CN104514146A - 一种耐高温涂层绳索的涂层液配比 - Google Patents
一种耐高温涂层绳索的涂层液配比 Download PDFInfo
- Publication number
- CN104514146A CN104514146A CN201310446113.XA CN201310446113A CN104514146A CN 104514146 A CN104514146 A CN 104514146A CN 201310446113 A CN201310446113 A CN 201310446113A CN 104514146 A CN104514146 A CN 104514146A
- Authority
- CN
- China
- Prior art keywords
- rope
- coating
- temperature resistant
- coating liquid
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种耐高温涂层绳索的涂层液配比,由水性聚丙烯酸酯乳液、稀释剂、耐高温环氧树脂、交联剂、消泡剂组成,通过浸渍涂层,在绳索表面形成一层耐高温薄膜,经济实用,安全环保。
Description
技术领域
本发明属于绳索技术领域,具体的说是一种耐高温涂层绳索的涂层液配比。
背景技术
目前,绳索种类繁多,市场应用及其广泛,涉及各个行业和领域。但是,一般化纤绳索常用原料对温度比较敏感,比如涤纶的软化温度在70℃左右,尼龙6和尼龙66的软化温度在60℃左右,聚乙烯绳索的软化温度在80℃左右,丙纶的软化温度在100℃左右,当使用温度高于软化温度时,绳索的机械性能会严重下降,这严重限制了绳索的应用领域。然而一些工业高温作业、消防、安全领域对耐高温绳索需求量较大,普通钢丝绳柔性差,笨重使用不方便,高性能纤维像芳纶,碳纤维虽然耐高温,但是价格昂贵。
发明内容
为解决上述存在的技术问题,本发明提供了一种经济实用、安全环保的耐高温涂层绳索的涂层液配比。。
本发明所技术方案是:耐高温涂层绳索的涂层液配比,按重量百分比由如下组分组成:
水性聚丙烯酸酯乳液 70%--80%;
稀释剂 10%--20%;
耐高温环氧树脂 5%--15%;
交联剂 1%--3%;
消泡剂 0--0.3%。
本发明的有益效果是:本发明以水性聚丙烯酸酯乳液为涂层剂,添加耐高温环氧树脂等成分,通过浸渍涂层,在绳索表面形成一层耐高温薄膜,能够使普通绳索的耐温性能提高到150℃-200℃,经济实用,安全环保,配比科学。
附图说明
图1为本发明的示意图;
图2为图1的截面图。
具体实施方式
下面结合附图和具体实施例对本发明进行详细描述,图1本发明的示意图、图2的截面图所示,本实施例是三股绳,可以直观看到绳索2表面的耐高温涂层1。
耐高温涂层绳索的涂层液配比,按重量百分比由如下组分组成:
水性聚丙烯酸酯乳液 70%--80%;
稀释剂 10%--20%;
耐高温环氧树脂 5%--15%;
交联剂 1%--3%;
消泡剂 0--0.3%。
绳索的加工工艺流程是:绳索经过预处理,采用本发明组成的涂层液进行浸渍涂胶、烘干固化(包括热风干燥、红外干燥、微波干燥),形成具有涂层的绳索。通过涂层加工处理后,形成表面耐高温涂层1,涂层占绳索重量的5%--15%左右。绳索不限原料种类,天然纤维和化纤都可以进行层处理,对绳索的编织结构也没有限制,处理后绳索的耐温性达到150℃-200℃水平。
实施例1:
耐高温涂层绳索的涂层液配比,按重量百分比由如下组分组成:
水性聚丙烯酸酯乳液 75%;
稀释剂 15%;
耐高温环氧树脂 8%;
交联剂 1.9%;
消泡剂 0.1%。
实施例2:
耐高温涂层绳索的涂层液配比,按重量百分比由如下组分组成:
水性聚丙烯酸酯乳液 80%;
稀释剂 10%;
耐高温环氧树脂 6.7%;
交联剂 3%;
消泡剂 0.3%。
实施例3:
耐高温涂层绳索的涂层液配比,按重量百分比由如下组分组成:
水性聚丙烯酸酯乳液 70%%;
稀释剂 20%;
耐高温环氧树脂 7.8%;
交联剂 2%;
消泡剂 0.2%。
实施例4:
耐高温涂层绳索的涂层液配比,按重量百分比由如下组分组成:
水性聚丙烯酸酯乳液 70.8%;
稀释剂 11%;
耐高温环氧树脂 15%;
交联剂 3%;
消泡剂 0.2%。
实施例5:
耐高温涂层绳索的涂层液配比,按重量百分比由如下组分组成:
水性聚丙烯酸酯乳液 74%;
稀释剂 18%;
耐高温环氧树脂 5%;
交联剂 3%;
消泡剂 0%。
市场上现有化纤绳索如涤纶、丙纶、尼龙、超高分子量聚乙烯绳索,热变形温度都在100℃以下,经过本发明浸胶涂层技术处理后,在绳索表面增加了耐温涂层,耐温性能提高30%~50%左右,拓展了绳索的应用领域。
当然,上述说明并非是对本发明的限制,本发明也并不仅限于上述举例,本技术领域的技术人员在本发明的实质范围内所做出的变化,也应属于本发明的保护范围。
Claims (1)
1.一种耐高温涂层绳索的涂层液配比,其特征在于,按重量百分比由如下组分组成:
水性聚丙烯酸酯乳液 70%--80%;
稀释剂 10%--20%;
耐高温环氧树脂 5%--15%;
交联剂 1%--3%;
消泡剂 0--0.3%。