CN104745111B - 一种解决防伪胶带掉胶的粘胶层及其涂布方法 - Google Patents
一种解决防伪胶带掉胶的粘胶层及其涂布方法 Download PDFInfo
- Publication number
- CN104745111B CN104745111B CN201310732349.XA CN201310732349A CN104745111B CN 104745111 B CN104745111 B CN 104745111B CN 201310732349 A CN201310732349 A CN 201310732349A CN 104745111 B CN104745111 B CN 104745111B
- Authority
- CN
- China
- Prior art keywords
- glue
- isopropanol
- layer
- resin
- adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明具体涉及一种解决防伪胶带掉胶的粘胶层及其涂布方法,粘胶层为两层,内层为异丙醇树脂胶水层,外层为水溶性丙烯酸树脂胶水层,所述异丙醇树脂胶水层由如下份数的原料组成:松香树脂1份;异丙醇35份。涂布方法的步骤如下:1)将松香树脂和异丙醇按份数比1:3混合,加温至80℃,搅拌至松香树脂完全溶解;2)将第一步制备的胶水与异丙醇按分数比1:8混合搅拌,将粘度调整到11”‑12”,制得异丙醇树脂胶水;3)利用涂布机将异丙醇树脂胶水涂布到胶带膜的涂胶面上;4)利用涂布机在异丙醇树脂胶水层上涂布水溶性丙烯酸树脂胶水;5)分切。本发明具有工艺步骤少、成本低,粘胶层粘合力强的优点。
Description
技术领域
本发明具体涉及一种解决防伪胶带掉胶的粘胶层及其涂布方法。
背景技术
传统的防伪胶带,都是在胶带膜的涂胶面上直接刷涂一层粘胶层,技术人员只考虑到粘胶层与产品之间的粘合力,却忽视了胶带和粘胶层之间的粘合力,防伪胶带粘贴到产品表面后,经常出现胶带和粘胶层剥离的情况,这就是“掉胶”现象。
发明内容
本发明的目的在于解决现有技术防伪胶带容易发生掉胶的缺陷,提供一种解决防伪胶带掉胶的粘胶层及其涂布方法,其胶带和粘胶层之间粘合力强、不易发生掉胶。
本发明通过如下技术方案来实现的:
即一种解决防伪胶带掉胶的粘胶层,其特征在于粘胶层为两层,内层为异丙醇树脂胶水层,外层为水溶性丙烯酸树脂胶水层,所述异丙醇树脂胶水层由如下份数的原料组成:
松香树脂 1份;
异丙醇 35份。
一种解决防伪胶带掉胶的粘胶层的涂布方法,其特征在于步骤如下:
1)将松香树脂和异丙醇按份数比1:3混合,加温至80℃,搅拌至松香树脂完全溶解;
2)将第一步制备的胶水与异丙醇按分数比1:8混合搅拌,将粘度调整到11”-12”,制得异丙醇树脂胶水;
3)利用涂布机将异丙醇树脂胶水涂布到胶带膜的涂胶面上;
4)利用涂布机在异丙醇树脂胶水层上涂布水溶性丙烯酸树脂胶水。
5)分切。
异丙醇树脂胶水层处于胶带膜和水溶性丙烯酸树脂胶水层之间,起到了很好的联接作用。
作为本发明的一个优选方案:涂布异丙醇树脂胶水时采用300目网纹辊,烘箱温度85-95℃,车速85-95米/分钟。
作为本发明的一个优选方案:涂布水溶性丙烯酸树脂胶水时,烘箱温度85-125℃,车速80-90米/分钟。
本发明具有工艺步骤少、成本低,粘胶层粘合力强的优点。本发明在传统的涂布水溶性丙烯酸树脂胶水工艺之前,先涂布一层异丙醇水质胶水,在保证粘胶层和产品之间粘合力的前提下,大大提高了胶带膜和粘胶层之间的粘合力,使用本发明后,防伪胶带掉胶现象大大减少。
具体实施方式
实施例1
本实施例的步骤如下:
1)将松香树脂和异丙醇按份数比1:3混合,加温至80℃,搅拌至松香树脂完全溶解;
2)将第一步制备的胶水与异丙醇按分数比1:8混合搅拌,将粘度调整到11”,制得异丙醇树脂胶水;
3)利用涂布机将异丙醇树脂胶水涂布到胶带膜的涂胶面上,涂布时采用300目网纹辊,烘箱温度85℃,车速85米/分钟。
4)利用涂布机在异丙醇树脂胶水层上涂布水溶性丙烯酸树脂胶水,涂布时,烘箱温度100℃,车速85米/分钟。
5)分切。
实施例2
本实施例的步骤如下:
1)将松香树脂和异丙醇按份数比1:3混合,加温至80℃,搅拌至松香树脂完全溶解;
2)将第一步制备的胶水与异丙醇按分数比1:8混合搅拌,将粘度调整到12”,制得异丙醇树脂胶水;
3)利用涂布机将异丙醇树脂胶水涂布到胶带膜的涂胶面上,涂布时采用300目网纹辊,烘箱温度95℃,车速95米/分钟。
4)利用涂布机在异丙醇树脂胶水层上涂布水溶性丙烯酸树脂胶水,涂布时,烘箱温度100℃,车速85米/分钟。
5)分切。
实施例3
本实施例的步骤如下:
1)将松香树脂和异丙醇按份数比1:3混合,加温至80℃,搅拌至松香树脂完全溶解;
2)将第一步制备的胶水与异丙醇按分数比1:8混合搅拌,将粘度调整到12”,制得异丙醇树脂胶水;
3)利用涂布机将异丙醇树脂胶水涂布到胶带膜的涂胶面上,涂布时采用300目网纹辊,烘箱温度90℃,车速88米/分钟。
4)利用涂布机在异丙醇树脂胶水层上涂布水溶性丙烯酸树脂胶水,涂布时,烘箱温度125℃,车速90米/分钟。
5)分切。
本发明不局限于以上实施例。烘箱温度、车速等参数均可以在限定的范围内合理选择。
Claims (2)
1.一种解决防伪胶带掉胶的粘胶层,其特征在于粘胶层为两层,内层为异丙醇树脂胶水层,外层为水溶性丙烯酸树脂胶水层,所述异丙醇树脂胶水层由如下份数的原料组成:
松香树脂 1份;
异丙醇 35份。
2.一种解决防伪胶带掉胶的粘胶层的涂布方法,其特征在于步骤如下:
1)将松香树脂和异丙醇按份数比1:3混合,加温至80℃,搅拌至松香树脂完全溶解;
2)将第一步制备的胶水与异丙醇按分数比1:8混合搅拌,将粘度调整到11”-12”,制得异丙醇树脂胶水;
3)利用涂布机将异丙醇树脂胶水涂布到胶带膜的涂胶面上,涂布异丙醇树脂胶水时采用300目网纹辊,烘箱温度85-95℃,车速85-95米/分钟;
4)利用涂布机在异丙醇树脂胶水层上涂布水溶性丙烯酸树脂胶水,涂布水溶性丙烯酸树脂胶水时,烘箱温度85-125℃,车速80-90米/分钟;
5)分切。