CN104628266A - 单层防火玻璃的制备方法 - Google Patents
单层防火玻璃的制备方法 Download PDFInfo
- Publication number
- CN104628266A CN104628266A CN201310569877.8A CN201310569877A CN104628266A CN 104628266 A CN104628266 A CN 104628266A CN 201310569877 A CN201310569877 A CN 201310569877A CN 104628266 A CN104628266 A CN 104628266A
- Authority
- CN
- China
- Prior art keywords
- glass
- glass substrate
- placing
- flame resistant
- potassium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种单层防火玻璃的制备方法，包括以下步骤：一、对浮法钠钙硅玻璃基片边部进行磨抛；二、清洗，将玻璃片置于不锈钢支架上进行干燥，预热，随后将玻璃基片从预热炉中置入450℃的含有硝酸铯、硝酸钾、硅藻土、三氧化二铝、氢氧化钾、氟化钾混合熔盐中进行离子交换8h；三、将玻璃片从熔盐中取出，置于退火炉中退火、冷却、清洗、干燥即得防火玻璃。本发明提供的单层防火玻璃的制备方法，制得的防火玻璃平整度高、透过率高、透光性好、强度高、结构简单，便于安装，耐火性能强。
Description
技术领域
本发明涉及一种玻璃的制备方法，具体涉及一种单层防火玻璃的制备方法。
背景技术
防火玻璃是一种在规定的耐火试验条件下能够保持其完整性和隔热性的特种玻璃，防火玻璃按结构可分为单层防火玻璃和复合防火玻璃，复合防火玻璃是由两层或两层以上玻璃复合而成或由一层玻璃和有机材料复合而成，并满足相应耐火等级要求的特种玻璃，由此也决定了复合防火玻璃透光性和耐候性差的缺点。
发明内容
本发明的目的在于，提供一种单层防火玻璃的制备方法，制得的防火玻璃平整度高、透过率高、透光性好、强度高、结构简单，便于安装。
所述单层防火玻璃的制备方法，它包括以下步骤：
一、对浮法钠钙硅玻璃基片边部进行磨抛；
二、清洗，将玻璃片置于不锈钢支架上进行干燥，预热，随后将玻璃基片从预热炉中置入450℃的含有硝酸铯、硝酸钾、硅藻土、三氧化二铝、氢氧化钾、氟化钾混合熔盐中进行离子交换8h；
三、将玻璃片从熔盐中取出，置于退火炉中退火、冷却、清洗、干燥即得防火玻璃。
本发明提供的单层防火玻璃的制备方法，其有益效果在于，制得的防火玻璃平整度高、透过率高、透光性好、强度高、结构简单，便于安装，耐火性能强。
具体实施方式
下面结合一个实施例，对本发明提供的单层防火玻璃的制备方法进行详细的说明。
实施例
一、对浮法钠钙硅玻璃基片边部进行磨抛；
二、清洗，将玻璃片置于不锈钢支架上进行干燥，预热，随后将玻璃基片从预热炉中置入450℃的含有硝酸铯、硝酸钾、硅藻土、三氧化二铝、氢氧化钾、氟化钾混合熔盐中进行离子交换8h；
三、将玻璃片从熔盐中取出，置于退火炉中退火、冷却、清洗、干燥即得防火玻璃。
Claims (1)
1.一种单层防火玻璃的制备方法，其特征在于：它包括以下步骤：
一、对浮法钠钙硅玻璃基片边部进行磨抛；
二、清洗，将玻璃片置于不锈钢支架上进行干燥，预热，随后将玻璃基片从预热炉中置入450℃的含有硝酸铯、硝酸钾、硅藻土、三氧化二铝、氢氧化钾、氟化钾混合熔盐中进行离子交换8h；
三、将玻璃片从熔盐中取出，置于退火炉中退火、冷却、清洗、干燥即得防火玻璃。