CN104729963B - 一种室温下齿轮用调质钢的奥氏体晶粒的检测显示方法 - Google Patents

一种室温下齿轮用调质钢的奥氏体晶粒的检测显示方法 Download PDF

Info

Publication number
CN104729963B
CN104729963B CN201510148112.6A CN201510148112A CN104729963B CN 104729963 B CN104729963 B CN 104729963B CN 201510148112 A CN201510148112 A CN 201510148112A CN 104729963 B CN104729963 B CN 104729963B
Authority
CN
China
Prior art keywords
room temperature
solution
sample
detection
added
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201510148112.6A
Other languages
English (en)
Other versions
CN104729963A (zh
Inventor
顾晓明
李康康
马良
王秀萍
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Changzhou Tianshan Heavy Industry Machinery Co Ltd
Original Assignee
Changzhou Tianshan Heavy Industry Machinery Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Changzhou Tianshan Heavy Industry Machinery Co Ltd filed Critical Changzhou Tianshan Heavy Industry Machinery Co Ltd
Priority to CN201510148112.6A priority Critical patent/CN104729963B/zh
Publication of CN104729963A publication Critical patent/CN104729963A/zh
Application granted granted Critical
Publication of CN104729963B publication Critical patent/CN104729963B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明属于物理检测技术领域，尤其是一种室温下齿轮用调质钢的奥氏体晶粒的检测显示方法，采用过饱和苦味酸溶液加十二烷基苯磺酸钠加浓盐酸，在室温下可以清晰显示齿轮用调质态原奥氏体晶界。本发明的有益效果是：1.侵蚀在室温下，无需加热处理，提高晶粒度检测的便捷性；2.配置的溶液可多次使用；3.浓盐酸的加入将提高室温溶液的离解能力，晶界与晶内腐蚀形成明显衬度，无需通过加热来提高离解能力；4.十二烷基苯磺酸钠是一种阴离子缓蚀剂，在饱和苦味酸溶液里能电离出阴离子，容易吸附在构成阳极的回火索氏体基体上，从而减慢基体组织的腐蚀；晶界处组织疏松，自由能高，腐蚀液更容易向晶界渗入，大大加速晶界的腐蚀，可以加快显示晶界。

Description

一种室温下齿轮用调质钢的奥氏体晶粒的检测显示方法
技术领域
本发明属于物理检测技术领域，尤其是一种室温下齿轮用调质钢的奥氏体晶粒的检测显示方法。
背景技术
晶粒度检测是齿轮材料质量控制的重要手段，42CrMoA、34CrNiMo6、35CrMoA是重载齿轮的常用调质钢，日常检验为调质状态，金相组织为回火索氏体，有时出现贝氏体组织，用一般侵蚀剂很难显示奥氏体晶界，中碳高合金钢的原奥氏体晶粒度显示是行业内的难题。
调质钢晶界难腐蚀的原因在于随着回火温度升高，碳化物将从马氏体中析出，析出的碳化物使其基体易侵蚀，晶界与基体无法形成色觉差异，导致晶粒度难显示。
发明内容
本发明要解决的技术问题是：基于上述问题，经过反复摸索实践，采用过饱和苦味酸溶液加十二烷基苯磺酸钠加浓盐酸，在室温下可以清晰显示齿轮用调质态原奥氏体晶界。
本发明解决其技术问题所采用的技术方案是：提供一种室温下齿轮用调质钢的奥氏体晶粒的检测显示方法，其特征在于依次包括以下步骤：
a.室温下，在一烧杯内加入100ml蒸馏水，将2～4g苦味酸加入烧杯中，用玻璃棒搅拌使晶体溶解，直至有微量晶体析出，形成过饱和苦味酸溶液，将上面的饱和溶液倒入另一个烧杯中待用；
b.在饱和苦味酸溶液内加入9～11g十二烷基苯磺酸钠，搅拌直至完全溶解；
c.步骤(b)中配置的混合溶液内加入0.4～0.6ml盐酸，盐酸含量为36～38％的分析纯，搅拌；
d.将调质态试样放入步骤(c)中配置的混合溶液内，检测面朝上，液面必须高于检测面5mm以上；
e.试样在溶液内侵蚀20min，试样检测面形成黑色腐蚀物质；
f.用镊子将试样取出，用脱脂棉轻轻擦拭黑色物质，或者用抛光机抛光检测面1～2s，检测面达到深灰色，擦拭或抛光完成；
g.试样检测面用清水冲洗后吹干；
h.试样检测面在显微镜下观察，可清晰显示原奥氏体晶粒度。
进一步地，步骤(c)中配置的混合溶液进行侵蚀后未变成黑色前，该混合溶液按每100ml加入0.2～0.3ml的盐酸配比后即可再次使用，进行试样的侵蚀。步骤(c)中配置的混合溶液可多次使用，侵蚀效果不明显时，在溶液内加入0.2～0.3ml盐酸(每100ml)，可延长溶液寿命，当溶液变成黑色时，溶液失效，加入盐酸将无效。
本发明的有益效果是：
1.侵蚀在室温下，无需加热处理，提高晶粒度检测的便捷性；
2.配置的溶液可多次使用；
3.浓盐酸的加入将提高室温溶液的离解能力，晶界与晶内腐蚀形成明显衬度，无需通过加热来提高离解能力；
4.十二烷基苯磺酸钠是一种阴离子缓蚀剂，在饱和苦味酸溶液里能电离出阴离子，容易吸附在构成阳极的回火索氏体基体上，从而减慢基体组织的腐蚀；晶界处组织疏松，自由能高，腐蚀液更容易向晶界渗入，大大加速晶界的腐蚀，可以加快显示晶界。
附图说明
下面结合附图实施例对本发明进一步说明。
图1是本发明实施例1试样在金相显微镜放大200倍下观察到的奥氏体晶粒。
具体实施方式
现在结合具体实施例对本发明作进一步说明，以下实施例旨在说明本发明而不是对本发明的进一步限定。
实施例1
a.室温下，在一烧杯内加入100ml蒸馏水，将3g苦味酸加入烧杯中，用玻璃棒搅拌使晶体溶解，直至有微量晶体析出，形成过饱和苦味酸溶液，将上面的饱和溶液倒入另一个烧杯中待用；
b.在饱和苦味酸溶液内加入10g十二烷基苯磺酸钠，搅拌直至完全溶解；
c.步骤(b)中配置的混合溶液内加入0.5ml盐酸，盐酸含量为36～38％的分析纯，搅拌；
d.将调质态试样放入步骤(c)中配置的混合溶液内，检测面朝上，液面必须高于检测面5mm以上；
e.试样在溶液内侵蚀20min，试样检测面形成黑色腐蚀物质；
f.用镊子将试样取出，用脱脂棉轻轻擦拭黑色物质，或者用抛光机抛光检测面1～2s，检测面达到深灰色，擦拭或抛光完成；
g.试样检测面用清水冲洗后吹干；
h.试样检测面在显微镜下观察，可清晰显示原奥氏体晶粒度。
如图1所示，实施例1试样在金相显微镜放大200倍下观察到的奥氏体晶粒，清楚、直观，利用定量金相法进行奥氏体晶粒度的测定，其平均奥氏体晶粒大小约为50μm。
以上述依据本发明的理想实施例为启示，通过上述的说明内容，相关工作人员完全可以在不偏离本项发明技术思想的范围内，进行多样的变更以及修改。本项发明的技术性范围并不局限于说明书上的内容，必须要根据权利要求范围来确定其技术性范围。

Claims (2)

1.一种室温下齿轮用调质钢的奥氏体晶粒的检测显示方法，其特征在于依次包括以下步骤：
a.室温下，在一烧杯内加入100ml蒸馏水，将2～4g苦味酸加入烧杯中，用玻璃棒搅拌使晶体溶解，直至有微量晶体析出，形成过饱和苦味酸溶液，将上面的饱和溶液倒入另一个烧杯中待用；
b.在饱和苦味酸溶液内加入9～11g十二烷基苯磺酸钠，搅拌直至完全溶解；
c.步骤(b)中配置的混合溶液内加入0.4～0.6ml盐酸，盐酸含量为36～38％的分析纯，搅拌；
d.将调质态试样放入步骤(c)中配置的混合溶液内，检测面朝上，液面必须高于检测面5mm以上；
e.试样在溶液内侵蚀20min，试样检测面形成黑色腐蚀物质；
f.用镊子将试样取出，用脱脂棉轻轻擦拭黑色物质，或者用抛光机抛光检测面1～2s，检测面达到深灰色，擦拭或抛光完成；
g.试样检测面用清水冲洗后吹干；
h.试样检测面在显微镜下观察，可清晰显示原奥氏体晶粒度。
2.根据权利要求1所述的一种室温下齿轮用调质钢的奥氏体晶粒的检测显示方法，其特征在于：步骤(c)配置的混合溶液进行侵蚀后未变成黑色前，该混合溶液按每100ml加入0.2～0.3ml的盐酸配比后即可再次使用，进行试样的侵蚀。
CN201510148112.6A 2015-03-31 2015-03-31 一种室温下齿轮用调质钢的奥氏体晶粒的检测显示方法 Active CN104729963B (zh)