CN104178084A - 一种抗菌效果优异的铅笔制造用热熔胶 - Google Patents
一种抗菌效果优异的铅笔制造用热熔胶 Download PDFInfo
- Publication number
- CN104178084A CN104178084A CN201410352005.0A CN201410352005A CN104178084A CN 104178084 A CN104178084 A CN 104178084A CN 201410352005 A CN201410352005 A CN 201410352005A CN 104178084 A CN104178084 A CN 104178084A
- Authority
- CN
- China
- Prior art keywords
- parts
- melt adhesive
- resin
- hot
- take out
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种抗菌效果优异的铅笔制造用热熔胶,其是由下述重量份的原料制得:松香20-30、C5石油树脂15-25、巴西棕榈蜡1-2、环氧硬脂酸辛酯1-2、三元已丙橡胶10-15、松香季戊四醇酯2-4、戊二酸1-2、硼酸1-2、脲醛树脂3-5、羧甲基玉米粉1-2、羟基磷灰石2-4、羊毛脂0.1-0.4、硬脂酸铝0.2-0.4、苯乙醇胺0.1-0.2、硅烷偶联剂KH5701-2,复合改性树脂3-5;本发明热熔胶采用新配方组合,不仅提高了热熔胶的耐寒性,同时增加了热熔胶接着强度,可以完全满足铅笔制造对热熔胶性能的要求,同时添加了一些抗菌物质,增加了抗菌的效果。
Description
技术领域
本发明属粘结剂领域,尤其涉及一种抗菌效果优异的铅笔制造用热熔胶。
背景技术
铅笔杆用料主要包括木材和胶合剂。木材用于制作笔杆,要求纹理正直,结构细而匀,质软或稍软,略带脆性,少含树脂,吸湿性低,胀缩性小,不变形。主要有铅笔柏(红柏)、香杉、西达木、椴木、桤木等。胶合剂应有适当粘度、流动性和润湿性,硬化后胶层有韧性,对刀具损伤小,具有一定耐水、耐热、耐老化性能,常温下易固化,硬化时间短,无毒等。主要有动物胶、聚酯酸乙烯乳液、热熔胶等。
发明内容
本发明的目的是提供一种抗菌效果优异的铅笔制造用热熔胶。
为了实现上述目的本发明采用如下技术方案:
一种抗菌效果优异的铅笔制造用热熔胶,其特征在于,其是由下述重量份的原料制得:松香20-30、C5石油树脂15-25、巴西棕榈蜡1-2、环氧硬脂酸辛酯1-2、三元已丙橡胶10-15、松香季戊四醇酯2-4、戊二酸1-2、硼酸1-2、脲醛树脂3-5、羧甲基玉米粉1-2、羟基磷灰石2-4、羊毛脂0.1-0.4、硬脂酸铝0.2-0.4、苯乙醇胺0.1-0.2、硅烷偶联剂KH570 1-2,复合改性树脂3-5;
所述的复合改性树脂由下述重量份的原料制备而得:
酚醛树脂10-20、达玛树脂30-40、二氯化钙1-2、硼砂1-2、膨润土2-4、聚碳酸酯1-2、氰尿酸三聚氰胺1-2、石油磺酸钡0.3-0.5、乙二醇单甲醚0.1-0.2、抗氧剂626 1-2、椰子油脂肪酸二乙醇酰胺 1-2、山梨坦单油酸酯 0.1-0.2、单硬脂酸甘油酯1-2、富马酸1-2;
所述的复合改性树脂的制备方法为:
(1)将达玛树脂、二氯化钙、硼砂、膨润土、聚碳酸酯、氰尿酸三聚氰胺、石油磺酸钡混匀后,于捏合机中120-140℃捏合20-30min,取出冷却,得改性达玛树脂料备用;
(2)将改性达玛树脂料与其余原料混匀后,于捏合机中150-160℃捏合20-30min,取出冷却,即得。
所述的一种抗菌效果优异的铅笔制造用热熔胶,其特征在于:制备方法包括以下步骤:
(1)将羟基磷灰石于700-800℃下煅烧1-2小时,取出冷却后,破碎,加适量水,再加入戊二酸、硬脂酸铝,于60-80℃下搅拌1-2小时后,烘干,得改性填料备用;
(2)将C5石油树脂、环氧硬脂酸辛酯、松香、硅烷偶联剂KH570、巴西棕榈蜡混匀后,于捏合机中150-160℃捏合30-35min,取出冷却,得树脂料备用;
(3)将改性填料、树脂料、以及其余原料混匀,双螺杆挤出机中160-175℃下挤出造粒即得。
本发明的有益效果:
本发明热熔胶采用新配方组合,不仅提高了热熔胶的耐寒性,同时增加了热熔胶接着强度,可以完全满足铅笔制造对热熔胶性能的要求,同时添加了一些抗菌物质,增加了抗菌的效果。
具体实施方式、
一种抗菌效果优异的铅笔制造用热熔胶,其是由下述重量(kg)的原料制得:松香30、C5石油树脂17、巴西棕榈蜡2、环氧硬脂酸辛酯1、三元已丙橡胶15、松香季戊四醇酯4、戊二酸2、硼酸2、脲醛树脂5、羧甲基玉米粉1、羟基磷灰石2、羊毛脂0.4、硬脂酸铝0.4、苯乙醇胺0.2、硅烷偶联剂KH570 1.5,复合改性树脂5;
所述的复合改性树脂由下述重量(kg)的原料制备而得:
酚醛树脂20、达玛树脂40、二氯化钙2、硼砂1、膨润土4、聚碳酸酯1、氰尿酸三聚氰胺1、石油磺酸钡0.5、乙二醇单甲醚0.2、抗氧剂626 1.7、椰子油脂肪酸二乙醇酰胺 2、山梨坦单油酸酯 0.1、单硬脂酸甘油酯 2、富马酸 1;
所述的复合改性树脂的制备方法为:
(1)将达玛树脂、二氯化钙、硼砂、膨润土、聚碳酸酯、氰尿酸三聚氰胺、石油磺酸钡混匀后,于捏合机中133℃捏合26min,取出冷却,得改性达玛树脂料备用;
(2)将改性达玛树脂料与其余原料混匀后,于捏合机中160℃捏合30min,取出冷却,即得。
所述的一种抗菌效果优异的铅笔制造用热熔胶,制备方法包括以下步骤:
(1)将羟基磷灰石于800℃下煅烧2小时,取出冷却后,破碎,加适量水,再加入戊二酸、硬脂酸铝,于60℃下搅拌1小时后,烘干,得改性填料备用;
(2)将C5石油树脂、环氧硬脂酸辛酯、松香、硅烷偶联剂KH570、巴西棕榈蜡混匀后,于捏合机中160℃捏合30min,取出冷却,得树脂料备用;
(3)将改性填料、树脂料、以及其余原料混匀,双螺杆挤出机中175℃下挤出造粒即得。
本实施例的热熔胶主要技术指标检测如下:
本实施例的热熔胶的表观粘度为5300MPa.s,剥离强度61N/2.5cm,初粘力达到5号钢球,开放时间39s,24小时热稳定性状稳定。
Claims (2)
1.一种抗菌效果优异的铅笔制造用热熔胶,其特征在于,其是由下述重量份的原料制得:松香20-30、C5石油树脂15-25、巴西棕榈蜡1-2、环氧硬脂酸辛酯1-2、三元已丙橡胶10-15、松香季戊四醇酯2-4、戊二酸1-2、硼酸1-2、脲醛树脂3-5、羧甲基玉米粉1-2、羟基磷灰石2-4、羊毛脂0.1-0.4、硬脂酸铝0.2-0.4、苯乙醇胺0.1-0.2、硅烷偶联剂KH570 1-2,复合改性树脂3-5;
所述的复合改性树脂由下述重量份的原料制备而得:
酚醛树脂10-20、达玛树脂30-40、二氯化钙1-2、硼砂1-2、膨润土2-4、聚碳酸酯1-2、氰尿酸三聚氰胺1-2、石油磺酸钡0.3-0.5、乙二醇单甲醚0.1-0.2、抗氧剂626 1-2、椰子油脂肪酸二乙醇酰胺 1-2、山梨坦单油酸酯 0.1-0.2、单硬脂酸甘油酯1-2、富马酸1-2;
所述的复合改性树脂的制备方法为:
(1)将达玛树脂、二氯化钙、硼砂、膨润土、聚碳酸酯、氰尿酸三聚氰胺、石油磺酸钡混匀后,于捏合机中120-140℃捏合20-30min,取出冷却,得改性达玛树脂料备用;
(2)将改性达玛树脂料与其余原料混匀后,于捏合机中150-160℃捏合20-30min,取出冷却,即得。
2.根据权利要求1所述的一种抗菌效果优异的铅笔制造用热熔胶,其特征在于:制备方法包括以下步骤:
(1)将羟基磷灰石于700-800℃下煅烧1-2小时,取出冷却后,破碎,加适量水,再加入戊二酸、硬脂酸铝,于60-80℃下搅拌1-2小时后,烘干,得改性填料备用;
(2)将C5石油树脂、环氧硬脂酸辛酯、松香、硅烷偶联剂KH570、巴西棕榈蜡混匀后,于捏合机中150-160℃捏合30-35min,取出冷却,得树脂料备用;
(3)将改性填料、树脂料、以及其余原料混匀,双螺杆挤出机中160-175℃下挤出造粒即得。