CN104727271A - 一种复合生态导渗反滤材料的制备方法 - Google Patents
一种复合生态导渗反滤材料的制备方法 Download PDFInfo
- Publication number
- CN104727271A CN104727271A CN201510089935.6A CN201510089935A CN104727271A CN 104727271 A CN104727271 A CN 104727271A CN 201510089935 A CN201510089935 A CN 201510089935A CN 104727271 A CN104727271 A CN 104727271A
- Authority
- CN
- China
- Prior art keywords
- preparation
- guidance
- slag
- filtration material
- mold
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种复合生态导渗反滤材料的制备方法,按以下步骤:将秸秆编织成10mm~16mm厚的片材,炉渣破碎成2mm~4mm的颗粒,选择直径8mm~16mm的陶粒;按工程设计需要准备相应尺寸的模具,模具空间高度300mm~400mm,将编织好的秸秆片材置于模板底部;将炉渣和水泥浆按质量比1:1~4:1拌合均匀,倒入模内,扒平,稍作震动,形成厚50mm~80mm的炉渣小孔混凝土层;将陶粒与水泥浆按质量比1.5:1~5:1拌合均匀,倒入模内的炉渣小孔混凝土层上,扒平,稍作震动,形成厚度200mm~300mm轻质多孔陶粒混凝土层;常温、相对湿度≥80%,养护10~15天。本发明原材料来源丰富,制备方法简单,成本低,不仅可用作堤防工程的导渗反滤层,还可作为防汛储备材料替代每年防汛时大量使用的砂袋和石料。
Description
技术领域
本发明属于复合材料制备领域。涉及反滤材料的制备方法。
背景技术
堤防工程是防洪的重要屏障,关系到人民生命财产的安全。堤坝的设计遵循上堵下排的原则,但目前实际情况并不乐观。一方面,堤坝迎水面在长期水浸泡下,不可能“堵”住全部来水,必有部分水向内部渗透;另一方面,渗透进堤坝的水不能有效“排”出,堤坝内渗透水压力过高,导致土体失稳、流土、管涌、滑坡等险情。当堤坝出现险情时,目前常采用抛砂袋、填石、筑围堰等紧急除险方法,费资、费力、费时,处理不当可能延误抢险时机,造成溃坝等重大安全事故。
发明内容
本发明的目的是提出一种复合生态导渗反滤材料的制备方法,利用反滤原理,制备质轻、反滤作用好的复合式生态导渗反滤材料及其制品,不仅可用作堤防工程的导渗反滤层,还可作为防汛储备材料替代每年防汛时大量使用的砂袋和石料,可以在堤坝抢险中快速填堵流土和管涌、疏通渗水、消能减压,对堤防工程的安全意义重大。
本发明是通过以下技术方案实现的。
本发明按以下步骤。
(1)将秸秆编织成10mm~16mm厚的片材,炉渣破碎成2mm~4mm的颗粒,并选择直径8mm~16mm的陶粒,备用。
(2)按工程设计需要准备相应尺寸的模具,模具空间高度300mm~400mm。将编织好的秸秆片材放置于模板的底部。
(3)将2mm~4mm颗粒的炉渣和水泥浆按质量比1:1~4:1的比例拌合均匀,倒入模内,扒平,稍作震动,形成厚度50mm~80mm的炉渣小孔混凝土层。
(4)将陶粒与水泥浆按质量比1.5:1~5:1的比例拌合均匀,倒入模内的炉渣小孔混凝土层上,扒平,稍作震动,形成厚度200mm~300mm轻质多孔陶粒混凝土层。
(5)在常温、相对湿度≥80%条件下,养护10~15天,即制得复合生态导渗反滤材料。
本发明以炉渣、陶粒、桔杆为主要原料,以水泥基材料为胶结料,通过常温养护制备复合生态导渗反滤材料,原材料来源丰富,制备方法简单,成本低。不仅可用作堤防工程的导渗反滤层,还可作为防汛储备材料替代每年防汛时大量使用的砂袋和石料,可以在堤坝抢险中快速填堵流土和管涌、疏通渗水、消能减压。
具体实施方式
本发明将通过以下实施例作进一步说明。
实施例1。
将稻草杆编织成12mm厚的片材,炉渣破碎成2mm~4mm的颗粒,并选择直径12mm左右的陶粒。按工程设计需要准备1000mm×500mm×400mm的模具。将编织好的稻草秸秆片材放置于模板的底部;将2mm~4mm颗粒的炉渣和水泥浆按质量比1.5:1拌合均匀,倒入模内,扒平,稍作震动,形成50mm厚的炉渣小孔混凝土层;将陶粒与水泥浆按质量比3.5:1拌合均匀,倒入模内的炉渣小孔混凝土层上,扒平,稍作震动,形成300mm厚的轻质多孔陶粒混凝土层;在常温、相对湿度≥80%条件下,养护10~15天,即制得复合生态导渗反滤材料。
实施例2。
将麦桔杆编织成10mm厚的片材,炉渣破碎成2mm~4mm的颗粒,并选择直径10mm左右的陶粒。按工程设计需要准备1000mm×500mm×350mm的模具。将编织好的麦桔杆片材放置于模板的底部;将2mm~4mm颗粒的炉渣和水泥浆按质量比2:1拌合均匀,倒入模内,扒平,稍作震动,形成50mm厚的炉渣小孔混凝土层;将陶粒与水泥浆按质量比2.5:1拌合均匀,倒入模内的炉渣小孔混凝土层上,扒平,稍作震动,形成280mm厚的轻质多孔陶粒混凝土层;在常温、相对湿度≥80%条件下,养护10~15天,即制得复合生态导渗反滤材料。
实施例3。
将麦桔杆编织成14mm厚的片材,炉渣破碎成2mm~4mm的颗粒,并选择直径16mm左右的陶粒。按工程设计需要准备800mm×500mm×350mm的模具。将编织好的麦桔杆片材放置于模板的底部;将2mm~4mm颗粒的炉渣和水泥浆按质量比3:1拌合均匀,倒入模内,扒平,稍作震动,形成80mm厚的炉渣小孔混凝土层;将陶粒与水泥浆按质量比2.5:1拌合均匀,倒入模内的炉渣小孔混凝土层上,扒平,稍作震动,形成260mm厚的轻质多孔陶粒混凝土层;在常温、相对湿度≥80%条件下,养护10~15天,即制得复合生态导渗反滤材料。
Claims (1)
1.一种复合生态导渗反滤材料的制备方法,其特征是按以下步骤:
(1)将秸秆编织成10mm~16mm厚的片材,炉渣破碎成2mm~4mm的颗粒,并选择直径8mm~16mm的陶粒,备用;
(2)按工程设计需要准备相应尺寸的模具,模具空间高度300mm~400mm,将编织好的秸秆片材放置于模板的底部;
(3)将2mm~4mm颗粒的炉渣和水泥浆按质量比1:1~4:1的比例拌合均匀,倒入模内,扒平,稍作震动,形成厚度50mm~80mm的炉渣小孔混凝土层;
(4)将陶粒与水泥浆按质量比1.5:1~5:1的比例拌合均匀,倒入模内的炉渣小孔混凝土层上,扒平,稍作震动,形成厚度200mm~300mm轻质多孔陶粒混凝土层;
(5)在常温、相对湿度≥80%条件下,养护10~15天,即制得复合生态导渗反滤材料。