CN104087034A - 一种无机耐高温抗静电涂料 - Google Patents

一种无机耐高温抗静电涂料 Download PDF

Info

Publication number
CN104087034A
CN104087034A CN201410345865.1A CN201410345865A CN104087034A CN 104087034 A CN104087034 A CN 104087034A CN 201410345865 A CN201410345865 A CN 201410345865A CN 104087034 A CN104087034 A CN 104087034A
Authority
CN
China
Prior art keywords
temperature resistant
phosphoric acid
aluminium
inorganic high
phosphate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410345865.1A
Other languages
English (en)
Inventor
关锦池
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201410345865.1A priority Critical patent/CN104087034A/zh
Publication of CN104087034A publication Critical patent/CN104087034A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种无机耐高温抗静电涂料。本涂料包含以下重量含量的组分：硅溶胶5～20％、硼酸2～10％、水20～50％、钛酸酯偶联剂2～5％、导电云母粉8～20％、铝掺杂氧化锌粉体5～10％，余量为磷酸盐。本发明制备的无机耐高温抗静电涂料，其同时具有耐高温和抗静电性能，且其成本低。

Description

一种无机耐高温抗静电涂料
技术领域
本发明涉及一种无机耐高温抗静电涂料，属于无机涂料领域。
背景技术
耐高温抗静电涂层主要用于高热富静电场合下材料的防护，特别适用于超音速天线罩的防护。传统的无机耐高温抗静电涂层兼具良好的耐高温性能和抗静电性能，但无机涂层脆、受热冲击易遭到破坏，此外，现有无机涂层还存在工艺性差、成本高的缺点。
同时随着化工原料的日益上涨，涂料厂都在追求着成本最低化，希望用最低的原材料开发出最优异品质的产品。现市场上耐高温涂料存在于成本高、防腐性能较差等缺陷。
发明内容
为解决上述问题，本发明一种低成本无机耐高温抗静电涂料，其同时具有耐高温和抗静电性能。
一种无机耐高温抗静电涂料，包含以下重量含量的组分：
硅溶胶5～20％、
硼酸2～10％、
水20～50％、
钛酸酯偶联剂2～5％、
导电云母粉8～20％、
铝掺杂氧化锌粉体5～10％，
余量为磷酸盐。
优选的，其中所述磷酸盐由含镁、铝、锌的金属氧化物或金属氢氧化物与磷酸反应得到。
优选的，其中所述磷酸盐为磷酸镁、磷酸二氢镁、磷酸一氢镁、磷酸铝、磷酸二氢铝、磷酸一氢铝、磷酸锌、磷酸二氢锌和磷酸一氢锌中的一种或多种。
优选的，所述无机耐高温抗静电涂料包含以下重量含量的组分：硅溶胶10～15％、硼酸4～8％、水25～40％、钛酸酯偶联剂2～5％、导电云母粉10～15％、铝掺杂氧化锌粉体5～8％，余量为磷酸盐。
优选的，磷酸盐基料至少由下列物质制备而成：(1)一种金属氧化物或金属氢氧化物和磷酸在去离子水中反应，金属氧化物或金属氢氧化物为氢氧化铝、氧化镁、氧化锌，与磷酸在去离子水中反应生成磷酸盐基料。(2)两种金属氧化物或金属氢氧化物和磷酸在去离子水中反应，金属氧化物或金属氢氧化物选自氢氧化铝、氧化镁、氧化锌等，与磷酸在去离子水中反应生成磷酸盐基料。
本发明制备的无机耐高温抗静电涂料，其同时具有耐高温和抗静电性能，且其成本低。
具体实施方式
以下通过具体实施例对本发明进行详细说明，但所描述内容不应视为对本发明的限制，根据本发明思想作出的任何改变和修饰，应视为属于本发明的保护范围。
实施例1
一种无机耐高温抗静电涂料，包含以下重量含量的组分：
硅溶胶5％、
硼酸2％、
水20％、
钛酸酯偶联剂2％、
导电云母粉8％、
铝掺杂氧化锌粉体5％，
余量为磷酸一氢镁。
实施例2
一种无机耐高温抗静电涂料，包含以下重量含量的组分：
硅溶胶10％、
硼酸10％、
水20％、
钛酸酯偶联剂5％、
导电云母粉20％、
铝掺杂氧化锌粉体10％，
余量为磷酸二氢镁。
实施例3
一种无机耐高温抗静电涂料，包含以下重量含量的组分：
硅溶胶5～20％、
硼酸2～10％、
水20～50％、
钛酸酯偶联剂2～5％、
导电云母粉8～20％、
铝掺杂氧化锌粉体5～10％，
余量为磷酸盐。
实施例4
一种无机耐高温抗静电涂料，包含以下重量含量的组分：
硅溶胶20％、
硼酸2％、
水20％、
钛酸酯偶联剂5％、
导电云母粉10％、
铝掺杂氧化锌粉体10％，
余量为磷酸锌。
实施例5
一种无机耐高温抗静电涂料，包含以下重量含量的组分：
硅溶胶20％、
硼酸10％、
水40％、
钛酸酯偶联剂5％、
导电云母粉8％、
铝掺杂氧化锌粉体5％，
余量为磷酸二氢铝。
实施例6
一种无机耐高温抗静电涂料，包含以下重量含量的组分：
硅溶胶20％、
硼酸10％、
水40％、
钛酸酯偶联剂5％、
导电云母粉8％、
铝掺杂氧化锌粉体5％，
余量为磷酸一氢铝。

Claims (4)

1.一种无机耐高温抗静电涂料，包含以下重量含量的组分：硅溶胶5～20％、硼酸2～10％、水20～50％、钛酸酯偶联剂2～5％、导电云母粉8～20％、铝掺杂氧化锌粉体5～10％，余量为磷酸盐。
2.根据权利要求1所述的无机耐高温抗静电涂料，其中所述磷酸盐由含镁、铝、锌的金属氧化物或金属氢氧化物与磷酸反应得到。
3.根据权利要求2所述的无机耐高温抗静电涂料，其中所述磷酸盐为磷酸镁、磷酸二氢镁、磷酸一氢镁、磷酸铝、磷酸二氢铝、磷酸一氢铝、磷酸锌、磷酸二氢锌和磷酸一氢锌中的一种或多种。
4.根据权利要求1所述的无机耐高温抗静电涂料，包含以下重量含量的组分：硅溶胶10～15％、硼酸4～8％、水25～40％、钛酸酯偶联剂2～5％、导电云母粉10～15％、铝掺杂氧化锌粉体5～8％，余量为磷酸盐。
CN201410345865.1A 2014-07-18 2014-07-18 一种无机耐高温抗静电涂料 Pending CN104087034A (zh)