CN105132920A - 一种钢铁用气相防锈剂及其制备方法 - Google Patents
一种钢铁用气相防锈剂及其制备方法 Download PDFInfo
- Publication number
- CN105132920A CN105132920A CN201510603167.1A CN201510603167A CN105132920A CN 105132920 A CN105132920 A CN 105132920A CN 201510603167 A CN201510603167 A CN 201510603167A CN 105132920 A CN105132920 A CN 105132920A
- Authority
- CN
- China
- Prior art keywords
- parts
- add
- component
- vapor phase
- iron
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种钢铁用气相防锈剂,制备该防锈剂所需的原料包括如下重量分数的组分:苯甲酸单乙醇胺5~10份,癸二酸二辛酯2~5份,白矿油1~3份,棉籽油3~6份,肉桂酸苄酯5~8份,山梨酸钾0.5~1.5份,壳聚糖1~5份,聚乙二醇5~8份,聚丙烯酸钠3~7份,季戊四醇油酸酯1~2份,8-羟基喹啉1~2份,乙二胺四乙酸二钠6~8份,改性助剂8~10份,水40~50份。本发明的防锈剂兼具接触防锈和气相防锈的功效,对钢铁工件的防锈效果好,持续时间长,且具有缓释、控释的效应,适用于既要求水性防锈、又要求密封空间气相防锈的场合。
Description
技术领域
本发明涉及金属处理领域,尤其涉及一种钢铁用气相防锈剂;本发明还涉及一种钢铁用气相防锈剂的制备方法。
背景技术
金属加工件在生产加工及运输的过程中容易生锈,而一旦发生锈蚀,不仅影响外观和功能,甚至有可能造成资源浪费。防锈剂是加入到介质中以达到金属防锈目的的化学药剂,能在部件表面上形成一层保护膜,抑制湿气及其它化学成分造成的腐蚀。然而,有些金属工件具有弯曲的小孔等涂油防锈难以达到的部位,气相防锈剂对此具有特殊的防护效果。气相防锈剂的原理是通过自动不断的升华,挥发成气体,当这种气体达到饱和状态时就能对钢铁等金属实行防锈保护。气相防锈剂具有防锈保护期长久、能提供无孔不入的保护的特点,它的使用保护和去除非常方便,环境负担小,用途十分广泛。
发明内容
本发明所要解决的技术问题是针对技术现状提供一种防锈保护期长、能提供无孔不入保护的钢铁用气相防锈剂。
本发明所要解决的第二个技术问题是提供一种钢铁用气相防锈剂的制备方法。
本发明解决上述第一个技术问题所采用的技术方案为:一种钢铁用气相防锈剂,制备所需的原料包括如下重量分数的组分:苯甲酸单乙醇胺5~10份,癸二酸二辛酯2~5份,白矿油1~3份,棉籽油3~6份,肉桂酸苄酯5~8份,山梨酸钾0.5~1.5份,壳聚糖1~5份,聚乙二醇5~8份,聚丙烯酸钠3~7份,季戊四醇油酸酯1~2份,8-羟基喹啉1~2份,乙二胺四乙酸二钠6~8份,改性助剂8~10份,水40~50份。
其中,制备所述改性助剂的原料包括如下重量份数的组分:麦饭石粉1~5份,硅藻土6~8份,十二烷基三甲基氯化铵1~1.5份,茶树油0.1~0.5份,单宁酸0.1~0.2份,生育酚0.05~0.1份,肉豆蔻酸异丙酯0.1~0.2份。
其中,所述改性助剂通过如下方法制备而得:将麦饭石粉和硅藻土混合后300~400℃处理5~8h,冷却后研磨均匀,加入单宁酸、生育酚和适量无水乙醇后超声分散10~15min,再加入其余原料400~600r/min搅拌0.5~1h,过滤并真空干燥,再次研磨均匀,过1000~1250目筛,即得。
本发明解决上述第二个技术问题所采用的技术方案为:一种所述的钢铁用气相防锈剂的制备方法,包括如下步骤:
(1)将白矿油、棉籽油和肉桂酸苄酯混合后搅拌均匀,再加入苯甲酸单乙醇胺、8-羟基喹啉、癸二酸二辛酯和季戊四醇油酸酯,35~40℃、400~600r/min搅拌10~20min,最后加入山梨酸钾、乙二胺四乙酸二钠、聚丙烯酸钠和1/4~1/3量的水,同样条件下搅拌0.5~1h,得组分A;
(2)在余量的水中加入醋酸配制成1~1.5%的醋酸溶液,加入壳聚糖溶解完全,加入聚乙二醇40~60℃、800~1000r/min搅拌0.5~1h,得组分B;
(3)将组分A加入组分B中并500~600r/min搅拌15~30min,再加入改性助剂超声分散5~10min,分装后即得。
与现有技术相比,本发明的优点在于:一方面,通过配方与工艺的改进,使防锈剂兼具接触防锈和气相防锈的功效,对钢铁工件具有优良的防锈作用,防锈持续时间长;另一方面,结合微胶囊技术制得气相防锈剂,具有缓释的特点,且能通过改变外界条件的方式调整防锈剂的释放速度,适用于既要求水性防锈、又要求密封空间气相防锈的场合。
具体实施方式
以下结合实施例对本发明作进一步详细描述。
实施例1
制备本实施例的钢铁用气相防锈剂所需的原料由如下重量分数的组分组成:苯甲酸单乙醇胺5份,癸二酸二辛酯2份,白矿油1份,棉籽油3份,肉桂酸苄酯5份,山梨酸钾0.5份,壳聚糖1份,聚乙二醇5份,聚丙烯酸钠3份,季戊四醇油酸酯1份,8-羟基喹啉1份,乙二胺四乙酸二钠6份,改性助剂8份,水40份。
其中,制备改性助剂的原料由如下重量份数的组分组成:麦饭石粉1份,硅藻土6份,十二烷基三甲基氯化铵1份,茶树油0.1份,单宁酸0.1份,生育酚0.05份,肉豆蔻酸异丙酯0.1份。
其中,改性助剂通过如下方法制备而得:将麦饭石粉和硅藻土混合后300~400℃处理5~8h,此处的温度与时间的选择只需满足两者充分溶解混合即可,冷却后研磨均匀,加入单宁酸、生育酚和适量无水乙醇后超声分散10~15min,再加入其余原料400~600r/min搅拌0.5~1h,过滤并真空干燥,再次研磨均匀,过1000~1250目筛,即得。
本实施例的钢铁用气相防锈剂的制备方法包括如下步骤:
(1)将白矿油、棉籽油和肉桂酸苄酯混合后搅拌均匀,再加入苯甲酸单乙醇胺、8-羟基喹啉、癸二酸二辛酯和季戊四醇油酸酯,35℃、400r/min搅拌10min,最后加入山梨酸钾、乙二胺四乙酸二钠、聚丙烯酸钠和1/4量的水,同样条件下搅拌0.5h,得组分A;
(2)在余量的水中加入醋酸配制成1%(质量分数)的醋酸溶液,加入壳聚糖溶解完全,加入聚乙二醇40℃、800r/min搅拌0.5h,得组分B;
(3)将组分A加入组分B中并500r/min搅拌15min,再加入改性助剂超声分散5min,分装后即得。
实施例2
本实施例的钢铁用气相防锈剂,在制备时所需的原料由如下重量分数的组分组成:苯甲酸单乙醇胺8份,癸二酸二辛酯3份,白矿油2份,棉籽油5份,肉桂酸苄酯6份,山梨酸钾1份,壳聚糖3份,聚乙二醇6份,聚丙烯酸钠5份,季戊四醇油酸酯1.5份,8-羟基喹啉1.5份,乙二胺四乙酸二钠7份,改性助剂9份,水45份。
制备改性助剂的原料包括如下重量份数的组分:麦饭石粉3份,硅藻土7份,十二烷基三甲基氯化铵1.2份,茶树油0.5份,单宁酸0.2份,生育酚0.05份,肉豆蔻酸异丙酯0.15份。
改性助剂的制备方法参考实施例1。
本实施例钢铁用气相防锈剂的制备方法包括如下步骤:
(1)将白矿油、棉籽油和肉桂酸苄酯混合后搅拌均匀,再加入苯甲酸单乙醇胺、8-羟基喹啉、癸二酸二辛酯和季戊四醇油酸酯,38℃、500r/min搅拌15min,最后加入山梨酸钾、乙二胺四乙酸二钠、聚丙烯酸钠和1/3量的水,同样条件下搅拌0.7h,得组分A;
(2)在余量的水中加入醋酸配制成1.2%的醋酸溶液,加入壳聚糖溶解完全,加入聚乙二醇50℃、900r/min搅拌0.8h,得组分B;
(3)将组分A加入组分B中并550r/min搅拌20min,再加入改性助剂超声分散8min,分装后即得。
实施例3
本实施例的钢铁用气相防锈剂,在制备时所需的原料由如下重量分数的组分组成:苯甲酸单乙醇胺10份,癸二酸二辛酯5份,白矿油3份,棉籽油6份,肉桂酸苄酯8份,山梨酸钾1.5份,壳聚糖5份,聚乙二醇8份,聚丙烯酸钠7份,季戊四醇油酸酯2份,8-羟基喹啉2份,乙二胺四乙酸二钠8份,改性助剂10份,水50份。
制备改性助剂的原料由如下重量份数的组分组成:麦饭石粉5份,硅藻土8份,十二烷基三甲基氯化铵1.5份,茶树油0.5份,单宁酸0.2份,生育酚0.1份,肉豆蔻酸异丙酯0.2份。
改性助剂的制备方法参考实施例1。
本实施例钢铁用气相防锈剂的制备方法包括如下步骤:
(1)将白矿油、棉籽油和肉桂酸苄酯混合后搅拌均匀,再加入苯甲酸单乙醇胺、8-羟基喹啉、癸二酸二辛酯和季戊四醇油酸酯,40℃、600r/min搅拌20min,最后加入山梨酸钾、乙二胺四乙酸二钠、聚丙烯酸钠和1/3量的水,同样条件下搅拌1h,得组分A;
(2)在余量的水中加入醋酸配制成1.5%的醋酸溶液,加入壳聚糖溶解完全,加入聚乙二醇60℃、1000r/min搅拌1h,得组分B;
(3)将组分A加入组分B中并600r/min搅拌30min,再加入改性助剂超声分散10min,分装后即得。
以上内容仅为本发明的较佳实施例,对于本领域的普通技术人员,依据本发明的思想,在具体实施方式及应用范围上均会有改变之处,本说明书内容不应理解为对本发明的限制。
Claims (4)
1.一种钢铁用气相防锈剂,其特征在于,制备所需的原料包括如下重量分数的组分:苯甲酸单乙醇胺5~10份,癸二酸二辛酯2~5份,白矿油1~3份,棉籽油3~6份,肉桂酸苄酯5~8份,山梨酸钾0.5~1.5份,壳聚糖1~5份,聚乙二醇5~8份,聚丙烯酸钠3~7份,季戊四醇油酸酯1~2份,8-羟基喹啉1~2份,乙二胺四乙酸二钠6~8份,改性助剂8~10份,水40~50份。
2.根据权利要求1所述的钢铁用气相防锈剂,其特征在于,制备所述改性助剂的原料包括如下重量份数的组分:麦饭石粉1~5份,硅藻土6~8份,十二烷基三甲基氯化铵1~1.5份,茶树油0.1~0.5份,单宁酸0.1~0.2份,生育酚0.05~0.1份,肉豆蔻酸异丙酯0.1~0.2份。
3.根据权利要求2所述的钢铁用气相防锈剂,其特征在于,所述改性助剂通过如下方法制备而得:将麦饭石粉和硅藻土混合后300~400℃处理5~8h,冷却后研磨均匀,加入单宁酸、生育酚和适量无水乙醇后超声分散10~15min,再加入其余原料400~600r/min搅拌0.5~1h,过滤并真空干燥,再次研磨均匀,过1000~1250目筛,即得。
4.一种权利要求1所述的钢铁用气相防锈剂的制备方法,其特征在于,包括如下步骤:
(1)按配比将白矿油、棉籽油和肉桂酸苄酯混合后搅拌均匀,再加入苯甲酸单乙醇胺、8-羟基喹啉、癸二酸二辛酯和季戊四醇油酸酯,35~40℃、400~600r/min搅拌10~20min,最后加入山梨酸钾、乙二胺四乙酸二钠、聚丙烯酸钠和1/4~1/3量的水,同样条件下搅拌0.5~1h,得组分A;
(2)在余量的水中加入醋酸配制成1~1.5%的醋酸溶液,按配比加入壳聚糖溶解完全,按配比加入聚乙二醇40~60℃、800~1000r/min搅拌0.5~1h,得组分B;
(3)将组分A加入组分B中并500~600r/min搅拌15~30min,再按配比加入改性助剂超声分散5~10min,分装后即得。