CN104789017A - 耐高温脱粒烘干机用涂料 - Google Patents
耐高温脱粒烘干机用涂料 Download PDFInfo
- Publication number
- CN104789017A CN104789017A CN201510210758.2A CN201510210758A CN104789017A CN 104789017 A CN104789017 A CN 104789017A CN 201510210758 A CN201510210758 A CN 201510210758A CN 104789017 A CN104789017 A CN 104789017A
- Authority
- CN
- China
- Prior art keywords
- parts
- threshing
- dryer
- temperature
- resistant paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种耐高温脱粒烘干机用涂料，该涂料由以下重量份的成份组成：环氧树脂25-38份；偏氯乙烯10-18份；醇酸聚氨酯2-8份；松油2-6份；顺丁烯二酐5-15份；硼酸钡4-18份；二氧化钼4-12份；三聚磷酸铝6-16份；高岭土0.5-3份；轻质碳酸钙1-4份；去离子水8-20份。本发明提供的耐高温脱粒烘干机用涂料，具有优异的防锈和耐磨功能，在长时间的日晒下或高温环境下，仍具有很好的粘结性，能够有效地保护机械设备，延长机械设备的使用寿命。
Description
技术领域
本发明涉及涂料领域，特别地，涉及一种耐高温脱粒烘干机用涂料。
背景技术
机械设备存在于各行各业中，给人们带来了很多的产品和便利，现有的机械涂料，主要作用是降防止机械部件与外界隔离开来，避免机械部件被氧化、腐蚀。
机械设备一般使用金属制成，因此需要做防锈处理。同时，机械设备在使用过程中容易被磨损。目前解决这些问题的方法之一就是涂覆涂料。但是，现有的机械涂料的耐高温性能还不够，在高温和长期日晒的环境下，很容易变质。
发明内容
本发明目的在于提供一种耐高温脱粒烘干机用涂料，以解决现有技术中涂料耐高温性能差，易变质的问题。
为实现上述目的，本发明提供一种耐高温脱粒烘干机用涂料，其中，该涂料由以下重量份的成份组成：
环氧树脂25-38 份；
偏氯乙烯10-18 份；
醇酸聚氨酯2-8 份；
松油2-6 份；
顺丁烯二酐5-15 份；
硼酸钡4-18 份；
二氧化钼4-12 份；
三聚磷酸铝6-16 份；
高岭土0.5-3 份；
轻质碳酸钙1-4 份；以及
去离子水8-20 份。
进一步地，本发明提供一种耐高温脱粒烘干机用涂料，其特征在于；该涂料由以下重量份的成份组成：环氧树脂25份；偏氯乙烯12份；醇酸聚氨酯2份；松油3份；顺丁烯二酐5份；硼酸钡4份；二氧化钼5份；三聚磷酸铝6份；高岭土1份；轻质碳酸钙2份；去离子水10份。
进一步地，本发明提供一种耐高温脱粒烘干机用涂料，其特征在于；该涂料由以下重量份的成份组成：环氧树脂36份；偏氯乙烯16份；醇酸聚氨酯8份；松油5份；顺丁烯二酐13份；硼酸钡14份；二氧化钼10份；三聚磷酸铝15份；高岭土2.5份；轻质碳酸钙4份；去离子水18份。
本发明具有以下有益效果；本发明提供的耐高温脱粒烘干机用涂料，具有优异的防锈和耐磨功能，在长时间的日晒下或高温环境下，仍具有很好的粘结性，能够有效地保护机械设备，延长机械设备的使用寿命。
具体实施方式
本优选实施例提供的一种耐高温脱粒烘干机用涂料，其具体实现过程如下；
本发明提供一种耐高温脱粒烘干机用涂料，其中，该涂料由以下重量份的成份组成：
环氧树脂25-38 份；
偏氯乙烯10-18 份；
醇酸聚氨酯2-8 份；
松油2-6 份；
顺丁烯二酐5-15 份；
硼酸钡4-18 份；
二氧化钼4-12 份；
三聚磷酸铝6-16 份；
高岭土0.5-3 份；
轻质碳酸钙1-4 份；以及
去离子水8-20 份。
实施例1：
其中，该耐高温脱粒烘干机用涂料由以下重量份的成份组成：环氧树脂25份；偏氯乙烯12份；醇酸聚氨酯2份；松油3份；顺丁烯二酐5份；硼酸钡4份；二氧化钼5份；三聚磷酸铝6份；高岭土1份；轻质碳酸钙2份；去离子水10份。
实施例2：
其中，该耐高温脱粒烘干机用涂料由以下重量份的成份组成：环氧树脂36份；偏氯乙烯16份；醇酸聚氨酯8份；松油5份；顺丁烯二酐13份；硼酸钡14份；二氧化钼10份；三聚磷酸铝15份；高岭土2.5份；轻质碳酸钙4份；去离子水18份。
从以上的描述中，可以看出，本发明上述的实施例实现了如下技术效果；
本发明提供的耐高温脱粒烘干机用涂料，具有优异的防锈和耐磨功能，在长时间的日晒下或高温环境下，仍具有很好的粘结性，能够有效地保护机械设备，延长机械设备的使用寿命。
以上所述仅为本发明的优选实施例而已，并不用于限制本发明；对于本领域的技术人员来说，本发明可以有各种更改和变化。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (3)
1.一种耐高温脱粒烘干机用涂料，其特征在于，该涂料由以下重量份的成份组成：
环氧树脂25-38 份；
偏氯乙烯10-18 份；
醇酸聚氨酯2-8 份；
松油2-6 份；
顺丁烯二酐5-15 份；
硼酸钡4-18 份；
二氧化钼4-12 份；
三聚磷酸铝6-16 份；
高岭土0.5-3 份；
轻质碳酸钙1-4 份；以及
去离子水8-20 份。
2.根据权利要求1所述的耐高温脱粒烘干机用涂料，其特征在于；该涂料由以下重量份的成份组成：环氧树脂25份；偏氯乙烯12份；醇酸聚氨酯2份；松油3份；顺丁烯二酐5份；硼酸钡4份；二氧化钼5份；三聚磷酸铝6份；高岭土1份；轻质碳酸钙2份；去离子水10份。
3.根据权利要求1所述的耐高温脱粒烘干机用涂料，其特征在于；该涂料由以下重量份的成份组成：环氧树脂36份；偏氯乙烯16份；醇酸聚氨酯8份；松油5份；顺丁烯二酐13份；硼酸钡14份；二氧化钼10份；三聚磷酸铝15份；高岭土2.5份；轻质碳酸钙4份；去离子水18份。