CN104530813A - 一种防腐防锈颜料 - Google Patents
一种防腐防锈颜料 Download PDFInfo
- Publication number
- CN104530813A CN104530813A CN201510018582.0A CN201510018582A CN104530813A CN 104530813 A CN104530813 A CN 104530813A CN 201510018582 A CN201510018582 A CN 201510018582A CN 104530813 A CN104530813 A CN 104530813A
- Authority
- CN
- China
- Prior art keywords
- pigment
- parts
- corrosion
- antiseptic
- rust
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于颜料技术领域,特别涉及一种防腐防锈颜料,由以下重量份的原料制成:超细聚酰亚胺树脂15~20份、松香3~7份、钛白粉2~6份、氯化钙1~4份、甲基纤维素1~5份、乙酸乙酯5~25份、甘油1~5份、聚四氟乙烯1~5份、氟化钙1~6份、聚天冬氨酸1~3份。本发明的颜料防腐防锈能力强,优于现有颜料,可抗老化,延长使用寿命,有较好附着力,色泽较于现有颜料好,夜晚可发光。
Description
技术领域
本发明属于颜料技术领域,特别涉及一种防腐防锈颜料。
背景技术
颜料(Pigment)用来着色的粉末状物质。在水、油脂、树脂、有机溶剂等介质中不溶解,但能均匀地在这些介质中分散并能使介质着色,而又具有一定的遮盖力。现有颜料功能单一,不能够满足传统颜料的需求,颜料的制作原料成本较高,制作过程比较复杂,颜料一般不具备防锈和防腐等多重作用,这是传统颜料存在的缺陷。同时传统的防锈颜料,如硅铬酸铅、铬酸锌、铬酸锶、红丹、高铅酸钙、黄丹、铅粉等,一般含铅、铬及镉等元素,虽然防锈性能优异,但有毒、污染环境和危害健康。
申请号201310368209.9的中国发明专利公开了一种防腐颜料,其组分的重量份数为:丙稀酸树脂:15~20份、酚醛氯丁:16~21份、环氧树脂:15~18份、鳞片状石墨:3~7份、氧化铬绿:11~16份、填料:7~12份、稀释剂:8~15份、稳定剂:6~8份、助剂:5~7份。在该发明配方中含有铬元素,有毒、污染环境和危害健康。
申请号201310678373.X本发明公开了一种防锈颜料,由如下原料制成:1~2质量份乙二醇单硬脂酸酯,2~3质量份乙烯基三甲氧基硅烷,21质量份钛白粉,32质量份磷酸锌,4质量份单烷氧基脂肪酸钛酸酯类偶联剂,17质量份纳米二氧化硅,27质量份硫酸钡,23质量份氧化锌,28质量份三聚磷酸铝,46质量份碳酸钙,55质量份磷铁粉,8质量份颜料分散剂。该发明的颜料防锈效果差,颜料色泽不够亮。
发明内容
本发明所要解决的技术问题是提供一种抗老化、寿命长、色泽亮的防腐防锈颜料。
为实现上述目的,本发明采用如下技术方案:
防腐防锈颜料,由以下重量份的原料制成:
本发明所述的超细聚酰亚胺树脂粉的粒径为10~18μm。超细聚酰亚胺树脂粉具有优良的耐热性、耐磨性,有较好的润湿和粘结性能,固化时不产生低分子挥发物,与各种填料相容性好,粘结强度高,具有良好的柔韧性,其机械强度高,耐热温度高。
本发明所述的聚四氟乙烯的粒径为1~5μm。聚四氟乙烯耐高温,耐低温,耐腐蚀,老化寿命长,无毒害,具有良好的机械韧性,有较大硬度,作为颜料填充剂,提高颜料的机械性能。
甘油作为颜料的润湿剂和扩散剂,提高颜料的粘合力和稳定性。
本发明所述的钛白粉为金红石型钛白粉。金红石型钛白粉折射率高,遮盖力高,稳定,耐候性好。由于涂料中的白色颜料钛白粉其折光率为2.7,对紫外线具有较强的反射能力,因此涂层的抗紫外线辐射性能大大加强,使用有效寿命会大大延长。
本发明所述的氯化钙为食品级。本发明配比中含有适量防冻剂氯化钙,在颜料吸水后可有效抵御-30℃低温,使颜料中吸水不产生结冰结晶引起膨胀应力的破坏。颜料中所含吸湿物质氯化钙在吸水时,会产生的放热反应,其瞬间温度可达50℃左右,而吸热时又会使水蒸发排出,就从根本上阻止了水气结露结冰的可能性。同时,氯化钙还具有防腐能力。
乙酸乙酯被金属表面吸附或与金属作用生成一层薄膜,覆盖在金属表面,防止金属腐蚀生锈。
本发明中,甲基纤维素性能稳定,能耐酸碱、微生物、热,能够分散超细聚酰亚胺树脂,有助于涂料成膜,还具有粘合作用。
本发明配方中松香能增加涂料色泽,松香的软化作用,使颜料保存较长时间,不致过早硬化,延长使用时间。
氟化钙为荧光材料,主要作用为吸蓄太阳光,黑夜自发光,而且氟化钙低毒。
聚天冬氨酸是一种人工仿生合成的水溶性高分子物质,具有无毒、无公害和可完全生物降解的特性,是一种国际公认的“绿色化学品”。聚天冬氨酸因含有肽键和羧基等活性基团的结构特点,具有极强的螯合、分散、吸附等作用,且配伍性极佳,使本发明的各原料达到最佳配伍状态。
优选地,本发明所述的防腐防锈颜料,由以下重量份的原料制成:
本发明的有益效果在于:
1、本发明颜料防腐防锈能力强,优于现有颜料。
2、在颜料中加入超细聚酰亚胺树脂和聚四氟乙烯填充剂,提高颜料的机械性能。
3、配方中钛白粉抗紫外线,延缓老化,氯化钙防腐防冻,松香防早硬化,破坏颜料韧性,这些原料的加入,配合延长颜料的使用寿命。
4、超细聚酰亚胺树脂和松香配合,还可以提高颜料的附着力,提高颜料的实用性,松香还能够提高颜料的色泽。
5、甲基纤维素和聚天冬氨酸共同配合,起到分散作用,提高颜料的均匀性和稳定性,其中聚天冬氨酸还可以提高各原料的搭配效果,使各原料达到最佳状态。
6、氟化钙作为荧光材料,使颜料晚上发光,即使晚上也不失颜料颜色。
具体实施方式
以下结合实施例对本发明作进一步说明,但本发明并不局限于这些实施例。
实施例1
防腐防锈颜料,由以下重量份的原料制成:
实施例2
防腐防锈颜料,由以下重量份的原料制成:
实施例3
防腐防锈颜料,由以下重量份的原料制成:
实施例4
防腐防锈颜料,由以下重量份的原料制成:
实施例5
防腐防锈颜料,由以下重量份的原料制成:
实施例6
防腐防锈颜料,由以下重量份的原料制成:
实施例7
防腐防锈颜料,由以下重量份的原料制成:
Claims (4)
1.一种防腐防锈颜料,其特征在于,由以下重量份的原料制成:
2.根据权利要求1所述的防腐防锈颜料,其特征在于,由以下重量份的原料制成:
3.根据权利要求1所述的防腐防锈颜料,其特征在于:所述的超细聚酰亚胺树脂的粒径为10~18μm。
4.根据权利要求1所述的防腐防锈颜料,其特征在于:所述的聚四氟乙烯的粒径为1~5μm。