CN104559447A - Castor oil solvent printing ink and preparation method thereof - Google Patents
Castor oil solvent printing ink and preparation method thereof Download PDFInfo
- Publication number
- CN104559447A CN104559447A CN201410825808.3A CN201410825808A CN104559447A CN 104559447 A CN104559447 A CN 104559447A CN 201410825808 A CN201410825808 A CN 201410825808A CN 104559447 A CN104559447 A CN 104559447A
- Authority
- CN
- China
- Prior art keywords
- viscotrol
- ink
- silicone antifoam
- water soluble
- antifoam agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a castor oil solvent printing ink and a preparation method thereof. The printing ink is an environment-friendly printing ink prepared from castor oil instead of a petroleum solvent, and the color of the printing ink is pure and saturated.
Description
Technical field
The present invention relates to a kind of ink, particularly a kind of vegetables oil that utilizes is as the environment-friendly ink of solvent, belongs to ink manufacture field.
Summary of the invention
Ink is a kind of to be mixed equably by pigment, low-melting ink vehicle and auxiliary agent etc. and through the gluey fluid of a kind of viscosity of repeat-rolling.It is the important materials for wrapping material printing, such as, for fields such as books and periodicals, packing and decorating, building decorations by printing by pattern, literal table now on the substrate.The U.S. is maximum ink producing country and country of consumption in the world, and Japan takes second place, and Germany the 3rd, China occupies the 4th.Along with the develop rapidly of Chinese national economy, the fast development of China's nearly ten years packaging industries, make the ink industry of China have also been obtained larger expansion, emerge rapidly and become one of ink manufacture big country of the world, current domestic ink industry size just maintains sustained and rapid growth with the speed of more than 10%.
Develop the ink kind of various performance in recent years, along with the attention degree of environmental protection is increasing, have the regulation limitations such as heavy metal content, packing material solvent residues amount and other VOC limit standard in other related fields such as food product pack especially, exploitation non-toxic ink is the study hotspot of current ink.
In China, what ink production was produced substantially is traditional synthetic resins ink, containing the high point petroleum solvent of 35% ~ 40% in this kind of ink, thus containing more multiring aromatic hydrocarbon substance, and 3,4-benzo pyrroles, 3-nitro benzo ketone etc. are wherein also containing carcinogenic components, on printed matter, residual quantity is large, the survival time is long, can endanger user's health, is also the important source of pollution in Printing ink producing process simultaneously.In today that environmental pollution attracts people's attention day by day, non-toxic ink replaces traditional ink will be inexorable trend.
Viscotrol C is a kind of based on containing the commodity grease of hydroxyl through base acid, mainly from the seed (oil-containing about 50%) of castor-oil plant.The general grease of viscosity ratio is high a lot, viscosity index 84, the good fluidity of Viscotrol C simultaneously, solvent is made with Viscotrol C, not only environmental protection but also the resource of available regenerative replaced non-renewable petroleum solvent to the ink of preparation, and when reclaiming, than traditional ink, deinking is easier to useless printed matter process, little to the damage of paper.
Summary of the invention
The invention provides a kind of Viscotrol C solvent ink and preparation method thereof, for realizing this purpose, this ink comprises the material of following weight percent:
Viscotrol C 20-40%
Thanomin 10-20%
Water soluble acrylic resin 20-30%
Water soluble acrylic acid mill base 10-20%
Soybean lecithin wetting agent 1-2%
Silicone antifoam agent 1-2%
Water surplus.
The preparation method of this ink carries out as follows:
(1) load a certain proportion of water, Viscotrol C, thanomin and silicone antifoam agent by a dispersion cylinder, by the rotating speed of 500-600 r/min, dispersed 1-2 hour;
(2) after dispersion, then add appropriate silicone antifoam agent, filter;
(3) the emulsion of filtration is put in dispersion cylinder more again;
(4) add water soluble acrylic resin, water soluble acrylic acid mill base, soybean lecithin wetting agent and silicone antifoam agent more successively, by the rotating speed of 600-8000r/min, dispersed 2-4 hour;
(5) filter after finally adding appropriate silicone antifoam agent, a kind of Viscotrol C solvent ink.
Step (4) in, in described water soluble acrylic acid mill base, the color of pigment powder is one or more in red, yellow, blue, black.
The present invention has following advantages and characteristic:
(1) this ink colors is pure, look full;
(2) good environmental protection;
(3) raw material sources are extensive.
Embodiment
Embodiment one:
The water of 17 parts is loaded by a dispersion cylinder, the Viscotrol C of 20 parts, the silicone antifoam agent of the thanomin of 10 parts and 0.5 part, by the rotating speed of 500 r/min, the silicone antifoam agent of 0.5 part is added again after dispersed 2 hours, filter, the emulsion of filtration is put in dispersion cylinder more again, then the water soluble acrylic resin of 30 parts is added successively, the water soluble acrylic acid mill base of 20 parts, the silicone antifoam agent of the soybean lecithin wetting agent of 1 part and 0.5 part, by the rotating speed of 600 r/min, dispersed 4 hours, filter after finally adding the silicone antifoam agent of 0.5 part, a kind of Viscotrol C solvent ink.
Embodiment two:
The water of 12 parts is loaded by a dispersion cylinder, the Viscotrol C of 30 parts, the silicone antifoam agent of the thanomin of 20 parts and 0.25 part, by the rotating speed of 600 r/min, the silicone antifoam agent of 0.25 part is added again after dispersed 1 hour, filter, the emulsion of filtration is put in dispersion cylinder more again, then the water soluble acrylic resin of 25 parts is added successively, the water soluble acrylic acid mill base of 10 parts, the silicone antifoam agent of the soybean lecithin wetting agent of 2 parts and 0.25 part, by the rotating speed of 800 r/min, dispersed 2 hours, filter after finally adding the silicone antifoam agent of 0.25 part, a kind of Viscotrol C solvent ink.
Embodiment three:
The water of 8 parts is loaded by a dispersion cylinder, the Viscotrol C of 40 parts, the silicone antifoam agent of the thanomin of 15 parts and 0.25 part, by the rotating speed of 550 r/min, the silicone antifoam agent of 0.25 part is added again after dispersed 1.5 hours, filter, the emulsion of filtration is put in dispersion cylinder more again, then the water soluble acrylic resin of 20 parts is added successively, the water soluble acrylic acid mill base of 15 parts, the silicone antifoam agent of the soybean lecithin wetting agent of 1 part and 0.25 part, by the rotating speed of 700 r/min, dispersed 3 hours, filter after finally adding the silicone antifoam agent of 0.25 part, a kind of Viscotrol C solvent ink.
Claims (3)
1. a Viscotrol C solvent ink, is characterized in that, this ink comprises the material of following weight percent:
Viscotrol C 20-40%
Thanomin 10-20%
Water soluble acrylic resin 20-30%
Water soluble acrylic acid mill base 10-20%
Soybean lecithin wetting agent 1-2%
Silicone antifoam agent 1-2%
Water surplus.
2. a kind of Viscotrol C solvent ink according to claim 1, it is characterized in that, the preparation method of this ink comprises the steps:
(1) load a certain proportion of water, Viscotrol C, thanomin and silicone antifoam agent by a dispersion cylinder, by the rotating speed of 500-600 r/min, dispersed 1-2 hour;
(2) after dispersion, then add appropriate silicone antifoam agent, filter;
(3) the emulsion of filtration is put in dispersion cylinder more again;
(4) add water soluble acrylic resin, water soluble acrylic acid mill base, soybean lecithin wetting agent and silicone antifoam agent more successively, by the rotating speed of 600-8000r/min, dispersed 2-4 hour;
(5) filter after finally adding appropriate silicone antifoam agent, a kind of Viscotrol C solvent ink.
3. the preparation method of a kind of Viscotrol C solvent ink according to claim 2, is characterized in that, step (4) in, in described water soluble acrylic acid mill base, the color of pigment powder is one or more in red, yellow, blue, black.