CN104538085A - 一种环保导电银浆 - Google Patents

一种环保导电银浆 Download PDF

Info

Publication number
CN104538085A
CN104538085A CN201510007838.8A CN201510007838A CN104538085A CN 104538085 A CN104538085 A CN 104538085A CN 201510007838 A CN201510007838 A CN 201510007838A CN 104538085 A CN104538085 A CN 104538085A
Authority
CN
China
Prior art keywords
parts
sodium
conductive silver
environment
conductive
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510007838.8A
Other languages
English (en)
Inventor
王乐乐
刘战
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI FENGYANG DECHENG TECHNOLOGY Co Ltd
Original Assignee
ANHUI FENGYANG DECHENG TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI FENGYANG DECHENG TECHNOLOGY Co Ltd filed Critical ANHUI FENGYANG DECHENG TECHNOLOGY Co Ltd
Priority to CN201510007838.8A priority Critical patent/CN104538085A/zh
Publication of CN104538085A publication Critical patent/CN104538085A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种环保导电银浆，其是由下述重量份的原料制得：导电银粉60-70、导电石墨烯1-1.5、丙烯酸树脂9-12、苯甲醇 10-20、硝酸纤维素0.3-0.5、三乙醇胺1-2、改性玻璃粉10-16、三氯乙烯10-20、均苯四甲酸四异辛酯0.3-0.5、甲酸银0.4-0.8、三羟甲基丙烷2-3，氢化蓖麻油1-2,138松香树脂9-11。本发明使用导电石墨烯，增加导电性能的同时减少环境污染，环保健康。

Description

一种环保导电银浆
技术领域
本发明属导电银浆领域，尤其涉及一种环保导电银浆。
背景技术
烧结型银导电浆料需要烧结成膜，烧结温度>500℃，玻璃粉或氧化物作为粘接相。银粉按照粒径分类，平均粒径<0.1μm(100nm)为纳米银粉； 0.1μm< Dav(平均粒径) <10.0μm为银微粉；Dav(平均粒径)> 10.0μm为粗银粉。粉末的制备方法有很多，就银而言，可一次采用物理法（等离子、雾化法），化学法（硝酸银热分解法、液相还原）。由于银是贵金属，易被还原而回到单质状态，因此液相还原法是目前制备银粉的最主要的方法。即将银盐（硝酸银等）溶于水中，加入化学还原剂（如水合肼等），沉积出银粉，经过洗涤、烘干而得到银还原粉，平均粒径在0.1-10.0μm之间，还原剂的选择、反应条件的控制、界面活性剂的使用，可以制备不同物理化学特性的银微粉（颗粒形态、分散程度、平均粒径以及粒径分布、比表面积、松装密度、振实密度、晶粒大小、结晶性等），对还原粉进行机械加工（球磨等）可得光亮银粉（polished silver powder），片状银粉（silver flake）。
发明内容
本发明的目的是提供一种环保导电银浆。
为了实现上述目的本发明采用如下技术方案：
一种环保导电银浆，其特征在于，其是由下述重量份的原料制得：
导电银粉60-70、导电石墨烯1-1.5、丙烯酸树脂9-12、苯甲醇 10-20、硝酸纤维素0.3-0.5、三乙醇胺1-2、改性玻璃粉10-16、三氯乙烯10-20、均苯四甲酸四异辛酯0.3-0.5、甲酸银0.4-0.8、三羟甲基丙烷2-3，氢化蓖麻油1-2, 138松香树脂9-11；
改性玻璃粉由下述重量份的原料制得：废玻璃粉10-20、AS2O3  4.3-6.7，Sb2O3 4-6，K2O8-10,CuO8-10，B2O3  3.3-5,、铝酸钠1-2、聚乙烯蜡2-4、氯化石蜡1-2、烷基苯磺酸钠2-4、偏硅酸钠3-5、土耳其红油 0.1-0.2，亚硫酸氢钠1-2、卵磷脂1-2、去离子水100-150；
所述的改性玻璃粉的制备方法为：
（1）将铝酸钠、聚乙烯蜡、氯化石蜡、以及去离子水加入反应釜中，300-400转/分搅拌均匀，再加入烷基苯磺酸钠、偏硅酸钠、土耳其红油 、亚硫酸氢钠、卵磷脂、升温至130-150℃，200-500rpm下搅拌均匀，得改性液；
（2）其余原料混匀烧结，烧结温度为1200-1400℃，时间为0.5-2小时，得玻璃熔融体淬火、球磨、干燥，过筛得30-50μm玻璃粉；
（3）将玻璃粉与改性液混匀，于30-50℃下搅拌1-2小时，静置5-8小时，抽滤干燥，即得。
所述的一种环保导电银浆，其特征在于：制备方法包括以下步骤：
（1）丙烯酸树脂、苯甲醇、硝酸纤维素、三乙醇胺、三氯乙烯、均苯四甲酸四异辛酯、甲酸银、三羟甲基丙烷，氢化蓖麻油, 138松香树脂放入反应釜，于45-55℃搅拌10-15min，即得有机载体备用；
（2）将改性玻璃粉加入到有机载体中，搅拌混和，再加入其余原料，45-55℃下混和均匀，得到浆料；
（3）浆料球磨，研磨至浆料细度小于10μm，调粘度后即得。
本发明的有益效果：
本发明使用导电石墨烯，增加导电性能的同时减少环境污染，环保健康。
具体实施方式
一种环保导电银浆，其是由下述重量（kg)的原料制得：
导电银粉60、导电石墨烯1.5、丙烯酸树脂9、苯甲醇 20、硝酸纤维素0.3、三乙醇胺1、改性玻璃粉16、三氯乙烯20、均苯四甲酸四异辛酯0.3、甲酸银0.4、三羟甲基丙烷2，氢化蓖麻油1, 138松香树脂9；
改性玻璃粉由下述重量（kg)的原料制得：废玻璃粉17、AS2O3  4，Sb2O3 5，K2O8,CuO8，B2O3  3.5,、铝酸钠1、聚乙烯蜡2、氯化石蜡1、烷基苯磺酸钠2、偏硅酸钠3.5、土耳其红油 0.1，亚硫酸氢钠1.2、卵磷脂2、去离子水150；
所述的改性玻璃粉的制备方法为：
（1）将铝酸钠、聚乙烯蜡、氯化石蜡、以及去离子水加入反应釜中，350转/分搅拌均匀，再加入烷基苯磺酸钠、偏硅酸钠、土耳其红油 、亚硫酸氢钠、卵磷脂、升温至150℃，500rpm下搅拌均匀，得改性液；
（2）其余原料混匀烧结，烧结温度为1400℃，时间为0.8小时，得玻璃熔融体淬火、球磨、干燥，过筛得30-50μm玻璃粉；
（3）将玻璃粉与改性液混匀，于40℃下搅拌2小时，静置5小时，抽滤干燥，即得。
所述的一种环保导电银浆，制备方法包括以下步骤：
（1）丙烯酸树脂、苯甲醇、硝酸纤维素、三乙醇胺、三氯乙烯、均苯四甲酸四异辛酯、甲酸银、三羟甲基丙烷，氢化蓖麻油, 138松香树脂放入反应釜，于、55℃搅拌、15min，即得有机载体备用；
（2）将改性玻璃粉加入到有机载体中，搅拌混和，再加入其余原料，48℃下混和均匀，得到浆料；
（3）浆料球磨，研磨至浆料细度小于10μm，调粘度后即得。
采用丝网印刷机将银浆印刷于125mm×125mm Si基板上，然后在180℃干燥，再在880℃进行快速烧制电极引线，高温烧结后制成的电极引线表面银白，光滑无缺陷，剥离强度12.8N/cm,锡焊性能良好，方阻＜10 Siements/sq，制备的太阳能电池光电转化效率为21.2%，拉力测试结果为附着力>13.3N/mm2。

Claims (2)

1.一种环保导电银浆，其特征在于，其是由下述重量份的原料制得：
导电银粉60-70、导电石墨烯1-1.5、丙烯酸树脂9-12、苯甲醇 10-20、硝酸纤维素0.3-0.5、三乙醇胺1-2、改性玻璃粉10-16、三氯乙烯10-20、均苯四甲酸四异辛酯0.3-0.5、甲酸银0.4-0.8、三羟甲基丙烷2-3，氢化蓖麻油1-2, 138松香树脂9-11；
改性玻璃粉由下述重量份的原料制得：废玻璃粉10-20、AS2O3  4.3-6.7，Sb2O3 4-6，K2O8-10,CuO8-10，B2O3  3.3-5,、铝酸钠1-2、聚乙烯蜡2-4、氯化石蜡1-2、烷基苯磺酸钠2-4、偏硅酸钠3-5、土耳其红油 0.1-0.2，亚硫酸氢钠1-2、卵磷脂1-2、去离子水100-150；
所述的改性玻璃粉的制备方法为：
（1）将铝酸钠、聚乙烯蜡、氯化石蜡、以及去离子水加入反应釜中，300-400转/分搅拌均匀，再加入烷基苯磺酸钠、偏硅酸钠、土耳其红油 、亚硫酸氢钠、卵磷脂、升温至130-150℃，200-500rpm下搅拌均匀，得改性液；
（2）其余原料混匀烧结，烧结温度为1200-1400℃，时间为0.5-2小时，得玻璃熔融体淬火、球磨、干燥，过筛得30-50μm玻璃粉；
（3）将玻璃粉与改性液混匀，于30-50℃下搅拌1-2小时，静置5-8小时，抽滤干燥，即得。
2.根据权利要求1所述的一种环保导电银浆，其特征在于：制备方法包括以下步骤：
（1）丙烯酸树脂、苯甲醇、硝酸纤维素、三乙醇胺、三氯乙烯、均苯四甲酸四异辛酯、甲酸银、三羟甲基丙烷，氢化蓖麻油, 138松香树脂放入反应釜，于45-55℃搅拌10-15min，即得有机载体备用；
（2）将改性玻璃粉加入到有机载体中，搅拌混和，再加入其余原料，45-55℃下混和均匀，得到浆料；
（3）浆料球磨，研磨至浆料细度小于10μm，调粘度后即得。
CN201510007838.8A 2015-01-08 2015-01-08 一种环保导电银浆 Pending CN104538085A (zh)