
Method is comprised the steps of:
1) prepare dressing liquid:The component and content of dressing liquid is shown in Table 16;
The component and content of 16 dressing liquid of table
2) dressing liquid is foamed, design parameter is shown in Table 17;
3) foam is applied to fabric:Foam, design parameter such as table are discontinuously applied to the two-sided of fabric using foaming machine
Shown in 17;
The parameter of 17 foaming machine of table
Speed | Blowing ratio | Liquid carrying rate | Grammes per square metre | Fabric width | Proportion | Mixing rotating speed |
90m/min | 1:8 | 6% | 130g/m2 | 1.5m | 1.08kg/L | 600r/min |
4) fabric is first dried, is then baked:Drying temperature is 90 DEG C, and drying time is 0.75min;
The fabric after drying is baked using baker, the baking temperature of baker is 150 DEG C, the time of baking is
3min, speed are 45m/min;
5) to baking after fabric dye:Take Evercion Red H-E3B (TAITEX (ASIA) COMPANY
LIMITED the fabric after) reactive dye are to baking is dyeed;
6) fabric is soaped and fixation after dyeing, is obtained article.The surface of the fabric presents depth friendship
The dyeing style replaced.
The article of the present embodiment is carried out into related color fastness test, method of testing and test result are as shown in table 18.
18 test result of table
Content from table 18 can be seen that every test index of fabric and can reach requirement.
Claims (22)
1. a kind of method that utilization subtraction principle production depth alternately dyes Fabrics, which comprises the steps of:
Step a:Prepare dressing liquid;
Step b:Above-mentioned dressing liquid is foamed, foam is formed;
Step c:By the way of discontinuous applying, foam is put on the single or double of fabric;
Step d:Fabric to being applied with foam is first dried, and is then baked again or decatize;
Step e:Process is baked or the fabric of decatize is dyeed, obtain the fabric of style is alternately dyeed with the depth;
Wherein:With the stereometer of dressing liquid, the dressing liquid includes cellulose fibre reaction suppressor 50-500g/L, catalyst
0-50g/L and foaming agent 10-80g/L;
The cellulose fibre reaction suppressor is resin cross-linking agent or waterproofing agent.
2. method according to claim 1, wherein:The resin cross-linking agent is 2D resins or melmac;It is described
Waterproofing agent is without fluoro water proofing agent or fluorine-containing water repellent.
3. method according to claim 1 and 2, wherein:The catalyst includes MgCl2。
4. method according to claim 1 and 2, wherein:The dressing liquid also includes foam stabilizer 1-20g/L.
5. method according to claim 3, wherein, the dressing liquid also includes foam stabilizer 1-20g/L.
6. the method according to claim 1,2 or 5, wherein:Described when foaming to dressing liquid, blowing ratio is 1:5-
15。
7. method according to claim 3, wherein:Described when foaming to dressing liquid, blowing ratio is 1:5-15.
8. method according to claim 4, wherein:Described when foaming to dressing liquid, blowing ratio is 1:5-15.
9. method according to claim 6, wherein:The blowing ratio is 1:8-10.
10. the method according to claim 7 or 8, wherein:The blowing ratio is 1:8-10.
11. methods according to claim 1,2,5,7,8 or 9, wherein:It is described when foam is applied on fabric, band liquid
Rate is 6-15%.
12. methods according to claim 3, wherein:Described when foam is applied on fabric, liquid carrying rate is 6-15%.
13. methods according to claim 4, wherein:Described when foam is applied on fabric, liquid carrying rate is 6-15%.
14. methods according to claim 6, wherein:Described when foam is applied on fabric, liquid carrying rate is 6-15%.
15. methods according to claim 11, wherein:The liquid carrying rate is 7-10%.
16. methods according to any one of claim 12-14, wherein:The liquid carrying rate is 7-10%.
17. methods according to claim 1, wherein:The temperature for baking is 130-170 DEG C, and the time for baking is 1-
6min;The temperature of the decatize is 101-105 DEG C, and the time of decatize is 7-15min.
18. methods according to claim 1, wherein:The dyestuff for adopting that dyes is for reactive dye, reducing dye or straight
Connect dyestuff.
19. methods according to claim 18, wherein:The dyestuff is reactive dye.
20. methods according to claim 1, wherein:The material of the fabric is cellulose fibre, or cellulose fibre
With the combination of other fibers.
21. methods according to claim 20, wherein:The fabric is that textile, pure fiber crops, tencel, the blending of cotton and fiber crops are knitted
The blend fabric of the blend fabric of thing, cotton and tencel or cotton and terylene.
A kind of 22. depths alternately dye the fabric of style, wherein:The fabric is by described in any one of the claims 1-21
Prepared by the method for alternately dyeing Fabrics using the subtraction principle production depth.