CN104741533A - 一种铸件的生产方法 - Google Patents
一种铸件的生产方法 Download PDFInfo
- Publication number
- CN104741533A CN104741533A CN201310749983.4A CN201310749983A CN104741533A CN 104741533 A CN104741533 A CN 104741533A CN 201310749983 A CN201310749983 A CN 201310749983A CN 104741533 A CN104741533 A CN 104741533A
- Authority
- CN
- China
- Prior art keywords
- production method
- sand
- sandbox
- casting
- moulding
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种铸件的生产方法,该方法包括制造白模,上涂料后烘干;将白模放入砂箱;在所述砂箱内填入干砂以完成造型;对沙箱造型进行超声波振动,用来强化造型;对所述砂箱抽真空并进行浇注。本发明的有益效果是:通过超声波振动提高了砂型的强度,大幅度减少因砂型原因导致的铸件缺陷。
Description
技术领域
本发明涉及铸造领域,尤其涉及一种铸件的生产方法,
背景技术
消失模铸造是将与铸件尺寸形状相似的泡沫材料制成的消失模白模并进行砂型处理,由于砂型不坚固,容易导致铸件出现气孔、疏松、夹砂、裂纹、重皮等缺陷。
发明内容
为了克服上述缺陷,本发明提供一种铸件的生产方法。
为了实现上述目的,本发明的技术方案是:一种铸件的生产方法,包括以下步骤:
1)、制造白模,上涂料后烘干;
2)、将白模放入砂箱;
3)、在所述砂箱内填入干砂以完成造型;
4)、对沙箱造型进行超声波振动,用来强化造型;
5)、对所述砂箱抽真空并进行浇注。
进一步,所述的消失模白模的易变形部位设置有用于防止该易变形部位发生变形的支撑件。
本发明的有益效果是:通过超声波振动提高了砂型的强度,大幅度减少因砂型原因导致的铸件缺陷。
具体实施方式
下面结合具体实施例对本发明做进一步的说明。
一种铸件的生产方法,包括以下步骤:
1)、制造白模,上涂料后烘干;
2)、将白模放入砂箱;
3)、在所述砂箱内填入干砂以完成造型;
4)、对沙箱造型进行超声波振动,用来强化造型;
5)、对所述砂箱抽真空并进行浇注。
进一步,所述的消失模白模的易变形部位设置有用于防止该易变形部位发生变形的支撑件。
本发明的技术方案不限于上述具体实施例的限制,凡是根据本发明的技术方案做出的技术变形,均落入本发明的保护范围之内。
Claims (2)
1.一种铸件的生产方法,其特征在于:包括以下步骤:
1)、制造白模,上涂料后烘干;
2)、将白模放入砂箱;
3)、在所述砂箱内填入干砂以完成造型;
4)、对沙箱造型进行超声波振动,用来强化造型;
5)、对所述砂箱抽真空并进行浇注。
2.根据权利要求1所述的铸件的生产方法,其特征在于:所述的消失模白模的易变形部位设置有用于防止该易变形部位发生变形的支撑件。