CN104674555B - A kind of fabric antistatic treatment agent and preparation method thereof - Google Patents
A kind of fabric antistatic treatment agent and preparation method thereof Download PDFInfo
- Publication number
- CN104674555B CN104674555B CN201510101054.1A CN201510101054A CN104674555B CN 104674555 B CN104674555 B CN 104674555B CN 201510101054 A CN201510101054 A CN 201510101054A CN 104674555 B CN104674555 B CN 104674555B
- Authority
- CN
- China
- Prior art keywords
- treatment agent
- antistatic treatment
- parts
- fabric antistatic
- fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of fabric antistatic treatment agent and preparation method thereof.Above-mentioned antistatic treatment agent, is made up of the component comprising following weight portion: polyoxypropyleneglycol 25 38 parts, chitosan 12 18 parts, hydroxypropyl starch sodium phosphate 48 parts, silicon dioxide 23 parts, polylysine 1.2 1.6 parts, 0.5 1.2 parts of EDTA tetra-sodium, lauric acid 0.5 0.8 parts and 95 105 parts of water.Present invention also offers the preparation method of a kind of fabric antistatic treatment agent, by above-mentioned material is pulverized, stir 10 25 minutes at 85 105 DEG C, obtain fabric antistatic treatment agent.
Description
Technical field
The invention belongs to textile material field, particularly to a kind of fabric antistatic treatment agent and preparation method thereof.
Background technology
Along with improving constantly of people's living standard, feel and quality for various textile materials have had requirements at the higher level
Meanwhile, the maintenance inorganic agent of fabric be there has also been the most specialized requirement.
Most of textile materials, after cyclic washing, can produce situation that is hardening and that fade, even produces electrostatic and inhales
Dirt, produces discomfort to human body.Simultaneously the fabric feeling after cyclic washing is coarse, pliability declines, and even can produce balling-up, mill
The phenomenon damaged.
Typically result in these situation Producing reason confficient of static friction mostly for fabric and become big, how to reduce rubbing of fabric
Wipe coefficient, make the fine structure between fiber and fiber be prone to be mutually shifted.
Along with various new fabrics and fabric are also constantly presenting, because its raw material has some residuals in processing procedure
A small amount of organic nuisance and poisonous inorganic agent, although by washing, the harmful substance of part residual can be removed, but still have one
Certain residues can not be removed by washing.
Summary of the invention
For above-mentioned demand, a kind of fabric antistatic treatment agent and preparation side thereof are it is an object of the invention to provide
Method.
The purpose of the present invention can be achieved through the following technical solutions:
A kind of fabric antistatic treatment agent, is made up of the component comprising following weight portion:
Polyoxypropyleneglycol 25-38 part,
Chitosan 12-18 part,
Hydroxypropyl starch sodium phosphate 4-8 part,
Silicon dioxide 2-3 part,
Polylysine 1.2-1.6 part,
EDTA tetra-sodium 0.5-1.2 part,
Lauric acid 0.5-0.8 part,
Water 95-105 part.
The particle diameter of described silicon dioxide is 25-48 micron.
Described polylysine is tree.
A kind of preparation method of fabric antistatic treatment agent, the method comprises the following steps:
(1) by polyoxypropyleneglycol 25-38 part, chitosan 12-18 part, hydroxypropyl starch sodium phosphate 4-8 part, titanium dioxide
Silicon 2-3 part, polylysine 1.2-1.6 part and lauric acid 0.5-0.8 part, pulverize, obtain mixture;
(2) said mixture kind is sequentially added into water 95-105 part and EDTA tetra-sodium 0.5-1.2 part, stirs at 85-105 DEG C
Mix 10-25 minute, obtain fabric antistatic treatment agent.
Crushing process described in step 1 is for passing through ultra-fine pulverizer disintegrating.
Compared with prior art, beneficial effects of the present invention:
(1) the fabric antistatic treatment agent of the present invention is with polyoxypropyleneglycol and chitosan as primary raw material, for ring
Border friendly material.
(2) the fabric antistatic treatment agent of the present invention is owing to adding hydroxypropyl starch sodium phosphate, polylysine and the moon
Cinnamic acid so that the fabric after the inorganic agent of the present invention processes has good submissive performance, can effectively reduce between fiber
Friction, reduce balling-up and the generation of electrostatic phenomenon, and can have certain ageing resistace.
Detailed description of the invention
Below in conjunction with embodiment, the present invention is further illustrated.
Embodiment 1
(1) by polyoxypropyleneglycol 25kg, chitosan 18kg, hydroxypropyl starch sodium phosphate 4kg, the titanium dioxide of 25 microns
Silicon 2kg, polylysine 1.2kg and lauric acid 0.5kg, ultra-fine pulverizer disintegrating, obtain mixture;
(2) said mixture kind is sequentially added into water 95kg and EDTA tetra-sodium 0.5kg, stirs 10 minutes at 85 DEG C,
To fabric antistatic treatment agent.
The performance test results preparing fabric antistatic treatment agent is as shown in table 1.
Embodiment 2
(1) by polyoxypropyleneglycol 25kg, chitosan 12kg, hydroxypropyl starch sodium phosphate 4kg, the titanium dioxide of 25 microns
Silicon 2kg, polylysine 1.2kg and lauric acid 0.5kg, ultra-fine pulverizer disintegrating, obtain mixture;
(2) said mixture kind is sequentially added into water 95kg and EDTA tetra-sodium 0.5kg, stirs 10 minutes at 85 DEG C,
To fabric antistatic treatment agent.
The performance test results preparing fabric antistatic treatment agent is as shown in table 1.
Embodiment 3
(1) by polyoxypropyleneglycol 38kg, chitosan 18kg, hydroxypropyl starch sodium phosphate 8kg, the titanium dioxide of 25 microns
Silicon 3kg, polylysine 1.6kg and lauric acid 0.8kg, ultra-fine pulverizer disintegrating, obtain mixture;
(2) said mixture kind is sequentially added into water 105kg and EDTA tetra-sodium 1.2kg, stirs 25 minutes at 105 DEG C,
Obtain fabric antistatic treatment agent.
The performance test results preparing fabric antistatic treatment agent is as shown in table 1.
Embodiment 4
(1) by polyoxypropyleneglycol 38kg, chitosan 18kg, hydroxypropyl starch sodium phosphate 8kg, the titanium dioxide of 48 microns
Silicon 3kg, polylysine 1.2kg and lauric acid 0.8kg, ultra-fine pulverizer disintegrating, obtain mixture;
(2) said mixture kind is sequentially added into water 105kg and EDTA tetra-sodium 1.2kg, stirs 25 minutes at 105 DEG C,
Obtain fabric antistatic treatment agent.
The performance test results preparing fabric antistatic treatment agent is as shown in table 1.
Embodiment 5
(1) by polyoxypropyleneglycol 30kg, chitosan 16kg, hydroxypropyl starch sodium phosphate 6kg, the titanium dioxide of 38 microns
Silicon 2kg, the polylysine 1.2kg of tree and lauric acid 0.5kg, ultra-fine pulverizer disintegrating, obtain mixture;
(2) said mixture kind is sequentially added into water 100kg and EDTA tetra-sodium 0.8kg, stirs 15 minutes at 95 DEG C,
To fabric antistatic treatment agent.
The performance test results preparing fabric antistatic treatment agent is as shown in table 1.
Table 1
The invention is not restricted to embodiment here, those skilled in the art are according to the announcement of the present invention, without departing from the present invention
Improvement and amendment that category is made all should be within protection scope of the present invention.
Claims (1)
1. a fabric antistatic treatment agent, it is characterised in that be made up of the component comprising following weight portion:
Polyoxypropyleneglycol 25-38 part,
Chitosan 12-18 part,
Hydroxypropyl starch sodium phosphate 4-8 part,
Silicon dioxide 2-3 part,
Polylysine 1.2-1.6 part,
EDTA tetra-sodium 0.5-1.2 part,
Lauric acid 0.5-0.8 part,
Water 95-105 part;
The particle diameter of described silicon dioxide is 25-48 micron;
Described polylysine is tree;
Described a kind of fabric antistatic treatment agent is prepared by following preparation method:
(1) by polyoxypropyleneglycol 25-38 part, chitosan 12-18 part, hydroxypropyl starch sodium phosphate 4-8 part, silicon dioxide 2-
3 parts, polylysine 1.2-1.6 part and lauric acid 0.5-0.8 part, pulverize, obtain mixture;
(2) said mixture kind is sequentially added into water 95-105 part and EDTA tetra-sodium 0.5-1.2 part, stirs at 85-105 DEG C
10-25 minute, obtain fabric antistatic treatment agent;
Crushing process described in step 1 is for passing through ultra-fine pulverizer disintegrating.