CN104760751A - 一种仿陶瓷红酒瓶塞及其制备方法 - Google Patents
一种仿陶瓷红酒瓶塞及其制备方法 Download PDFInfo
- Publication number
- CN104760751A CN104760751A CN201510040207.6A CN201510040207A CN104760751A CN 104760751 A CN104760751 A CN 104760751A CN 201510040207 A CN201510040207 A CN 201510040207A CN 104760751 A CN104760751 A CN 104760751A
- Authority
- CN
- China
- Prior art keywords
- wine bottle
- bottle block
- ceramic wine
- red wine
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开一种仿陶瓷红酒瓶塞及其制备方法,所述仿陶瓷红酒瓶塞由美术雕塑成型泥所制成;所述美术雕塑成型泥中,按质量百分比计,其组分为:环氧树脂 60%-80%;固化剂 10%-30%;聚酯树脂 5%-10%。所述仿陶瓷红酒瓶塞的制备方法为:A、将环氧树脂、固化剂和聚酯树脂进行搅拌混合,配制美术雕塑成型泥;B、将美术雕塑成型泥加工成所述仿陶瓷红酒瓶塞,在40℃下保温10min,并在室温下干燥2h;C、再在仿陶瓷红酒瓶塞上涂上一层无毒涂料,进行干燥成膜,制得成品。通过本发明所制备出的仿陶瓷红酒瓶塞,其在使用过程中不会产生异味或变质,另外由于所述仿陶瓷红酒瓶塞的弹性好,密封性能好,从而保证红酒品质。
Description
技术领域
本发明涉及仿陶瓷领域,尤其涉及一种仿陶瓷红酒瓶塞及其制备方法。
背景技术
瓶塞是一种为了防止各种容量瓶内部物体溢出或发散的工具,而用于红酒的瓶塞形式多种多样,但基本结构及功能大致相同,都是将瓶塞塞紧在瓶口以起到封闭的作用。然而在现有的红酒瓶塞多为橡木等软木塞结构,其制备工艺繁琐,通常需要半个月以上时间才能完成整个木塞的制备过程,并且其容易产生瓶塞味,如橡木树皮上有黄色斑点,在制做时没有风干好,或者软木塞上因干燥而产生裂缝,依次会产生诸如腐烂、臭水和焦油种种不好闻的气味。另外,现有红酒瓶塞多为一体结构,其在使用时塞紧和拔出操作都比较费力,不够方便,影响使用效果。
因此,现有技术还有待于改进和发展。
发明内容
鉴于上述现有技术的不足,本发明的目的在于提供一种仿陶瓷红酒瓶塞及其制备方法,旨在解决现有技术中橡胶木塞因制备工艺容易产生腐烂、焦油等木塞味,降低红酒品质,且其多为一体结构,使用不够方便的问题。
本发明的技术方案如下:
一种仿陶瓷红酒瓶塞,其中,所述仿陶瓷红酒瓶塞由美术雕塑成型泥所制成;所述美术雕塑成型泥中,按质量百分比计,其组分为:
环氧树脂 60%-80%;
固化剂 10%-30%;
聚酯树脂 5%-10%。
所述仿陶瓷红酒瓶塞,其中,所述环氧树脂为对氨基苯酚环氧树脂,其环氧值为0.87,平均分子量为4000-5000。
所述仿陶瓷红酒瓶塞,其中,所述固化剂为二亚乙基三胺固化剂,其平均分子量为150-200。
所述仿陶瓷红酒瓶塞,其中,所述聚酯树脂为乙二醇聚酯树脂,其分子量为1000-1200。
所述仿陶瓷红酒瓶塞,其中,所述仿陶瓷红酒瓶塞包括塞帽及与塞帽连接的圆台,所述圆台下方还连接有一用于密封的密封套。
一种仿陶瓷红酒瓶塞的制备方法,其中,所述步骤包括:
A、将环氧树脂、固化剂和聚酯树脂进行搅拌混合,配制美术雕塑成型泥;
B、将美术雕塑成型泥加工成所述仿陶瓷红酒瓶塞,在40℃下保温10min,并在室温下干燥2h;
C、再在仿陶瓷红酒瓶塞上涂上一层无毒涂料,在室温下进行干燥成膜,制得成品。
所述仿陶瓷红酒瓶塞的制备方法,其中,所述无毒涂料按质量百分比计,包括:
聚四氟乙烯 70%-90%;
增塑剂 10%-30%。
所述仿陶瓷红酒瓶塞的制备方法,其中,步骤C中干燥的温度为25-45℃,时间为2-4h。
有益效果:通过本发明提供的仿陶瓷红酒瓶塞及其制备方法,采用美术成型泥作为原料制备所述仿陶瓷红酒瓶塞,有效解决了解决现有技术中橡胶木塞因制备工艺容易产生腐烂、焦油等木塞味,降低红酒品质,且其多为一体结构,使用不够方便的问题。本发明所制备出的仿陶瓷红酒瓶塞能代替传统的橡胶木塞,其具有仿陶瓷效果的美感,且其在使用过程中不会产生异味或变质,另外由于所述仿陶瓷红酒瓶塞的弹性好,且采用密封套结构设计,其密封性能好,从而保证红酒品质。
附图说明
图1为本发明所述仿陶瓷红酒瓶塞的结构示意图。
图2为本发明所述仿陶瓷红酒瓶塞制备方法的流程图。
具体实施方式
本发明提供一种仿陶瓷红酒瓶塞及其制备方法,为使本发明的目的、技术方案及效果更加清楚、明确,以下对本发明进一步详细说明。应当理解,此处所描述的具体实施例仅仅用以解释本发明,并不用于限定本发明。
本发明提供一种仿陶瓷红酒瓶塞,所述仿陶瓷红酒瓶塞由美术雕塑成型泥所制成,具体而言,本发明中所述美术雕塑成型泥,其按质量百分比计包括:环氧树脂 60%-80%;固化剂 10%-30%;聚酯树脂 5%-10%。
通过本发明所述一种仿陶瓷红酒瓶塞,其是由具有仿陶瓷效果的美术雕塑成型泥所制备而成的,有效解决了解决现有技术中橡胶木塞因制备工艺容易产生腐烂、焦油等木塞味,降低红酒品质,且其多为一体结构,使用不够方便的问题。本发明所制备出的仿陶瓷红酒瓶塞能代替传统的橡胶木塞,其具有仿陶瓷效果的美感,且其在使用过程中不会产生异味或变质,另外由于所述环氧树脂和聚酯树脂具有一定的粘性和韧性,使得所制备出的仿陶瓷红酒瓶塞具有一定的弹性,其能与红酒瓶紧密结合,密封性能好,从而保证红酒品质。
具体而言,本发明实施例中所述环氧树脂为对氨基苯酚环氧树脂,其环氧值为0.87,平均分子量为4000-5000。环氧树脂是指1个分子结构中至少含有2个环氧基的化合物,其以脂肪族、脂环族或芳香族链段为主链的低聚物。本发明中选用对氨基苯酚环氧树脂作为原料,并加入固化剂后交联形成网状体型结构,具有优良的仿陶瓷效果。
进一步地,本发明所述固化剂为二亚乙基三胺固化剂,其平均分子量为150-200。二亚乙基三胺固化剂为室温固化剂,其在室温条件下便可迅速进行固化,使得本发明所述美术雕塑成型泥快速干燥,形成具有一定力学强度的仿陶瓷红酒瓶塞。
进一步地,本发明所述聚酯树脂为乙二醇聚酯树脂,其分子量为1000-1200。乙二醇聚酯树脂为无毒无害物质,且其具有一定弹性,本发明中通过加入质量百分比为5%-10%的乙二醇聚酯树脂,使得所制备出的仿陶瓷红酒瓶塞具有一定的弹性性能,其能与红酒瓶紧密贴合,保证红酒的质量。当加入质量百分比低于5%的乙二醇聚酯树脂时,所述美术雕塑成型泥的硬度较大,使得制成的仿陶瓷红酒瓶塞与红酒瓶之间会产生缝隙,不利于保存红酒;当加入质量百分比高于10%的仿陶瓷红酒瓶塞时,其弹性过大,不利于塑型,所制备出的仿陶瓷红酒瓶塞的力学强度差,也不利于红酒的保存。
请参见图1,本发明较佳实施例中,所述仿陶瓷红酒瓶塞包括塞帽100及与塞帽100连接的圆台200,所述圆台下方还连接有一用于密封的密封套300。本发明中通过将美术雕塑成型泥制成具有塞帽、圆台及密封套结构的仿陶瓷红酒瓶塞,其中,所述塞帽的直径大于红酒瓶瓶口的直径,保证所述仿陶瓷红酒瓶塞不会被掉入红酒瓶中,所述圆台的直径略小于红酒瓶的瓶口直径,从而避免了盖塞和拔塞困难的问题,另外所述密封套结构的直径约与红酒瓶的直径相同,其在仿陶瓷红酒瓶塞塞进红酒瓶中时,能与红酒瓶紧密贴合一起进行密封,从而保证了红酒的品质。
优选地,本发明所述圆台的截面为一梯形结构。此外,还可以在所述圆台的外表面上设置螺纹结构,增加所述仿陶瓷红酒瓶塞和红酒瓶的接触面,使得密封性能更好。
另外,请参见图2,本发明还提供一种仿陶瓷红酒瓶塞的制备方法,其中,所述步骤包括:
S100、将环氧树脂、固化剂和聚酯树脂进行搅拌混合,配制美术雕塑成型泥;
S200、将美术雕塑成型泥加工成所述仿陶瓷红酒瓶塞,在40℃下保温10min,并在室温下干燥2h;
S300、再在仿陶瓷红酒瓶塞上涂上一层无毒涂料,在室温下进行干燥成膜,制得成品。
较佳实施例中,步骤S300中干燥的温度为25-45℃,时间为2-4h。干燥的温度太低,会延长制作时间,干燥的温度过高,容易导致仿陶瓷红酒瓶塞脆性增大,降低其质量。
本发明所述仿陶瓷红酒瓶塞的制备方法,其在加工过程中不易干裂,所制备出的仿陶瓷红酒瓶塞的仿陶瓷效果良好,具有良好的观赏性和实用性,本发明所述制备方法简单易实现,且其制备所需时间短,大大提高了生产效率。
具体而言,本发明所述无毒涂料按质量百分比计,包括:聚四氟乙烯 70%-90%;增塑剂 10%-30%。无毒涂料在室温下能形成一层保护膜,保护仿陶瓷红酒瓶塞,且可以避免红酒渗入所述仿陶瓷红酒瓶塞中。
综上所述,本发明所述的仿陶瓷红酒瓶塞及其制备方法,其采用美术成型泥作为原料制备所述仿陶瓷红酒瓶塞,有效解决了解决现有技术中橡胶木塞因制备工艺容易产生腐烂、焦油等木塞味,降低红酒品质,且其多为一体结构,使用不够方便的问题。通过本发明所制备出的仿陶瓷红酒瓶塞能代替传统的橡胶木塞,其具有仿陶瓷效果的美感,且其在使用过程中不会产生异味或变质,另外由于所述仿陶瓷红酒瓶塞的弹性好,且采用螺纹结构和密封套结构设计,其密封性能好,从而保证红酒品质,具有良好的应用前景。
应当理解的是,本发明的应用不限于上述的举例,对本领域普通技术人员来说,可以根据上述说明加以改进或变换,所有这些改进和变换都应属于本发明所附权利要求的保护范围。
Claims (8)
1.一种仿陶瓷红酒瓶塞,其特征在于,所述仿陶瓷红酒瓶塞由美术雕塑成型泥所制成;所述美术雕塑成型泥中,按质量百分比计,其组分为:
环氧树脂 60%-80%;
固化剂 10%-30%;
聚酯树脂 5%-10%。
2.根据权利要求1所述仿陶瓷红酒瓶塞,其特征在于,所述环氧树脂为对氨基苯酚环氧树脂,其环氧值为0.87,平均分子量为4000-5000。
3.根据权利要求1所述仿陶瓷红酒瓶塞,其特征在于,所述固化剂为二亚乙基三胺固化剂,其平均分子量为150-200。
4.根据权利要求1所述仿陶瓷红酒瓶塞,其特征在于,所述聚酯树脂为乙二醇聚酯树脂,其分子量为1000-1200。
5.根据权利要求1所述仿陶瓷红酒瓶塞,其特征在于,所述仿陶瓷红酒瓶塞包括塞帽及与塞帽连接的圆台,所述圆台下方还连接有一用于密封的密封套。
6.一种如权利要求1所述仿陶瓷红酒瓶塞的制备方法,其特征在于,所述步骤包括:
A、将环氧树脂、固化剂和聚酯树脂进行搅拌混合,配制美术雕塑成型泥;
B、将美术雕塑成型泥加工成所述仿陶瓷红酒瓶塞,在40℃下保温10min,并在室温下干燥2h;
C、再在仿陶瓷红酒瓶塞上涂上一层无毒涂料,进行干燥成膜,制得成品。
7.根据权利要求6所述仿陶瓷红酒瓶塞的制备方法,其特征在于,步骤C中所述无毒涂料按质量百分比计,包括:
聚四氟乙烯 70%-90%;
增塑剂 10%-30%。
8.根据权利要求6所述仿陶瓷红酒瓶塞的制备方法,其特征在于,步骤C中干燥的温度为25-45℃,时间为2-4h。