CN104513988A - 一种环保型气相防锈剂及其制备方法 - Google Patents
一种环保型气相防锈剂及其制备方法 Download PDFInfo
- Publication number
- CN104513988A CN104513988A CN201410697899.7A CN201410697899A CN104513988A CN 104513988 A CN104513988 A CN 104513988A CN 201410697899 A CN201410697899 A CN 201410697899A CN 104513988 A CN104513988 A CN 104513988A
- Authority
- CN
- China
- Prior art keywords
- parts
- add
- oil
- component
- modified additive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种环保型气相防锈剂,其特征是由下述重量份的原料制得:肌醇六磷酸酯2-4,卵磷脂0.3-0.5,樟脑油1-2,香茅油0.5-1,橄榄油1-2,苯甲酸叶醇酯0.5-1,聚甘油蓖麻醇酯1-2,海藻胶1-2,丙三醇2-4,壳聚糖6-8,三乙醇胺2-4,三聚磷酸钠6-8,改性助剂4-6,水40-50。本发明的防锈剂兼具接触防锈和气相防锈的功效,且采用绿色环保的原料,在生产、制造、使用过程中对环境污染小,环境效益高。
Description
技术领域
本发明涉及金属处理领域,具体涉及一种环保型气相防锈剂及其制备方法。
背景技术
金属加工件在生产加工及运输的过程中容易生锈,而一旦发生锈蚀,不仅影响外观和功能,甚至有可能造成资源浪费。防锈剂是加入到介质中以达到金属防锈目的的化学药剂,能在部件表面上形成一层保护膜,抑制湿气及其它化学成分造成的腐蚀。然而,有些金属工件具有弯曲的小孔等涂油防锈难以达到的部位,气相防锈剂对此具有特殊的防护效果。气相防锈剂的原理是通过自动不断的升华,挥发成气体,当这种气体达到饱和状态时就能对钢铁等金属实行防锈保护。气相防锈剂具有防锈保护期长久、能提供无孔不入的保护的特点,它的使用保护和去除非常方便,环境负担小,用途十分广泛。
发明内容
本发明的目的是提供一种环保型气相防锈剂。
本发明是通过以下技术方案实现的:
一种环保型气相防锈剂,其特征在于,其是由下述重量份的原料制得:
肌醇六磷酸酯2-4,卵磷脂0.3-0.5,樟脑油1-2,香茅油0.5-1,橄榄油1-2,苯甲酸叶醇酯0.5-1,聚甘油蓖麻醇酯1-2,海藻胶1-2,丙三醇2-4,壳聚糖6-8,三乙醇胺2-4,三聚磷酸钠6-8,改性助剂4-6,水40-50;
其中改性助剂由下列重量份的原料制成:
麦饭石粉5-10,硅藻土3-5,十二烷基三甲基氯化铵0.3-0.5,茶树油0.2-0.4,单宁酸0.1-0.2,生育酚0.05-0.1,肉豆蔻酸异丙酯0.1-0.2;
改性助剂的制备方法是:
将麦饭石粉和硅藻土混合后300-400℃处理5-8h,冷却后研磨均匀,加入单宁酸、生育酚和适量无水乙醇后超声分散10-15min,再加入其余原料400-600r/min搅拌0.5-1h,过滤并真空干燥,再次研磨均匀,过1000-1250目筛,即得。
一种环保型气相防锈剂的制备方法,其特征在于,包括以下步骤:
(1)将樟脑油、香茅油、橄榄油和卵磷脂混合后搅拌均匀,再加入苯甲酸叶醇酯和聚甘油蓖麻醇酯,35-40℃、400-600r/min搅拌10-20min,最后加入三聚磷酸钠和1/4-1/3量的水,同样条件下搅拌0.5-1h,得组分A;
(2)在余量的水中加入醋酸配制成1-1.5%的醋酸溶液,加入壳聚糖溶解完全,加入海藻胶和丙三醇40-60℃、800-1000r/min搅拌0.5-1h,冷却后加入三乙醇胺和肌醇六磷酸酯,得组分B;
(3)将组分A加入组分B中并500-600r/min搅拌15-30min,再加入改性助剂超声分散5-10min,分装后即得。
本发明的优点是:
1. 本发明的防锈剂兼具接触防锈和气相防锈的功效,防锈蚀效果好,防锈持续时间长,且采用绿色环保的原料,在生产、制造、使用过程中对环境污染小,环境效益高;
2. 结合微胶囊技术制得气相防锈剂,具有缓释的特点,且能通过改变外界条件的方式调整防锈剂的释放速度,适用于既要求水性防锈、又要求密封空间气相防锈的场合。
具体实施方式
本发明非限定实施例如下:
一种环保型气相防锈剂,由下列重量(kg)的组分原料制备而成:
肌醇六磷酸酯3,卵磷脂0.4,樟脑油1.5,香茅油0.6,橄榄油1.5,苯甲酸叶醇酯0.6,聚甘油蓖麻醇酯1.5,海藻胶1.5,丙三醇3,壳聚糖7,三乙醇胺3,三聚磷酸钠7,改性助剂5,水45;
其中,改性助剂由下列重量(kg)的原料制成:
麦饭石粉8,硅藻土4,十二烷基三甲基氯化铵0.4,茶树油0.3,单宁酸0.15,生育酚0.08,肉豆蔻酸异丙酯0.15;
改性助剂的制备方法:
将麦饭石粉和硅藻土混合后400℃处理6h,冷却后研磨均匀,加入单宁酸、生育酚和适量无水乙醇后超声分散15min,再加入其余原料600r/min搅拌0.5h,过滤并真空干燥,再次研磨均匀,过1000目筛,即得。
环保型气相防锈剂的制备方法包括以下步骤:
(1)将樟脑油、香茅油、橄榄油和卵磷脂混合后搅拌均匀,再加入苯甲酸叶醇酯和聚甘油蓖麻醇酯,40℃、600r/min搅拌20min,最后加入三聚磷酸钠和1/4量的水,同样条件下搅拌0.5h,得组分A;
(2)在余量的水中加入醋酸配制成1%的醋酸溶液,加入壳聚糖溶解完全,加入海藻胶和丙三醇60℃、1000r/min搅拌0.5h,冷却后加入三乙醇胺和肌醇六磷酸酯,得组分B;
(3)将组分A加入组分B中并600r/min搅拌15min,再加入改性助剂超声分散5min,分装后即得。
经检验,本实施例产品对试片45号钢的湿热试验10天合格,盐雾试验7天合格。
Claims (2)
1.一种环保型气相防锈剂,其特征在于,其是由下述重量份的原料制得:
肌醇六磷酸酯2-4,卵磷脂0.3-0.5,樟脑油1-2,香茅油0.5-1,橄榄油1-2,苯甲酸叶醇酯0.5-1,聚甘油蓖麻醇酯1-2,海藻胶1-2,丙三醇2-4,壳聚糖6-8,三乙醇胺2-4,三聚磷酸钠6-8,改性助剂4-6,水40-50;
所述改性助剂由下列重量份的原料制成:
麦饭石粉5-10,硅藻土3-5,十二烷基三甲基氯化铵0.3-0.5,茶树油0.2-0.4,单宁酸0.1-0.2,生育酚0.05-0.1,肉豆蔻酸异丙酯0.1-0.2;
所述改性助剂的制备方法是:
将麦饭石粉和硅藻土混合后300-400℃处理5-8h,冷却后研磨均匀,加入单宁酸、生育酚和适量无水乙醇后超声分散10-15min,再加入其余原料400-600r/min搅拌0.5-1h,过滤并真空干燥,再次研磨均匀,过1000-1250目筛,即得。
2.根据权利要求1所述的一种环保型气相防锈剂的制备方法,其特征在于,包括以下步骤:
(1)将樟脑油、香茅油、橄榄油和卵磷脂混合后搅拌均匀,再加入苯甲酸叶醇酯和聚甘油蓖麻醇酯,35-40℃、400-600r/min搅拌10-20min,最后加入三聚磷酸钠和1/4-1/3量的水,同样条件下搅拌0.5-1h,得组分A;
(2)在余量的水中加入醋酸配制成1-1.5%的醋酸溶液,加入壳聚糖溶解完全,加入海藻胶和丙三醇40-60℃、800-1000r/min搅拌0.5-1h,冷却后加入三乙醇胺和肌醇六磷酸酯,得组分B;
(3)将组分A加入组分B中并500-600r/min搅拌15-30min,再加入改性助剂超声分散5-10min,分装后即得。