CN104529355A - 一种干粉弹性拉毛砂浆及制造方法 - Google Patents
一种干粉弹性拉毛砂浆及制造方法 Download PDFInfo
- Publication number
- CN104529355A CN104529355A CN201510029132.1A CN201510029132A CN104529355A CN 104529355 A CN104529355 A CN 104529355A CN 201510029132 A CN201510029132 A CN 201510029132A CN 104529355 A CN104529355 A CN 104529355A
- Authority
- CN
- China
- Prior art keywords
- mortar
- dry powder
- powder
- ether
- defoamer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种新型干粉弹性拉毛砂浆。该弹性拉毛砂浆是一种粉状体,由5-30%水泥、0-5%石灰、50-80%天然石粉填料、2-20%可再分散乳胶粉、0.1-2%促变剂、0.1-0.5%纤维素醚类聚合物、0.1-0.3%憎水剂、0-0.3%木质纤维、0-0.2%润湿剂、0-0.1%缓凝剂、0.1-0.3%消泡剂组成。本发明还公开了干粉弹性拉毛砂浆的制造方法,即将水泥、丙烯酸乳胶粉、天然石粉填料、促变剂等按照在弹性拉毛砂浆中的质量百分比投入螺杆式干粉砂浆搅拌机中搅拌3-15分钟,即获得干粉弹性拉毛砂浆。本发明产品施工后有很强的粘结强度及良好的耐碱性、耐候性,并且无保存及运输麻烦,环保安全。
Description
技术领域
本发明属于建筑装饰新材料技术领域,具体涉及一种干粉弹性拉毛砂浆。
背景技术
弹性拉毛是指对弹性涂料用涂膜拉毛外观的施工方法,得到凹凸起伏的涂膜外观的一种简称。弹性拉毛材料是一种立体花纹涂料,具有极好的装饰性,优良的漆膜机械性能,如硬度、附着性。和面漆配套使用,可提供优异的耐候性、抗碱性、防污性。而且在较宽的温度变化范围内有惊人的回弹性、持久的柔韧性和优良的伸长率,以适应建筑物表面裂缝的产生和运动。通过施工手法的调整,可获得多种装饰效果。特别是人们对内外墙涂料装饰性能要求提高,弹性拉毛涂料越来越受广大用户喜爱。因此必将得到更广泛的应用。
然而,目前市面上应用的都是膏状弹性涂料,产品保存困难,运输麻烦,施工后产品粘结强度低,耐碱性差,耐候性不好,尤其是有VOC等有害物质添加剂,施工时对环境污染严重,尤其是做室内装饰时,产品有害物质影响更大。因此,现有技术有待于更进一步的改进和发展。
发明内容
为了解决现有技术存在的上述问题,本发明提供了一种干粉弹性拉毛砂浆及制造方法,对现有建筑装饰涂料配方进行科学合理的改进,所得产品不仅具有很强的粘结强度及良好的耐碱性、耐候性,并且无保存及运输麻烦,尤其是不含VOC添加剂,无APEO含量,环保安全。
本发明所采用的技术方案为:
本发明提供的弹性拉毛砂浆是一种粉状体,其由如下组分组成:5-30%水泥、0-5%石灰、50-80%天然石粉填料、2-20%可再分散乳胶粉、0.1-2%促变剂、0.1-0.5%纤维素醚类聚合物、0.1-0.3%憎水剂、0-0.3%木质纤维、0-0.2%润湿剂、0-0.1%缓凝剂、0.1-0.3%的粉末消泡剂,其中的百分含量均为质量百分含量。
其中所述水泥为32.5,32.5R,42.5,42.5R,52.5,52.5R强度的白水泥或者灰水泥;其中所述石灰细度在150~800目;本发明所述天然石粉细度为100~300目,是天然碳酸盐类单斜晶系矿物硬石(如方解石)经过精选、加工研磨后形成的粉末,主要成分为含水碳酸钙(CaCO3),其含量不少于95wt%,不但坚固、耐火、耐水、防潮、透气、易清洁,而且无化学和放射性污染、无异味、无静电、不褪色、不老化。
其中所述可再分散乳胶粉为聚丙烯酸类可再分散乳胶粉或者聚乙烯/醋酸乙烯类可再分散乳胶粉,或者为聚丙烯酸类可再分散乳胶粉与聚乙烯/醋酸乙烯类可再分散乳胶粉的任意比例混合物,所选可再分散乳胶粉具有极突出的粘结强度,提高砂浆的柔性并有较长之开放时间,赋予砂浆优良的耐碱性并且能改善砂浆的粘附性/粘合性;其中所述促变剂为膨润土、凹凸棒土、淀粉醚及其改性物质中的一种;其中所述纤维素醚类聚合物为选自甲基羟乙基纤维素醚、羟丙基甲基纤维素醚、乙基羟乙基类纤维素醚中的一种,或者为甲基羟乙基纤维素醚、羟丙基甲基纤维素醚、乙基羟乙基类纤维素醚以任意比例混合所得混合物,粘度为2-15万mPa.s。
其中所述憎水剂为有机硅类、硬脂酸盐类、油酸盐类憎水剂中的一种。
其中所述木质纤维平均长度50μm-600μm,能吸附自重5-8倍的水分,它的结构和特点提高了材料的操作性能,具有很好的保温抗裂作用。
其中所述润湿剂为含水率小于0.5wt%的干粉类润湿剂;其中所述缓凝剂为柠檬酸、柠檬酸盐、酒石酸、酒石酸盐、硼酸、硼酸盐类中的一种,或者为柠檬酸、柠檬酸盐、酒石酸、酒石酸盐、硼酸、硼酸盐类以任意比例混合所得混合物;其中所述消泡剂为选自聚醚型消泡剂、有机硅类消泡剂、非离子类消泡剂中的一种,或者为聚醚型消泡剂、有机硅类消泡剂、非离子类消泡剂以任意比例混合所得混合物。
本发明还提供一种制造干粉弹性拉毛砂浆的方法,将上述组分按照在弹性拉毛砂浆中的质量百分比投入螺杆式干粉砂浆搅拌机中搅拌3-15分钟,即获得干粉弹性拉毛砂浆。本发明中所用的制造干粉弹性拉毛砂浆的方法,不仅速度快、产量高,搅拌无死角、均匀度高,而且所需工艺对温度等环境因素无要求,适合工业化规模生产。
其中所述搅拌机为螺杆卧式干粉砂浆搅拌机或者螺杆立式干粉砂浆搅拌机,所选搅拌机具有分散性好、速度快、产量高,搅拌无死角、均匀度高,占地面积小,能耗低,易操作等特点。
本发明的有益效果为:
(1)与传统弹性中涂产品相比,本发明产品施工后有很强的粘结强度,并且该产品耐紫外线,耐候性好,气温使用范围宽,并具有良好的耐碱性;
(2)本发明制备的干粉弹性拉毛砂浆,具有良好的浸水强度,能显著改善墙体的防水性能;具有良好的柔韧性,抗拉伸能力强,可有效桥连墙体的龟裂,可保证建筑物外墙表面长久的保持清洁华丽的表面;
(3)与传统膏状弹性涂料产品相比,本发明产品为粉状体,无保存及运输麻烦;
(4)本发明产品不含VOC添加剂,无APEO含量,绿色环保,安全无害。
具体实施方式
下面结合具体的实施例对本发明做进一步详细的说明。
实施例1
一种干粉弹性拉毛砂浆,按质量百分比计,其原料配方如下:
42.5强度的白水泥5%,100目天然石粉72%,聚丙烯酸类可再分散乳胶粉20%,凹凸棒土2%,粘度为15万mPa.s的羟丙基甲基纤维素醚0.5%,硬脂酸盐类憎水剂0.3%,有机硅类消泡剂0.2%。
将上述材料按质量百分比投入螺杆卧式干粉砂浆搅拌机中搅拌15min,即获得干粉弹性拉毛砂浆。
实施例2
一种干粉弹性拉毛砂浆,按质量百分比计,其原料配方如下:
32.5R强度的白水泥5%,150目石灰2%,聚乙烯/醋酸乙烯酯乳胶粉20%,300目天然石粉71.59%,膨润土0.3%,粘度为2万mPa.s的羟丙基甲基纤维素醚0.2%,300μm木质纤维0.3%,有机硅憎水剂0.2%,含水量0.3wt%的干粉润湿剂0.1%,柠檬酸缓凝剂0.01%,聚醚型消泡剂0.3%。
将上述材料按质量百分比投入螺杆卧式干粉砂浆搅拌机中搅拌5min,即获得干粉弹性拉毛砂浆。
实施例3
一种干粉弹性拉毛砂浆,按质量百分比计,其原料配方如下:
52.5强度的灰水泥30%,450目石灰5%,聚丙烯酸类可再分散乳胶粉11.9%,200目天然石粉50%,凹凸棒土2%,粘度为15万mPa.s的甲基羟乙基纤维素醚0.5%,600μm木质纤维0.2%,含水量0.4wt%的干粉润湿剂0.2%,有机硅类消泡剂0.2%。
将上述材料按质量百分比投入螺杆立式砂浆搅拌机中搅拌15min,即获得干粉弹性拉毛砂浆。
实施例4
一种干粉弹性拉毛砂浆,按质量百分比计,其原料配方如下:
42.5R强度的白水泥12.1%,800目石灰5%,聚乙烯/醋酸乙烯类可再分散乳胶粉2%,100目天然石粉80%,淀粉醚0.1%,粘度为8万mPa.s的乙基羟乙基类纤维素醚0.1%,50μm木质纤维0.1%,油酸盐憎水剂0.3%,含水量0.1wt%的干粉润湿剂0.15%,硼酸盐缓凝剂0.05%,非离子类消泡剂0.1%。
将上述材料按质量百分比投入螺杆立式砂浆搅拌机中搅拌3min,即获得干粉弹性拉毛砂浆。
实施例5
一种干粉弹性拉毛砂浆,按质量百分比计,其原料配方如下:
32.5强度的灰水泥20%,聚乙烯/醋酸乙烯类可再分散乳胶粉18%,100目天然石粉60%,凹凸棒土1%,粘度为6万mPa.s的乙基羟乙基类纤维素醚0.4%,400μm木质纤维0.3%,硬脂酸盐憎水剂0.1%,酒石酸盐缓凝剂0.1%,有机硅类消泡剂0.1%。
将上述材料按质量百分比投入螺杆立式砂浆搅拌机中搅拌10min,即获得干粉弹性拉毛砂浆。
采用本发明制备的干粉弹性拉毛砂浆与传统膏状弹性涂料性能指标比较如下表1所示。
其中储存温度要求是指干粉弹性拉毛砂浆或者传统膏状弹性涂料的最佳储存温度范围。
其中操作性的评价方法为施工的可操作性,即判定操作是否简单方便,是否产生伤害施工的气体,是否能达到拉毛效果;
其标准如下:
一般:是指操作比较简单,有微量伤害施工的气体产生,基本能达到拉毛效果;
良好:是指操作简单方便,无伤害施工的气体产生,基本能达到拉毛效果。
粘结强度的评价方法为按照JGJ 110-97《建筑外墙用腻子》中6.13粘结强度试验方法进行测定。
浸水强度的评价方法为按照JC/T 907-2002中5.4.4浸水处理的拉伸粘结强度试验步骤测定。
柔韧性的评价方法为按照JGJ 110-97《建筑外墙用腻子》中6.14腻子膜柔韧性的测试方法进行测定。
表1性能测试结果
依据本发明制备的干粉弹性拉毛砂浆,施工后有很强的粘结强度及良好的浸水强度、柔韧性。并且无保存及运输麻烦,尤其是不含VOC添加剂,无APEO含量,环保安全。
本发明不局限于上述最佳实施方式,任何人在本发明的启示下都可得出其他各种形式的产品,但不论在其形状或结构上作任何变化,凡是具有与本申请相同或相近似的技术方案,均落在本发明的保护范围之内。
Claims (8)
1.一种干粉弹性拉毛砂浆,其特征在于:该弹性拉毛砂浆是一种粉状体,其由如下组分组成:5-30%水泥、0-5%石灰、50-80%天然石粉填料、2-20%可再分散乳胶粉、0.1-2%促变剂、0.1-0.5%纤维素醚类聚合物、0.1-0.3%憎水剂、0-0.3%木质纤维、0-0.2%润湿剂、0-0.1%缓凝剂、0.1-0.3%消泡剂,其中的百分含量均为质量百分含量。
2.根据权利要求1所述的干粉弹性拉毛砂浆,其特征在于:所述水泥为32.5,32.5R,42.5,42.5R,52.5,52.5R强度的白水泥或者灰水泥;所述石灰细度在150~800目;所述天然石粉细度为100~300目。
3.根据权利要求1所述的干粉弹性拉毛砂浆,其特征在于:所述可再分散乳胶粉为聚丙烯酸类可再分散乳胶粉或者聚乙烯/醋酸乙烯类可再分散乳胶粉,或者为聚丙烯酸类可再分散乳胶粉与聚乙烯/醋酸乙烯类可再分散乳胶粉的任意比例混合物;所述促变剂为膨润土、凹凸棒土、淀粉醚及其改性物质中的一种;所述纤维素醚类聚合物为选自甲基羟乙基纤维素醚、甲基羟丙基纤维素醚、乙基羟乙基类纤维素醚中的一种,或者为甲基羟乙基纤维素醚、甲基羟丙基纤维素醚、乙基羟乙基类纤维素醚以任意比例混合所得混合物,粘度为2-15万mPa.s。
4.根据权利要求1所述的干粉弹性拉毛砂浆,其特征在于:所述憎水剂为有机硅类、硬脂酸盐类、油酸盐类憎水剂中的一种。
5.根据权利要求1所述的干粉弹性拉毛砂浆,其特征在于:所述木质纤维平均长度为50μm-600μm。
6.根据权利要求1所述的干粉弹性拉毛砂浆,其特征在于:所述润湿剂为含水率小于0.5wt%的干粉类润湿剂;所述缓凝剂为柠檬酸、柠檬酸盐、酒石酸、酒石酸盐、硼酸、硼酸盐类中的一种,或者为柠檬酸、柠檬酸盐、酒石酸、酒石酸盐、硼酸、硼酸盐类以任意比例混合所得混合物;所述消泡剂为选自聚醚型消泡剂、有机硅类消泡剂、非离子类消泡剂中的一种,或者为聚醚型消泡剂、有机硅类消泡剂、非离子类消泡剂以任意比例混合所得混合物。
7.权利要求1-6中任一项所述的一种干粉弹性拉毛砂浆的制造方法,其特征在于:将所述组分按照在弹性拉毛砂浆中的质量百分比投入螺杆式干粉砂浆搅拌机中搅拌3-15分钟,即获得所述干粉弹性拉毛砂浆。
8.根据权利要求7所述的干粉弹性拉毛砂浆的制造方法,其特征在于:所述搅拌机为螺杆卧式干粉砂浆搅拌机或者螺杆立式干粉砂浆搅拌机。