CN104630700A - 带螺纹不锈钢零件多弧离子镀镀铝前处理工艺及其应用 - Google Patents
带螺纹不锈钢零件多弧离子镀镀铝前处理工艺及其应用 Download PDFInfo
- Publication number
- CN104630700A CN104630700A CN201410755334.XA CN201410755334A CN104630700A CN 104630700 A CN104630700 A CN 104630700A CN 201410755334 A CN201410755334 A CN 201410755334A CN 104630700 A CN104630700 A CN 104630700A
- Authority
- CN
- China
- Prior art keywords
- stainless steel
- arc ion
- threaded stainless
- ion coating
- steel components
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种带螺纹不锈钢零件多弧离子镀镀铝前处理工艺，属于不锈钢工艺处理技术领域。工艺步骤如下：不锈钢螺钉喷砂前进行干燥洁净处理；处理后的螺钉进行手动喷砂处理；进行超声波热水洗，吹干零件表面；电解抛光，恒定电压，电解抛光30-120s，电流密度控制在5-7A/dm2；钝化处理；放入38-42℃的热水中清洗2min后吹干。本发明进行手动喷砂及电解抛光处理后，不但可以提高螺钉镀铝后的表面亮度，还能明显减少黑点缺陷，使成品率显著提高，满足镀铝螺钉在使用过程中的润滑性和导电性的要求。
Description
技术领域
本发明属于焊接工艺技术领域，特别是涉及一种带螺纹不锈钢零件多弧离子镀镀铝前处理工艺及其应用。适用于IC装备(半导体器件、集成电路芯片和平板显示器的专用生产设备 )中不锈钢螺钉镀纯铝的前处理工艺，是不锈钢螺钉多弧离子镀镀纯铝前的专业技术。
背景技术
目前采用多弧离子镀使不锈钢表面镀纯铝，虽已在IC装备中大量使用，但是镀纯铝后螺钉表面存在大量黑点缺陷，且表面光亮度较低，导致成品率较低，无法满足镀铝螺钉在使用过程中的润滑性和导电性的要求。
发明内容
针对上述存在的技术问题，为了解决带螺纹不锈钢零件镀纯铝后螺钉表面存在大量黑点缺陷，且表面亮度不够，导致成品率较低的问题，本发明的目的是提供一种带螺纹不锈钢零件多弧离子镀镀铝前处理工艺及其应用。
本发明的目的是通过如下技术方案实现的：
一种带螺纹不锈钢零件多弧离子镀镀铝前处理工艺，包括如下步骤：
（1）带螺纹不锈钢零件喷砂前进行干燥洁净处理；
（2）将（1）处理后的零件进行手动喷砂处理；
（3）零件喷砂处理后，进行超声波热水洗，然后使用压缩空气吹干零件表面；
（4）将（3）吹干后零件用钛丝上挂，放入电抛槽后，立刻通电，进行电解抛光，恒定电压，电解抛光30-120s，电流密度控制在5-7A/dm2；
（5）将零件放入38-42℃的热水中清洗2-5min后吹干。
进一步地，所述喷砂采用白刚玉（Al2O3），其砂材型号的范围是36#至240#。
进一步地，所述喷砂工艺的喷砂压力为40-80PSI。
进一步地，所述超声波热水洗工艺清洗时间为3-5min，温度为40-50℃。
进一步地，所述电解抛光工艺中，电解抛光溶液为 Isopol 140电解抛光药水。
进一步地，所述电解抛光工艺，使用钛丝作为阴极，极板面积为零件面积的1/3-1/5。
进一步地，所述电解抛光工艺：温度：50-70℃，电压：8-12V，电抛时间：0.5min-2min。
进一步地，所述第（4）电解抛光工艺后还增加钝化处理工艺，是将不锈钢螺钉放入体积分数为50%的HNO3钝化槽中钝化处理30min。
进一步地，所述干燥清洁处理工艺，是将零件进行脱脂清洗去除表面油污，使用压缩空气吹干零件表面。
一种带螺纹不锈钢零件多弧离子镀镀铝前处理工艺用于除SUS303以外的带螺纹不锈钢材质多弧离子镀镀铝前处理工艺。
本发明的有益效果是：
1.本发明解决带螺纹不锈钢零件镀纯铝后螺钉表面存在大量黑点缺陷，且表面亮度不够，导致成品率较低，无法满足镀铝螺钉在使用过程中的润滑性和导电性要求的问题。
2.本发明将不锈钢零件在镀铝之前使用白刚玉（Al2O3）进行手动喷砂处理，然后进行电解抛光，通过以上两个工艺处理，不但可以提高螺钉镀铝后的表面亮度，还能明显减少黑点缺陷，使成品率显著提高，满足镀铝螺钉在使用过程中的润滑性和导电性的要求。
具体实施方式
下面结合实施例对本发明进行详细描述。
实施例1：本发明带螺纹不锈钢零件多弧离子镀镀铝前处理工艺，以螺钉为例，包括如下步骤：
（1）不锈钢螺钉喷砂前进行干燥洁净处理，将螺钉进行脱脂清洗去除表面油污，使用压缩空气吹干零件表面；
（2）将（1）处理后的螺钉进行手动喷砂处理；采用白刚玉（Al2O3），其砂材型号的范围是36#；喷砂压力为40PSI（0.276MPa）；
（3）不锈钢螺钉喷砂处理后，进行超声波热水洗，然后使用压缩空气吹干零件表面，清洗时间为3min，温度为40℃；
（4）将（3）吹干后螺钉用钛丝上挂，放入电抛槽后，立刻通电，进行电解抛光，电解抛光溶液为 Isopol 140电解抛光药水；恒定电压，电解抛光30s，电流密度控制在5A/dm2；使用钛丝作为阴极，极板面积为零件面积的1/5；温度：50℃、电压：8V 电抛时间：0.5min；
（5）将不锈钢螺钉放入38℃的热水中清洗2min后吹干。
本发明适用于除SUS303以外的不锈钢材质螺钉多弧离子镀镀铝前处理工艺。
实施例2：本例与实施例1不同的是：本例在所述第（4）电解抛光工艺后还增加钝化处理工艺，是将不锈钢螺钉放入体积分数为50%的HNO3钝化槽中钝化处理30min。
本例中喷砂采用白刚玉（Al2O3），其砂材型号的范围是150#；喷砂压力为60PSI；
超声波热水洗时间为4min，温度为45℃；
电解抛光70s，电流密度控制在6A/dm2；使用钛丝作为阴极，极板面积为零件面积的1/4；温度：60℃、电压：10V 电抛时间：1min；
钝化处理是在体积分数为50%的HNO3中钝化处理30min；
钝化完成后将不锈钢螺钉放入40℃的热水中清洗4min后吹干。
实施例3：本例与实施例2不同的是：本例中喷砂采用白刚玉（Al2O3），其砂材型号的范围是240#；喷砂压力为80PSI（0.552 MPa）；
超声波热水洗时间为5min，温度为50℃；
电解抛光120s，电流密度控制在7A/dm2；使用钛丝作为阴极，极板面积为零件面积的1/3；温度： 70℃、电压： 12V 电抛时间： 2min；
钝化处理是在体积分数为50%的HNO3中钝化处理30min；
钝化完成后将不锈钢螺钉放入42℃的热水中清洗5min后吹干。
Claims (10)
1.一种带螺纹不锈钢零件多弧离子镀镀铝前处理工艺，其特征在于：包括如下步骤：
（1）带螺纹不锈钢零件喷砂前进行干燥洁净处理；
（2）将（1）处理后的零件进行手动喷砂处理；
（3）零件喷砂处理后，进行超声波热水洗，然后使用压缩空气吹干零件表面；
（4）将（3）吹干后零件用钛丝上挂，放入电抛槽后，立刻通电，进行电解抛光，恒定电压，电解抛光30-120s，电流密度控制在5-7A/dm2；
（5）将零件放入38-42℃的热水中清洗2-5min后吹干。
2.按照权利要求1所述的带螺纹不锈钢零件多弧离子镀镀铝前处理工艺，其特征在于：所述喷砂采用白刚玉（Al2O3），其砂材型号的范围是36#至240#。
3.按照权利要求1所述的带螺纹不锈钢零件多弧离子镀镀铝前处理工艺，其特征在于：所述喷砂工艺的喷砂压力为40-80PSI。
4.按照权利要求1所述的带螺纹不锈钢零件多弧离子镀镀铝前处理工艺，其特征在于：所述超声波热水洗工艺清洗时间为3-5min，温度为40-50℃。
5.按照权利要求1所述的带螺纹不锈钢零件多弧离子镀镀铝前处理工艺，其特征在于：所述电解抛光工艺中，电解抛光溶液为 Isopol 140电解抛光药水。
6.按照权利要求1所述的带螺纹不锈钢零件多弧离子镀镀铝前处理工艺，其特征在于：所述电解抛光工艺，使用钛丝作为阴极，极板面积为零件面积的1/3-1/5。
7.按照权利要求1所述的带螺纹不锈钢零件多弧离子镀镀铝前处理工艺，其特征在于：所述电解抛光工艺：温度：50-70℃，电压：8-12V，电抛时间：0.5min-2min。
8.照权利要求1所述的带螺纹不锈钢零件多弧离子镀镀铝前处理工艺，其特征在于：所述第（4）电解抛光工艺后还增加钝化处理工艺，是将不锈钢螺钉放入体积分数为50%的HNO3钝化槽中钝化处理30min。
9.按照权利要求1所述的带螺纹不锈钢零件多弧离子镀镀铝前处理工艺，其特征在于：所述干燥清洁处理工艺，是将零件进行脱脂清洗去除表面油污，使用压缩空气吹干零件表面。
10.一种权利要求1-9所述的带螺纹不锈钢零件多弧离子镀镀铝前处理工艺用于除SUS303以外的带螺纹不锈钢材质多弧离子镀镀铝前处理工艺。