CN104559466A - Mixed oleoresin printing ink - Google Patents
Mixed oleoresin printing ink Download PDFInfo
- Publication number
- CN104559466A CN104559466A CN201410825487.7A CN201410825487A CN104559466A CN 104559466 A CN104559466 A CN 104559466A CN 201410825487 A CN201410825487 A CN 201410825487A CN 104559466 A CN104559466 A CN 104559466A
- Authority
- CN
- China
- Prior art keywords
- oil
- ink
- silicone antifoam
- antifoam agent
- soluble acrylic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a mixed oleoresin printing ink and a preparation method thereof. The printing ink comprises the following components in percentage by weight: 10-20% of industrial soybean vegetable oil, 10-20% of tung oil, 10-20% of ethanolamine, 20-30% of a water-soluble acrylic resin, 10-20% of water-borne acrylic color paste, 1-2% of a soybean lecithin wetting agent, 1-2% of an organosilicon antifoaming agent, and an appropriate amount of water. The soybean oil-tung oil synthetic resin is used as the connecting material of the printing ink, so that the drying performance of the printing ink is improved.
Description
Technical field
The present invention relates to a kind of environment-friendly ink, particularly a kind of ink utilizing mixed vegetable oil resin-made standby, belongs to ink manufacture field.
Background technology
Ink forms a kind of mixing equably by binder, colouring matter and auxiliary agent etc., is a kind of stable colloidal dispersion system.It is the important materials for wrapping material printing by printing by pattern, literal table now on the substrate.
Along with the develop rapidly of Chinese national economy, the fast development of China's nearly ten years packaging industries, the ink industry of China is made to have also been obtained larger expansion, rapid emergence becomes world's ink and manufactures one of big country, current domestic ink industry size just maintains sustained and rapid growth with the speed of more than 10%, the ink kind of various performance is developed in succession, and along with the attention degree of environmental protection is increasing, exploitation non-toxic ink is the study hotspot of current ink.
In China, what ink production was produced substantially is traditional synthetic resins ink, the high point petroleum solvent containing 35%-40% in this kind of ink, thus containing more multiring aromatic hydrocarbon substance, can endanger user's health.In today that environmental pollution attracts people's attention day by day, non-toxic ink replaces traditional ink will be inexorable trend.Soya-bean ink is owing to adopting the soy resins of natural environmental-protective as matrix resin, VOC content is low, there is the various features such as upper machine stability and good post-press finishing of biological degradation and excellence, the leading role of following environment-friendly ink, and when reclaiming, than traditional ink, deinking is easier to useless printed matter process, little to the damage of paper, the waste residue after deinking is also better degraded.
But soybean oil resin ink setting poor-performing, the invention provides a kind of soybean oil-tung oil hybrid resin ink for this reason, improve the drying property of ink.
Summary of the invention
The invention provides a kind of mixing oil resin ink and preparation method thereof, for realizing this purpose, this ink comprises the material of following weight percent:
Industry soybean plants oil 10-20%
Tung oil 10-20%
Thanomin 10-20%
Water soluble acrylic resin 20-30%
Water soluble acrylic acid mill base 10-20%
Soybean lecithin wetting agent 1-2%
Silicone antifoam agent 1-2%
Water surplus.
The preparation method of this ink carries out as follows:
(1) load a certain proportion of water, industrial soybean plants oil, tung oil, thanomin and silicone antifoam agent by a dispersion cylinder, by the rotating speed of 500-600 r/min, dispersed 1-2 hour;
(2) after dispersion, then add appropriate silicone antifoam agent, filter;
(3) the emulsion of filtration is put in dispersion cylinder more again;
(4) add water soluble acrylic resin, water soluble acrylic acid mill base, soybean lecithin wetting agent and silicone antifoam agent more successively, by the rotating speed of 600-8000r/min, dispersed 2-4 hour;
(5) filter after finally adding appropriate silicone antifoam agent, a kind of mixing oil resin ink.
Preferential, step (1) in, the industrial soybean plants oil of interpolation and the weight of tung oil are added than being 1:1.
The present invention has following advantages and characteristic:
(1) this ink raw materials wide material sources and renewable;
(2) color is pure, look full;
(3) good environmental protection.
Embodiment
Embodiment one:
The water of 17 parts is loaded by a dispersion cylinder, the industrial soybean plants oil of 10 parts, the tung oil of 10 parts, the silicone antifoam agent of the thanomin of 10 parts and 0.5 part, by the rotating speed of 500 r/min, the silicone antifoam agent of 0.5 part is added again after dispersed 2 hours, filter, the emulsion of filtration is put in dispersion cylinder more again, then the water soluble acrylic resin of 30 parts is added successively, the water soluble acrylic acid mill base of 20 parts, the silicone antifoam agent of the soybean lecithin wetting agent of 1 part and 0.5 part, by the rotating speed of 600 r/min, dispersed 4 hours, filter after finally adding the silicone antifoam agent of 0.5 part, a kind of mixing oil resin ink.
Embodiment two:
The water of 12 parts is loaded by a dispersion cylinder, the industrial soybean plants oil of 15 parts, the tung oil of 15 parts, the silicone antifoam agent of the thanomin of 20 parts and 0.25 part, by the rotating speed of 600 r/min, the silicone antifoam agent of 0.25 part is added again after dispersed 1 hour, filter, the emulsion of filtration is put in dispersion cylinder more again, then the water soluble acrylic resin of 25 parts is added successively, the water soluble acrylic acid mill base of 10 parts, the silicone antifoam agent of the soybean lecithin wetting agent of 2 parts and 0.25 part, by the rotating speed of 800 r/min, dispersed 2 hours, filter after finally adding the silicone antifoam agent of 0.25 part, a kind of mixing oil resin ink.
Embodiment three:
The water of 8 parts is loaded by a dispersion cylinder, the industrial soybean plants oil of 20 parts, the tung oil of 20 parts, the silicone antifoam agent of the thanomin of 15 parts and 0.25 part, by the rotating speed of 550 r/min, the silicone antifoam agent of 0.25 part is added again after dispersed 1.5 hours, filter, the emulsion of filtration is put in dispersion cylinder more again, then the water soluble acrylic resin of 20 parts is added successively, the water soluble acrylic acid mill base of 15 parts, the silicone antifoam agent of the soybean lecithin wetting agent of 1 part and 0.25 part, by the rotating speed of 700 r/min, dispersed 3 hours, filter after finally adding the silicone antifoam agent of 0.25 part, a kind of mixing oil resin ink.
Claims (3)
1. a mixing oil resin ink, is characterized in that, this ink comprises the material of following weight percent:
Industry soybean plants oil 10-20%
Tung oil 10-20%
Thanomin 10-20%
Water soluble acrylic resin 20-30%
Water soluble acrylic acid mill base 10-20%
Soybean lecithin wetting agent 1-2%
Silicone antifoam agent 1-2%
Water surplus.
2. a kind of mixing oil resin ink according to claim 1, it is characterized in that, the preparation method of this ink comprises the steps:
(1) load a certain proportion of water, industrial soybean plants oil, tung oil, thanomin and silicone antifoam agent by a dispersion cylinder, by the rotating speed of 500-600 r/min, dispersed 1-2 hour;
(2) after dispersion, then add appropriate silicone antifoam agent, filter;
(3) the emulsion of filtration is put in dispersion cylinder more again;
(4) add water soluble acrylic resin, water soluble acrylic acid mill base, soybean lecithin wetting agent and silicone antifoam agent more successively, by the rotating speed of 600-8000r/min, dispersed 2-4 hour;
(5) filter after finally adding appropriate silicone antifoam agent, a kind of mixing oil resin ink.
3. the preparation method of a kind of mixing oil resin ink according to claim 2, is characterized in that, step (1) in, the industrial soybean plants oil of interpolation and the weight of tung oil are added than being 1:1.