CN104745121A - Flame-retardant wire rope core conveyer belt bonding rubber - Google Patents
Flame-retardant wire rope core conveyer belt bonding rubber Download PDFInfo
- Publication number
- CN104745121A CN104745121A CN201510139496.5A CN201510139496A CN104745121A CN 104745121 A CN104745121 A CN 104745121A CN 201510139496 A CN201510139496 A CN 201510139496A CN 104745121 A CN104745121 A CN 104745121A
- Authority
- CN
- China
- Prior art keywords
- parts
- conveyer belt
- flame
- rope core
- rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a flame-retardant wire rope core conveyer belt bonding rubber, relating to the field of conveyer belt production. The flame-retardant wire rope core conveyer belt bonding rubber is composed of the following raw materials in parts by mass: 30-50 parts of blended rubber, 20-25 parts of natural rubber, 30-35 parts of cis-1,4-polybutadiene rubber, 5-7 parts of zinc oxide, 4-10 parts of magnesium oxide, 1-3 parts of stearic acid, 0.5-2 parts of accelerator NOBS, 1-2 parts of anti-aging agent 4010, 1-3 parts of anti-aging agent BLE, 15-25 parts of carbon black N330, 10-20 parts of silica white, 2-4 parts of cobalt boroacylate, 20-30 parts of chlorinated paraffin wax, 5-8 parts of antimony oxide, 10-15 parts of zinc borate, 10-15 parts of aluminum hydroxide and 1-3 parts of sulfur. The conveyer belt prepared from the flame-retardant wire rope core conveyer belt bonding rubber has the advantages of favorable toughness, favorable strength and excellent flame retardancy.
Description
Technical field
The present invention relates to conveying belt production field, particularly relate to a kind of flame-proof armored rope core conveyer belt adhesive glue.
Background technology
Coal is the important basic energy resource of China and raw material, has important strategic position in national economy.In China's primary energy structure, the main energy sources that coal will be China for a long time.Closely for a certain period, in succession there is particularly serious industrial accident in some collieries.As the safety performance of coal conveying major parts-fire retarding conveying band, be directly connected to life property safety of people.Therefore, the Steel cord adhesive glue with flame retardant properties becomes the product needed badly in production.
Summary of the invention
For overcoming the deficiency in prior art, the object of the invention is to provide a kind of flame-proof armored rope core conveyer belt adhesive glue.
For realizing object of the present invention, technical scheme of the present invention is as follows:
A kind of flame-proof armored rope core conveyer belt adhesive glue; be made up of the raw material of following masses number: blend compounds 30 ~ 50 parts; natural rubber 20 ~ 25 parts; cis-1,4-polybutadiene rubber 30 ~ 35 parts, 5 ~ 7 parts, zinc oxide, 4 ~ 10 parts, magnesium oxide; stearic acid 1 ~ 3 part; accelerant NOBS 0.5 ~ 2 part, antioxidant 4010 1 ~ 2 part, antioxidant BLE 1 ~ 3 part; carbon black N330 15 ~ 25 parts; white carbon black 10 ~ 20 parts, cobalt boracylate 2 ~ 4 parts, clorafin 20 ~ 30 parts; weisspiessglanz 5 ~ 8 parts; zinc borate 10 ~ 15 parts, 10 ~ 15 parts, aluminium hydroxide, Sulfur 1 ~ 3 part.
Preferably, be made up of the raw material of following masses number: blend compounds 50 parts, natural rubber 20 parts; cis-1,4-polybutadiene rubber 30 parts, 5 parts, zinc oxide, 4 parts, magnesium oxide; stearic acid 1 part, accelerant NOBS 0.8 part, antioxidant 4010 1 part; antioxidant BLE 1 .5 part, carbon black N330 20 parts, white carbon black 15 parts; cobalt boracylate 2 .5 part, clorafin 20 parts, weisspiessglanz 5 parts; zinc borate 10 parts, 10 parts, aluminium hydroxide, Sulfur 1 .5 part.
Preferably, described blend compounds is the mixture of chloroprene rubber and altax.
Beneficial effect of the present invention: the travelling belt that the flame-proof armored rope core conveyer belt adhesive glue utilizing the present invention to produce manufactures, has good toughness and intensity, and excellent fireproof performance.
Embodiment
The technique means realized for making the present invention, creation characteristic, reaching object and effect is easy to understand, below in conjunction with embodiment, setting forth the present invention further.
embodiment 1:a kind of flame-proof armored rope core conveyer belt adhesive glue; be made up of the raw material of following masses number: blend compounds 50 parts; natural rubber 20 parts, cis-1,4-polybutadiene rubber 30 parts, 5 parts, zinc oxide; 4 parts, magnesium oxide; stearic acid 1 part, accelerant NOBS 0.8 part, antioxidant 4010 1 part; antioxidant BLE 1 .5 part; carbon black N330 20 parts, white carbon black 15 parts, cobalt boracylate 2 .5 part; clorafin 20 parts; weisspiessglanz 5 parts, zinc borate 10 parts, 10 parts, aluminium hydroxide; Sulfur 1 .5 part, described blend compounds is the mixture of chloroprene rubber and altax.
The invention provides a kind of flame-proof armored rope core conveyer belt adhesive glue, the travelling belt that the flame-proof armored rope core conveyer belt adhesive glue utilizing the present invention to produce manufactures, there is good toughness and intensity, and excellent fireproof performance.
The foregoing is only embodiments of the invention; not thereby the scope of the claims of the present invention is limited; every utilize specification sheets of the present invention to do equivalent structure or the conversion of equivalent flow process, or be directly or indirectly used in other relevant technical fields, be all in like manner included in scope of patent protection of the present invention.
Claims (3)
1. a flame-proof armored rope core conveyer belt adhesive glue, it is characterized in that: be made up of the raw material of following masses number: blend compounds 30 ~ 50 parts, natural rubber 20 ~ 25 parts, cis-1,4-polybutadiene rubber 30 ~ 35 parts, 5 ~ 7 parts, zinc oxide, 4 ~ 10 parts, magnesium oxide, stearic acid 1 ~ 3 part, accelerant NOBS 0.5 ~ 2 part, antioxidant 4010 1 ~ 2 part, antioxidant BLE 1 ~ 3 part, carbon black N330 15 ~ 25 parts, white carbon black 10 ~ 20 parts, cobalt boracylate 2 ~ 4 parts, clorafin 20 ~ 30 parts, weisspiessglanz 5 ~ 8 parts, zinc borate 10 ~ 15 parts, 10 ~ 15 parts, aluminium hydroxide, Sulfur 1 ~ 3 part.
2. a kind of flame-proof armored rope core conveyer belt adhesive glue according to claim 1; it is characterized in that; be made up of the raw material of following masses number: blend compounds 50 parts, natural rubber 20 parts, cis-1,4-polybutadiene rubber 30 parts; 5 parts, zinc oxide; 4 parts, magnesium oxide, stearic acid 1 part, accelerant NOBS 0.8 part; antioxidant 4010 1 part; antioxidant BLE 1 .5 part, carbon black N330 20 parts, white carbon black 15 parts; cobalt boracylate 2 .5 part; clorafin 20 parts, weisspiessglanz 5 parts, zinc borate 10 parts; 10 parts, aluminium hydroxide, Sulfur 1 .5 part.
3. a kind of flame-proof armored rope core conveyer belt adhesive glue according to claim 1, is characterized in that, described blend compounds is the mixture of chloroprene rubber and altax.