CN104535384A - 一种粉末状非金属矿制备sem样品的方法 - Google Patents

一种粉末状非金属矿制备sem样品的方法 Download PDF

Info

Publication number
CN104535384A
CN104535384A CN201410761011.1A CN201410761011A CN104535384A CN 104535384 A CN104535384 A CN 104535384A CN 201410761011 A CN201410761011 A CN 201410761011A CN 104535384 A CN104535384 A CN 104535384A
Authority
CN
China
Prior art keywords
sample
ore
sem
powdery
small amount
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410761011.1A
Other languages
English (en)
Inventor
庞建涛
方世祥
肖喆
王灿霞
杨稳权
何向文
周建一
字佳林
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Yunnan Phosphate Chemical Group Corp Ltd
Original Assignee
Yunnan Phosphate Chemical Group Corp Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Yunnan Phosphate Chemical Group Corp Ltd filed Critical Yunnan Phosphate Chemical Group Corp Ltd
Priority to CN201410761011.1A priority Critical patent/CN104535384A/zh
Publication of CN104535384A publication Critical patent/CN104535384A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种粉末状非金属矿制备SEM样品的方法,针对粉末状非金属矿制备SEM观测样品的方法,本发明工艺为:(1)将粉末状非金属矿样烘干;(2)取一只干净的烧杯,先加入10ml无水乙醇,再加入少量的矿样;(3)将烧杯放入超声波仪中20~30分钟,使样品完全分散;(4)用吸管吸取含矿样的乙醇,并滴少量在金属片上;(5)待乙醇完全挥发后对矿样进行喷碳或者喷金。完成以上步骤即可获得合格的SEM观测样品。本发明操作简单、快速,且分散性好,利于SEM对样品的观测。

Description

一种粉末状非金属矿制备SEM样品的方法
技术领域
本发明涉及一种针对粉末状非金属矿制备SEM观测样品的方法,该方法操作简单、快速,且分散性好,利于SEM对样品的观测。
背景技术
SEM是扫描电子显微镜的英文缩写,SEM是一种大型的分析仪器,主要功能是用于固态物质的形貌显微分析和对常规成分的微区分析,有分辨高、放大倍数大、景深大、立体感强、样品制备简单的优点,广泛应用于化工、材料、医药、生物、矿产、司法等领域。由于其价格昂贵及特殊的工作原理,它对样品制备有着较高的要求,样品的制备好坏,直接影响着样品分析是否成功。
SEM分析的样品必须是固体,且要无毒、无放射性、无污染、无磁、无水分,成分稳定,块状样品大小要适中,粉末样品要进行特殊处理, 对不导电和导电性能差的样品要进行镀膜。
随着矿产资源的日渐贫化和科技的快速发展,大型高精度仪器SEM 已在非金属矿研究领域应用,以往对非金属矿制样多采用直接用导电胶粘的方法,其制样方法存在样品分散难(特别是微细粒样品),粉末状样品颗粒易掉落污染SEM样品仓等问题。此次发明的制样方法首先是将样品置于无水乙醇中,用超声波对样品进行分散,解决了样品分散难的问题;然后将含有矿样的乙醇溶液滴于金属片上,待乙醇完全挥发后镀碳或者镀金,使矿样导电且不易掉落。该制样方法不但新提供了一种针对粉末状非金属矿制备SEM观测样品的方法,同时还解决了导电胶粘样法矿样不易分散及矿样颗粒易掉落的问题,为SEM在非金属矿研究领域的应用奠定了更宽广的基础。
发明内容
本发明的目的是提供一种针对粉末状非金属矿制备SEM观测样品的方法,该方法解决了粉末状矿样的分散问题,解决了非金属矿的导电问题,与以往的制样方法相比,粉末状样品分散性好,不易掉落,利于在SEM下观测。
本发明中针对粉末状非金属矿制备SEM样品的具体技术方案是:
(1)将粉末状非金属矿样品完全烘干;
(2)10ml无水乙醇和少量的样品混合,并利用超声波仪对样品进行20~30分钟的搅拌,使样品完全分散;
(3)用吸管吸取含有矿样的乙醇,滴于在金属片上;
(4)待乙醇完全挥发后对矿样进行喷碳或者喷金。
      本发明的有益效果是:
①  预先使粉末状矿样完全分散;
②  利用金属片作为载体,利于导电;
③  对非金属矿样进行喷碳或者喷金,使矿样导电,并使矿样固定在金属片上。
附图说明
   图1为本发明方法步骤流程图。
图2为磷石膏晶体的照片。
图3 为白云石晶体的照片。
具体实施方式
下面结合附图对本发明制样的操作步骤进行详细说明。
本发明一种粉末状非金属矿制备SEM样品的方法,其特征在于含有以下工艺步骤:
(1)将粉末状非金属矿样品完全烘干;
(2)10ml无水乙醇和少量样品混合,并利用超声波仪对样品进行20~30分钟的搅拌,使样品完全分散;
(3)用吸管吸取含有矿样的乙醇,滴少量在金属片上;
(4)待乙醇完全挥发后对矿样进行喷碳或者喷金。
实施例1:
(1)利用微波炉将磷石膏样品烘干;
(2)取一只洁净的烧杯,先加入10ml无水乙醇,再加入少量的磷石膏样品,利用超声波仪对样品进行20~30分钟的搅拌,使样品完全分散;
(3)准备一个金属片,并用吸管吸取含有矿样的乙醇,滴少量在金属片上;
(4)待乙醇完全挥发后对矿样进行喷碳或者喷金。
本发明的有益效果是:
①  磷石膏完全分散;
②  可以在SEM下获得清晰的磷石膏晶体图像(图2)。
实施例2
(1)利用微波炉将磷石膏样品烘干;
(2)取一只洁净的烧杯,先加入10ml无水乙醇,再加入少量的磷石膏样品,利用超声波仪对样品进行30分钟的搅拌,使样品完全分散;
(3)准备一个金属片,并用吸管吸取含有矿样的乙醇,滴少量在金属片上;
(4)待乙醇完全挥发后对矿样进行喷碳或者喷金。
针对粉末状白云石样品完成以上步骤,也可在SEM下可清晰的观察到白云石晶体,如图3。
获得的清晰照片,说明了该方法的可行性。

Claims (1)

1.一种粉末状非金属矿制备SEM样品的方法,其特征在于含有以下工艺步骤:
(1)将粉末状非金属矿样品完全烘干;
(2)10ml无水乙醇和少量样品混合,并利用超声波仪对样品进行20~30分钟的搅拌,使样品完全分散;
(3)用吸管吸取含有矿样的乙醇,滴少量在金属片上;
(4)待乙醇完全挥发后对矿样进行喷碳或者喷金。
CN201410761011.1A 2014-12-13 2014-12-13 一种粉末状非金属矿制备sem样品的方法 Pending CN104535384A (zh)