CN104497918A - 一种含有竹炭粉透气性铅笔杆制备用热熔胶 - Google Patents

一种含有竹炭粉透气性铅笔杆制备用热熔胶 Download PDF

Info

Publication number
CN104497918A
CN104497918A CN201410793421.4A CN201410793421A CN104497918A CN 104497918 A CN104497918 A CN 104497918A CN 201410793421 A CN201410793421 A CN 201410793421A CN 104497918 A CN104497918 A CN 104497918A
Authority
CN
China
Prior art keywords
parts
hot melt
melt adhesive
bamboo charcoal
charcoal powder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410793421.4A
Other languages
English (en)
Inventor
李成功
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201410793421.4A priority Critical patent/CN104497918A/zh
Publication of CN104497918A publication Critical patent/CN104497918A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种含有竹炭粉透气性铅笔杆制备用热熔胶，其是由下述重量份的原料制得：EVA50-55、叔丁基酚醛树脂204 25-38、石蜡6-8、聚二甲基硅氧烷4-8，聚氨酯树脂2-4、聚己二酸1-2、HIPS 2-4、抗氧剂DLTP 1-2、氢氧化钠 3-5、竹炭粉1-2、环氧硬脂酸辛酯 0.2-0.4、烟片胶1-2、丁苯橡胶2-4、N-甲基-2-吡咯烷酮 2-4、磷酸酐 1-2、叔十二烷基硫醇 1-2、己二胺2-4、复合改性树脂10-20；本发明热熔胶采用新配方原料组合,不仅提高了热熔胶透气性，同时增加了热熔胶粘结强度,可以完全满足铅笔杆制备胶合过程中对热熔胶性能的要求。

Description

一种含有竹炭粉透气性铅笔杆制备用热熔胶
技术领域
本发明属粘结剂领域，尤其涉及一种含有竹炭粉透气性铅笔杆制备用热熔胶。
背景技术
铅笔杆用料主要包括木材和胶合剂。木材用于制作笔杆，要求纹理正直，结构细而匀，质软或稍软，略带脆性，少含树脂，吸湿性低，胀缩性小，不变形。主要有铅笔柏(红柏)、香杉、西达木、椴木、桤木等。胶合剂应有适当粘度、流动性和润湿性，硬化后胶层有韧性，对刀具损伤小，具有一定耐水、耐热、耐老化性能，常温下易固化，硬化时间短，无毒等。主要有动物胶、聚酯酸乙烯乳液、热熔胶等。
发明内容
本发明的目的是提供一种含有竹炭粉透气性铅笔杆制备用热熔胶。
为了实现上述目的本发明采用如下技术方案：
一种含有竹炭粉透气性铅笔杆制备用热熔胶，其特征在于，其是由下述重量份的原料制得：EVA50-55、叔丁基酚醛树脂204  25-38、石蜡6-8、聚二甲基硅氧烷4-8，聚氨酯树脂2-4、聚己二酸1-2、HIPS 2-4、抗氧剂DLTP 1-2、氢氧化钠 3-5、竹炭粉1-2、环氧硬脂酸辛酯 0.2-0.4、烟片胶1-2、丁苯橡胶2-4、N-甲基-2-吡咯烷酮 2-4、磷酸酐 1-2、叔十二烷基硫醇 1-2、己二胺2-4、复合改性树脂10-20；
所述的复合改性树脂由下述重量份的原料制备而得：
酚醛树脂10-20、达玛树脂30-40、二氯化钙1-2、硼砂1-2、膨润土2-4、聚碳酸酯1-2、氰尿酸三聚氰胺1-2、石油磺酸钡0.3-0.5、乙二醇单甲醚0.1-0.2、抗氧剂626 1-2、椰子油脂肪酸二乙醇酰胺 1-2、山梨坦单油酸酯 0.1-0.2、单硬脂酸甘油酯1-2、富马酸1-2；
所述的复合改性树脂的制备方法为：
（1）将达玛树脂、二氯化钙、硼砂、膨润土、聚碳酸酯、氰尿酸三聚氰胺、石油磺酸钡混匀后，于捏合机中120-140℃捏合20-30min，取出冷却，得改性达玛树脂料备用；
（2）将改性达玛树脂料与其余原料混匀后，于捏合机中150-160℃捏合20-30min，取出冷却，即得。
所述的一种含有竹炭粉透气性铅笔杆制备用热熔胶，其特征在于：
制备方法为：
（1）将氢氧化钠 、竹炭粉、环氧硬脂酸辛酯加适量水混匀，于38-42℃下搅拌20-25分钟后，烘干，得改性竹炭粉备用；
（2）将叔丁基酚醛树脂、石蜡、抗氧剂DLTP、叔十二烷基硫醇混匀后，于捏合机中140-150℃捏合15-25min，取出冷却，得树脂料备用；
（3）将改性填料、树脂料、以及其余原料混匀，双螺杆挤出机挤出造粒即得。
本发明的有益效果：
本发明热熔胶采用新配方原料组合,通过添加竹炭粉，增加孔隙，不仅提高了热熔胶透气性，同时增加了热熔胶粘结强度,可以完全满足铅笔杆制备胶合过程中对热熔胶性能的要求。
具体实施方式、
一种含有竹炭粉透气性铅笔杆制备用热熔胶，其是由下述重量（kg）的原料制得：EVA55、叔丁基酚醛树脂204  38、石蜡8、聚二甲基硅氧烷8，聚氨酯树脂4、聚己二酸1、HIPS  4、抗氧剂DLTP 1、氢氧化钠5、竹炭粉2、环氧硬脂酸辛酯0.4、烟片胶2、丁苯橡胶4、N-甲基-2-吡咯烷酮4、磷酸酐 1、叔十二烷基硫醇2、己二胺2、复合改性树脂20；
所述的复合改性树脂由下述重量（kg）的原料制备而得：
酚醛树脂10、达玛树脂40、二氯化钙2、硼砂1、膨润土2、聚碳酸酯1、氰尿酸三聚氰胺1、石油磺酸钡0.3、乙二醇单甲醚0.1、抗氧剂626   1、椰子油脂肪酸二乙醇酰胺 1、山梨坦单油酸酯0.2、单硬脂酸甘油酯1、富马酸1；
所述的复合改性树脂的制备方法为：
（1）将达玛树脂、二氯化钙、硼砂、膨润土、聚碳酸酯、氰尿酸三聚氰胺、石油磺酸钡混匀后，于捏合机中120℃捏合25min，取出冷却，得改性达玛树脂料备用；
（2）将改性达玛树脂料与其余原料混匀后，于捏合机中152℃捏合30min，取出冷却，即得。
所述的一种含有竹炭粉透气性铅笔杆制备用热熔胶，
制备方法为：
（1）将氢氧化钠 、竹炭粉、环氧硬脂酸辛酯加适量水混匀，于42℃下搅拌20分钟后，烘干，得改性竹炭粉备用；
（2）将叔丁基酚醛树脂、石蜡、抗氧剂DLTP、叔十二烷基硫醇混匀后，于捏合机中150℃捏合18min，取出冷却，得树脂料备用；
（3）将改性填料、树脂料、以及其余原料混匀，双螺杆挤出机挤出造粒即得。
本实施例的热熔胶主要技术指标检测如下：
本实施例的热熔胶的表观粘度为5000MPa.s，剥离强度66N/2.5cm，初粘力达到5号钢球，开放时间39s，24小时热稳定性状稳定。

Claims (2)

1.一种含有竹炭粉透气性铅笔杆制备用热熔胶，其特征在于，其是由下述重量份的原料制得：EVA50-55、叔丁基酚醛树脂204  25-38、石蜡6-8、聚二甲基硅氧烷4-8，聚氨酯树脂2-4、聚己二酸1-2、HIPS 2-4、抗氧剂DLTP 1-2、氢氧化钠 3-5、竹炭粉1-2、环氧硬脂酸辛酯 0.2-0.4、烟片胶1-2、丁苯橡胶2-4、N-甲基-2-吡咯烷酮 2-4、磷酸酐 1-2、叔十二烷基硫醇 1-2、己二胺2-4、复合改性树脂10-20；
所述的复合改性树脂由下述重量份的原料制备而得：
酚醛树脂10-20、达玛树脂30-40、二氯化钙1-2、硼砂1-2、膨润土2-4、聚碳酸酯1-2、氰尿酸三聚氰胺1-2、石油磺酸钡0.3-0.5、乙二醇单甲醚0.1-0.2、抗氧剂626 1-2、椰子油脂肪酸二乙醇酰胺 1-2、山梨坦单油酸酯 0.1-0.2、单硬脂酸甘油酯1-2、富马酸1-2；
所述的复合改性树脂的制备方法为：
将达玛树脂、二氯化钙、硼砂、膨润土、聚碳酸酯、氰尿酸三聚氰胺、石油磺酸钡混匀后，于捏合机中120-140℃捏合20-30min，取出冷却，得改性达玛树脂料备用；
（2）将改性达玛树脂料与其余原料混匀后，于捏合机中150-160℃捏合20-30min，取出冷却，即得。
2.根据权利要求1所述的一种含有竹炭粉透气性铅笔杆制备用热熔胶，其特征在于：
制备方法为：
（1）将氢氧化钠 、竹炭粉、环氧硬脂酸辛酯加适量水混匀，于38-42℃下搅拌20-25分钟后，烘干，得改性竹炭粉备用；
（2）将叔丁基酚醛树脂、石蜡、抗氧剂DLTP、叔十二烷基硫醇混匀后，于捏合机中140-150℃捏合15-25min，取出冷却，得树脂料备用；
（3）将改性填料、树脂料、以及其余原料混匀，双螺杆挤出机挤出造粒即得。
CN201410793421.4A 2014-12-20 2014-12-20 一种含有竹炭粉透气性铅笔杆制备用热熔胶 Pending CN104497918A (zh)