CN103043969A - 预防水泥渗漏结晶型防水涂料 - Google Patents

预防水泥渗漏结晶型防水涂料 Download PDF

Info

Publication number
CN103043969A
CN103043969A CN2012105839521A CN201210583952A CN103043969A CN 103043969 A CN103043969 A CN 103043969A CN 2012105839521 A CN2012105839521 A CN 2012105839521A CN 201210583952 A CN201210583952 A CN 201210583952A CN 103043969 A CN103043969 A CN 103043969A
Authority
CN
China
Prior art keywords
parts
agent
concrete
crystalline
cement
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012105839521A
Other languages
English (en)
Other versions
CN103043969B (zh
Inventor
赵斌
张志远
戎彧颖
尹晋尧
张亮
王利国
程英剑
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
China Shanxi Sijian Group Co Ltd
Original Assignee
China Shanxi Sijian Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by China Shanxi Sijian Group Co Ltd filed Critical China Shanxi Sijian Group Co Ltd
Priority to CN201210583952.1A priority Critical patent/CN103043969B/zh
Publication of CN103043969A publication Critical patent/CN103043969A/zh
Application granted granted Critical
Publication of CN103043969B publication Critical patent/CN103043969B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明属于建筑工程中防水工程领域，是一种预防水泥渗漏结晶型防水涂料。解决现有混凝土防治渗透的技术问题，由以下原材料按照重量比配制而成;普通硅酸盐水泥52.5、粒化高炉矿粉95#、渗透剂、膨胀剂、硅灰、石英砂、改性膨润土、改性硅酸钠、络合剂、结晶沉淀剂。本发明所述的水泥基防水涂料促使混凝土自身达到防水效果，属无机材料、与混凝土同寿命，增加混凝土密实性、从而提高混凝土强度，具有不易渗漏，抗碳化、抗有害物质渗透功能，施工操作简单、造价低等特点。

Description

预防水泥渗漏结晶型防水涂料
技术领域
本发明属于建筑工程中防水工程领域，是一种预防水泥渗漏结晶型防水涂料。
背景技术
我们社会中所见到的建筑物一般都有防水抗渗的要求，但建筑工程中所使用的普通混凝土防水功能较差，普通混凝土中存在许多肉眼能看到甚至看不到的微小空隙，水通过微小空隙渗透到建筑物内部，形成混凝土结构渗漏现象，
防水涂料的主要原理是混凝土在活性化学物质的作用下发生二次水化反应、生成不溶于水和其它液体的结晶体从而堵塞混凝土的毛细孔实现防水的目的、而这结晶体与混凝土的寿命是同步的、所以它能起到永久性防水。
传统的防水涂料靠材料自身达到防水效果，多属有机材料、易老化，对混凝土无帮助，导致渗漏的因素较多，如材料老化搭接分离、外力破坏等。只能在混凝土表面防水、容易破坏，材料与混凝土不同质、热膨性差别较大，材料与混凝土不同质、粘结后易脱离，无透气性，无自身修复能力，在温变、冻融影响下易剥离、老化、鼓泡，普遍有刺激性气味、对人体有害。
现有技术中也提供了一些新型的水泥基涂料，例如申请号为2010105460925水泥基渗透结晶型防水涂料，2010102265348一种渗透结晶型防水涂料，2011103491209水泥基渗透结晶型涂料及其制备方法等技术，在这些技术中，都是由不同原料按照相应的比例组合而成。
发明内容
本发明为了解决现有混凝土防治渗透的技术问题，提供一种预防水泥渗漏结晶型防水涂料。
本发明解决其技术问题所采取的技术方案：一种预防水泥渗漏结晶型防水涂料，由以下原材料按照重量比配制而成;
普通硅酸盐水泥52.5          55～60份
粒化高炉矿粉95#             15～20份
渗透剂                        1～2份
膨胀剂                      0.5～1份
硅灰                          3～6份
石英砂                        17～22份
改性膨润土                    2～5份
改性硅酸钠                     2～4份
络合剂                         7～12份
结晶沉淀剂                      1～2份。
上述材料中水泥为P.O52.5级普通硅酸盐水泥，硅灰的细度为1000目，石英砂细度为150目，渗透剂（JFC）也称脂肪醇聚氧乙烯醚，本发明可采用阴离子类型的耐碱渗透剂OEP-70、膨胀剂使用可生成钙矾石或氢氧化钙、氢氧化镁，选用有机改性膨润土，粉状改性二硅酸钠，采用聚丙烯酸类络合剂，采用以聚乙二醇为材料的结晶沉淀剂。在本申请技术方案中尤其是使用了粒化高炉矿粉95#，又称矿渣超微细粉，该产品的生产厂家为山西太钢不锈钢股份有限公司，该公司拥有全球最大矿渣超细粉立磨机，每年矿渣超微细粉生产能力大约在200万吨左右，经过试验发现，该产品应用在本发明中，具有显著的抗渗效果。
  在施工方面本防水涂料具有施工工艺简单、施工速度较快，在迎水面、背水面都可施工，效果不变，可在背水面进行修补渗漏，可与混凝土同步施工、相对节省工期，雨后即可施工、受天气影响不大，无需辅助材料、工具简单，异形部位不影响施工、整体性好、无渗漏隐患，施工后不需做特别保护层，易与外加层结合，因结构变化导致渗漏、容易修补，综合造价低，对混凝土具有渗透结晶的K11（本发明所述的渗透结晶型）水泥基通用型防水涂料能与混凝土合成一体、并且使混凝土能起到自身防水作用、而且水蒸气能自由通过、所以不会产生渗漏。
本发明所述的水泥基防水涂料促使混凝土自身达到防水效果，属无机材料、与混凝土同寿命，增加混凝土密实性、从而提高混凝土强度，导致渗漏的因素较少、不易渗漏，结晶体渗透在混凝土内部形成整体防水、不易破坏，热膨性同混凝土相同，产品涂层与混凝土粘结牢固，有透气性、保持建筑物表面干爽，可自身修复小于0.4mm的裂缝，不受温变、冻融影响，属绿色环保产品、无毒无味。同时具备表面增强、抗碳化、抗有害物质渗透功能，施工操作简单、造价低等特点。
具体实施方式
实施例1一种预防水泥渗漏结晶型防水涂料，由以下原材料按照重量比配制而成;
普通硅酸盐水泥52.5          55公斤
粒化高炉矿粉95#            20公斤
渗透剂脂肪醇聚氧乙烯醚           1.5公斤
膨胀剂氢氧化钙                 0.5公斤
硅灰                          4公斤
石英砂                       22公斤
改性膨润土                    3公斤
改性硅酸钠                    4公斤
聚丙烯酸络合剂                  10公斤
聚乙二醇结晶沉淀剂               2公斤。
配比步骤; 将普通硅酸盐水泥55重量份、粒化高炉矿粉20重量份、渗透剂1.5重量份、膨胀剂0.5重量份、硅灰4重量份、石英砂22重量份、改性膨润剂3重量份、改性硅酸钠4重量份、络合剂10重量份、结晶沉淀剂2重量份严格计量，按顺序输送加入至干粉混料机中，干粉混料机的速度350/min，搅拌15min，搅拌均匀后出料、计量、包装。
本发明实施例1所述的渗透结晶型防水涂料物理性能表
Figure 792379DEST_PATH_IMAGE002
实施例2、一种预防水泥渗漏结晶型防水涂料，由以下原材料按照重量比配制而成;
普通硅酸盐水泥52.5          60公斤
粒化高炉矿粉95#            20公斤
渗透剂脂肪醇聚氧乙烯醚      1公斤
膨胀剂氢氧化镁              1公斤
硅灰                        3公斤
石英砂                      22公斤
改性膨润土                   2公斤
改性硅酸钠                   4公斤
络合剂                       7公斤
结晶沉淀剂                     2公斤。
加工方法同实施例1
本发明实施例2所述的渗透结晶型防水涂料物理性能表
Figure 656430DEST_PATH_IMAGE004

Claims (3)

1. 一种预防水泥渗漏结晶型防水涂料，其特征在于：由以下原材料按照重量比配制而成;
普通硅酸盐水泥52.5          55～60份
粒化高炉矿粉95#             15～20份
渗透剂                        1～2份
膨胀剂                      0.5～1份
硅灰                          3～6份
石英砂                        17～22份
改性膨润土                    2～5份
改性硅酸钠                     2～4份
络合剂                         7～12份
结晶沉淀剂                      1～2份。
2.根据权利要求1所述的预防水泥渗漏结晶型防水涂料，其特征在于：由以下原材料按照重量比配制而成; 
普通硅酸盐水泥52.5          55份
粒化高炉矿粉95#            20份
渗透剂                       1.5份
膨胀剂                      0.5份
硅灰                          4份
石英砂                       22份
改性膨润土                    3份
改性硅酸钠                    4份
络合剂                  10份
结晶沉淀剂               2份。
3.根据权利要求1所述的预防水泥渗漏结晶型防水涂料，其特征在于：渗透剂为脂肪醇聚氧乙烯醚，膨胀剂为钙矾石或氢氧化钙、氢氧化镁，络合剂为聚丙烯酸，结晶沉淀剂为聚乙二醇。
CN201210583952.1A 2012-12-30 2012-12-30 预防水泥渗漏结晶型防水涂料 Active CN103043969B (zh)